Commitment to Excellence

Commitment to Excellence

S-660

S-780

S-550

S-390

S-330

S-280S-230

S-170

S-110

S-70

S-460

SPECIFICATIONS

SAE SHOT SIZE SPECIFICATIONS

SieveOpeningStandard

(in)

0.111

0.0937

0.0787

0.0661

0.0555

0.0469

0.0394

0.0331

0.0278

0.0234

0.0197

0.0165

0.0139

0.0117

0.0070

0.0049

0.0029

7

8

10

12

14

16

18

20

25

30

35

40

45

50

80

120

200

2.80

2.36

2.00

1.70

1.40

1.18

1.00

0.850

0.710

0.600

0.500

0.425

0.355

0.300

0.180

0.125

0.075

(mm) S780

All Pass

85% min

97% min 85% min

97% min 85% min

97% min 85% min

97% min 85% min

97% min 85% min

97% min 85% min

97% min 85% min

97% min

85% min

97% min

85% min

97% min 85% min

97% min

All Pass

All Pass

All Pass

5% max

All Pass

5% max

All Pass

5% max

All Pass

10% max

All Pass

10% max

All Pass

All Pass

10% max

All Pass

10% max

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

S550 S460

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

S330 S280

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

S170

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

S70

SieveDesignation

NominalSieve Opening

Test Sieve Opening Size and Designation with Maximum Cumulative PercantagesAllowed On Corresponding Test Sieves SAE Shot Number

S660 S390 S230 S110

PRODUCTION

DÜŞÜK KARBON YÜKSEK PERFORMANS TOSÇELİK GRANÜL, grup şirketlerinden aldığı en uygun alaşımları içeren hurdaları çelik bilye üretiminde değerlendirmektedir.

Bu durum, hurdaya büyük oranda bağlı olan düşük karbonlu çelik bilye kalitesinde devamlılığı garanti altına almaktadır.

Düşük karbonlu çelik bilye yüksek darbe emme kapasitesine sahip olup darbe enerjisi bilye üzerine eşit olarak dağılır.

Düşük karbonlu çelik bilye, yüksek karbonlu bilyenin aksine mikro çatlak barındırmadığı için daha uzun ömürlüdür.

Yapısal özelliği nedeniyle düşük karbonlu çelik bilye kullanım esnasında yüksek sertliğe ulaşır ve temizleme performansı artar.

+ DÜŞÜK KARBONLU ÇELİK BİLYESadece düşük karbonlu, düşük fosforlu ve düşük oranda kükürt içeren seçilmiş özel hurdalardan üretilir.

İkinci kez ısıl işlem uygulanmaması nedeniyle beynitik yapıya sahip çatlak içermeyen, darbe ve aşınmaya dayanıklı mükemmel taneler elde edilir.

Kumlama işlemi sırasında bilyeler kırılarak küçük parçalara ayrılmazlar, her zaman küreselliklerini koruyarak aşınırlar.

Düşük karbonlu çelik bilye, yüksek karbonlu bilyeye göre daha uzun ömürlü olması nedeniyle (yaklaşık %20 oranında) daha az tüketilir. ”Daha az bilye » daha çok iş » daha az doğal kaynak tüketimi” anlamına gelen düşük karbonlu çelik bilye, diğer taraftan daha az enerji sarfiyatı, işgücü kullanımı ve düşük seviyede atık miktarı demektir.

- YÜKSEK KARBONLU ÇELİK BİLYE

Üretimlerinde her türlü hurda kullanılır. Döküm sonrası sert, kırılgan martenzitik yapıya sahiptirler. Döküm sonrası uygulanması zorunlu ikincil ısıl işlem bilye yüzeyinde çatlaklara sebep olur.

Üretim sırasında oluşan çatlaklar nedeniyle taneler kısa sürede sert ve köşeli parçalar halinde kırılırlar. Bu nedenle yüksek karbonlu bilyeler kumlama makinesi parçalarını daha fazla aşındırarak yüksek bakım maliyetlerine sebep olurlar.

LOW CARBON HIGH PERFORMANCETOSÇELİK GRANÜL uses the best alloy content scrap that it receives from the group companies in the low carbon steel shot production.

This assures stability in the quality of low carbon steel shots which is higly dependent on the scrap content.

Low carbon steel shot features increased impact absorbing capacity as the impact energy is distributed evenly on the shots.

In contrary to high carbon steel shot, low carbon steel shot enjoys more life time as it does not feature micro cracks.

Structural properties of low carbon steel shot reaches increased hardness and thus offers better cleaning performance during usage.

+ LOW CARBON STEEL SHOT

Low Carbon Steel Shot is only produced using carefully selected scraps with low carbon, low phosphor, and low sulphur content.

Since the production process does not require secondary heat treatment, perfect shots of bainitic structure are produced without cracks also resistant to impact and wear.

Low Carbon Steel Shots do not break into small pieces but on the contrary they wear maintaining their spherical form during usage.

Low Carbon Steel Shot has longer life time and thus less consumed than high carbon steel shot (approx. 20%). Low carbon steel shot not only assures longer life time » more blasting with less media » less consumption of natural resources but also means less energy cost, labor use and low amount of waste.

- HIGH CARBON STEEL SHOT

High Carbon Steel Shot is produced by any sort of scrap. It gets rigid and brittle martensitic structure after the casting.

Secondary heat treatment that must be applied after the shots are cast cause cracks on the surface of the shots.

Because of these cracks produced during the production, shots are broken rapidly during blasting and start to have edges due to rigidity. Consequently, high carbon shots damage blasting machine parts easily and lead very high maintenance costs.

