In comparison of glass cloth, carbon fabric carries absolutely high strength, high elasticity, and high thermo-stable

characteristics in the current composite market. It also broadly used in industrial field by using its functional property.

Specific use : Carbon fabric also can be produced prepreg type and even if it is definitely stronger than steel, it is lighter than general F.R.P. Currently, it is widely applied in the aerospace business field and also it is used for industrial, constructional

and sports leisure business field.

Product IDWidth(mm)

Density(count/inch2)

Thickness

(mm)

Weight(g/m2)

Woven type

Warp Fill

YC-3K 200gsm 1,000 12.5 13.5 0.25 200PLAINTWILL

YC-3K 240gsm 1,000 15 15 0.26 240PLAINTWILL

YC-3K PVC 240gsm

1,000 15 15 0.30 380PVC

Black

CB131Carbon & Basalt

hybrid1,000 12.5 13.5 0.25 303 PLAIN

YC-3K 380gsm 1,000 25 25 0.34 3808H

SATIN

YC-12K 400gsm 1,000 6 6 0.43 400PLAINTWILL

Width=> 1,000~1,500mmWeight=> 200gsm~400gsm

General prepreg type=> Epoxy & Phenol

Carbon fabric and Prepreg

YOU CHANG

Sample

Carbon fiber Vinyl

Face FilmSolvent

AdhesiveRelease Liner Size

0.09mm 30μ 140g 127cm X 50m

YOU CHANG

UD Prepreg Carbon Fabric

General Modulus Prepreg(24Ton) without Scrim-Standard Resin Content-

High Modulus Prepreg(46Ton) with Scrim-Low Resin content-

Product ID

CFWt

(g/m²)

ResinWt

(g/m²)

ResinContent(%)

TotalWt(g/m²)

Thickness(mm)

CP 050NS 50 37 40 92 0.061

CP 075NS 75 46 38 121 0.080

CP 100NS 100 54 35 154 0.101

CP 125NS 125 62 33 187 0.121

CP 150NS 150 74 33 224 0.145

CP 175NS 175 86 33 261 0.169

CP 200NS 200 99 33 299 0.194

CP 250NS 250 123 33 373 0.241

Product ID

CFWt

(g/m²)

ResinWt

(g/m²)

ResinContent

(%)

ScrimWt

(g/m²)Total

Wt(g/m²)Thickness

(mm)

46H 0503 55 37 40 35 127 0.091

46H 0693 69 36 34 35 140 0.098

46H 0923 92 39 30 35 166 0.114

46H 1163 116 50 30 35 201 0.136

46H 1393 139 60 30 35 234 0.157

46H 1603 160 69 30 35 264 0.176

46H 1843 184 79 30 35 298 0.198

YOU CHANG

APPLICATION

After the heating process for surface treatment of glass fabric, we manufacture semi-hardened materials called "prepreg" with proper

resin such as, epoxy, phenolic, and unsaturated polyester.

The application is going to be for fishing rods, arrowheads, and it is also applicable for industrial use.

Product ID

Width(mm)

Density(count/inch2) Thickness

(mm) Weight(g/m2)

Woven type

Remarks

Warp Fill

YC-103 1,030 60 52 0.03 25 PLAIN

YC-210 1,020 64 25 0.10 1084H

SATIN

YC-218 1,020 64 26 0.18 2084H

SATIN

YC-224 1,020 50 26 0.24 3024H

SATIN

YC-7781 1,020 57 54 0.23 3008H

SATIN

YC-1522 AN2

24”,25”27”,30”

24 22 0.15 122 (4oz) PLAINSurfingboard

YC-2110 N2

24”,25”27”,30”

18 17 0.21 187 (6oz) PLAINSurfingboard

Glass fiber fabric & Prepreg

YOU CHANG

YOU CHANG

After the heating process for surface treatment of glass fabric, we manufacture semi-hardened materials called "prepreg" with proper

resin such as, epoxy, phenolic, and unsaturated polyester.

