Paper-Based Sensors for Contaminant Detection Using Surface Enhanced Raman Spectroscopy
Ishan Jain
Thesis submitted to the faculty of the Virginia Polytechnic Institute and State University in partial fulfillment of the requirements for the degree of
Master of Science
In
Environmental Engineering
Peter J. Vikesland, Chair
Amy Pruden
Richey M. Davis
April 23, 2015
Blacksburg, Virginia
Keywords:
surface enhanced Raman spectroscopy, gold nanoparticles, paper-based sensors, SERS substrates, pathogen detection, µPads, microfluidic device
Paper-Based Sensors for Contaminant Detection Using Surface Enhanced Raman Spectroscopy
Ishan Jain
ABSTRACT
Surface enhanced Raman spectroscopy (SERS) is highly promising analytical technique
for trace detection of analytes. It is particularly well suited for environmental analyses due to its
high sensitivity, specificity, ease of operation and rapidity. The detection and characterization of
environmental contaminants, using SERS is highly related to the uniformity, activity and
reproducibility of the SERS substrate.
In this thesis, SERS substrates were produced by gold nanoparticle formation on wax
patterned chromatography paper. In situ reduction of hydrogen tetrachloroaurate (gold precursor)
by trisodium citrate dihydrate (reducing agent) was used to produce gold nanoparticles within a
paper matrix. These gold nanoparticle based SERS substrates were analyzed by FE-SEM, UV-
Vis and Raman spectroscopy. This work discusses the SERS signal enhancements for Raman
active MGITC dye for a series of substrates prepared by in situ reduction of gold salt and pre-
produced gold nanoparticles. UV-Vis analysis was performed to understand the effect of
different molar ratio (reducing agent to gold precursor) and reaction time on the size and shape
of the localized surface plasmon resonance (LSPR) band that dictates the SERS enhancements. It
was concluded that lower molar ratio (1:1 and 2:1) of citrate-to gold produced better SERS
signal enhancements and broader LSPR band. Therefore, use of lower molar ratio (MR) was
recommended for paper-based substrates using in situ-based reduction approach.
iii
For my father:
Shri Ishwar Jain
“The beginning of knowledge is the discovery of something we don’t understand.”
-Frank Herbert
iv
Acknowledgments
My MS program experience was the most challenging, yet, great learning experience of
my life. I had the opportunity of working with Dr. Peter J. Vikesland, who was instrumental in
helping me to complete my thesis. I sincerely thank him for his support, guidance, and patience
throughout the period of my MS.
I am also grateful to my committee members Dr. Amy Pruden, and Dr. Richey Davis for
their encouragement throughout the time of my graduate studies.
I am also very thankful to my colleagues, particularly in Dr. Vikesland’s group, for
helping me with data analysis, experiments and lab training. They include Dr. Rebecca
Halvorson Lahr, Dr. Weinan Leng, Xinzhe Zhou, Ron Kent and Marjorie Willner.
This research was supported by the National Science Foundation (NSF), Bill and Melinda
Gates Foundation, and the Virginia Tech Institute for Critical Technology and Applied Science
(ICTAS).
Ishan Jain
Blacksburg, VA, USA
v
TABLE OF CONTENTS
List of Figures .............................................................................................................................. vii
List of Tables ................................................................................................................................ xi
Chapter 1. Introduction ............................................................................................................... 1
1.1 Significance and motivation .................................................................................... 1
1.2 Specific objectives .................................................................................................... 5
1.3 Overview of chapters ............................................................................................... 5
Chapter 2. Literature Review ...................................................................................................... 7
2.1 Raman spectroscopy and its application ............................................................... 7
2.1.1 Origin of Raman ............................................................................................................. 7
2.1.2 Raman scattering ........................................................................................................... 7
2.1.3 Comparison between Raman spectroscopy and other technologies ............................ 8
2.1.4 Limitation of Raman spectroscopy .............................................................................. 10
2.2 Surface enhanced Raman spectroscopy (SERS) ................................................. 11
2.2.1 Introduction ................................................................................................................. 11
2.2.2 SERS mechanism .......................................................................................................... 11
2.2.3 SERS substrates ............................................................................................................ 12
2.3 Gold nanoparticles: synthesis and properties ..................................................... 16
2.3.1 Synthesis of gold nanoparticles ................................................................................... 16
2.3.2 Properties of gold nanoparticles .................................................................................. 19
vi
2.3.3 In situ reduction of metal salts .................................................................................... 19
2.4 Microfluidic paper-based devices (µPADs) ......................................................... 20
Chapter 3. Experimental Methods and Instruments ............................................................... 24
3.1 Material .................................................................................................................................. 24
3.2 Preparation of wax printed microfluidic wells/channels .................................... 24
3.3 Preparation of paper-based SERS substrates ..................................................... 25
3.4 Instrumentation ..................................................................................................... 27
3.4.1 UV-‐Vis .......................................................................................................................... 27
3.4.2 Surface enhanced Raman spectroscopy (SERS) ........................................................... 27
3.4.3 FE-‐SEM ......................................................................................................................... 28
Chapter 4. Results and Discussion ............................................................................................ 29
4.1 Synthesis of gold nanoparticles by in situ reduction within paper .................... 32
4.2 UV-Vis analysis to study effect of the variation in gold precursor and reducing
agent concentration with increase in reaction time .............................................................. 44
4.3 SERS signal optimization strategy for MGITC using paper based substrates 50
Chapter 5. Conclusions and Future Work ............................................................................... 56
5.1 Conclusions ............................................................................................................. 56
5.2 Future work ............................................................................................................ 57
References .................................................................................................................................... 60
vii
List of Figures
Figure 1. Schematic representation of Raman (Stokes & anti-Stokes) and Rayleigh scattering. .. 8
Figure 2. Example of lightning rod effect for Ag Trigonal prism (side length 100 nm and
thickness is 16 nm); Sharp angles and edges produces extra enhancement. Electric field scale is
from 0 to 20 units. ......................................................................................................................... 15
Figure 3. Illustration of gold nanoparticle formation by nucleation and growth mechanism.. ... 18
Figure 4. (A) Paper-based SERS substrates prepared by gold nanorods (AuNRs) solution before
and after exposure showing the strong color change; (B) UV-Vis extinction spectrum of the
AuNRs solution and the AuNRs loaded paper. ............................................................................. 22
Figure 5. (A) Wax printed circular paper-based sensors (2 mm circular wells) (B) Wax printed
microfluidic paper-based channels; dark red color is due to formed gold nanoparticles. .......... 25
Figure 6. In situ reduction of gold precursor (hydrogen tetrachloroaurate solution) by reducing
agent (trisodium citrate); HAuCl4 stands for gold precursor ....................................................... 26
Figure 7. The wax spreads during heating, creating narrower channels in the tested µPADs; (A)
Unheated wax channel and heated wax channel; (B) Unheated and heated circular microfluidic
well. The µPAD dimension describes the printed measurements. ................................................ 30
Figure 8. Characterization of wax printed-paper before and after heating; (A) SEM images of
microfluidic channel before (at magnification of 500x); (B) FESEM images of microfluidic
channel after heating (at magnification of 500x); (C) One of the waxed coated cellulosic fiber is
zoomed in (at magnification of 1000x). ........................................................................................ 31
Figure 9. Example of color change in chromatography paper in 10 mm circular well (left) and 2
mm circular wells (right); HAuCl4 and Na3Ctr stand for gold chloride and sodium citrate
solution respectively. ..................................................................................................................... 33
viii
Figure 10. UV-Vis spectrum of various substrates prepared by different citrate-to- gold ratio
(refer Table 4); Different shape and size of LSPR is observed. (A). 25 mM gold chloride, 23 mM
Citrate Solution (MR= 0.95) (B). 20 mM gold chloride, 27 mM Citrate Solution (MR= 1.35) (C).
15 mM gold chloride, 30 mM Citrate Solution (MR= 2) (D) 10 mM gold chloride, 30 mM Citrate
Solution (MR= 3) .......................................................................................................................... 35
Figure 11. SERS of MGITC dye in MGITC-methanol solution. MGITC assignments are at 1200,
1380 and 1600 cm-1. ...................................................................................................................... 36
Figure 12. Comparative analyses of paper-based substrates prepared by various different molar
ratio of citrate to gold chloride; 2 mm wax printed wells are loaded with gold chloride solution
followed by citrate solution (reducing agent); Reaction time: 7 days with addition of 1 µL of
MGITC dye; (A) the difference in the region of 100 ~ 350 cm-1 may be caused by the size or
shape of Gold NPs in the paper; (B) SERS spectrum of MGITC dye with various molar ratios
(MR). Raman parameters: Laser wavelength 633 nm, and micrometer reading 1.2 mm (0.261
mW for 10x objective lens). ........................................................................................................... 37
Figure 13. (A) FE-SEM image of chromatography paper (blank) at magnification ~10 kx; (B)
Different FE-SEM image of chromatography paper (blank) at magnification ~10 kx; (C) EDX
image showing strong C, O elemental peaks and negligible gold peaks. Gold peak is a result of
gold-palladium coating. ................................................................................................................ 40
Figure 14. (A) SEM image of chromatography paper loaded with 50 nm sized gold nanoparticles
prepared by citrate reduction method at magnification of 30.00 kx; (B) SEM image of
chromatography paper loaded with 50 nm sized gold nanoparticles prepared by citrate reduction
method at magnification of 100.00 kx; (C) EDX image confirming presence of gold
ix
nanoparticles. Images produced at working distance (WD) ~8.5 mm and Voltage (EHT) ~ 20kV.
....................................................................................................................................................... 41
Figure 15. SEM analysis of paper-based SERS substrates prepared by in situ reduction based
gold nanoparticle synthesis (5 mM gold chloride, molar ratio of citrate to gold chloride~ 4, and
allowed reaction time ~ 7 days) (A) Clusters (circles) of formed AuNPs in sample image with
magnification ~ 101.4 KX; (B) Clusters of formed AuNPs in sample image with magnification ~
30.4 KX; (C) Clusters of formed AuNPs in sample image with magnification ~ 100.36 KX; (D)
Clusters of formed AuNPs in sample image with magnification ~ 100.72 K X (used WD~ 5.7 mm,
EHT~ 2 kV). .................................................................................................................................. 42
Figure 16. SEM analysis of paper-based SERS substrates prepared by in situ reduction based
gold nanoparticle synthesis (5 mM gold chloride, molar ratio of citrate to gold chloride~ 4 and
allowed reaction time ~ 7 days); (A) Sample image with magnification ~40 K X, WD~ 5.7 mm,
EHT~ 2 kV; (B) EDX image showing elemental analysis of square box (pink color) in image (A).
....................................................................................................................................................... 43
Figure 17. Temporal variation of maximum absorption of different molar ratios of citrate
solution to gold chloride solution for a given initial concentration of gold chloride solution; (A)
Molar ratio (MR) = 1 (B) Molar Ratio = 3 (C) Molar Ratio= 5. ................................................ 46
Figure 18. Effect of initial gold precursor solution on absorption values for a given molar ratio
of citrate solution to gold chloride solution after reaction time of 35 days; (A) Molar ratio of 1
after 35 days (B) Molar ratio of 3 after 35 days (C) Molar ratio of 6 after 35 days .................... 47
Figure 19. LSPR Band and shape changes with the increase in molar ratio (MR) from 1 to 6.
[HAuCl4]= 20 mM, reaction time 35 days, and diameter of microfluidic wells are 10 mm. ....... 48
x
Figure 20. LSPR Band and shape changes with the increase in molar ratio (MR) from 1 to 6.
[HAuCl4]= 100 mM, reaction time 35 days, and diameter of microfluidic wells = 10 mm. ....... 49
Figure 21. Average SERS spectra (Large area scan) for MGITC dye using paper based
substrates. [HAuCl4]= 20 mM, reaction time= 28 days, Raman Laser 785 nm wavelength with
micrometer reading of 1.2 mm (18.3 mW of laser power for 10x objective lens). MR stands for
Molar Ratio. .................................................................................................................................. 51
Figure 22. Optimization of MGITC assignments with respect to peak at 1800 cm-1 (strategy -1);
Lower molar ratios produce less variability in peak ratios than high molar ratios (circled).
