first nano-wire finfets via uv-based nanoimprint lithography

BCAM

First Nano-wire FinFETs via UV-based Nanoimprint Lithography

Nanowire fin field effect transistors via UV-based nanoimprint lithography*A. Fuchs,a M. Bender, U. Plachetka, L. Kock, T. Wahlbrink, H. D. B. Gottlob, J. K. Efavi,

M. Moeller, M. Schmidt, T. Mollenhauer, C. Moormann, M. C. Lemme, and H. Kurz

Advanced Microelectronic Center Aachen (AMICA), AMO GmbH, Huyskensweg 25,

D-52074 Aachen, Germany

BCAM

Outline

1. Nanoimprint

2. UV-Nanoimprint

3. FinFETs

4. Fabrication of FinFETs

5. Performance of FinFETs fabricated

BCAM

Introduction to Nanoimprint

Nanoimprint lithography (NIL)

Conventional NIL processes, coined as stamp and step processes require thermal cycles between 140°C and 180°C and high pressures during the hot embossing procedure. Thermal and mechanical loads involved in these processes represent a nearly prohibitive burden for fast and high precision alignment. The mechanical masses to be moved in high throughput equipment require a large degree of complex mechanical handling.

BCAM

Background on UV-Nanoimprint

UV based nanoimprint lithography (UV-NIL)

The low pressure (<1bar) as well as the absence of any thermalcycles

appears very attractive for high precision printing down to 10 nm and

relaxes the technical requirements for placement accuracy and pattern

fidelity to a large extent.

BCAM

Wafer level UV-Nanoimprint

• Step & Repeat UV Nanoimprint 1. A resist is spin coated on the substrate.

2. For highest resolution and minimum distortion a rigid fused silica template is used to imprint features die by die. The template is pressed into a thin layer of imprint resist via uniform pressure of a few hundred millibar.

3. After alignment of substrate and template in contact UV light is used to harden the resist.

4. After detachment the template is moved to the next position on the wafer and the process is repeated until the wafer is completely patterned.

BCAM

Introduction on FETs

BCAM

Introduction on FinFETs

BCAM

Process flow of FinFETs via UV-Nanoimprint

5 mm thick 1in mold used with 150nm deep features.

1. Pattern the S/D and channel structure

a. Imprint process at reduced ambient pressure 20 mbars and imprint pressure of 300mbars.

b. UV curing resist---mold detached---RIE etching

2. CVD polysilicon for gate (heavily doped)

3. Pattern the gate

4. S/D implantation (As=2 x 10E20 ions/cm^2)

BCAM

SEM images of FinFETs via Nanoimprint

BCAM

Performance result of FinFETs

Transistor output characteristics exhibits linear and saturation regions!!!

Typical field effect transistor behavior is clearly observed!!!

Wait…….

BCAM

Conclusion

1. Promising approach.

2. Yield??

Questions???