WELDING PROCEDURE
QUALIFICATION RECORD (WPQR)
WPQR No.: 2016-02 Rev.0 According to: NS-EN ISO 15614-1
Manufacturer: TH RØR-SVEIS AS Place and date of welding: Rygge, 05.07.2016 Project: All Drawing No.:
Requirements beyond standard / Purchasers spec. no.:
Sketch of joint: Material Specification, Delivery Condition:
I: TP316L/ 1.4404/ ASTM A270/ EN 10217-7
Heat no. 0444105, Welded tube, Pickled
II: TP316L/ 1.4404/ ASTM A270/ EN 10217-7
Heat no. 0444105, Welded tube, Pickled
Grade I C, % C eq % Grade II C, % C eq %
TP316L 0,020 NA TP316L 0,020 NA
Diameter and/or thickness, mm: OD 38,0 x WT 1,2
Welding process: 141 – Automatic (Orbital)
Welding position: PK - Rotated
Single-/double sided welding: Single Sided
WELDING CONSUMABLES
Index Consumable(s), trade name and manufacturer Classification
A N/A
WELDING PARAMETERS
Pass
No. Index
Diam.
mm
Gas shielding,
composition
Gas,
L/min
Current,
Polarity
Ampere,A
(Peak/Back)
Voltage,V
(Peak/Back)
Travelspeed
mm/min
Wire feed
m/min
Heat input
kJ/mm
1 - - 99,998%Ar 14 DC- 35,4
(54,9/15,9)
12,7
(15,6/9,7)
117 - 0,23
Program pass No’s. 1: Log no. 25, 27, 31, 33, 35 and 37 ; Pulse freq 3,2/ Pulse width 50
OTHER INFORMATION: Groove preparation : Machined Weaving, max. : No weaving
Cleaning : Methylated spirits
Gas shielding : Yara Praxair Argon 4.8 (99,998%Ar)
Prepurge 20 sec. and postpurge 20 sec.
Torch angle : 90°
Gas backing : Yara Praxair Argon 4.8 (99,998%Ar) Tungsten electrode : WC 20 (grey), Ø 2,4 mm
Pass No. 1: 10-11 L/min Gas cup size : Ø 9 mm
HEAT TREATMENT : Preheat min.: 20°C Interpass max.: N/A PWHT/Ageing: N/A Time, hr(s):
Heating/cooling rate: Others: Digital temp. control
WELDING CARRIED OUT BY: David Axelsson TEST PIECE MARKED: WPQR no. 2016-02, No’s 1-6
VISUAL INSPECTION AND NON-DESTRUCTIVE EXAMINATION:
Visual Inspection: ACCEPTED (IKM) Report No. 120-8919-16-VT-2
Dye Penetrant Inspection: ACCEPTED (IKM) Report No. 120-8919-16-PT-2-REV1
Radiographic Examination: ACCEPTED (IKM) Report No. 120-8919-16-RT-2-REV1
DESTRUCTIVE TESTING AND EXAMINATION: ACCEPTED Test Report No. 024336
TECHNICAL QUERY: N/A
SUPPLEMENTARY INFORMATION: Attachments: Weld Logs, Mat’cert, VT-/PT-/RT-/DT-reports
Welding equipment: Liburdi Dimetrics PTW 160
Certified that test welds prepared,
welded and tested satisfactorily in
accordance with the requirements of
the code/testing standard indicated
above.
Place and date Oslo, 22.07.2016
Stamp
Examiners name and sign.