Sample 1 and sample 2 are replicate of same substrates (for initial gold chloride conc. = 20
mM) ............................................................................................................................................... 53
Figure 23. Optimization of MGITC assignments with respect to the peak at 105 cm-1 (strategy-
2); Sample 1 and sample 2 are replicate of same substrates (for initial gold chloride conc. = 20
mM). .............................................................................................................................................. 54
xi
List of Tables
Table 1. Properties and advantages of SERS. Springer Science and Business Media/
Microchimica Acta, 181, 2014, 23-43, Recent Progress in Surface Enhanced Raman
Spectroscopy for the Detection of Environmental Pollutants. Li, D.-W., et al., excerpts,
Copyright © 2013, Springer Science+Business Media [1]. Used with kind permission from
Springer Science and Business Media, 2015. ________________________________________ 2
Table 2. SERS application in organic pollutant detection. Springer Science and Business
Media/ Microchimica Acta, 181, 2014, 23-43, Recent Progress in Surface Enhanced Raman
Spectroscopy for the Detection of Environmental Pollutants, Li, D. -W., et al., excerpts,
Copyright © 2013, Springer Science+Business Media [1]. Used with kind permission from
Springer Science and Business Media, 2015. ________________________________________ 4
Table 3. Comparison between Raman spectroscopy and other techniques. Springer Science
and Business Media/ Cancer and Metastasis Reviews, 33 (2-3), 2014, 673-693, Emerging
Technology: Applications of Raman Spectroscopy for Prostate Cancer, Kast, R.E., et al.,
excerpts, Copyright © 2014, Springer Science+Business Media [71]. Used with kind permission
from Springer Science and Business Media, 2015. __________________________________ 10
Table 4. Concentration of gold chloride and sodium citrate solution for UV-Vis analysis;
data used in Figure 10. ________________________________________________________ 34
Table 5. Concentration of Gold Chloride and Sodium Citrate (data used in Figure 12) ___ 37
1
Chapter 1. Introduction
1.1 Significance and motivation
Environmental pollutants or toxins include a varied set of natural and synthetic
constituents present in soil, air and water that can cause adverse effects on ecosystems [1, 2].
Exposure to pollutants such as halogenated compounds, dioxins, heavy metals (for instance, lead
and arsenic), pesticides (organophosphates and other insecticides), and various forms of
pathogens (such as cyanobacteria and polio virus) can cause hazardous effects and acute diseases
in humans and animals [1, 3].
Environmental pollutants that pose harmful effects and threats to ecological species
should be regularly monitored and detected to evaluate their risks towards the environment [4-8].
Several analytical techniques including solvent extraction, chromatography, spectrometry, and
electrochemical methods are extensively used for environmental analyses [9-14]. However,
widespread use of many of these techniques is limited as they can be time consuming, complex,
costly or lack the capacity to recognize different contaminant distributions, thus resulting in
incomplete assessment of analytes [1, 15]. Therefore, researchers have been exploring
microfluidics, biosensors, and surface enhanced Raman spectroscopy (SERS) [1, 16, 17]. Among
these techniques, SERS is well suited for environmental analyses because it provides unique
fingerprints for specific analytes with high selectivity, sensitivity, and rapidity [1, 15, 18-23].
Relative to many other analytical techniques, SERS has outstanding advantages. These
advantages are briefly summarized in Table 1.
2
Table 1. Properties and advantages of SERS. Springer Science and Business Media/
Microchimica Acta, 181, 2014, 23-43, Recent Progress in Surface Enhanced Raman
Spectroscopy for the Detection of Environmental Pollutants. Li, D.-W., et al., excerpts,
Copyright © 2013, Springer Science+Business Media [1]. Used with kind permission from
Springer Science and Business Media, 2015.
Properties Advantages of SERS [1]
Sensitivity [24] SERS is highly sensitive to very low concentration of analytes
(even at the molecular level)
Unique fingerprint of
analytes [19, 20, 24]
It provides information about the inherent chemical structure of
analytes
Rapid detection [20, 25] It requires less than one minute for each measurement (it may
vary with analytes)
Detection in water [8, 15] As “water is a poor Raman scatter” [26], SERS can be applied
to water samples directly
Cost effective detection Good laboratory and field detection
Variable detection [19,
22, 27-30]
It detects chemical and biological variability in analytes
It is advantageous to use SERS for trace-level detection of aqueous and airborne
contaminants, cyanobacteria and other pathogens [15, 18, 19, 21, 31]. The capacity for SERS to
achieve these applications is highly dependent on the activity, plasmon absorption, and
reproducibility of the SERS substrates [18, 24, 32].
Lin XM et al. discussed various methods to prepare SERS substrates, which are briefly
covered in Chapter 2 [32]. SERS substrates made of roughened noble metal (Au, Ag) surfaces
3
are used to get signal enhancement factors ranging from 104 to 1010 [15, 33]. A summary of
different examples of SERS substrates and their applications are described in Table 2.
An SERS substrate (an ideal substrates) should have high SERS activity, decent
reproducibility (less than 20%), good stability and uniformity (deviation less than 20%). It
should provide high sensitivity, which can be controlled by changing the nanoparticle size and
inter-particle spacing (less than 10 nm) of nanoparticles [32, 34]. Uniform and reproducible
SERS substrates minimize variations in signal enhancement of the analytes [34, 35]. However, it
is difficult to design ideal SERS substrates to satisfy all of the above requirements [32, 34].
Therefore, researchers have recently begun fabricating paper based microfluidic
substrates [36-40]. Depositing metal (usually Au, Ag, Cu) nanoparticles on the patterned paper
produces paper-based SERS substrates [21, 37, 41-46]. These SERS substrates may be prepared
by using pre-formed metal nanoparticles and then subsequent addition of these nanoparticles to
paper [21, 22, 27, 38, 47, 48] or synthesis of metal nanoparticles within paper by the addition of
metal precursor and the subsequent addition of reducing agent [49-53]. This latter approach can
be considered as in situ reduction based synthesis of metal nanoparticles, which is further
discussed in Chapter 3.
Lee C. H. et al. fabricated SERS substrates by directly depositing pre-formed gold
nanorods (AuNRs) on the filter paper [21]. However, direct deposition of metal nanoparticles on
cellulose filter paper usually causes aggregation and heterogeneous distribution of nanoparticles
at the edge (boundary), producing a “coffee ring effect” due to drying process [13, 21, 37, 54]. In
this thesis, we hypothesized that we could reduce the potential “coffee ring effect” [54] by
4
producing more uniform substrates by using in situ reduction based synthesis of gold
nanoparticles on chromatography (or filter) paper.
Table 2. SERS application in organic pollutant detection. Springer Science and Business
Media/ Microchimica Acta, 181, 2014, 23-43, Recent Progress in Surface Enhanced Raman
Spectroscopy for the Detection of Environmental Pollutants, Li, D. -W., et al., excerpts,
Copyright © 2013, Springer Science+Business Media [1]. Used with kind permission from
Springer Science and Business Media, 2015.
Pollutant Category
Analytes SERS Substrates Sensitivity (LOD)
Pesticides Thiram Gold Nanorods ~34 nM [48] Chlortoluron Ag-quantum dots " sponge"
nanocomposite ~0.94 µM [55]
PAHs & PCBs Fluoranthene 1-Hexanethiol functioned Ag NPs ~24.7 nM [29]
Pyrene Viologen functionalized Ag NP 1 nM [56] Anthracene CD-SH functionalized Au NPs 100 nM [25] Pyrene Au NPs-modified alginate gel
network 10 nM [57]
Explosives 3,3’, 4,4’-tetrachlorobiphenyl
Ag nanosheet-assembled hemispheres modified with CD-SH
0.1 µM [58]
2,4-dinitroanisole Ag NPs modified by L-cysteine methyl ester hydrochloride
~0.1 µM [59]
Other Organic Pollutants
Phosphorus triphenyl Metal nanostructured film/graphene oxide
1 nM [60]
Rhodamine 6G Ag NPs-decorated reduced graphene oxide
10 nM [61]
Herein, we fabricated simple paper-based microfluidic SERS substrates via in situ
reduction of hydrogen tetrachloroaurate (gold precursor) to form gold nanoparticles. We
illustrated that in situ reduction of gold precursor produced gold nanoparticles within the paper
5
matrix to develop SERS substrates. These SERS substrates were used to measure the SERS
signal enhancement of MGITC dye. An attempt to understand the localized surface plasmon
resonance (LSPR) band, uniformity, and optimization of these substrates (with different molar
ratio of reducing agent to gold precursor) was made.
1.2 Specific objectives
The primary objective of this research was to develop paper based SERS substrates
(sensors) using in situ -based reduction of gold precursor. This goal was achieved by focusing on
the following specific objectives:
1) Synthesis of gold nanoparticles (AuNPs) using in situ reduction of hydrogen
tetrachloroaurate (gold precursor) within paper, and
2) Effect of various parameters such as gold precursor, and reducing agent concentration
and reaction time on SERS signal enhancement for MGITC dye.
1.3 Overview of chapters
Chapter 2. Literature Review
This chapter provides an overview of relevant topics including the review of surface
enhanced Raman spectroscopy and its applications. The three primary topics covered in this
review are Raman and SERS principles, microfluidic paper-based devices for SERS applications,
and the preparation of gold nanoparticles (AuNPs).
Chapter 3. Experimental Methods and Instruments
This chapter summarizes various experimental methods and processes used for synthesis
of paper based sensors. It also provides a detailed discussion about the instruments (UV-Vis,
Raman, SEM, and TEM) used to characterize the paper-based SERS substrates.
6
Chapter 4. Results and Discussion
This chapter summarizes the experimental results that describe the synthesis of gold
nanoparticles using in situ based reduction of gold salt within paper. It also discusses the effect
of variations in gold salt and reducing agent (citrate solution) concentrations on the SERS signal
enhancements of Raman active MGITC dye. Also, detailed analysis of collected UV-Vis data is
performed to understand shape and size of LSPR band.
Chapter 5. Conclusions and Future Work
This chapter summarizes the conclusions drawn from the previous chapters and the future
direction for this research.
7
Chapter 2. Literature Review
2.1 Raman spectroscopy and its application
2.1.1 Origin of Raman
Dr. Chandrasekhara Venkata Raman, an Indian professor of physics, described the
important phenomena of light scattering in a paper on “molecular diffraction of light” in 1928
[62]. This observed phenomena indicated that “when a light is scattered by any material some of
the scattered light will have different frequency than the frequency of incident light” [62]. This
phenomenon was named as “Raman effect”.
2.1.2 Raman scattering
When a monochromatic light is scattered by a material, two types of scattering i.e., elastic
or inelastic scattering occur [40, 62-64]. The first type of scattering is known as Rayleigh
scattering, which doesn’t have any energy transfer between molecules and the incident light
photons [62]. Therefore, it is also called elastic scattering [62, 65].
The latter type of scattering involves the exchange of energy between incident photons of
monochromatic light and molecules of analytes, therefore, the scattered light photon energy will
be different from the incident photon energy [62]. This second type of scattering is known as
inelastic, or Raman scattering [62]. Raman scattering can be further classified as either “Stokes”
or “anti-Stokes” [64]. Stokes scattering reflects the lower energy of scattered photons than the
incident light, whereas, anti-Stokes scattering has higher energy of scattered light photons than
the incident light photon [62]. Inelastic scattering provides information about various transitions
(such as vibrational, and rotational) in the samples [66]. However, Raman scattering is a very
weak phenomena as Rayleigh scattering is six order of magnitude higher than the Raman
8
scattering [62, 64]. The schematic representation of Raman and Rayleigh scattering is shown in
Figure 1.
A Raman spectrometer consists of a laser, illumination system (collection of lens and
optical systems), filter or spectrophotometer, and a detector [26, 62, 67, 68].
Figure 1. Schematic representation of Raman (Stokes & anti-Stokes) and Rayleigh
scattering. Modified from: (http://www.doitpoms.ac.uk/tlplib/raman/raman_scattering.php.)
Used under fair use, 2015.
The sample of interest (analyte) is normally illuminated with a monochromatic laser
beam and the laser beam is then reflected by mirrors [67, 69, 70]. Afterwards, scattered light is
filtered and detected to obtain the Raman spectrum of the desired sample [67, 69, 70].
2.1.3 Comparison between Raman spectroscopy and other technologies
Raman spectroscopy is very useful for obtaining molecular and chemical information
about the desired molecules in the sample as it enables non-destructive, rapid and real time
9
spatial resolution of micron size [71]. Detailed comparison between Raman spectroscopy and the
other technologies are in Table 3.
X-ray diffraction (XRD) is commonly used to analyze solid structures, but not liquid or
gas samples [71, 72]. Whereas, Raman is fast and it can produce unique structure/spectrum for
target analytes [71, 72]. Raman Spectroscopy is based on the changes in the polarizability of
vibrating molecules whereas, infrared (IR) spectroscopy is based on the changes in dipole
moment [71]. Raman can be used for aqueous samples, and IR inactive samples can often be
analyzed by Raman spectroscopy [73].
10
Table 3. Comparison between Raman spectroscopy and other techniques. Springer Science
and Business Media/ Cancer and Metastasis Reviews, 33 (2-3), 2014, 673-693, Emerging
Technology: Applications of Raman Spectroscopy for Prostate Cancer, Kast, R.E., et al.,
excerpts, Copyright © 2014, Springer Science+Business Media [71]. Used with kind permission
from Springer Science and Business Media, 2015.
Properties Raman Fourier Transform Infrared Spectroscopy
X-Ray Diffraction
Gas chromatography/ Mass Spectroscopy
Spatial Resolution <1 µm <1 µm Generally for crystal analysis
Generally Bulk analysis
Destructive No No Yes Yes Extensive sample preparation
No No Yes No
Influenced by water
Limited, Depends
Yes Yes No
Surface Near surface penetration
Near surface penetration
Crystal structure
Bulk
Phases Solid, Liquid, Gas
Solid, Liquid, Gas
Solid
2.1.4 Limitation of Raman spectroscopy
Raman scattering is a very weak phenomena as Rayleigh scattering is six order of
magnitude higher than the Raman scattering [62]. Rayleigh scattering doesn’t provide any useful
information for molecular characterization [62]. Only the inelastic scattering (Raman scattering)
is practically useful for the purpose of molecular detection [62]. However, Raman scattering is
difficult to detect as the Raman signals are often overshadowed by Rayleigh scattering,
competitive fluorescence (another type of inelastic scattering) and thermal emission [68, 74].
