Trends for Hardfacing Wolfgang Wahl, Stuttgart 1. General Hardfacing is applied in cases where the surface of engine parts is being subject to abrasion by wear, corrosion or heat.
Rev: 1.0 6
VAUTIDf i g h t s w e a r
R
GeneralDefinition Hard-Surfacing (DIN 1910)
Characteristics DescriptionHard-surfacing of linings Hard-surfacing with material that is- Hardfacing preferably more wear-resistant than
the base material.
Hard-surfacing of platings Hard-surfacing with material which is - Cladding chemically more persistent than the
base material
Hard-surfacing of buffer layers Hard-surfacing with material which provides- Buffering a wear resistant link between different
materials
According to the definition hardfacing is applied when the surface is going to be damaged by wear due to hard minerals. This happens in all domains of mechanical processing, where processes are realised at room temperature or increased temperatures, such as in crushing, conveying, mixing and separating in the field of mining, steel and iron industry, cement industry, coal power plants, overground and underground working, recycling and environmental protection. In chemical industry it is applied in areas of sharp mineral dressing. The objective of hardfacing according to DIN 50320
Rev: 1.0 7
VAUTIDf i g h t s w e a r
R
Wear Systemin accordance with DIN 50320
is to surface a layer onto the basebody, which is most beneficially resisting to the wear-causing mineral. The meaning of hardsurfacing did significantly increase in the course of the last 10 years, as standstills do become more and more expensive for big factories, due to increased wages and salaries, but also for reasons of networking. Layers of between 2 mm and 200 mm thickness can be produced
Rev: 1.0 9
VAUTIDf i g h t s w e a r
RHard-surfacing procedure
Oxygen-ethylene weldingManual hardfacing with stick electrodesMIG-MAG weldingTIG-weldingPTA-procedure Sub-Arc welding Electroslag weldingSpecial welding procedures
by application of the different hardfacing procedures, whereas the fusion-efficiency rate can vary between 0,5 and 50 kg/hour, with fusion penetrations of between 0,5 mm and 10 mm. The welding procedures can be differentiated by the intensity of mixture with the base body, which is usually increasing along with an increasing fusion efficieny rate. Nearly all kinds of weldable materials can be hardfaced and mostly all types of known wear-resistant metals in combination can be used as hardfacing materials. Ceramic materials, which can only be coated by spraying-on thin layers, cannot be hardfaced. 2. Trends for Welding 2.1 Stick Electrodes and Filler wires
Rev: 1.0 12
VAUTIDf i g h t s w e a r
RMixer blade lined with VAUTID-Stellite
Stick electrodes will be further used, before all for reparation in built-in condition, as they can be processed not only in tub position. Anyhow, their low fusion-efficiency rate, which results in costs of more than 50 Euro per kg, is a disadvantage. Filler wires can be regarded as an absolutely necessary welding process, with regard to a consumption per buyer of more than 1 ton of material per year. The fusion penetration per burner is usually between 3 – 6 kg per hour, so that the costs per kg welding material are decreased to an amount of about 20 Euro per kg. But this processing can almost only be easily used in tub position. This means, that the engine parts to be protected have to be moved accordingly, so that welding in built-in condition is often impossible. The results of fusion efficiencies of the latest developments in the sector of filler wires where up to 15 kg per hour, so that the costs per kg welding material decreased to 10 – 15 Euro per kg. It is most important for tubular-wire welding that removal by suction is made very carefully. 2.2 Plasmapowder-Hardfacing
Rev: 1.0 13
VAUTIDf i g h t s w e a r
R
PTA welding with powdercontaining an extreme high share in carbide
Trends in the welding processPTA Welding
Plasmapowder-hardfacing made a triumphant march through hardfacing of valves for the motor car industry. A mechanical hardsurfacing at permanent operation was achieved, with very slight mixtures and good surface qualities, so that the material consumption was only half compared to the demand for continuous casting sticks as used before. This procedure is also qualified for tungsten carbides, which are not added into the metal arc, but behind it, in order to have them gently inserted into the melt, without their dissolution, what is a second advantage. Thus a higher rate of tungsten carbides is achieved, which means a significantly better resistance to abrasive minerals compared to usual chromium carbides. This processing, as a special procedure, is widely applied at Rheinbraun, but also for processing of oil sands and in oil mining. The trend for this area has not yet become obvious. 2.3 Submerged hardfacing Submerged welding processes give us the chance of achieving fully mechanically even higher fusion efficiencies, compared to tubular-wire welding with open metal-arc, which often do achieve between 8 – 10 kg.
