tpe 210-s - stratasys · alm tpe 210-s: 02.04.2013 advanced laser materials, llc l tel:...
TRANSCRIPT
For reference use only. Actual properties may vary signi�cantly from those listed above based on processing parameters, operating conditionsand end use applications. The above properties were based on virgin ALM TPE 210-S using normal processing parameters on a 2500+ platformas outlined in the ALM Material Processing Guide. Advanced Laser Materials, LLC makes no warranties of materials for any application, nor does it make a warranty of any type, expressed or implied, but not limited to, the warranties of merchantability for a particular purpose.
TPE 210-SHIGHLIGHTS
• Soft, white parts out of the machine
• Extreme elongations achievable without permanent deformation
• Easy to infiltrate to obtain maximumproperties
• 100% recyclable
APPLICATIONS
• Footwear prototyping
• Automotive gaskets and seals
• Cushioning applications
MATERIAL SPECIFICATIONS
TYPICAL PHYSICAL PROPERTIES - Unin�ltratedPROPERTY Color/Appearance
Bulk Density
Elongation at Break
Flexural Modulus (-40 C)
Flexural Modulus (23 C)
Flexural Modulus (100 C)
Initial Tear Resistance, Die C, 23 C
Abrasion Resistance, Taber H-18 Wheel
Shore Hardness, Shore “A”
Tensile Modulus
Average Particle Size (D50) Particle Size Range (D10-D90)
Sintered Part Density
TEST METHODVisual
ASTM D1895
ASTM D638
ASTM D790
ASTM D790
ASTM D790
ASTM D624
ASTM D4060
ASTM D2240
ASTM D638
Laser DiffractionLaser Diffraction
U.S. STANDARDWhite
0.214 oz/in3
110%
3,336 psi
1,885 psi
435 psi
7.4 lbf
0.012 oz
40
1,160 psi
0.003 inches0.001 - 0.005 inches
0.595 oz/in 1.03 g/cm
METRICWhite
0.37 g/cm 3
110%
23 MPa
13 MPa
3 MPa
33 N
535 mg
40
8 MPa
85 microns20 - 130 microns
ALM TPE 210-S: 02.04.2013
Advanced Laser Materials, LLC l Tel: 254.773.3080 l Fax: 254.773.30843115 Lucius McCelvey, Temple, TX 76504 l www.alm-llc.com
• Ideal for applications requiring softerparts with excellent ductility andsurface finish.
ASTM D792 33