11
For these reasons, researchers are trying to develop various techniques to improve Raman
signal intensity for detection of desired analytes. One of the techniques used for Raman signal
enhancement is ‘surface enhanced Raman spectroscopy (SERS)’ [18, 71, 75-77]. In this thesis,
SERS is used for signal enhancements of Raman active MGITC dye.
2.2 Surface enhanced Raman spectroscopy (SERS)
2.2.1 Introduction
SERS is a reliable, economical, highly surface selective and ultrasensitive method to
qualitative identify and quantitative analyze aqueous and airborne contaminants, cyanobacteria
and other pathogens [15].
2.2.2 SERS mechanism
SERS signal enhancement depends on roughened (nanoparticles based) metal surface
[78-80]. Usually, silver or gold metal are used to produce rough surface as they produce high
signal enhancements. Compared to normal Raman, SERS may produce signal enhancements of
up to ~1014, in general, enhancements of 106 or 108 are most readily observed [15, 37]. The
SERS signal enhancement can be attributed to two main mechanisms: a) electromagnetic
enhancement by electromagnetic field produced at or near nanostructured surfaces, and b)
chemical enhancement by chemical/ physical adsorption of the analyte to the metal surface [37].
When an electromagnetic wave from an excitation laser interacts with the roughened
metal surface, it leads to enhancements of the e-field by surface plasmon resonance (with
incident laser wave) and hence enhancement in Raman signals [32, 81-84]. Detailed discussion
on surface plasmon resonance is performed later in this chapter.
12
Chemical enhancement involves covalent bonds formation (i.e. adsorption) between the
analytes molecules and the roughened metal surface [84, 85]. These chemical bonds lead to
charge transfer from the metal surface to adsorbate thus resulting in an increased polarizability of
the analyte molecules (adsorbate) [84]. It is generally believed that enhancement due to charge
transfer mechanism is lesser with respect to electromagnetic enhancements [84].
Roughness of the metal surface and wavelength of the Raman laser are important
component for a good SERS enhancement [31, 78, 80]. Smooth surface will not produce
effective surface plasmons [31]. Usually, size of nanoparticles is commonly in the range of 20 to
100 nanometers for Raman laser wavelengths in the range of 532 to 780 nanometers [31].
2.2.3 SERS substrates
The choice of SERS substrate/support material (such as silicon, paper, polymers or glass
plate) and noble metals (Au, Ag, or Cu) are very important for SERS [18, 24, 31, 86]. In general,
SERS substrates are prepared by depositing molecules of noble metals on the support material.
One of the main reason to select noble metals (such as Ag, Au or Cu) is that they are easy to
handle in acidic/basic, ambient, electrochemical or vacuum conditions and they also produce
significant Raman signal enhancements for a wide variety of analytes [87].
2.2.3.1 Methods to prepare SERS substrates
The applications of SERS mainly depend on activity and reproducibility of the SERS
substrates [38, 48, 58, 88]. According to Lin X.M. et al., electrochemical oxidation and reduction
cycle (EC-ORC), wet chemical synthesis methods, or lithography methods are often used to
produce SERS substrates [32].
13
Besides above-mentioned methods, other methods such as chemical assembly method,
aluminum oxide template method, and lithography are also used to fabricate SERS substrates
[32, 89, 90]. In this research, paper-based substrates are synthesized by chemical reduction
method; therefore, it is reviewed in detail to discuss synthesis of various types of nanoparticles
(especially gold nanoparticles) and their effect on LSPR band and Raman signal enhancements.
Gold nanoparticles are mainly produced by reduction of metal precursor in aqueous or
non-aqueous solution [32, 51, 52, 91-96]. Various reducing agents such as sodium citrate
(Na3Ctr), and Sodium borohydride (NaBH4) are widely used for this purpose [32]. However,
these formed nanoparticles tend to aggregate or oxidized back to metal atoms [34, 94, 97].
Therefore, various capping agents, usually surfactants, are also added to avoid aggregation, and
oxidation of formed nanoparticles [32, 34, 53]. These surfactants (capping agents) also help to
regulate growth rate of various features/sides to produce controlled size or shaped nanoparticles
[32, 53]. Different methods to synthesize gold nanoparticle are also discussed later in this
chapter.
Various factors such as type of metal salt, reducing agent, or capping agent, and their
concentration in solution, and reaction conditions (such as temperature, and pH) affects the size,
and shape of nanoparticles [32, 33, 50, 94, 98, 99]. In this review, metal salts of silver (Ag) and
gold (Au) are discussed in detailed as they are widely used to prepare SERS substrates. It is
estimated that Raman signal enhancements for a single AuNP and a single AgNP is about 103 -
104 and 106-107 respectively [18, 30, 32, 38, 47, 100, 101].
In a study by Emory SR et al., Ag colloidal nanoparticles were used to study SERS of
rhodamine 6G (R6G) [32, 102]. Single Ag nanoparticle exhibited maximum SERS enhancement
14
(as large as 1014 - 1015) compared to colloidal nanoparticles aggregates or bulk with 647-nm
excitation [32, 102]. Similarly, AuNPs (~60 nm) with 647 nm laser excitation showed maximum
enhancement of SERS signals [32, 103].
Kelly et al., studied the electrostatic field generated by spherical, non-spherical and
truncated tetrahedrons shaped nanoparticles, and it was observed that metal nanoparticles with
the sharp edge and angles would produce extra enhancement (Figure 2) due larger electric field
values at sharp edge and angles [32, 104]. This is also called ‘Lightning rod effect’. Due to
lightning rod effect non-spherical SERS enhancements were higher [32, 104].
15
Figure 2. Example of lightning rod effect for Ag Trigonal prism (side length 100 nm and
thickness is 16 nm); Sharp angles and edges produces extra enhancement. Electric field
scale is from 0 to 20 units. Kelly, K.L., et al., The optical properties of metal nanoparticles: The
influence of size, shape, and dielectric environment. Journal of Physical Chemistry, 2003.
107(3): p. 668-677. Copyright © (2003) American Chemical Society. Used with kind permission
from Rightslink, 2015.
16
Orendorff et al. studied the effect of shape and architecture of gold nanoparticle on SERS
spectrum of 4-mercaptobenzoic acid (4-MBA) [32, 88]. It was concluded that larger signal
enhancements were produced due to increase in localized electromagnetic field enhancement at
the interface of 4-MBA and nanoparticles on the surface of substrates [32, 88]. It was also
established that shape of AuNPs may vary enhancement factors by a factor of 102 [88].
Gold nanorods produced transverse and longitudinal modes in absorption spectrum in
UV-Vis analysis [105, 106]. According to the study by Huang et al., Au nanorods (aspect ratio =
4) produced surface plasmon band at about 800 nm; therefore, these gold nanorods based
substrates were suitable for 785-nm (Raman laser) excitation [105].
As mentioned before, ideal SERS substrates should have high SERS activity and good
uniformity; also should provide sensitive detection of analytes [32, 37]. Substrates should be
uniform and reproducible to minimize the deviation/variation in signal enhancement [36, 37,
107]. It is challenging to prepare ideal SERS substrates that can be simultaneously be uniform,
reproducible, and produce good signal enhancements [21, 32]. Therefore, researchers are
fabricating microfluidic paper-based SERS substrates [21, 37, 108]. The detailed discussion of
microfluidic paper-based devices (sensors) is performed later in this chapter.
2.3 Gold nanoparticles: synthesis and properties
2.3.1 Synthesis of gold nanoparticles
In this research, gold nanoparticles are used to produce paper-based sensors (refer
Chapter 3). Therefore, in this thesis, gold nanoparticle synthesis is reviewed in detail. Various
approaches have been developed to produce gold nanoparticles of different dimensions and
functionality [34, 53, 109]. In “top down” approach, bulk state gold is broken into smaller
17
dimensions of required size and shape. However, “bottom up” approach involves chemical or
biological reduction of individual molecules (gold precursor) to form gold nanoparticles [53].
Chemical reduction of gold precursor involves nucleation or growth mechanisms of gold
nanoparticles (bottom up approach) [53]. In “in situ synthesis” of gold nanoparticles both
nucleation and growth steps are performed in the same process whereas, in “seed-growth
method” nucleation and successive growth happens in two different processes [53].
The schematic illustration of gold nanoparticle formation through nucleation or growth
mechanism is shown in Figure 3. Reduction of gold chloride by various reducing agents
converts Au+3 ions into neutral gold atoms in the solution [53]. As more and more gold atoms are
formed, nucleation of gold atoms occur and gold atoms will start precipitating in nanometer
particles [110]. These nucleated gold atoms combine and grow to form nanoparticles (Figure 3).
In this thesis, a modified Turkevich method approach is used for in situ based reduction
of hydrogen tetrachloroaurate [53]. Turkevich et al. produced spherical gold nanoparticles in
1951 by simply adding and stirring hydrogen tetrachloroaurate (HAuCl4) with sodium citric acid
in aqueous solution [34, 95, 111]. In this approach, various parameters such as reaction
temperature, the ratio of citrate to gold, and gold salt (HAuCl4) concentration affect the size
distribution of gold NPs [53, 95].
18
Figure 3. Illustration of gold nanoparticle formation by nucleation and growth mechanism.
Polte, J., et al., Nucleation and Growth of Gold Nanoparticles Studied via in situ Small Angle X-
ray Scattering at Millisecond Time Resolution. ACS Nano, 2010. 4(2): p. 1076-1082. Copyright
© 2010, American Chemical Society. Used with kind permission from Rightslink, 2015.
Turkevich method was further improved by changing the citrate-to-gold ratio for
production of relatively small sized spherical gold nanoparticles (diameter = 10 to 20 nm) [53,
99]. Use of surfactant during this reaction can prevent the aggregation of citrate reduced AuNPs
[21, 53, 96].
Seeding techniques are also used to produce large spherical and non-spherical particles
[53, 112]. It is also a popular method to make gold nanorods. In this method, gold precursor is
reduced to seed particles for controlled formation of nanorods [92, 97].
19
2.3.2 Properties of gold nanoparticles
AuNPs possess important property to produce surface plasmon resonance (SPR), and to
reduce fluorescence produced during SERS analysis [35, 99]. Because of these properties,
AuNPs has applications in imaging, sensing and sensor fabrications [35].
Spherical AuNPs exhibit red or purple color in aqueous solution depending on the
diameter and UV-Vis extinction (absorption and scattering) peak [33, 34]. Toma et al. defined
surface plasmon band as “the result of the collective oscillations of the conduction band
electrons” [113]. It is effected by dimension of NPs, type of solvent, reducing agents, reaction
conditions (i.e. temperature), closeness and aggregation of nanoparticles [35, 113].
Accumulation or aggregation of nanoparticles allows electronic coupling of gold nanoparticles,
which causes broadening and shifting of spectrum peaks [113]. A SERS spectrum is a function
of various factors such as shape, size, proximity and extent of plasmon coupling and the nature
of molecules adsorbed [30, 35, 99].
Typically extinction spectrum (UV-Vis) of spherical AuNPs have the plasmon band
range from 520 nm to 560 nm [113]. Non-spherical gold NPs shows two distinct longitudinal and
transverse dipole polarization modes (transverse and longitudinal) [113]. Transverse modes and
longitudinal modes show resonance coinciding with the plasmon band of gold NPs at blue shift
(520- 560 nm) and red shift (650-750 nm) respectively [94, 99, 111, 112].
2.3.3 In situ reduction of metal salts
To deposit nanoparticles on cellulose based polymer/paper various methodology such as
blending of components, in situ reduction of metal salt, electrostatic assembly, and UV reduction
are used [35, 114]. Blending of metal NPs and cellulose i.e. direct deposition of metal
20
nanoparticles on cellulose filter paper usually causes aggregates and heterogeneous distribution
of nanoparticles at the edge producing a “coffee ring effect” due to drying process [13, 21, 37,
54].
In situ reduction of metal precursors by external reducing agents is a simple process [35,
51-53, 114-118]. It entraps metal salt in the fibers, and then, entrapped metal salt are reduced by
an external reducing agent [33, 34, 96, 114]. In situ reduction avoids aggregation of
nanoparticles (NPs) and improves homogenous distribution of NPs [50, 52, 53]. Sodium
borohydride, and tri-sodium citrate are effective and widely used external reducing agents for
gold precursors [114].
2.4 Microfluidic paper-based devices (µPADs)
Paper, a cellulose fiber web, is hydrophilic in nature and has high surface area [41, 119,
120]. Structure and porosity of paper can be modified easily to achieve desired properties [13,
42, 100]. It is portable, disposable, degradable, cheap and easy to use [119]. Therefore, paper is
widely used to fabricate microfluidic devices for variety of applications in healthcare and
environmental monitoring [108, 121, 122].