Rev: 1.0 14
VAUTIDf i g h t s w e a r
R
Trends in the welding processSubmerged-arc welding of rotor disks and impellers
But when applying this process, using wire or band, it is nearly impossible to produce high-quality hardfacings. Therefore this process, within the scope of hardfacing, is meant for big construction parts, such as cones of blast furnaces, but also for regenerating of earth shifting units, especially in the Far East, whereas in Europe it seems to be more economic to use new parts, which are scrapped after their wear reserve has been exhausted. Hardfacing is a wage-intensive process, which is only to be applied, where operation costs in Western European countries, where wages costs are high, can really be decreased by applying this technology, or when operativeness cannot be guaranteed in another way.
2.4 Application of prefabricated hardfaced plates Instead of hardfacing the part by own production, semifinished hardfaced products are more and more used.
Rev: 1.0 15
VAUTIDf i g h t s w e a r
R
Trends in the welding processManufacturing hardfaced plates
Hard-surfacing with automated welding lines
These polyburner-technology plates with a high fusion-efficiency rate can be produced much more economically than having them manufactured by own production. Constuction parts, such as hoppers, chutes, screens, tubes, fans, separators or others, can be manufactures by plasma-cutting and forming of such plates. 3. Trends for Welding Fillers 3.1 Increased Application of titanium-carbide containing martensitic alloys The main application of hardsurfacing was formerly the use of martensitic alloys with 400 – 600 Brinell, but nowadays such material contain titanium-carbide fortifications, although the removal of slag is quite difficult when using such addings. Especially when using these materials, or those where niobium is added to martensitic alloys, the application is recommended for wear problems of so-called high-pressure rollers in a wide range.
Rev: 1.0 17
VAUTIDf i g h t s w e a r
R
Trends in welding fillers Alloy containing titanium carbide (matrix)
Titanium caribide in a martensiticmatrix1,8%C,2%Mn,7%Cr,0,6%Mo,5%Ti, remainder Fe (VAUTID-Delta)
Recommended for combinedimpact and abrasive wear
3.2 Use of highly-chromium containing materials with higher carbon contents then those of filler wires Compared to formerly used hardfacing materials as filler wires, normally of the alloy group 10 with 4,5% C and 30% Cr, there is a clear trend towards higher alloyed filler wires to be seen, as only when using these filler wires as a second and third layer a significantly longer lifetime will be achieved. In general such materials do contain 5,5% C, 20% Cr and 7% niobium, at higher temperatures they do also contain molybdenum and tungsten.
Rev: 1.0 18
VAUTIDf i g h t s w e a r
R
Trends in welding fillersVAUTID-145
In a certain range these materials can also be applied for higher temperatures up to ca. 750° C, but they will lose their wear-resistance at higher temperatures due to transformation of the matrix. 3.3 Tungsten-carbide containing hardfacings In former times such materials were only used in oil-mining due to reasons of costs, whereas their application
Rev: 1.0 19
VAUTIDf i g h t s w e a r
R
NiCrB matrix containing compositetungsten carbidesGrain size: 1-2 mm
VAUTID-Ultra III-recommended for extreme wearby abrasion and corrosion
Matrix: 500 HVCarbide: 2000 HV
Iron matrix containing composite tungsten carbidesGrain size: 0,5 mm
VAUTID-Ultra I-recommended for extremeabrasive wear
Matrix: 650 HVCarbide: 2000 HV
Iron matrix containing composite tungsten carbidesGrain size: 0,5 mm
VAUTID-Ultra II-recommended for extremeabrasive wear
Matrix: 850 HVCarbide: : 2000 HV
Trends in welding fillers Welding fillers containing tungsten carbides
Matrix Ultra IIIMatrix Ultra I Matrix Ultra II
did meanwhile considerably increase, not only for stick electrodes, but also for filler wires and PTA-welding and special-welding procedures, as the lifetime is significantly higher, whereas the wages costs are the same.