Jarle Børrud
Teknologisk Institutt as SK-0746 b Materials Technology Page 1 of 1
WELD LIMITS
LIBURDI DIMETRICS CORPORATION
Job Number: Site:
Material: Operator:
Diameter: Wall Thickness:
Electrode Type: Electrode Diameter:
Shielding Gas Type: Shielding Gas Flow:
Backing Gas Type: Backing Gas Flow:
QA REPORT
SCHED ID: 3800 DATE: 5/7/2016
HEAD TYPE: 5002V TIME: 11:51:27
LOG NUMBER: 25
WELD NUMBER: 2942
ERROR FAULT VOLTS
PRI AMPS: 160.0 160.0 LOW HIGH
BKG AMPS: 160.0 160.0 6.0 50.0
TRAVEL: 25,4 25,4
SEGMENTSEG TIME
SLOPE TIME
PULSE FREQ
PULSE WIDTH
PRI AMPS
BKG AMPS
PRI TRAV
BKG TRAV
PRI VOLTS
BKG VOLTS
1 16.7 0.0 3.2 50 54.7 16.4 2,66 2,66
16.7 54.9 15.9 2,59 2,69 15.5 10.1
2 14.3 0.0 3.2 50 52.7 16.4 2,66 2,66
14.3 52.8 16.0 2,62 2,69 15.1 10.1
3 14.3 0.0 3.2 50 50.6 16.4 2,66 2,66
14.3 50.8 16.0 2,62 2,67 14.8 10.0
4 15.9 0.0 3.2 50 48.5 16.4 2,66 2,66
15.9 48.7 16.0 2,62 2,67 14.3 9.9
Liburdi Dimetrics Europe
The Netherlands
[email protected] www.liburdi.com
Side 1 av 1
08.07.2016file:///F:/TH%20RØR-SVEIS%20AS/ORBITAL%20SVEISEMASKIN/Logg%20Sve...
WELD LIMITS
LIBURDI DIMETRICS CORPORATION
Job Number: Site:
Material: Operator:
Diameter: Wall Thickness:
Electrode Type: Electrode Diameter:
Shielding Gas Type: Shielding Gas Flow:
Backing Gas Type: Backing Gas Flow:
QA REPORT
SCHED ID: 3800 DATE: 5/7/2016
HEAD TYPE: 5002V TIME: 12:00:48
LOG NUMBER: 27
WELD NUMBER: 2944
ERROR FAULT VOLTS
PRI AMPS: 160.0 160.0 LOW HIGH
BKG AMPS: 160.0 160.0 6.0 50.0
TRAVEL: 25,4 25,4
SEGMENTSEG TIME
SLOPE TIME
PULSE FREQ
PULSE WIDTH
PRI AMPS
BKG AMPS
PRI TRAV
BKG TRAV
PRI VOLTS
BKG VOLTS
1 16.7 0.0 3.2 50 54.7 16.4 2,66 2,66
16.7 54.9 16.0 2,59 2,69 15.6 10.2
2 14.3 0.0 3.2 50 52.7 16.4 2,66 2,66
14.3 52.9 16.0 2,59 2,69 15.2 10.1
3 14.3 0.0 3.2 50 50.6 16.4 2,66 2,66
14.3 50.8 16.0 2,59 2,69 14.8 10.1
4 15.9 0.0 3.2 50 48.5 16.4 2,66 2,66
15.9 48.7 16.0 2,59 2,69 14.3 10.0
Liburdi Dimetrics Europe
The Netherlands
[email protected] www.liburdi.com
Side 1 av 1
08.07.2016file:///F:/TH%20RØR-SVEIS%20AS/ORBITAL%20SVEISEMASKIN/Logg%20Sve...