According to Thuo et al., paper microfluidic is defined as: “a methodology in which fluid
flow in paper is driven by capillary wetting and directed by channel boundaries of hydrophobic
wax or polymer patterned in the paper by printing, photolithography, or other methods” [123].
Wax printing and photolithography are widely used fabricating and patterning technology
for preparations of paper-based microfluidic devices [42, 46, 120]. Wax printing is a rapid,
inexpensive and easier than photolithography and other mentioned techniques [42]. In this
research, wax printing is used to prepare SERS substrates therefore; only wax printing method of
21
patterning is discussed. Wax printer deposits wax on the paper; wax is melted by a heat source;
and spreads in lateral and vertical direction creating a 3-D hydrophobic barrier across the
thickness [42, 124]. Molten Wax spreads and hence hydrophobic walls are wider than original
printed pattern (Figure 7).
Wax printed microfluidic devices are suited for aqueous solutions of various pHs as it
(aqueous solution) doesn’t cross the hydrophobic barrier of wax on cellulose paper but flow with
in the hydrophobic barriers (channels). Analytes transport can also be controlled by changing the
channel shape, size and by adding soluble or insoluble barriers [68].
Microfluidic devices (µPads) are used for colorimetric detections of glucose, protein, and
copper using silver nanoparticles [41, 125]. Low cost paper-based sensors present a great
platform for detection of cancer biomarkers, heavy metal, identification of blood type and
various bacteria [15, 17, 23, 41, 105, 126, 127]. They are also used with SERS for detection of
various environmental contaminates and pathogens [23, 100, 101].
Depositing metal (usually Au, Ag, Cu) nanoparticles on the patterned paper forms paper-
based SERS substrates [21, 37, 41-46]. These SERS substrates may be prepared by using pre-
formed metal nanoparticles and then subsequent addition of these nanoparticles to paper [21, 22,
27, 38, 47, 48] or synthesis of metal nanoparticles within paper by the addition of metal
precursor and the subsequent addition of reducing agent [49-53].
As mentioned in Chapter 1, Lee C.H. et al. fabricated SERS substrates by directly
depositing gold nanorods (AuNRs) solution in filter paper, which can be used for detection of
desired analytes using SERS (Figure 4) [21]. Also, LSPR band in the UV-Vis analysis was
observed to be in between from 520 nm - 700 nm.
22
Figure 4. (A) Paper-based SERS substrates prepared by gold nanorods (AuNRs) solution
before and after exposure showing the strong color change; (B) UV-Vis extinction spectrum
of the AuNRs solution and the AuNRs loaded paper. Lee, C.H., L. Tian, and S. Singamaneni,
Paper-Based SERS Swab for Rapid Trace Detection on Real World Surfaces. Applied Materials
& Interfaces, 2010. 2(12): p. 3429-3435. Copyright (2010) American Chemical Society. Used
with kind permission from Rightslink, 2015.
23
However, very little is known and reported for SERS substrates prepared by in situ
reduction of gold salt to produce gold nanoparticles (AuNPs) in the paper [114]. This method can
reduce effect of “coffee ring” due to nanoparticle transport and it can be expected to get more
uniform substrates. Therefore, in this thesis, an effort is made to fabricate simple paper-based
SERS substrates using in situ reduction based synthesis of gold nanoparticles.
24
Chapter 3. Experimental Methods and Instruments
3.1 Material
Tri-sodium citrate dihydrate (F.W. 294.1) was purchased from Fisher Chemical. ACS
reagent grade hydrogen tetrachloroaurate (F.W 393.8) was purchased from Sigma Aldrich. Stock
solutions of 200 mM hydrogen tetrachloroaurate and 600 mM trisodium citrate dihydrate were
prepared at ambient temperature in nanopure water. The stock solution was diluted to achieve
various concentrations from 5 to 200 mM of hydrogen tetrachloroaurate and 5 to 600 mM
trisodium citrate dihydrate. In this thesis, tri-sodium citrate dehydrate solution is simply referred
as citrate solution and similarly, hydrogen tetrachloroaurate is called gold chloride solution or
gold precursor.
3.2 Preparation of wax printed microfluidic wells/channels
Wax printed Microfluidic channels/wells were designed using Adobe Photoshop CS5
software. Various designs such as a) circular wells of 2 mm diameter (Figure 5), b) circular
wells of 10 mm diameter, and c) channels of 3 mm diameter with 1.2 mm channel length each
with wax wall thickness of 300 µm (Figure 5) were produced on chromatography paper using a
wax printer (Xerox Colorqube 8570).
The wax printed microfluidic channels or wells were heated to spread the wax in the
paper to create a 3D hydrophobic barrier. After printing these designs on chromatography paper,
the channels/wells were heated at 150 ℃ for 2 minutes in the following manner: a) the back side
of the wax printed channels/spots was heated for 1 min; b) the front side of the sample was
heated for 30 sec; and c) the back side of the samples was heated again for 30 sec. In this way,
the wax melted into the paper creating a three-dimensional microfluidic channel or well with
25
hydrophobic boundaries. These wax boundaries provide the barrier for aqueous solutions of
hydrogen tetrachloroaurate or trisodium citrate (Figure 7).
Figure 5. (A) Wax printed circular paper-based sensors (2 mm circular wells) (B) Wax
printed microfluidic paper-based channels; dark red color is due to formed gold
nanoparticles.
3.3 Preparation of paper-based SERS substrates
Paper-based SERS substrates (Figure 5) were prepared by in situ reduction (Figure 6) of
hydrogen tetrachloroaurate with trisodium citrate in microfluidic channels/wells under room
temperature conditions (Temperature ~25oC & RH ~65%). The citrate reduction method
(Turkevich method [95, 111]) was used with the following modifications (Figure 6). In the
Turkevich method, gold nanoparticles are synthesized by citrate reduction in aqueous solution
whereas, in this case in situ reduction involved reaction of hydrogen tetrachloroaurate with
sodium citrate within the microfluidic channels/wells. First, addition of hydrogen
tetrachloroaurate was done in microfluidic channels/spots under room temperature conditions
A B
26
(Temperature ~25oC & RH ~65%). Afterwards, trisodium citrate (reducing agent) was added to
reduce hydrogen tetrachloroaurate (gold precursor). The time gap between the addition of gold
salt precursor and reducing agent was approximately 1-2 minutes. Hydrogen tetrachloroaurate
and trisodium citrate were adsorbed and transported within the prepared 3D microfluidic
channel. The gold precursor was then reduced by citrate and gold nanoparticles were formed
within the paper after a given reaction time Figure 6. The molar ratio of reducing agent
(trisodium citrate solution) to gold precursor (gold chloride) was systematically varied from 1 to
6 and the substrates were analyzed over a fixed time interval (immediately after preparation, on
day 1, and week-1 to week-5)
Figure 6. In situ reduction of gold precursor (hydrogen tetrachloroaurate solution) by
reducing agent (trisodium citrate); HAuCl4 stands for gold precursor
The prepared substrates were kept under ambient laboratory conditions to dry or for the
reaction to proceed (reaction time varies). The samples were then used as SERS substrates for
analysis of the Raman active MGITC dye. Parameters such as the concentration of reducing
agent, the room temperature and type of reducing agent, humidity, pH of aqueous solution and
the molar ratio of reducing agent to gold salt precursor affect the rate of in situ reduction of gold
chloride solution.
HAuCl4
27
3.4 Instrumentation
3.4.1 UV-Vis
The UV-Vis extinction (scattering and absorption) spectra between 400-800 nm of 10
mm circular microfluidic substrates (µPads) were collected using a Varian Cary 5000
spectrophotometer with a solid sample analyzer with reduced slit height. Samples were analyzed
at regular time intervals (immediately after preparation, on day 1, and week-1 to week-5) for
different molar ratios (MRs) of reducing agent to gold precursor. It was found that transmittance
of the light beam through these µPads was negligible (less than 1%) with respect to adsorption
and reflection of light. Therefore, the UV-Vis solid sample analyzer measured the percentage of
light beam reflected by each sample substrate. On the basis of the percentage reflected data,
extinction coefficient (varies from 0 to 1) vs. wavelength (400 nm - 800 nm) graphs were plotted
and analyzed.
3.4.2 Surface enhanced Raman spectroscopy (SERS)
SERS spectra were collected using a WITec Alpha500R AFM Raman spectrometer. It
consists of a UHTS300 spectrometer, DU 401 BR-DD CCD camera, 10× and 100× microscope
objectives, and 633 nm and 785 nm He-Ne lasers. SERS substrates were prepared primarily
using 2 mm wax printed microfluidic circular wells. Various substrates of different molar ratio
(MR) of reducing agent to gold precursor were prepared according to the above-mentioned
method (Figure 6). MGITC dye (1 µL, 1 µM) was added to each SERS substrate to enable
collection of the surface-enhanced Raman spectrum. After addition of MGITC dye, these
substrates were taped to glass microscope slides.
Before collecting the SERS of substrates, the laser alignment was adjusted, the sample
position was calibrated, and the Raman spectrum of a reference silica wafer was collected. For
28
sampling, the laser needed to be focused at the center of the sample by using a 100× microscope
objective lens. Optical images, single Raman spectra and large area scans were collected using a
particular set of parameters such as 10× microscope objective lens, 785 nm or 633 nm laser,
spectral center of 1800 cm-1 and laser power of 1.0 or 1.2 on the micrometer. For 785 nm laser
1.0 and 1.2 reading on micrometer corresponds to 5 mW and 18.3 mW of power respectively for
10x microscopic objective. After obtaining optical images of a sample of interest, large area
scans (i.e., image scans) of 50 × 50 µm2 with 50 points per line, 50 lines per image and an
integration time of 0.11 sec/sample were collected.
3.4.3 FE-SEM
A Leo ZEISS Field Emission Scanning Electron Microscope (FE-SEM) was used to
observe the formation of gold nanoparticles in the microfluidic channels/wells by in situ
reduction of gold precursor. To prepare samples for FE-SEM analysis, wax was removed from
the SERS substrates to minimize charging and they were attached to the SEM stubs using double
stick tape. A sputter-coater was used to coat samples with gold and palladium (60% Au and 40%
Pd). SEM images of interest were collected by setting the voltage source (EHT) around 5 kV and
using a working distance of 10 mm. Energy Dispersive X-Ray Spectroscopy (EDS/EDX) was
used to analyze the chemical composition of selected SEM images of substrates by adjusting the
voltage to 10 kV and using a working distance of approximately 8.5 mm.
29
Chapter 4. Results and Discussion
Paper based SERS substrates (µPADs) were prepared using a wax printer to create 3D
hydrophobic wax boundaries within chromatography paper (refer Section 3.2 & 3.3). It was
observed that after heating, the width of the channels or the diameter of the circular wells was
reduced due to the spreading of the wax (Figure 7). In general, for a wax printed channel
(µPAD), the available area for transport of analyte will be reduced; however, the as formed wax
boundaries constrain the transport of analyte and solution as illustrated in Figure 7.
After heating, the cellulosic fibers of the filter paper were covered by the hydrophobic
layer of wax. Figure 8 illustrates wax-coated paper prior to heating and after heating. Because of
the wax coating, the aqueous analytes were forced/constrained to flow within the wax printed
boundaries. These wax-printed paper based microfluidic channels or wells (µPADs) were used to
further develop SERS substrates using in situ reduction of gold precursor.
30
Figure 7. The wax spreads during heating, creating narrower channels in the tested
μPADs; (A) Unheated wax channel and heated wax channel; (B) Unheated and heated
circular microfluidic well. The μPAD dimension describes the printed measurements.
31
Figure 8. Characterization of wax printed-paper before and after heating; (A) SEM images
of microfluidic channel before (at magnification of 500x); (B) FESEM images of
microfluidic channel after heating (at magnification of 500x); (C) One of the waxed coated
cellulosic fiber is zoomed in (at magnification of 1000x).
Unheated wax Fresh paper, no wax
100 μm
100 μm 2 μm
B C
A
After Heating
32
4.1 Synthesis of gold nanoparticles by in situ reduction within paper
The synthesis of gold nanoparticles by citrate reduction is a commonly used method that
involves hydrogen tetrachloroaurate, sodium citrate, and water [33, 111]. In this research, gold
nanoparticles were synthesized within the microfluidic paper based substrates by ‘in situ
reduction’. As described in Section 3.3, ‘in situ reduction’ occurs when nucleation and growth of
nanoparticles occur in the same process/step within the paper matrix [50-52, 110, 115, 116, 128].
Here, paper-based SERS substrates were prepared by loading gold precursor on chromatography
paper or microfluidic paper based devices (Figure 6), followed by addition of sodium citrate as a
reducing agent.
Hydrogen tetrachloroaurate (also referred as gold chloride or HAuCl4) and trisodium
citrate (referred to as citrate or Na3Ctr) are adsorbed and transported on microfluidic paper based
devices. Due to redox reaction, gold ions (Au+3) are reduced to gold atoms that nucleate to form
gold nanoparticles (Figure 3).
