TEST CERTIFICATE Telefax: 2510 6298
CUSTOMER : ROTARY EQUIP PVT, LTD P.O No. REPL/GEMINI-622/21-2/PO Date: 4/10/2009
AMBERNATH /PO/041/09-10
Certified that good mentioned below meets requirements of ___SS 304____For Studs/Bolt and of ___SS 304______for Nuts.
CHEMICAL ANALYSIS
Size & Description Lot no. Qty. C% S% P% Si% Mn% Cr% Mo% Ni% V%
STUD
M 16 X 80MM LG SB-096 12 0.048 0.023 0.040 0.42 1.80 18.21 8.04
NUT
M 16 N-097 24 0.052 0.015 0.030 0.31 1.64 18.17 8.02
PHYSICAL TESTProof Load For Nut
RemarkLoad in KN Remarks
HEAT TREATMENT PROCESSQuenching Media
THREADS BOLT: IS : 4218 6g
NUT: IS : 4218 6h
JYOTI ENGINEERING WORKS 4th KURLA INDUSTRIAL ESTATE, NARAYAN NAGAR, GHATKOPAR (W), MUMBAI-4000086
CHALLEN NO. __ 280____ CERTIFICAT NO. __JEW-303
INVOICE NO.____280_____ Date: ___16/10/2009_
Heat No.
Size / Lot No.
Hardness RB
Yield Stress
Kg/mm2
(Mpa)
U.T.S. Kg/mm2 (Mpa)
Elongati -on %
Reducti -on
Area %
Hardness after 24 hours
Tempering
Hardening Temprature0 C Tempering Temp 0C
Remarks: SATISFACTORY. FOR JYOTI ENGINEERING WORKSInspected by: STAMPED AS JEW-304
TEST CERTIFICATE Telefax: 2510 6298
CUSTOMER : ROTARY EQUIP PVT, LTD P.O No. REPL/GEMINI/T-503/635-2 Date: 4/10/2009
AMBERNATH /PO/042/09-10
Certified that good mentioned below meets requirements of ___SS 316____For Studs/Bolt and of ___SS 316____for Nuts.
CHEMICAL ANALYSIS
Size & Description Lot no. Qty. C% S% P% Si% Mn% Cr% Mo% Ni% V%
HEX BOLT
M 16 X 40MM LG SB-147 1 0.047 0.025 0.032 0.35 1.39 16.36 2.26 10.27
M 12 X 50MM LG SB-137 12 0.034 0.021 0.038 0.33 1.39 16.40 2.19 10.48
NUT
M 12 N-153 24 0.065 0.009 0.034 0.47 1.20 16.45 2.25 10.02
PHYSICAL TESTProof Load For Nut
RemarkLoad in KN Remarks
HEAT TREATMENT PROCESSQuenching Media
THREADS BOLT: IS : 4218 6g
NUT: IS : 4218 6h
JYOTI ENGINEERING WORKS 4th KURLA INDUSTRIAL ESTATE, NARAYAN NAGAR, GHATKOPAR (W), MUMBAI-4000086
CHALLEN NO. __ 279____ CERTIFICAT NO. __JEW-302
INVOICE NO.____279_____ Date: ___16/10/2009_
Heat No.
Size / Lot No.
Hardness RB
Yield Stress
Kg/mm2
(Mpa)
U.T.S. Kg/mm2 (Mpa)
Elongati -on %
Reducti -on
Area %
Hardness after 24 hours
Tempering
Hardening Temprature0 C Tempering Temp 0C
Remarks: SATISFACTORY. FOR JYOTI ENGINEERING WORKSInspected by: STAMPED AS JEW-316
TEST CERTIFICATE Telefax: 2510 6298
CUSTOMER : CLEARSEP TECHNOLOGIES (I) PVT. LTD.P.O No. C17/BO/02 Date: 19/11/2009
BHANDUP(W), MUMBAI-400078.
Certified that good mentioned below meets requirements of ___S.S. 304____For Studs/Bolt and of ___S.S. 304___for Nuts.