3.4 Replacement of cobalt-containing hardfacings by iron-containing hardfacing It is not quite a long time ago that valves have been hardfaced by nickel-containing Stellites.
Rev: 1.0 19
VAUTIDf i g h t s w e a r
R
NiCrB matrix containing compositetungsten carbidesGrain size: 1-2 mm
VAUTID-Ultra III-recommended for extreme wearby abrasion and corrosion
Matrix: 500 HVCarbide: 2000 HV
Iron matrix containing composite tungsten carbidesGrain size: 0,5 mm
VAUTID-Ultra I-recommended for extremeabrasive wear
Matrix: 650 HVCarbide: 2000 HV
Iron matrix containing composite tungsten carbidesGrain size: 0,5 mm
VAUTID-Ultra II-recommended for extremeabrasive wear
Matrix: 850 HVCarbide: : 2000 HV
Trends in welding fillers Welding fillers containing tungsten carbides
Matrix Ultra IIIMatrix Ultra I Matrix Ultra II
But meanwhile there is a clear trend towards iron-containing materials, which are, as a consequence, cheaper. 4. Trends for Applications 4.1 Hardfacing of Strips and Disks for Coal- and Cement-Crushing Generally such strips do consist of materials which are known from the literature as being unweldable, having a high carbon-, chromium- or nickel-content. Anyhow this is the second-largest application worldwide
Rev: 1.0 11
VAUTIDf i g h t s w e a r
R
Ni Hard VAUTID 100
Lösche mill: Roller after a running time of 4000 h
Rev: 1.0 26
VAUTIDf i g h t s w e a r
R
Trends in applications - South America Worn and regenerated segments of rolls
for hardfacing with chromium-containing hardfacing materials. Compared to casting materials, the achieved lifetime is twice or three times longer and the grinding result is much better for a long period of time. In the same way the disk, on which the strip rolls, can thus be regenerated and the lifetime extended. 4.2 Sinter-crusher stars with cobalt-base alloys and inserted mixed carbides Sinter crushers are a considerable wear problem in each iron and steel work worldwide.
Rev: 1.0 27
VAUTIDf i g h t s w e a r
R
Sinter crusher blades hardfaced withVAUTID-145
Generally their lifetime in hardfaced condition is about 2-4 months. Actually tests are made, in order to find out if the use of tungsten-chromium carbides can increase lifetime significantly, which are promising. But with regard to bar frames (the counter-part) it already became obvious that with such materials a longer lifetime is not achieved, due to even higher temperatures. 4.3 Use of hardfaced Plates as semifinished Products
The main trend and most important application for hardfacing worldwide is the production of hardfaced plates in standard sizes, of which parts ready to be installed are being manufactured. Processes according to drawings of parts to be manufactured
can be made of such hardfaced plates, using plasma-burners or water-jet. Even complicated equipments can be made by cold-work, like some examples show. The cheap production of the semi-finished products is mainly interesting, whereas the welding mechanization is most important. This can be achieved by using special procedures with an extremely intensive fusion efficiency rate per burner, or by combining many burners, e.g. up to 10 burners for filler-wire weldings. 5. Trends as a Result of Environmental Protection Prescriptions The environmental protection is a very important trend for hardfacing, which will cause much more problems in the future than it did the last 100 years. Steams are emerging whilst hardfacing, which are not that dangerous, as they do nearly not contain hexavalent chromium. The size of dust particles is dangerous, so that a good suction during work shall be ensured. In addition, there are new trends coming up with regard to valuation of danger of nickel and manganese, which will probably afford high investments with regard to the suction of such welding-steams within the next 10 years. For that reason we assume that in the future there will be a concentration of orders in less locations, where an excellent suction is guaranteed, or where in fully-enclosed cabins, supported by robots, the main hardfacing work will be done. 6. Summary Hardfacing is a modern procedure, which nowadays is mainly applied for bigger construction parts, in order to extend the lifetime, instead of using massive solutions, such as castings. This “added value” makes the parts more valuable, and the demand for it will be constant, as the standstill of concatenated machines will become more and more expensive.