As shown in Figure 9, the observed color of the microfluidic paper based sensors
(µPADs) changed to dark pink (red/violet) as a result of in situ nanoparticle formation. In situ
nanoparticles synthesis was affected by the change in the concentration of gold salt, reducing
agent, the ambient conditions, and the reaction time. Figure 12 shows the UV-Vis spectra for
samples with variable gold salt and citrate solution concentrations (Table 4). The molar ratio of
citrate to gold chloride has been shown to be the primary parameter that controls nucleation and
growth of AuNPs in suspension and therefore during preparation of paper based samples the
molar ratio (MR) was varied from 1 to 6 by changing the gold chloride and sodium citrate
concentrations.
33
Figure 9. Example of color change in chromatography paper in 10 mm circular well (left)
and 2 mm circular wells (right); HAuCl4 and Na3Ctr stand for gold chloride and sodium
citrate solution respectively.
The UV-Vis spectrum of spherical gold nanoparticle suspensions typically consists of a
maximum absorption peak with size dependent wavelength of 520-580 nm [53, 113]. However,
the UV-Vis spectra of non-spherical gold nanoparticles typically consist of two maximum
absorption peaks that correlate to two different nanoparticle dimensions (longitudinal and
transverse). These two different peaks are blue shifted (500 nm - 580 nm) and red shifted (600
nm - 700 nm) relative to the band location for spherical particles [97, 100, 113].
In the UV-Vis spectra (Figure 10) of the paper-based substrates, two absorption peaks
were observed for the samples where a lower molar ratio of reducing agent to gold precursor was
used. For higher molar ratio of citrate-to-gold precursor only one peak was observed. The
observed LSPR band provides an indication of the formation of gold nanoparticles within the
paper matrix. However, as the reaction time increases, the maximum absorbance intensity
increases with time.
34
Table 4. Concentration of gold chloride and sodium citrate solution for UV-Vis analysis;
data used in Figure 10.
Gold Chloride Conc. (Volume used: 10 µL)
Sodium Citrate Conc. (Volume used: 10 µL)
Molar Ratio (Citrate/ Gold Chloride)
25 mM 23 mM 0.95 25 mM 27 mM 1.08 20 mM 27 mM 1.35 15 mM 27 mM 1.8 15 mM 30 mM 2 10 mM 30 mM 3
For the lowest concentration of citrate (when MR is from 0.95 to 1.35) two plasmon
bands (blue shifted and red shifted) are observed. It is likely that this is because of the non-
spherical nature of the as formed gold nanoparticles or is the result of the coupling of the surface
plasmons of multiple particles. For excess citrate (molar ratio of citrate to gold chloride 2 to 3)
only one maximum absorbance peak (blue shifted) was observed. The effect of gold precursor
concentration, reducing agent and reaction time are discussed later in this chapter in Section 4.2
and Section 4.3.
35
Figure 10. UV-Vis spectrum of various substrates prepared by different citrate-to- gold
ratio (refer Table 4); Different shape and size of LSPR is observed. (A). 25 mM gold
chloride, 23 mM Citrate Solution (MR= 0.95) (B). 20 mM gold chloride, 27 mM Citrate
Solution (MR= 1.35) (C). 15 mM gold chloride, 30 mM Citrate Solution (MR= 2) (D) 10
mM gold chloride, 30 mM Citrate Solution (MR= 3)
A B
C D
Extin
ction coeff.
Extin
ction coeff.
Extin
ction coeff.
Wavelength (nm) Extin
ction coeff.
36
SERS spectrums of MGITC dye were collected from a concentrated MGITC-methanol
solution (Figure 11). In MGITC-methanol solution, MGITC has primary bands at 1200, 1380
and 1600 cm-1 and therefore the spectrum from 1100 cm-1 to 1800 cm-1 was primarily considered
for further analysis in Section 4.3.
Figure 11. SERS of MGITC dye in MGITC-methanol solution. MGITC assignments are at
1200, 1380 and 1600 cm-1. Leng, W. and P.J. Vikesland, MGITC Facilitated Formation of
AuNP Multimers. Langmuir, 2014. 30(28): p. 8342-8349. Copyright (2014) American Chemical
Society. Used with kind permission from Rightslink, 2015.
Different molar ratio (MR) of reducing salt and gold precursor also affect the SERS
signals intensity/enhancements. Large area scans (SERS spectrum) of different MR were plotted
in Figure 12 to understand the effect of MR, and the effects of changes in the initial
concentration of gold precursor. The general method to obtain SERS spectrum is reported in
Section 3.4.2. However, to obtain Figure 12, Raman laser of 633 nm wavelengths was used
instead of 785 nm Raman Laser. The Raman laser of 785 nm produced less fluorescence and
background noise for these SERS substrates.
37
Table 5. Concentration of Gold Chloride and Sodium Citrate (data used in Figure 12)
Gold Chloride Conc. (Volume used= 1 µL)
Sodium Citrate Conc. (Volume used= 1 µL)
Molar Ratio (Citrate/ Gold Chloride)
25 mM 17 mM 0.68 15 mM 20 mM 1.33 10 mM 27 mM 2.7 5 mM 20 mM 4.0 5 mM 27 mM 5.4 4 mM 27 mM 6.75 4 mM 30 mM 7.5
Figure 12. Comparative analyses of paper-based substrates prepared by various different
molar ratio of citrate to gold chloride; 2 mm wax printed wells are loaded with gold
chloride solution followed by citrate solution (reducing agent); Reaction time: 7 days with
addition of 1 µL of MGITC dye; (A) the difference in the region of 100 ~ 350 cm-1 may be
caused by the size or shape of Gold NPs in the paper; (B) SERS spectrum of MGITC dye
with various molar ratios (MR). Raman parameters: Laser wavelength 633 nm, and
micrometer reading 1.2 mm (0.261 mW for 10x objective lens).
38
The SERS spectra for substrates with MR of 0.68 and 1.33 have higher initial gold
precursor than other samples and they (MR= 0.68 and 1.33) have clear and uniquely
distinguishable MGITC spectrum. Higher gold chloride concentrations produce more gold
nanoparticles (for same conditions and same reducing salt concentration). Also, if MR of
reducing agent (citrate solution) to gold chloride solution is less than the 1:2 (reaction
stoichiometry) then it may produce larger and irregular dimensions of gold nanoparticles in the
paper based substrates that will result into higher peak heights in the SERS spectrum of MGITC
dye [104]. This analysis shows that paper based substrates prepared by in situ based reduction
based method can be used for detection and monitoring of analytes. However, ideal paper-based
substrates should be uniform and reproducible so that variation in signal enhancement may be
reduced. For this purpose, an additional set of experiments and optimization strategies were
conducted and are further discussed in Section 4.3.
A Leo ZEISS Field Emission Scanning Electron Microscope (FE-SEM) was used to
observe the formed gold nanoparticles in microfluidic channels/wells by in situ reduction of gold
salt. Figure 13 shows chromatography paper SEM image and EDX analysis. A very small
elemental peak for gold (Au) element was observed, which can be attributed to the gold-
palladium sputter coating. Figure 14 shows SEM images and EDX analysis of chromatography
paper loaded with pre-formed gold nanoparticles (size 50 nm) prepared by Turkevich method.
Due to the presence of 50 nm size AuNPs a significant elemental peak for Au element was
observed. Analysis of paper-based substrates prepared by in situ reduction of gold salt was also
performed. Figure 15 shows clusters of AuNPs formed via in situ reduction method. Figure 16
illustrates SEM and EDX images for paper based SERS substrates prepared by loading 5 mM
39
auric acid (3 µL) followed by 20 mM citrate solution (3 µL) with allowed reaction time of 7 days
(with a desiccator time ~ 1 day). Detailed discussion on FE-SEM method is discussed in Section
3.4.3. It is observed that the elemental peak of gold in paper-based substrates prepared by in situ
reduction of gold salt is significant.
40
Figure 13. (A) FE-SEM image of chromatography paper (blank) at magnification ~10 kx;
(B) Different FE-SEM image of chromatography paper (blank) at magnification ~10 kx;
(C) EDX image showing strong C, O elemental peaks and negligible gold peaks. Gold peak
is a result of gold-palladium coating.
B A
C
41
Figure 14. (A) SEM image of chromatography paper loaded with 50 nm sized gold
nanoparticles prepared by citrate reduction method at magnification of 30.00 kx; (B) SEM
image of chromatography paper loaded with 50 nm sized gold nanoparticles prepared by
citrate reduction method at magnification of 100.00 kx; (C) EDX image confirming
presence of gold nanoparticles. Images produced at working distance (WD) ~8.5 mm and
Voltage (EHT) ~ 20kV.
A B
C
42
Figure 15. SEM analysis of paper-based SERS substrates prepared by in situ reduction
based gold nanoparticle synthesis (5 mM gold chloride, molar ratio of citrate to gold
chloride~ 4, and allowed reaction time ~ 7 days) (A) Clusters (circles) of formed AuNPs in
sample image with magnification ~ 101.4 KX; (B) Clusters of formed AuNPs in sample
image with magnification ~ 30.4 KX; (C) Clusters of formed AuNPs in sample image with
magnification ~ 100.36 KX; (D) Clusters of formed AuNPs in sample image with
magnification ~ 100.72 K X (used WD~ 5.7 mm, EHT~ 2 kV).
A B
C D
43
Figure 16. SEM analysis of paper-based SERS substrates prepared by in situ reduction
based gold nanoparticle synthesis (5 mM gold chloride, molar ratio of citrate to gold
chloride~ 4 and allowed reaction time ~ 7 days); (A) Sample image with magnification ~40
K X, WD~ 5.7 mm, EHT~ 2 kV; (B) EDX image showing elemental analysis of square box
(pink color) in image (A).
44
On the basis of scanning electron microscope (SEM), UV-Vis absorption analysis and
signal enhancement of surface Raman enhancement spectroscopy, formation of AuNPs within
the microfluidic paper-based device (µPADs) was confirmed. However, to study effect of
variation in gold precursor i.e. gold chloride and reducing agent concentration on LSPR band and
shape, detailed UV-Vis and SERS analysis of different samples were performed.
4.2 UV-Vis analysis to study effect of the variation in gold precursor and reducing agent
concentration with increase in reaction time
UV-Vis spectra of paper-based sensors were collected using a solid UV-Vis analyzer as
discussed in Section 3.2. It is expected that different gold precursor and reducing agent
concentrations will produce different UV-Vis spectrum. In this analysis, the effect of variation in
gold precursor and reducing agent concentration with an increase in reaction time was studied.
For this purpose four different gold salt concentrations (10, 20, 50, and 100 mM) were
considered. The molar ratio of citrate to gold chloride was varied from ~ 1 to ~ 6. Reaction time
for the reaction and analysis were day 1, week 1, week 3 and week 5. Detailed experimental
method for UV-Vis is described in Section 3.4.
Temporal changes in the maximum extinction peak of various molar ratios (MR) are
reported in Figure 17. It is observed that the initial rate of change in the maximum extinction
peak intensity is fast, and finally an equilibrium value of the maximum extinction peak was
achieved. As the gold precursor concentration increased from 10 to 100 mM, the maximum
extinction value also increased for a given reaction time. The use of 100 mM gold chloride
resulted in the highest equilibrium value of maximum extinction coefficient (Figure 17). This
may be because of the high gold nanoparticle density for the given molar ratio of citrate to gold
chloride. This trend was also observed for other MRs of citrate to gold chloride. After 35 days,
45
maximum extinction peak value associated to 50 mM initial gold precursor approaches to
maximum absorption value 100 mM gold precursor (red circle in Figure 17). It is observed that
as the initial gold precursor concentration is increased from 10 mM to 100 mM the spectrum
became broader (Figure 18). It can be concluded that for [HAuCl4] greater than 20 mM, a
broader LSPR is observed. In this analysis, initial concentration of 20 mM for gold precursor
was used for further SERS analysis (refer Section 4.3).
46
Figure 17. Temporal variation of maximum absorption of different molar ratios of
citrate solution to gold chloride solution for a given initial concentration of gold chloride
solution; (A) Molar ratio (MR) = 1 (B) Molar Ratio = 3 (C) Molar Ratio= 5.