WELD LIMITS
LIBURDI DIMETRICS CORPORATION
Job Number: Site:
Material: Operator:
Diameter: Wall Thickness:
Electrode Type: Electrode Diameter:
Shielding Gas Type: Shielding Gas Flow:
Backing Gas Type: Backing Gas Flow:
QA REPORT
SCHED ID: 3800 DATE: 5/7/2016
HEAD TYPE: 5002V TIME: 12:23:49
LOG NUMBER: 31
WELD NUMBER: 2948
ERROR FAULT VOLTS
PRI AMPS: 160.0 160.0 LOW HIGH
BKG AMPS: 160.0 160.0 6.0 50.0
TRAVEL: 25,4 25,4
SEGMENTSEG TIME
SLOPE TIME
PULSE FREQ
PULSE WIDTH
PRI AMPS
BKG AMPS
PRI TRAV
BKG TRAV
PRI VOLTS
BKG VOLTS
1 16.7 0.0 3.2 50 54.7 16.4 2,66 2,66
16.7 54.9 16.0 2,59 2,69 15.5 10.1
2 14.3 0.0 3.2 50 52.7 16.4 2,66 2,66
14.3 52.9 16.0 2,59 2,69 15.2 10.1
3 14.3 0.0 3.2 50 50.6 16.4 2,66 2,66
14.3 50.8 16.0 2,59 2,69 14.8 10.0
4 15.9 0.0 3.2 50 48.5 16.4 2,66 2,66
15.9 48.7 16.0 2,59 2,69 14.3 9.9
Liburdi Dimetrics Europe
The Netherlands
[email protected] www.liburdi.com
Side 1 av 1
08.07.2016file:///F:/TH%20RØR-SVEIS%20AS/ORBITAL%20SVEISEMASKIN/Logg%20Sve...
WELD LIMITS
LIBURDI DIMETRICS CORPORATION
Job Number: Site:
Material: Operator:
Diameter: Wall Thickness:
Electrode Type: Electrode Diameter:
Shielding Gas Type: Shielding Gas Flow:
Backing Gas Type: Backing Gas Flow:
QA REPORT
SCHED ID: 3800 DATE: 5/7/2016
HEAD TYPE: 5002V TIME: 12:28:44
LOG NUMBER: 33
WELD NUMBER: 2950
ERROR FAULT VOLTS
PRI AMPS: 160.0 160.0 LOW HIGH
BKG AMPS: 160.0 160.0 6.0 50.0
TRAVEL: 25,4 25,4
SEGMENTSEG TIME
SLOPE TIME
PULSE FREQ
PULSE WIDTH
PRI AMPS
BKG AMPS
PRI TRAV
BKG TRAV
PRI VOLTS
BKG VOLTS
1 16.7 0.0 3.2 50 54.7 16.4 2,66 2,66
16.7 54.9 16.0 2,59 2,69 15.4 10.0
2 14.3 0.0 3.2 50 52.7 16.4 2,66 2,66
14.3 52.9 16.0 2,59 2,69 15.1 10.0
3 14.3 0.0 3.2 50 50.6 16.4 2,66 2,66
14.3 50.8 16.0 2,59 2,69 14.7 9.9
4 15.9 0.0 3.2 50 48.5 16.4 2,66 2,66
15.9 48.7 16.0 2,62 2,67 14.3 9.9
Liburdi Dimetrics Europe
The Netherlands
[email protected] www.liburdi.com
Side 1 av 1
08.07.2016file:///F:/TH%20RØR-SVEIS%20AS/ORBITAL%20SVEISEMASKIN/Logg%20Sve...
WELD LIMITS
LIBURDI DIMETRICS CORPORATION
Job Number: Site:
Material: Operator:
Diameter: Wall Thickness:
Electrode Type: Electrode Diameter:
Shielding Gas Type: Shielding Gas Flow:
Backing Gas Type: Backing Gas Flow:
QA REPORT
SCHED ID: 3800 DATE: 5/7/2016
HEAD TYPE: 5002V TIME: 12:33:40
LOG NUMBER: 35
WELD NUMBER: 2952
ERROR FAULT VOLTS
PRI AMPS: 160.0 160.0 LOW HIGH
BKG AMPS: 160.0 160.0 6.0 50.0
TRAVEL: 25,4 25,4
SEGMENTSEG TIME
SLOPE TIME
PULSE FREQ
PULSE WIDTH
PRI AMPS
BKG AMPS
PRI TRAV
BKG TRAV
PRI VOLTS
BKG VOLTS
1 16.7 0.0 3.2 50 54.7 16.4 2,66 2,66
16.7 54.9 15.9 2,59 2,69 15.5 10.0
2 14.3 0.0 3.2 50 52.7 16.4 2,66 2,66
14.3 52.9 15.9 2,59 2,69 15.1 10.0
3 14.3 0.0 3.2 50 50.6 16.4 2,66 2,66
14.3 50.8 15.9 2,59 2,69 14.7 9.8
4 15.9 0.0 3.2 50 48.5 16.4 2,66 2,66
15.9 48.7 15.9 2,62 2,67 14.2 9.7
Liburdi Dimetrics Europe
The Netherlands
[email protected] www.liburdi.com
Side 1 av 1
08.07.2016file:///F:/TH%20RØR-SVEIS%20AS/ORBITAL%20SVEISEMASKIN/Logg%20Sve...