CHEMICAL ANALYSIS
Size & Description Lot no. Qty. C% S% P% Si% Mn% Cr% Mo% Ni% V%
BOLT
EYE M16 X 90MM LGSB-107
6 0.07 0.025 0.036 0.47 1.37 18.33 9.17
HEX M16 X 50 MM LG 8 " " " " " " "
HEX M10 X 55MM LG
SB-104
4 0.01 0.017 0.041 0.56 1.45 19.12 10.04
ALL M10X20MM LG 2 " " " " " " "
HEX M08X 55MM LG 2 " " " " " " "
ALL M08X25MM LG 2 " " " " " " "
HEX M14 X 45MM LGSB-111
6 0.05 0.021 0.022 0.63 0.99 19.56 9.68
HEX M12 X 40 MM LG 4 " " " " " " "
EYE M24X155 MM LG SB-124 25 0.02 0.009 0.012 0.72 1.55 18.09 9.99
NUTM10 N-099 14 0.04 0.023 0.031 0.33 1.87 18.83 10.08
M08 N-103 2 0.08 0.017 0.023 0.56 1.66 18.97 10.34
M14 N-110 6 0.06 0.013 0.043 0.66 1.35 19.64 9.44
M16 N-119 8 0.07 0.026 0.030 0.86 1.49 18.98 8.77
M12 N-121 4 0.03 0.029 0.041 0.71 0.87 19.88 9.64
EYE M24 N-136 25 0.05 0.022 0.016 0.96 1.38 19.76 10.00
PHYSICAL TESTProof Load For Nut
RemarkLoad in KN Remarks
HEAT TREATMENT PROCESSQuenching Media
THREADS STUD: IS : 4218 6g.
NUT: IS : 4218 6h.
JYOTI ENGINEERING WORKS 4th KURLA INDUSTRIAL ESTATE, NARAYAN NAGAR, GHATKOPAR (W), MUMBAI-4000086
CHALLEN NO. __ 323____ CERTIFICAT NO. __JEW-330
INVOICE NO.____323_____ Date: ___10/12/2009_
Heat No.
Size / Lot No.
Hardness RB
Yield Stress
Kg/mm2
(Mpa)
U.T.S. Kg/mm2 (Mpa)
Elongati -on %
Reducti -on
Area %
Hardness after 24 hours
Tempering
Hardening Temprature0 C Tempering Temp 0C
Remarks: SATISFACTORY. FOR JYOTI ENGINEERING WORKS
Inspected by: STAMPED AS JEW-304
TEST CERTIFICATE Telefax: 2510 6298
CUSTOMER : ROTARY EQUIP PVT, LTD P.O No. REPL/GEMINI/T-503/42/09-10 Date: 4/10/2009
AMBERNATH
Certified that good mentioned below meets requirements of ___IS 1367 CL. 5.6____For Studs/Bolt and of ___IS 1367 CL. 5___for Nuts.
CHEMICAL ANALYSIS
Size & Description Lot no. Qty. C% S% P% Br% Mn% Cr% Mo% Ni% V%
BOLT
M 20 X 55MM LGSB-120
13 0.16 0.030 0.050 0.001
M 20 X 80MM LG 12 " " " "
M 16 X 65MM LG SB-123 9 0.44 0.050 0.030 0.002
M 12 X 55MM LGSB-119
24 0.32 0.040 0.020 0.001
M 12 X 40MM LG 6 " " " "
M 12 X 30MM LG 4 " " " "
M 10 X 20MM LG SB-125 4 0.22 0.020 0.050 0.003
NUT
M20 N-56 12 0.42 0.090 0.050
M16 N-57 9 0.19 0.120 0.032
M12 N-60 34 0.26 0.070 0.044
PHYSICAL TESTProof Load For Nut
RemarkLoad in KN Remarks
SB-120 83,84,85 312 21
SB-123 79,80,81 324 533 23
SB-119 90,90,91 327 540 21
SB-125 89,90,90 309 515 24
HV
N-56 160,161,162 154.40
N-57 199,200,200 96.60
N-60 140,141,142 51.40
HEAT TREATMENT PROCESSQuenching Media
THREADS BOLT: IS : 4218 6g
NUT: IS : 4218 6h
JYOTI ENGINEERING WORKS 4th KURLA INDUSTRIAL ESTATE, NARAYAN NAGAR, GHATKOPAR (W), MUMBAI-4000086
CHALLEN NO. __ 279____ CERTIFICAT NO. __JEW-302
INVOICE NO.____279_____ Date: ___16/10/2009_
Heat No.
Size / Lot No.
Hardness RB
Yield Stress
Kg/mm2
(Mpa)
U.T.S. Kg/mm2 (Mpa)
Elongati -on %
Reducti -on
Area %
Hardness after 24 hours
Tempering
517
Hardening Temprature0 C Tempering Temp 0C
Remarks: SATISFACTORY. FOR JYOTI ENGINEERING WORKSInspected by: STAMPED AS JEW-5.6 / 5