0
0.2
0.4
0.6
0.8
1
0 5 10 15 20 25 30 35 40
Max. A
bsorpW
on
Time (days)
Temporal change in Max. AbsorpWon (MR: 1)
10 mM gold precursor
20 mM gold Precursor
50 mM gold precursor
100 mM gold precursor
A
0 0.1 0.2 0.3 0.4 0.5 0.6 0.7 0.8 0.9
0 5 10 15 20 25 30 35 40
Max. A
bsorpW
on
Time (days)
Temporal change in Max. AbsorpWon (MR: 3)
10 mM gold precursor
20 mM gold Precursor
50 mM gold precursor
100 mM gold precursor
B
0
0.2
0.4
0.6
0.8
1
0 5 10 15 20 25 30 35 40
Max. A
bsorpW
on
Time (days)
Temporal change in Max. AbsorpWon (MR: 6)
10 mM gold precursor
20 mM gold Precursor
50 mM gold precursor
100 mM gold precursor
C
47
Figure 18. Effect of initial gold precursor solution on absorption values for a given molar
ratio of citrate solution to gold chloride solution after reaction time of 35 days; (A) Molar
ratio of 1 after 35 days (B) Molar ratio of 3 after 35 days (C) Molar ratio of 6 after 35 days
0
0.2
0.4
0.6
0.8
400 500 600 700 800
Abs
Wavelength
Molar RaWo 1 (Days 35)
Paper
10 mM
20 mM
50 mM
100 mM
A
0 0.1 0.2 0.3 0.4 0.5 0.6 0.7 0.8 0.9
400 500 600 700 800
Abs
Wavelength
Molar RaWo 3 (Days 35)
Paper
10 mM
20 mM
50 mM
100 mM
B
0
0.2
0.4
0.6
0.8
1
400 500 600 700 800
Abs
Wavelength
Molar RaWo 6 (Days 35)
Paper
10 mM
20 mM
50 mM
100 mM
C
As [HAuCl4] increases
As [HAuCl4] increases
As [HAuCl4] increases
48
The LSPR band and shape of the curve changes as MR is increased (Figure 19). In
Figure 19, the gold chloride concentration was kept constant (20 mM) and the concentration of
citrate solution was varied. Because of different concentration of reducing agent, different
dimensions (size or shapes) of AuNPs were produced in the paper-based substrates (circular
wells of size = 10 mm).
Figure 19. LSPR Band and shape changes with the increase in molar ratio (MR) from 1 to
6. [HAuCl4]= 20 mM, reaction time 35 days, and diameter of microfluidic wells are 10 mm.
0.4
0.5
0.6
0.7
0.8
0.9
1
1.1
400 450 500 550 600 650 700 750 800 850
Normalize
d exWn
cWon
Wavelenght (nm)
[HAuCl4]= 20 mM and ReacWon Time= 35 days
MR 1
MR 2
MR 3
MR 4
MR 5
MR 6
Increase in Molar Ratio (MR)
49
Figure 20. LSPR Band and shape changes with the increase in molar ratio (MR) from 1 to
6. [HAuCl4]= 100 mM, reaction time 35 days, and diameter of microfluidic wells = 10 mm.
0.4
0.5
0.6
0.7
0.8
0.9
1
1.1
400 450 500 550 600 650 700 750 800 850
Normalize
d exWn
cWon
Wavelength (nm)
[HAuCl4]= 100 mM and reacWon Time= 35 days
MR 1
MR 2
MR 3
MR 4
MR 5
MR 6
Increase in Molar RaWo
50
Similarly, for [HAuCl4] = 100 mM concentration, by changing molar ratio (MR) change
in LSPR shape and band is observed (Figure 20). For molar ratio (MR = 1), both blue shift and
red shift are observed.
It can be concluded that for a given gold chloride (gold precursor) solution concentration
and given reaction time, the highest molar ratio produces the most intense extinction peak in the
UV-Vis spectrum. This may be because of excess citrate reduction of gold salt into AuNPs is
faster than lower citrate to gold salt molar ratio. As reaction time increased, different molar ratios
produced overlapping or similar maximum absorption peaks with different LSPR band shapes
and sizes.
For a given molar ratio (MR) and reaction time, the highest molar concentration of gold
chloride solution showed highest absorption peak. It may be because lower citrate conc.
(reducing agent) is available to gold salt, which produces larger nanoparticle in the paper. Larger
particle will scatter and absorb more UV-Vis light.
4.3 SERS signal optimization strategy for MGITC using paper based substrates
As discussed in Section 4.1, various molar ratios (MR) of citrate solution (reducing
agent) to gold chloride solution (gold precursor) produce different SERS signal enhancements,
and therefore, optimization of SERS signal enhancements for detection of MGITC dye or other
contaminants was performed in this section. An example of SERS spectrum for MGITC dye on
paper-based substrates is plotted in Figure 21. Using the procedure listed in Section 3.4.2, these
SERS spectra (large area scan, laser 785 nm and micrometer reading ~1.2 mm i.e. 18.3 mW of
laser power) were collected
51
Figure 21. Average SERS spectra (Large area scan) for MGITC dye using paper based
substrates. [HAuCl4]= 20 mM, reaction time= 28 days, Raman Laser 785 nm wavelength
with micrometer reading of 1.2 mm (18.3 mW of laser power for 10x objective lens). MR
stands for Molar Ratio.
As shown in Figure 21, higher molar ratio (such as MR = 5) produces lower signal
enhancements (lower peak heights) than lower molar ratio (i.e., MR= 1 or MR= 3). By
subtracting background signals (noise) from the spectrum, normalized SERS spectrum of various
initial gold precursor concentration and different molar ratios were collected. It can be concluded
that lower molar ratios such as MR= 1, 2 or 3 produce distinguishable signals/assignments for
MGITC dye.
660
680
700
720
740
760
780
800
-‐500 0 500 1000 1500 2000 2500 3000
Raman Intensity
(CCD
cou
nts)
Wavenumber (1/cm)
SERS spectrum of MGITC dye on paper based substrates
MR 1
MR 3
MR 5
1400 cm-‐1
1180 cm-‐1
230 cm-‐1
105 cm-‐1
[HAuCl4]= 20 mM and Reaction time= 28 days
1800 cm-‐1
52
It is desirable that variability of peak intensities (peak heights) are minimized for uniform
and reproducible SERS signals by using paper based SERS substrates. To understand peak
intensity variability of SERS signals, the MGITC assignments were compared to the peak at
1800 cm-1 wavenumber, which is one of the MGITC assignments (Figure 22). As discussed in
Figure 11, major MGITC assignments are at 1200 cm-1, 1400 cm-1, and 1600 cm-1. Therefore, in
these optimization strategies major MGITC assignments were normalized with respect to
smallest peak at 1800 cm-1 and at 105 cm-1 (peak associated to the gold nanoparticles).
53
Figure 22. Optimization of MGITC assignments with respect to peak at 1800 cm-1 (strategy
-1); Lower molar ratios produce less variability in peak ratios than high molar ratios
(circled). Sample 1 and sample 2 are replicate of same substrates (for initial gold chloride
conc. = 20 mM)
0
5
10
15
20
25
30
35
0 1 2 3 4 5 6
Normalize
d pe
ak intensity
/ height
Molar RaWo of reducing agent to gold chloride sol
Peak raWo (1180/1800) vs. molar raWo
Sample 1
Sample 2
Avg Value
A
0 0.1 0.2 0.3 0.4 0.5 0.6 0.7 0.8 0.9
0 1 2 3 4 5 6 7
Normalize
d pe
ak intensity
/heights
Molar RaWo of reducing agent to gold chloride sol
Peak raWo (1400/1800) vs. molar raWo
Sample 1
Sample 2
Avg Value
B
54
Figure 23. Optimization of MGITC assignments with respect to the peak at 105 cm-1
(strategy-2); Sample 1 and sample 2 are replicate of same substrates (for initial gold
chloride conc. = 20 mM).
0 10 20 30 40 50 60 70
0 1 2 3 4 5 6 7
100* ra
Wo of p
eaks 1180/105
RaWo
RaWo of ~1180/105 vs. Molar RaWo
Sample 1
Sample 2
Avg value
0 5
10 15 20 25 30 35
0 1 2 3 4 5 6 7
100* ra
Wo of p
eaks 1400/105
RaWo
RaWo of ~1400/105 vs. Molar RaWo
Sample 1
Sample 2
Avg
0 1 2 3 4 5 6 7
0 1 2 3 4 5 6 7
100* ra
Wo of p
eaks 1800/105
RaWo
RaWo of ~1800/105 vs. Molar RaWo
Sample 1
Sample 2
Avg
55
For lower MRs (such as of MR = 1, 2 or 3), the variability in peak intensities is
minimized (circled in Figure 22) and for higher ratios, the variability in peak intensities is
relatively high. Similar results were obtained if normalization was performed with respect to the
initial gold nanoparticle peaks i.e., 105 or 230 cm-1 (Figure 23). Also, SERS spectra (large area
scan) of various initial gold precursor concentrations and different MR were collected and it was
observed that lower molar ratio such as MR= 1, 2 or 3 produces lower variability in peak ratios
(peak intensities).
Similar analysis was performed for different initial gold precursor concentration
([HAuCl4]= 10 mM), and it was observed that for lower ratios (such as MR= 1, 2 or 3) the
variability in normalized peaks are lower than higher molar ratios (such as MR= 5 or 6). Also,
Raman laser of 785 nm or 633 nm can be used with citrate-to-gold molar ratio of 1:1 or 2:1 to
produce high signal enhancements of analyte.
As paper-based SERS substrates produce less variation in peak intensities for lower ratio
in comparison of higher molar ratios (MR), therefore, use of lower molar ratio is recommended
for further analysis of desired Raman active compound or environmental contaminants using
paper-based substrates.
56
Chapter 5. Conclusions and Future Work
5.1 Conclusions
In this thesis, in situ reduction based paper-based microfluidic SERS substrates were
discussed. These substrates were prepared for detection of environmental contaminants using
AuNPs, which were synthesized by reduction of gold chloride (gold precursor) within the wax
printed chromatography paper. These prepared substrates were mainly analyzed and
characterized by UV-Vis spectroscopy, scanning electron microscope (SEM), and SERS.
It was concluded that in situ reduction produced AuNPs in the microfluidic paper based
devices (Figure 14 and Figure 16) that can be further used for contaminant detection using
SERS. From EDX analysis (Figure 16), formed gold NP clusters were confirmed. From UV-Vis
analysis, it was concluded that for a given gold salt conc. and a given reaction time, the highest
molar ratio produced the highest peak of extinction coefficient in the UV-Vis spectrum (Figure
19 and Figure 20). Similarly, the highest molar concentration of gold salt showed the highest
extinction coefficient (maximum peak) for a given molar ratio and the reaction time (Figure 18),
which may be because of available higher gold density. UV-Vis analysis also showed that molar
ratio of citrate-to-gold around 1:1 or 2:1 produced broader LSPR band including red shift (~650
nm). Therefore, it is recommended to use lower molar ratio (MR) for SERS analysis using laser
source of 633 nm or 785 nm wavelength so that optimum signal enhancement can be achieved to
detect contaminants.
By optimizing conditions (such as gold precursor conc., reducing agent conc., and
temperature) paper based substrates (prepared by in situ reduction based method) may be
produced to identify analyte below limit of detection (LOD). Also, these paper-based SERS
57
substrates produced lesser variation in peak intensities for lower citrate-to-gold ratio in
comparison of higher molar ratio (Figure 22 and Figure 23).
In summary, lower molar ratio of reducing agent to gold precursor produced broader
LSPR band and Raman laser of 785 nm or 633 nm can be used with these substrates to produce
good signal enhancements (peak intensity) of MGITC dye. Therefore, use of lower molar ratio in
paper-based substrates (prepared by in situ method) is recommended for further analysis of the
desired Raman active compound or environmental contaminants.
5.2 Future work
SERS has a great potential for detection of pathogens, cyanobacteria and environmental
contaminants [15, 127, 129]. With SERS, detection of these pollutants may be handy, and
accurate. However, it requires proper SERS substrates that can be effectively used for this
purpose [18, 21, 24, 31].
Paper-based SERS substrates may hold a great hope for the future of detection and
characterization of environmental contaminants. However, there are few barriers associated with
uniformity and reproducibility of substrates [8, 38, 88]. It is still difficult to achieve ideal
substrates having uniformity and reproducibility, which are necessary to produce ideal detection
of environmental analyses [32, 34]. In situ reduction of gold precursor based approach may hold
the key to production of ideal SERS substrates. However, following steps may be taken to
further this research:
1. The effect of temperature on reaction yield
In situ reduction of metal salt in the paper is a complex process, which also depends on
ambient conditions such as humidity and temperature. Effect of these ambient conditions on
58
SERS signals enhancements should be studied further, which will help in better decision-making.
In this thesis, it was observed that at room temperature, reaction yield or conversion of gold
chloride was low. Therefore, use of higher temperature may increase the reaction yield. Higher
temperature may be maintained in a hot bath or a heating plate.
2. The effect of change in reducing agent
By increasing the reducing agent concentration, variation in peak enhancement/intensity
of MGITC dye was observed. However, effect of change in concentration of reducing agent on
the size and shape of formed nanoparticles should be further studied.
3. Microfluidic paper based devices for multiple analyte detection
In this thesis, an attempt is made to understand various parameters that may affect the
uniformity of paper-based substrates. However, extensive efforts are needed to develop specific
substrates for various contaminates. For example, specific substrates can be produced for
detection of various microcystins and particular viruses such as poliovirus [15, 127, 129].
Specific detection of various contaminants may also be achieved by developing proper
antibodies that can bind desired contaminants [43]. Also, paper surface may be modified to
achieve ideal detection of specific analytes.
4. Characterization and optimization of SERS signals of Raman active compounds
Currently, we used MGITC dye for characterization of paper-based substrates and for
optimization of Raman signals. However, other Raman active compounds may be used for
characterization of these substrates.
59
5. Quantitative studies for reaction conversion and AuNPs formation
Further quantitative study of the reaction conversion (in situ based reduction of gold
chloride) and density calculation of formed AuNPs may help in optimization of SERS signals.