WELD LIMITS
LIBURDI DIMETRICS CORPORATION
Job Number: Site:
Material: Operator:
Diameter: Wall Thickness:
Electrode Type: Electrode Diameter:
Shielding Gas Type: Shielding Gas Flow:
Backing Gas Type: Backing Gas Flow:
QA REPORT
SCHED ID: 3800 DATE: 5/7/2016
HEAD TYPE: 5002V TIME: 12:40:09
LOG NUMBER: 37
WELD NUMBER: 2954
ERROR FAULT VOLTS
PRI AMPS: 160.0 160.0 LOW HIGH
BKG AMPS: 160.0 160.0 6.0 50.0
TRAVEL: 25,4 25,4
SEGMENTSEG TIME
SLOPE TIME
PULSE FREQ
PULSE WIDTH
PRI AMPS
BKG AMPS
PRI TRAV
BKG TRAV
PRI VOLTS
BKG VOLTS
1 16.7 0.0 3.2 50 54.7 16.4 2,66 2,66
16.7 54.9 15.9 2,59 2,69 15.5 10.0
2 14.3 0.0 3.2 50 52.7 16.4 2,66 2,66
14.3 52.8 15.9 2,59 2,69 15.1 9.9
3 14.3 0.0 3.2 50 50.6 16.4 2,66 2,66
14.3 50.7 15.9 2,59 2,69 14.7 9.9
4 15.9 0.0 3.2 50 48.5 16.4 2,66 2,66
15.9 48.7 15.9 2,59 2,69 14.3 9.8
Liburdi Dimetrics Europe
The Netherlands
[email protected] www.liburdi.com
Side 1 av 1
08.07.2016file:///F:/TH%20RØR-SVEIS%20AS/ORBITAL%20SVEISEMASKIN/Logg%20Sve...
VT
CLIENT / KUNDETH Rør-Sveis AS
CLIENT O.NO / KUNDE O.NRWPQR 12/7-2016
DATE OF TESTING / KONTROLLDATO2016-07-12
REPORT NO. / RAPPORT NR.120-8919-16-VT-2
PAGE / SIDE1 of/av 1
DRAWING NO. / TEGNING NO.-
PLACE OF WORK / KONTROLLSTEDLarvik
OPERATOR / OPERATØRKjartan Sundet
ATTACHMENT / VEDLEGG0
OBJECT / KONTROLL AVWPQRno. 2016-02
PROCEDURE / PROSEDYREBPI-01.01.01 ISO 17637
REV EXTENT OF TESTING / KONTROLLOMFANG100%
ACCEPTANCE STANDARD / AKSEPTSTANDARDISO 15614-1
COMMENTS / KOMMENTARERVT inspection was done on pipe nr: 1-2-3-4-5 and 6.
