1.2083
DESCRIPTION
material 1.2083TRANSCRIPT
-
1.2083 X40Cr14
Chemical Composition :
C Si Mn P S Cr
Min. % 0.36 12.50
Max. % 0.42 1.00 1.00 0.030 0.030 14.50
Material Code :
DIN ASTM JIS GOST
1.2083 420 SUS 420J2 40Ch13X40Cr14
Properties :
Martensitic stainless chromium steel for plastic moulds, excellent polishability and corrosion resistance in hardenedcondition, high wear resistance, high compression strength, through hardening, low distorsion, good machinability andphotoetching properties. This grade can be produced on request by the process ESR and quenched and tempered con-dition.
Applications :
Moulds for corrosive plastic materials such as PVC, recycled polymers etc., moulds for chemically aggressive plastics andplastics containing abrasive fillers, mould inserts, dies and gauges for PVC extrusions, screws and barrels for extruders,moulds for automotive, food, medical and optical industry such as spectacles, compact discs, lenses.
Physical Properties :
Density : at 20 C 7,70 kg/dm3 Thermal expansion between : 20 C and... C, 10-6 m/(mK)
Thermal conductivity : at 20 C 22,0 W/(m.K)100 C 200 C 300 C 400 C 500 C
10,5 11,0 11,0 11,5 12,0
Heat Treatment :
Annealing : 810 - 830 C
Hardness after annealing : Max. 230 HB
Stress relieving : Approx. 650 C
Hot forming : 1050 - 850 C
Hardening : 970 - 990 C
Quenching media : Oil, Vacuum
Hardness after quenching : 52 - 56 HRC
Hardness after tempering :100 C 200 C 300 C 400 C
54 HRC 52 HRC 52 HRC 52 HRC
Z ELK TCARET LTD.T.
-
Ha
rdn
ess
, H
RC
Tem
pera
ture
, C
This grade is produced on request.
Time - Temperature - Transformation Diagram1000
900Austenitizing 980 C
A+K Ac1e
800
700P
90100
100100 Ac1b
F+K6005
500
400
Ms300
200M
100
642 635 627 606 525 234 222 214 209
01 10 102 103 104 105 106
Seconds
Time Minutes1 10 100 1000 10000
Tempering Diagram66
62N/mm2 HB
58 2194
2054
54 1912
1789
50 1677
1575 461
46 1482 436
1399 413
42 1327 392
1263 373
38 X40Cr14 1198 354
1138 337
34Heat treatment :
1080 319
1024 303
30
980 C / Oil
970 286
0 100 200 300 400 500 600 700 800
Tempering temperature, C