Various methods such as IPC-MS may be used for this purpose.
60
References
1. Li, D.-W., et al., Recent progress in surface enhanced Raman spectroscopy for the detection of environmental pollutants. Microchimica Acta, 2014. 181(1-2): p. 23-43.
2. World Health Report 2002. Geneva: WHO. 2002.
3. Arsenic pollution and remediation: an international perspective, in Reviews of Environmental Contamination and Toxicology, Vol 197, H. Garelick, et al., Editors. 2008.
4. Wang, B., Addressing the environmental risk of persistent organic pollutants in China. Environ. Sci. Engin., 2012. 6(1): p. 2–16.
5. Chorus I, B.J., eds., Toxic cyanobacteria in water: A guide to their public health consequences, monitoring and management. Published by E & FN Spon, London, on behalf of the World Health Organization, Geneva, 1999.
6. Graham JL, L.K., and Kamman N., Monitoring Recreational Freshwaters. Lakeline, 2009. Summer.
7. Kocagoz, R., et al., Environmental and biological monitoring of persistent organic pollutants in waterbirds by non-invasive versus invasive sampling. Toxicology Letters, 2014. 230(2): p. 208-217.
8. Spencer, K.M., et al. Surface-enhanced Raman for monitoring toxins in water. 2004.
9. Butler, O.T., et al., 2013 Atomic spectrometry update-A review of advances in environmental analysis. Journal of Analytical Atomic Spectrometry, 2014. 29(1): p. 17-50.
10. Koeber, R., J.M. Bayona, and R. Niessner, Determination of benzo a pyrene diones in air particulate matter with liquid chromatography mass spectrometry. Environmental Science & Technology, 1999. 33(10): p. 1552-1558.
11. Liu, Q., Q. Zhou, and G. Jiang, Nanomaterials for analysis and monitoring of emerging chemical pollutants. TrAC Trends in Analytical Chemistry, 2014. 58(0): p. 10-22.
12. Szulejko, J.E., et al., Review of progress in solvent-extraction techniques for the determination of polyaromatic hydrocarbons as airborne pollutants. TrAC Trends in Analytical Chemistry, 2014. 61(0): p. 40-48.
61
13. Lian, S., et al., Estimate of heavy metals in soil and streams using combined geochemistry and field spectroscopy in Wan-sheng mining area, Chongqing, China. International Journal of Applied Earth Observation and Geoinformation, 2015. 34: p. 1-9.
14. Li, C.W., M.M. Benjamin, and G.V. Korshin, Use of UV spectroscopy to characterize the reaction between NOM and free chlorine. Environmental Science & Technology, 2000. 34(12): p. 2570-2575.
15. Halvorson, R.A. and P.J. Vikesland, Surface-Enhanced Raman Spectroscopy (SERS) for Environmental Analyses. Environmental Science & Technology, 2010. 44(20): p. 7749-7755.
16. Jokerst, J.C., J.M. Emory, and C.S. Henry, Advances in microfluidics for environmental analysis. Analyst, 2012. 137(1): p. 24-34.
17. Li, C.-z., et al., Paper based point-of-care testing disc for multiplex whole cell bacteria analysis. Biosensors & Bioelectronics, 2011. 26(11): p. 4342-4348.
18. Cialla, D., et al., Surface-enhanced Raman spectroscopy (SERS): progress and trends. Analytical and Bioanalytical Chemistry, 2012. 403(1): p. 27-54.
19. Jarvis, R.M., A. Brooker, and R. Goodacre, Surface-enhanced Raman scattering for the rapid discrimination of bacteria. Faraday Discussions, 2006. 132(0): p. 281-292.
20. Kneipp, K., et al., Single molecule detection using surface-enhanced Raman scattering (SERS). Physical Review Letters, 1997. 78(9): p. 1667-1670.
21. Lee, C.H., L. Tian, and S. Singamaneni, Paper-Based SERS Swab for Rapid Trace Detection on Real-World Surfaces. Acs Applied Materials & Interfaces, 2010. 2(12): p. 3429-3435.
22. Luo, Z., et al., A SERS-based immunoassay for porcine circovirus type 2 using multi-branched gold nanoparticles. Microchimica Acta, 2013. 180(15-16): p. 1501-1507.
23. Wang, Y., et al., Duplex Microfluidic SERS Detection of Pathogen Antigens with Nanoyeast Single-Chain Variable Fragments. Analytical Chemistry, 2014. 86(19): p. 9930-9938.
24. Li, D.W., et al., Recent progress in surface enhanced Raman spectroscopy for the detection of environmental pollutants. Microchimica Acta, 2014. 181(1-2): p. 23-43.
62
25. Xie, Y., et al., Selective SERS detection of each polycyclic aromatic hydrocarbon (PAH) in a mixture of five kinds of PAHs. Journal of Raman Spectroscopy, 2011. 42(5): p. 945-950.
26. Jestel, N.L., Process Raman Spectroscopy, in Process Analytical Technology. 2007, Blackwell Publishing Ltd. p. 133-169.
27. Bell, S.E.J. and N.M.S. Sirimuthu, Surface-enhanced Raman spectroscopy (SERS) for sub-micromolar detection of DNA/RNA mononucleotides. Journal of the American Chemical Society, 2006. 128(49): p. 15580-15581.
28. Doering, W.E. and S.M. Nie, Single-molecule and single-nanoparticle SERS: Examining the roles of surface active sites and chemical enhancement. Journal of Physical Chemistry B, 2002. 106(2): p. 311-317.
29. Jiang, X., et al., Silver nanoparticle aggregates on copper foil for reliable quantitative SERS analysis of polycyclic aromatic hydrocarbons with a portable Raman spectrometer. Analyst, 2012. 137(17): p. 3995-4000.
30. Zhu, Y., et al., Gold nanorod assembly based approach to toxin detection by SERS. Journal of Materials Chemistry, 2012. 22(6): p. 2387-2391.
31. Bhavya Sharma, R.R.F., Anne-Isabelle Henry, Emilie Ringe, and Richard P. Van Duyne, SERS: Materials, applications, and the future. Materials Today, 2012. 15: p. 15-20.
32. Lin, X.-M., et al., Surface-enhanced Raman spectroscopy: substrate-related issues. Analytical and Bioanalytical Chemistry, 2009. 394(7): p. 1729-1745.
33. Ji, X., et al., Size control of gold nanocrystals in citrate reduction: The third role of citrate. Journal of the American Chemical Society, 2007. 129(45): p. 13939-13948.
34. Yeh, Y.-C., B. Creran, and V.M. Rotello, Gold nanoparticles: preparation, properties, and applications in bionanotechnology. Nanoscale, 2012. 4(6): p. 1871-1880.
35. Pinto, R.J.B., et al., Growth and Chemical Stability of Copper Nanostructures on Cellulosic Fibers. European Journal of Inorganic Chemistry, 2012(31): p. 5043-5049.
36. Fan, M., G.F.S. Andrade, and A.G. Brolo, A review on the fabrication of substrates for surface enhanced Raman spectroscopy and their applications in analytical chemistry. Analytica Chimica Acta, 2011. 693(1-2): p. 7-25.
63
37. Lee, C.H., et al., Highly Sensitive Surface Enhanced Raman Scattering Substrates Based on Filter Paper Loaded with Plasmonic Nanostructures. Analytical Chemistry, 2011. 83(23): p. 8953-8958.
38. Qian, C., et al., Comparison of Gold and Silver Nanoparticles as Active Substrates for SERS Spectra Measurements on Liver Cancer Cells. 2012 7th International Conference on System of Systems Engineering (Sose), 2012: p. 92-95.
39. Khlebtsov, B.N., et al., Surface-Enhanced Raman Scattering Substrates Based on Self-Assembled PEGylated Gold and Gold-Silver Core-Shell Nanorods. Journal of Physical Chemistry C, 2013. 117(44): p. 23162-23171.
40. Chen, H.-C., et al., Surfactant-assisted preparation of surface-enhanced Raman scattering-active substrates. Rsc Advances, 2014. 4(21): p. 10553-10559.
41. Davaji, B. and C.H. Lee, A paper-based calorimetric microfluidics platform for bio-chemical sensing. Biosensors & Bioelectronics, 2014. 59: p. 120-126.
42. Dungchai, W., O. Chailapakul, and C.S. Henry, A low-cost, simple, and rapid fabrication method for paper-based microfluidics using wax screen-printing. Analyst, 2011. 136(1): p. 77-82.
43. Fu, A., et al., Paper-based microfluidic immune sensor chip useful for detecting antigen, comprises paper base, microfluidic channel and labeled antibody marker carrier cluster. Chengdu Junya Technology Co Ltd.
44. Ge, X., et al., Nanomaterial-enhanced paper-based biosensors. TrAC Trends in Analytical Chemistry, 2014. 58(0): p. 31-39.
45. Lan, W.-J., et al., Paper-based electroanalytical devices with an integrated, stable reference electrode. Lab on a Chip, 2013. 13(20): p. 4103-4108.
46. Martinez, A.W., et al., Diagnostics for the Developing World: Microfluidic Paper-Based Analytical Devices. Analytical Chemistry, 2010. 82(1): p. 3-10.
47. Chen, Z., et al., Gold Nanoparticles-Modified Tapered Fiber Nanoprobe for Remote SERS Detection. Ieee Photonics Technology Letters, 2014. 26(8): p. 777-780.
48. Saute, B., et al., Gold nanorods as surface enhanced Raman spectroscopy substrates for sensitive and selective detection of ultra-low levels of dithiocarbamate pesticides. Analyst, 2012. 137(21): p. 5082-5087.
64
49. Dutta, A., et al., Nanoscale characterization of gold nanoparticles created by in situ reduction at a polymeric surface. Journal of Microscopy, 2013. 251(1): p. 27-34.
50. Ghosh, A., et al., Preparation and stabilization of gold nanoparticles formed by in situ reduction of aqueous chloroaurate ions within surface-modified mesoporous silica. Microporous and Mesoporous Materials, 2003. 58(3): p. 201-211.
51. Leiva, A., et al., In situ synthesis of gold nanoparticles at the air-water interface. Spontaneous reduction of Au(III) by poly(N-vinyl-2-pyrrolidone) monolayers. European Polymer Journal, 2013. 49(8): p. 2128-2137.
52. Mu, Z., et al., In situ synthesis of gold nanoparticles (AuNPs) in butterfly wings for surface enhanced Raman spectroscopy (SERS). Journal of Materials Chemistry B, 2013. 1(11): p. 1607-1613.
53. Zhao, P.X., N. Li, and D. Astruc, State of the art in gold nanoparticle synthesis. Coordination Chemistry Reviews, 2013. 257(3-4): p. 638-665.
54. Deegan, R.D., et al., Capillary flow as the cause of ring stains from dried liquid drops. Nature, 1997. 389(6653): p. 827-829.
55. Carrillo-Carrión, C., et al., Determination of pesticides by capillary chromatography and SERS detection using a novel Silver-Quantum dots “sponge” nanocomposite. Journal of Chromatography A, 2012. 1225(0): p. 55-61.
56. Guerrini, L., et al., Nanosensors Based on Viologen Functionalized Silver Nanoparticles: Few Molecules Surface-Enhanced Raman Spectroscopy Detection of Polycyclic Aromatic Hydrocarbons in Interparticle Hot Spots. Analytical Chemistry, 2009. 81(4): p. 1418-1425.
57. Bao, L., et al., Surface enhanced Raman spectroscopic detection of polycyclic aromatic hydrocarbons (PAHs) using a gold nanoparticles-modified alginate gel network. Analyst, 2012. 137(17): p. 4010-4015.
58. Zhu, C., et al., Large-scale well-separated Ag nanosheet-assembled micro-hemispheres modified with HS-[small beta]-CD as effective SERS substrates for trace detection of PCBs. Journal of Materials Chemistry, 2012. 22(5): p. 2271-2278.
59. Xu, Z., et al., Surface-Enhanced Raman Scattering Spectroscopy of Explosive 2,4-Dinitroanisole using Modified Silver Nanoparticles. Langmuir, 2011. 27(22): p. 13773-13779.
65
60. Liu, X., et al., Functionalizing Metal Nanostructured Film with Graphene Oxide for Ultrasensitive Detection of Aromatic Molecules by Surface-Enhanced Raman Spectroscopy. ACS Applied Materials & Interfaces, 2011. 3(8): p. 2944-2952.
61. Lu, G., et al., Surface enhanced Raman scattering of Ag or Au nanoparticle-decorated reduced graphene oxide for detection of aromatic molecules. Chemical Science, 2011. 2(9): p. 1817-1821.
62. Amer, M.S. and M.S. Amer, Raman Spectroscopy; the Diagnostic Tool, in Raman Spectroscopy, Fullerenes and Nanotechnology. 2010. p. 43-108.
63. Raman Scattering. 2014; Available from: http://www.doitpoms.ac.uk/tlplib/raman/raman_scattering.php.
64. Cheng, J.X. and X.S. Xie, Coherent anti-Stokes Raman scattering microscopy: Instrumentation, theory, and applications. Journal of Physical Chemistry B, 2004. 108(3): p. 827-840.