Accepted according to standard
REPAIRS MARKED ON / REPARASJONER AVMERKET PÅOBJECT / OBJEKT SKETCH / SKISSE
N3 NAME CERT. NO. / N3 NAVN SERT. NR.()
N2 NAME CERT. NO. / N2 NAVN SERT. NR.Kjartan Sundet (8900)
OPERATOR NAME CERT. NO. / OPERATØR NAVN SERT. NR.Kjartan Sundet (8900)
APPROVED / GODKJENT DATO: APPROVED / GODKJENT DATO:2016-07-12Approved / Godkjent
OPERATOR / OPERATØR DATO:2016-07-12
PT
CLIENT / KUNDETH Rør-Sveis AS
CLIENT O.NO / KUNDE O.NRWPQR 12/7-2016
DATE OF TESTING / KONTROLLDATO2016-07-12
REPORT NO. / RAPPORT NR.120-8919-16-PT-2-REV1
PAGE / SIDE1 of/av 1
DRAWING NO. / TEGNING NO.-
PLACE OF WORK / KONTROLLSTEDLarvik
OPERATOR / OPERATØRKjartan Sundet
ATTACHMENT / VEDLEGG0
OBJECT / KONTROLL AVWPQR no. 2016-02
PROCEDURE / PROSEDYREEN ISO 3452-1
REV EXTENT OF TESTING / KONTROLLOMFANG100%
ACCEPTANCE STANDARD / AKSEPTSTANDARDEN-ISO 15614-1
MATERIAL TYPE / MATERIALTYPESS
SURFACE / OVERFLATESom sveist
GROOVE / FUGEGEOMETRIBW
WELDING PROCESS / SVEISEPROSESSN/A
PENETRANT TYPE / PENETRANTTYPEBycotestBATCH / PARTI 140405
FLUORRESCENT / FLUORISERENDEYES / JA ✔ NO / NEI
APPLICATION METHOD / PÅFØRINGSMETODESpray
CLEANER TYPE / FJERNER TYPEBycotest WATER / VANN EMULSIFIER / EMULGATOR ✔ SOLVENT / LØSNINGSMIDDELDEVELOPER TYPE/ FREMKALLER TYPEBycotest D 30 A 1. DRY POWDER / TØRRPULVER 3. SUSPENSION IN WATER / OPPSLEMMET I VANNBATCH / PARTI 140707 2. SOLUTION IN WATER / OPPLØST I VANN ✔ 4. POWDER IN VOLATILE SOLVENT / PULVER I FLYKTIG VÆSKE (SPRAY)PENETRATION TIME / PENETRERINGSTID20 MIN.
DEVELOPING TEST TIME / FREMKALLINGSTID20 MIN.
OBJECT TEMPERATURE /OBJEKTTEMPERATUR20 °C
MATERIAL DIMENSION / MATERIAL DIMENSJON38X1,2EQUIPMENT / UTSTYRBRUSHTEST RESULTS - REMARKS / RESULTATER - BEMERKNINGERPT was done on pipe nr 1-2-3-4-5 and 6
no indication was found during the test.
REPAIRS MARKED ON / REPARASJONER AVMERKET PÅOBJECT / OBJEKT SKETCH / SKISSE
N3 NAME CERT. NO. / N3 NAVN SERT. NR.()
N2 NAME CERT. NO. / N2 NAVN SERT. NR.Kjartan Sundet (8900)
OPERATOR NAME CERT. NO. / OPERATØR NAVN SERT. NR.Kjartan Sundet (8900)
APPROVED / GODKJENT DATO: APPROVED / GODKJENT DATO:2016-07-12Approved / Godkjent
OPERATOR / OPERATØR DATO:2016-07-12
RT
CLIENT / KUNDETH Rør-Sveis AS
CLIENT O.NO / KUNDE O.NRWPQR 12/7-2016