TECHNICAL SPECIFICATIONSTEKNİK ÖZELLİKLER

Low Carbon Steel Shot Düşük Karbonlu Çelik Bilye

Chemical Analysis (Molten Metal)Kimyasal Bileşim(Eriyik Metal)

Carbon : 0.10 - 0.15%Manganese : 1.20 - 1.50%Silicon : 0.10 - 0.25%Sulphur : 0.035% maxPhosphorus : 0.035% max

Karbon : %0.10 - 0.15Mangan : %1.20 - 1.50Silis : %0.10 - 0.25Kükürt : maks %0.035Fosfor : maks %0.035

HardnessSertlik

TOÇELİK LOW CARBON STEEL SHOTS are subject to hardness testing that requires at least 90% of the shots falling within the range of 40-50 HRC.

Test edilen TOSÇELİK DÜŞÜK KARBONLU ÇELİK BİLYELERİN %90’ının sertliği 40-50 HRC arasında olmalıdır.

MicrostructureMikroyapı

As a result of its bainitic microstructure, TOSÇELİK LOW CARBON STEEL SHOT features high level of hardness, long service life and strength in optimum combination.

TOSÇELİK DÜŞÜK KARBONLU ÇELİK BİLYENİN mikroyapısı yüksek sertlik, uzun ömür ve dayanıklılık kombinasyonunu sağlayan beynittir.

General LookGenel Görünüm

Steel Shots are required to be in spherical form as much as possible. Extended or compound particles, tails, hollows, broken pieces, slag and dirt have to be at minimum level.

Çelik bilyeler mümkün olduğunca küresel olmalıdır. Kusurlu kabul edilen uzamış, yapışmış, kuyruklu, boşluk içeren taneler, kırık parçalar ve cüruf gibi hatalar minimum düzeyde olmalıdır.

ApplicationKullanım Alanları

They are mainly used in foundries, steel mills, forging shops, rolling mills, machine shops, structural steel mills that are serving automotive, construction, ship building, aircraft, agriculture and many other industries.

Otomotiv, uçak, gemi, yapı çeliği ve daha birçok sektöre hizmet veren dökümhaneler, çelikhaneler, dövmehaneler, haddehaneler ve makine üreticileri tarafından kullanılmaktadır.

PackagingAmbalaj

25 kg polyethylene bags on 1 ton wooden pallet wrapped with cardboard and shrink packed. Packaging materials are 100% recyclable and eco-friendly. 1000 kg big bags and 900 kg metal barrels are also available for shipment.

Çelik bilyeler 25 kg’lık polietilen torbalarda paketlenir ve 1 tonluk paletlere dizilip karton kutuyla kaplandıktan sonra şrinklenir. Paketlemede %100 geri dönüşümlü doğa dostu malzemeler kullanılmaktadır. 1000 kg’lık bigbag ve 900 kg’lık metal varillerde paketleme yapılabilir.

DensityYoğunluk

Density must be 7.0 gr/cm as minimum.

Yoğunluk minimum 7.0 gr/cm olmalıdır.

DIFFERENCE

LOWCARBON

LOWEMISSION

LOWPOLLUTION

LESS NATURALRESOURCE

CONSUMPTION

MÜKEMMELLİĞE GÖTÜREN FARKTOSÇELİK GRANÜL SANAYİ A.Ş. ürettiği DÜŞÜK KARBONLU ÇELİK BİLYE ile yüzey temizleme ve aşındırıcı malzemeler dünyasına çevre ve kalite konusunda yepyeni bir boyut kazandırmıştır.

Doğru hammadde seçimi yüksek kaliteli DÜŞÜK KARBONLU ÇELİK BİLYE üretiminin en önemli unsurlarından birisidir ve TOSÇELİK GRANÜL SAN. A.Ş.’nin yarattığı fark buradan gelmektedir.

DÜŞÜK KARBONLU ÇELİK BİLYE, yüksek karbonlu muadillerine kıyasla beynitik mikroyapısı gereği daha uzun ömürlüdür, daha etkili ve hızlı temizleme özelliği gösterir.

TOSÇELİK GRANÜL SAN. A.Ş. üretim teknolojisi gereği enerji tasarruflu çevre dostu bir fabrikadır.

Düşük karbonlu çelik bilye » daha uzun ömür » daha az bilyeyle daha çok iş » daha az doğal kaynak tüketimi

DIFFERENCE THAT LEADS TO EXCELLENCETOSÇELİK GRANÜL SANAYİ A.Ş. introduces a brand new aspect to the surface cleaning and abrasive materials world emphasizing environment and quality with its LOW CARBON STEEL SHOT.

Proper raw material selection is a foreground process to produce high quality LOW CARBON STEEL SHOT which brings the difference offered by TOSÇELİK GRANÜL SANAYİ A.Ş.

When compared to high carbon steel shot, LOW CARBON STEEL SHOT offers longer life time and blasts more effectively in less time thanks to its bainitic microstructure.

TOSÇELİK GRANÜL SAN. A.Ş. is proud to have an eco-friendly production plant as a result of its unique production technology.

Low carbon steel shot » longer life time » more blasting with less media » less consumption of natural resources

LESS LOWCARBONSTEEL SHOT

MOREBLASTING

Head Office:Barbaros Mh. Sütçüyolu Cd. Tosyalı Plaza No:72 TR-34746 Ataşehir - İstanbul - Turkey

Phone :+90 216 544 3600

Fax :+90 216 544 3606

E-mail :info@toscelikabrasives.cominfo@toscelikgranul.com.tr

Web :www.toscelikabrasives.comwww.toscelikgranul.com.tr

Profil ve Sac

Dış Ticaret

Denizcilik

Elektrik Üretim

Demir Çelik

Elektrik Ticaret

Steel

Iron Steel

Commitment to Excellence