65. Ishibashi, T. and H. Hamaguchi, Comparative study of partially coherent anti-Stokes Raman scattering (PCARS) and Rayleigh scattering: Concentration and temperature dependence of scattered intensities. Journal of Chemical Physics, 1997. 106(1): p. 11-17.
66. Efremov, E.V., F. Ariese, and C. Gooijer, Achievements in resonance Raman spectroscopy review of a technique with a distinct analytical chemistry potential. Analytica Chimica Acta, 2008. 606(2): p. 119-134.
67. Crawford A., S.E., York K., Li C., Raman Spectroscopy: A Comprehensive Review.
68. Instruments, P., Raman Spectroscopy Basics. p. 1-5.
69. Willard, H.H.M., Jr., L. L;Dean, J. A. , Raman Spectroscopy. 1974. D. Van Nostrand Co.: New York(5th ed.): p. 189-197.
70. Sree. Raman Spectroscopy. 2012; Available from: http://way2science.com/raman-‐spectroscopy/.
71. Kast, R.E., et al., Emerging technology: applications of Raman spectroscopy for prostate cancer. Cancer and Metastasis Reviews, 2014. 33(2-3): p. 673-693.
72. Raman Spectroscopy: Comparison with other types of spectroscopy. 2014; Available from: http://www.doitpoms.ac.uk/tlplib/raman/comparison.php.
66
73. Schrader, B., Infrared and Raman Spectroscopy, method and application. Weiley-VCH, Weinheim, 1995.
74. Lin, C.-C., M.-T. Kuo, and H.-C. Chang, Review: Raman Spectroscopy - A Novel Tool for Noninvasive Analysis of Ocular Surface Fluid. Journal of Medical and Biological Engineering, 2010. 30(6): p. 343-354.
75. Huh, Y.S., A.J. Chung, and D. Erickson, Surface enhanced Raman spectroscopy and its application to molecular and cellular analysis. Microfluidics and Nanofluidics, 2009. 6(3): p. 285-297.
76. Dieringer, J.A., et al., Surface enhanced Raman spectroscopy: new materials, concepts, characterization tools, and applications. Faraday Discussions, 2006. 132: p. 9-26.
77. Stiles, P.L., et al., Surface-Enhanced Raman Spectroscopy, in Annual Review of Analytical Chemistry. 2008. p. 601-626.
78. Gersten, J.I., The Effect Of Surface-Roughness On Surface Enhanced Raman-Scattering. Journal of Chemical Physics, 1980. 72(10): p. 5779-5780.
79. Zhang, W., et al., Nanoscale roughness on metal surfaces can increase tip-enhanced Raman scattering by an order of magnitude. Nano Letters, 2007. 7(5): p. 1401-1405.
80. Zhao, Y., et al., Effects of surface roughness of Ag thin films on surface-enhanced Raman spectroscopy of graphene: spatial nonlocality and physisorption strain. Nanoscale, 2014. 6(3): p. 1311-1317.
81. Chen, H., et al., A surface plasmon resonance study on the optical properties of gold nanoparticles on thin gold films. Microchimica Acta, 2011. 172(3-4): p. 489-494.
82. Chu, Y., M.G. Banaee, and K.B. Crozier, Double-Resonance Plasmon Substrates for Surface-Enhanced Raman Scattering with Enhancement at Excitation and Stokes Frequencies. Acs Nano, 2010. 4(5): p. 2804-2810.
83. Mulvaney, P., Surface plasmon spectroscopy of nanosized metal particles. Langmuir, 1996. 12(3): p. 788-800.
84. Chen, L. and J. Choo, Recent advances in surface-enhanced Raman scattering detection technology for microfluidic chips. Electrophoresis, 2008. 29(9): p. 1815-1828.
85. Qian, X.M. and S.M. Nie, Single-molecule and single-nanoparticle SERS: from fundamental mechanisms to biomedical applications. Chemical Society Reviews, 2008. 37(5): p. 912-920.
67
86. Baniukevic, J., et al., Magnetic gold nanoparticles in SERS-based sandwich immunoassay for antigen detection by well oriented antibodies. Biosensors & Bioelectronics, 2013. 43: p. 281-288.
87. Haynes, C.L., et al., Surface-enhanced Raman sensors: early history and the development of sensors for quantitative biowarfare agent and glucose detection. Journal of Raman Spectroscopy, 2005. 36(6-7): p. 471-484.
88. Orendorff, C.J., et al., Surface-enhanced Raman spectroscopy of self-assembled monolayers: Sandwich architecture and nanoparticle shape dependence. Analytical Chemistry, 2005. 77(10): p. 3261-3266.
89. Mehrvar, L., et al., Design and fabrication of SU-8 MEMS electrostatically tunable optical Fabry-Perot cavity based on photolithography technique. 22nd International Conference on Optical Fiber Sensors, Pts 1-3, 2012. 8421.
90. Wolfe, D.B., D. Qin, and G.M. Whitesides, Rapid Prototyping of Microstructures by Soft Lithography for Biotechnology, in Microengineering in Biotechnology, M.P. Hughes and K.F. Hoettges, Editors. 2010. p. 81-107.
91. Ahmadi, T.S., et al., Shape-controlled synthesis of colloidal platinum nanoparticles. Science, 1996. 272(5270): p. 1924-1926.
92. Anandhakumar, S., R. Rajaram, and J. Mathiyarasu, Unusual seedless approach to gold nanoparticle synthesis: application to selective rapid naked eye detection of mercury(II). Analyst, 2014. 139(13): p. 3356-3359.
93. Cui, Y., et al., Synthesis of AgcoreAushell bimetallic nanoparticles for immunoassay based on surface-enhanced Raman spectroscopy. Journal of Physical Chemistry B, 2006. 110(9): p. 4002-4006.
94. Deschaume, O., et al., Synthesis and Properties of Gold Nanoparticle Arrays Self-Organized on Surface-Deposited Lysozyme Amyloid Scaffolds. Chemistry of Materials, 2014. 26(18): p. 5383-5393.
95. Kimling, J., et al., Turkevich Method for Gold Nanoparticle Synthesis Revisited. The Journal of Physical Chemistry B, 2006. 110(32): p. 15700-15707.
96. Lee, C.-H., et al., Solid phase gold nanoparticle synthesis. 2014, National Health Research Institutes.
68
97. Perry, D.A. and K. Primm, Formation of gold nanoparticles and nanorods for applications in SERS and SEIRA. Abstracts of Papers of the American Chemical Society, 2012. 243.
98. Blakey, I., Z. Merican, and K.J. Thurecht, A Method for Controlling the Aggregation of Gold Nanoparticles: Tuning of Optical and Spectroscopic Properties. Langmuir, 2013. 29(26): p. 8266-8274.
99. Kang, S.K., et al., Aspect ratio controlled synthesis of gold nanorods. Korean Journal of Chemical Engineering, 2003. 20(6): p. 1145-1148.
100. Ngo, Y.H., et al., Gold nanoparticles-SERS for paper biodiagnostics applications. Abstracts of Papers of the American Chemical Society, 2012. 244.
101. Lee, C.H., et al., Plasmonic paper as a highly efficient SERS substrate. Chemical, Biological, Radiological, Nuclear, and Explosives (Cbrne) Sensing Xiii, 2012. 8358.
102. Emory, Sr., W.E. Haskins, and S.M. Nie, Direct observation of size-dependent optical enhancement in single metal nanoparticles. Journal of the American Chemical Society, 1998. 120(31): p. 8009-8010.
103. Krug, J.T., et al., Efficient Raman enhancement and intermittent light emission observed in single gold nanocrystals. Journal of the American Chemical Society, 1999. 121(39): p. 9208-9214.
104. Kelly, K.L., et al., The optical properties of metal nanoparticles: The influence of size, shape, and dielectric environment. Journal of Physical Chemistry B, 2003. 107(3): p. 668-677.
105. Huang, X., et al., Cancer cells assemble and align gold nanorods conjugated to antibodies to produce highly enhanced, sharp, and polarized surface Raman spectra: A potential cancer diagnostic marker. Nano Letters, 2007. 7(6): p. 1591-1597.
106. Orendorff, C.J., et al., Light scattering from gold nanorods: tracking material deformation. Nanotechnology, 2005. 16(11): p. 2601-2605.
107. Xia, J., et al., Synthesis of large flower-like substrates for surface-enhanced Raman scattering. Chemical Engineering Journal, 2014. 244: p. 252-257.
108. Hoppmann, E.P. and I.M. White, A paper-based inkjet-fabricated substrate for SERS detection and differentiation of PCR products. Advanced Environmental, Chemical, and Biological Sensing Technologies X, 2013. 8718.
69
109. Sau, T.K. and C.J. Murphy, Room temperature, high-yield synthesis of multiple shapes of gold nanoparticles in aqueous solution. Journal of the American Chemical Society, 2004. 126(28): p. 8648-8649.
110. Polte, J., et al., Nucleation and Growth of Gold Nanoparticles Studied via in situ Small Angle X-ray Scattering at Millisecond Time Resolution. ACS Nano, 2010. 4(2): p. 1076-1082.
111. Turkevich, J., P.C. Stevenson, and J. Hillier, A study of the nucleation and growth processes in the synthesis of colloidal gold. Discussions of the Faraday Society, 1951. 11(0): p. 55-75.
112. Daniel, M.A.D., Gold Nanoparticles: Assembly, Supramolecular Chemistry, Quantum-Size-Related Properties, and Applications toward Biology, Catlysis, and Nanotechnology. Chemical Review, 2004. 104: p. 293-346.
113. Toma, H.E.e.a., The Coordination Chemistry at Gold Nanoparticles. J. Braz. Chem. Soc., 2010. 21(7): p. 1158-1176.
114. RJB, P., Nanocomposites-New Trends and developments,. 2012. Chapter 4: p. 73-93.
115. Cho, S.J., et al., In situ deposition of gold nanostructures with well-defined shapes on unfunctionalized reduced graphene oxide through chemical reduction of a dry gold precursor with ethylene glycol vapor. Rsc Advances, 2013. 3(4): p. 1201-1209.
116. Ryu, D., et al., In situ reduction of gold nanoparticles in PDMS matrices and applications for large strain sensing. Smart Structures and Systems, 2011. 8(5): p. 471-486.
117. Xiong, R., et al., In situ growth of gold nanoparticles on magnetic gamma-Fe2O3@cellulose nanocomposites: a highly active and recyclable catalyst for reduction of 4-nitrophenol. Rsc Advances, 2014. 4(13): p. 6454-6462.
118. Puglia, D., et al., Multifunctional Ternary Polymeric Nanocomposites Based on Cellulosic Nanoreinforcements, in Nanocellulose Polymer Nanocomposites. 2014, John Wiley & Sons, Inc. p. 163-198.
119. Benhabib, M. and X.J. Li, 14 - Low-cost assays in paper-based microfluidic biomedical devices, in Microfluidic Devices for Biomedical Applications, X. Li and Y. Zhou, Editors. 2013, Woodhead Publishing. p. 492-528e.
70
120. Ballerini, D.R., X. Li, and W. Shen, Patterned paper and alternative materials as substrates for low-cost microfluidic diagnostics. Microfluidics and Nanofluidics, 2012. 13(5): p. 769-787.
121. Yu, W.W. and I.M. White, A simple filter-based approach to surface enhanced Raman spectroscopy for trace chemical detection. Analyst, 2012. 137(5): p. 1168-1173.
122. Whitesides, G.M., Analysis on paper-based microfluidic systems. Abstracts of Papers of the American Chemical Society, 2010. 240.
123. Thuo, M.M., et al., Fabrication of Low-Cost Paper-Based Microfluidic Devices by Embossing or Cut-and-Stack Methods. Chemistry of Materials, 2014. 26(14): p. 4230-4237.
124. Carrilho, E., A.W. Martinez, and G.M. Whitesides, Understanding Wax Printing: A Simple Micropatterning Process for Paper-Based Microfluidics. Analytical Chemistry, 2009. 81(16): p. 7091-7095.
125. Tomazelli Coltro, W.K., et al., Recent advances in low-cost microfluidic platforms for diagnostic applications. Electrophoresis, 2014. 35(16): p. 2309-2324.
126. Wang, L. and P.C.H. Li, Gold nanoparticle-assisted single base-pair mismatch discrimination on a microfluidic microarray device. Biomicrofluidics, 2010. 4(3).
127. Halvorson, R.A., W. Leng, and P.J. Vikesland, Differentiation of Microcystin, Nodularin, and Their Component Amino Acids by Drop-Coating Deposition Raman Spectroscopy. Analytical Chemistry, 2011. 83(24): p. 9273-9280.
128. Wu, X.-Q., et al., In situ synthesized gold nanoparticles in hydrogels for catalytic reduction of nitroaromatic compounds. Applied Surface Science, 2015. 331: p. 210-218.
129. Halvorson, R.A. and P.J. Vikesland, Drop Coating Deposition Raman (DCDR) for Microcystin-LR Identification and Quantitation. Environmental Science & Technology, 2011. 45(13): p. 5644-5651.