DATE OF TESTING / KONTROLLDATO2016-07-12
REPORT NO. / RAPPORT NR.120-8919-16-RT-2-REV1
PAGE / SIDE1 of/av 1
DRAWING NO. / TEGNING NO.-
PLACE OF WORK / KONTROLLSTEDLarvik
OPERATOR / OPERATØRKjartan Sundet
ATTACHMENT / VEDLEGG0
OBJECT / KONTROLL AVWPQR no. 2016-02
PROCEDURE / PROSEDYREBPI-01.08.03 RT ISO 17636
REV EXTENT OF TESTING / KONTROLLOMFANG100%
ACCEPTANCE STANDARD / AKSEPTSTANDARDEN-ISO-15614-1
MATERIAL TYPE / MATERIALTYPESS
SURFACE / OVERFLATESom sveist
GROOVE / FUGEGEOMETRIBW
WELDING PROCESS / SVEISEPROSESSIngen
EQUIPMENT / UTSTYRX-RAY TUBE / RØNTGENRØRCP 100 KV
EQUIPMENT / UTSTYRISOTOPE / ISOTOP
Ir 192 Co 60 Se 75 Yt 169 IngenFOCAL SPOT SIZE / BRENNFLEKK3,0x3,0
ACTIVITY / AKTIVITETGbq,Ci
EXP. DATA /EKS. DATA
A B C DTUBE/RØR VOLT kV FILMFOCUS DISTANCEFILMFOKUS AVSTAND mm 440 EXP.TIME/EKSP. TIME mAmin. Cimin. 3mAmin
I.Q.I SOURCE SIDE/KILDE SIDESOURCE SIDE/KILDESIDE
✔ FILM SIDE /FILMSIDE
RADIATION SOURCE POSITION / KILDEPOSISJONTECHNIQUE / TEKNIKK
1 2 3 4 5 6 7
TYPE OF I.Q.I. / I.Q.I. TYPEW 13 FE
DENSITY / SVERTNING2,5-3,7
Ug0,2
INTENSIFYING SCREENS / FOILER0,027
FILM TYPE / FILMTYPED3
WELD NOSVEIS NR
DATE AND TIMEDATO KL.
DIA. PIPEDIA RØR
FILM LOCATIONFILM PLASSERING
SENSITIVITYFØLSOMHET
%WIRE NR
WELDERSVEISER
MATERIALTHICKNESSTYKKELSE
mm
EVALUATIONBEDØMMELSE
DEFECT LOCATIONFEILENS PLASSERING
REMARKSBEMERKNINGER
EXP.DATAA-D
TECH.TEGN.
1-7
1 12/7-2016 38mm ABC W17 1,2 Accepted A 4
2 12/7-2016 38mm ABC W17 1,2 Accepted A 4
3 12/7-2016 38mm ABC W17 1,2 Accepted A 4
4 12/7-2016 38mm ABC W17 1,2 Accepted A 4
5 12/7-2016 38mm ABC W17 1,2 Accepted A 4
6 12/7-2016 38mm ABC W17 1,2 Accepted A 4
NS-EN ISO 6520-1:2007Kolonne gir et tresifret referansenummer for hovedgruppen av uregelmessigheten og et firesifret referansenummer for undergrupper. Colum gives a three – figure reference number for the maingroup of the imperfection and a four–figure reference number for sub–terms.Referanse no: - Reference No:100/1000=Sprekk - Crack 200/2000=Hulrom - Cavity 300/3000=Fast inneslutting - Solid inclusion 400/4000=Bindefeil og manglende gjennomsveising - Lack of fusion and penetration500/5000=Uregelmessig form - Imperfect shape 600/6000=Andre uregelmessigheter - Miscellaneous imperfection.COMMENTS / KOMMENTARER.
REPAIRS MARKED ON / REPARASJONER AVMERKET PÅ OBJECT / OBJEKT SKETCH / SKISSE
N3 NAME CERT. NO. / N3 NAVN SERT. NR.()
N2 NAME CERT. NO. / N2 NAVN SERT. NR.Kjartan Sundet (8900)
OPERATOR NAME CERT. NO. / OPERATØR NAVN SERT.NR.Kjartan Sundet (8900)
APPROVED / GODKJENT DATO: APPROVED / GODKJENT DATO:2016-07-12Approved /Godkjent
OPERATOR / OPERATØR DATO:2016-07-12
TEST 006
MATERIAL TESTING Report No.: 024336 Page 1 of 3
Client :
TH RØR-SVEIS AS Material :
Other details:
I/II: TP316L/ 1.4404/ ASTM A270/ EN 10217-7 - Heat no: 0444105
Augerødveien 15 1591 Sperrebotn
Welded tube, Pickled
Client Contact : Torgeir Hansen Dimensions : I/II: OD 38,00mm x WT 1,20mm
Order No. : Other Info : WPQR no. 2016-02 Specification : NS-EN ISO 15614-1 141-Automatic (Orbital), Butt weld
Sampling by TI: No Uncertainty is given upon request Applicable tests: Chemical / Tensile / Charpy Impact / Hardness
(whichever tested)
Accredited test: Vickers hardness test NS-EN ISO 6507-1:2006 Table 1 Tensile test
CROSS-WELD TENSILE TEST acc. to: NS-EN ISO 6892-1:2009 method B Rate of stressing: 10 MPa/s
Test Ident
Dimension (mm)
So mm2
Fmax N
Rm MPa
Remarks
1 of 2 Full-size specimen 138.73 76.85 554 Fracture in WM 2 of 2 Full-size specimen 138.73 76.41 551 Fracture in WM
Requirements: At ambient temp. min. NA 490 max. NA 690 LC = 200 mm
Date
21.07.2016
Test Responsible
Petter Dyrnes
Authorized Signature
Department Manager
Copying of this report is only authorised when copied in its complete form. Eventual test results apply only for the tested objects. SK-0750 c
Teknologisk Institutt as
Postadresse: Pb. 141 Økern 0509 Oslo Besøksadresse: Kabelgaten 2, 0580 Oslo
Telefon: 22 86 50 00 Telefaks: 22 72 45 02 E-post: [email protected] Web: www.teknologisk.no
Org.nr. 942 340 680
Kongsberg: Pb. 1019, NO-3601 Kongsberg Stavanger: Forusbeen 10, NO-4033 Stavanger Haugesund: Pb. 93, NO-4299 Avaldsnes Bergen: Pb. 23, NO-5346 Ågotnes
21.07.2016
MATERIAL TESTING Report No.: 024336 Page 2 of 3
Table 2 Bend test
BEND TEST acc. to: NS-EN ISO 5173:2010 Transverse Bend Test / Testing with a former Test
Ident. Dimensions
mm Bending
Angle Former
Diameter, mm
Distance between
Rollers, mm
Results Comments
Face 1 5.0 x 1.20 180 4.8 9.3 Accepted Face 2 5.0 x 1.20 180 4.8 9.3 Accepted
Root 1 5.0 x 1.20 180 4.8 9.3 Accepted
Root 2 5.0 x 1.20 180 4.8 9.3 Accepted
Table 3 Hardness test
CROSS-SECTION HARDNESS TEST acc. to: NS-EN ISO 9015-1:2011 / NS-EN ISO 6507-1:2006 Test Method: Vickers, HV5
Indentations 6 and 10, close to fusion line BM HAZ WM HAZ BM
◇◇◇ ◇◇◇ ◇◇◇ ◇◇◇ ◇◇◇ 1 / 2 / 3 4 / 5 / 6 7 / 8 / 9 10 / 11 / 12 13 / 14 / 15
RESULTS, HV5: BM HAZ WM HAZ BM
Mid-thickness
1 223 4 186 7 170 10 166 13 209 2 220 5 178 8 171 11 183 14 212 3 221 6 156 9 169 12 188 15 210
Requirements: NA
21.07.2016
MATERIAL TESTING Report No.: 024336 Page 3 of 3
Table 4 Macro
MACROSTRUCTURE acc. to: NS-EN ISO 17639:2013 / ASTM E3-11/E340-13/NS-EN ISO 5817:2014
One (1) cross-section of the weld metal, heat affected zone and base metal was carried out and prepared. The macro-section was examined up to 20X magnifications. Etchant: Kallings OBSERVATIONS: The macro satisfies the specified requirements.
MACRO 1 1 division = 1 mm