Glass Coated fabric

fabrics Finishing styleglass

fabrics Temp

glass fabrics Features glass fabrics Applications

Aluminum coated with fiberglass fabric

550℃heat reflection, abrasion

proofheat protection cushions, motor vehicle industry, protection for piping outside

Dying and coloring fiberglass fabric

550℃ heat protectionheat protection, welding defender and

differentiate work area

Graphite coated with fiberglass fabric

750℃increase resistance to

abrasion and flame, high temperature absorb mote

welding defender, general purpose insulation

Heat cleaning fiberglass fabric

550℃decrease pulverous mote,

good osmosis.welding defender, general purpose

insulation

PTFE coated with fiberglass fabric

550℃anti-adhesive surface, soil

repellent, acid resistantconveyor belt, acid resistant seclusion

Silicone rubber coating coated with fiberglass

fabric550℃

mechanical load, chemical, oil and corrosive of resistant

welding defender, compensators, insulation mats, heat production quilt

Polyurethane coated with fiberglass fabric

550℃good resistance to abrasion

and cuts, waterproof, allergen resistant

welding protection

Vermiculite coating 750℃increase resistance to

abrasion, flame, high heat

heavy duty insulation and seal, Widely used in exhausting, taking a breath,

ventilation, smoke and dust, waste gas of the steel, electricity, metallurgy, chemical industry the systematic

pipeline compensation of dealing with etc..

Steel wire reinforcing fiberglass fabric

550℃ increase tensile strength heavy duty insulation and seal

PVC coated fiberglass fabric

550℃good resistance to abrasion,

oil, and cuts, waterproofwelding protection, covering fabric

Acrylic coated fiberglass fabric

550℃good resistance to abrasion and cuts. allergen resistant and anti‐adhesive surface

welding protection

Neoprene coated fiberglass fabric

550℃good resistance to

abrasion，allergen resistantwelding protection

Level off veins fiberglass fabric

550℃good resistance to abrasion

and cutswelding protection, heat preservation

Latex coated fiberglass fabric

550℃

waterproof, gas defender and increase resistance to abrasion, high temperature

absorb

welding protection, waterproof material, fireproof material

Fluoroelastomer coated fiberglass

fabric550℃

increase resistance to abrasion, oil, acid and high

temperature

Non-metal expanse joints, heat preservation material

Ethylene propylene-diene monomer coated

fiberglass fabric550℃

increase resistance to abrasion and high

temperature

Non-metal expanse joints, heat preservation material

Acrylonitrile-butadiene rubber coated

fiberglass fabric550℃

increase resistance to abrasion and high

temperature

Non-metal expanse joints, heat preservation material

Glass cloth for industrial & constructional use

Product IDWidth(mm)

Density(count/inch2)

Thickness

(mm)

Weight(g/m2)

Woven type

Warp Fill

YC-108 1,070 4242

(52)0.08 77(84) PLAIN

YC-113 1.020 35 25 0.13 127 PLAIN

YC-1181,020~1,250

35 30 0.18 176 PLAIN

YC-3181,020~1,150

18 18 0.18 193 PLAIN

YC-318 black PVC coating

1,020 18 18 0.48 580 PLAIN

YC-533 silver & black

coating1,020 20 22 0.32 330 TWILL

YC-533 silver PVC coating

1,020 20 22 0.56 624 TWILL

YC-558 1,020 35 26 0.58 510 TWILL

YC-7500 1,020 15 13 0.25 300 PLAIN

YC-7500 Black coating

1,020 15 13 0.25 309 PLAIN

YC-7628 1,020 44 34 0.18 210 PLAIN

Glass cloth laminated with aluminum foil is required for thermo-stable materials for finishing work, vertical curtains for fireproof

materials for electromagnetic proof, and shipbuilding business field.

Using the application of its characteristics, such as, high-tensile strength, measure stability, and electrical insulation, various

adhesive tapes and Drybit for crack prevention are produced with the material.

For replacement of asbestos fabric, glass fabric coated with fireproof resin is manufactured for canvas.

For various purposes, fireproof and fire-resistant materials are produced with proper resin, for example, polyurethane, P.V.C,

silicone, rubber, and Teflon resin.

YOU CHANG

ALKALI-RESISTANT FIBERGLASS MESH

YOU CHANG

Alkali-resistant fiberglass mesh fabric is basis of any heat insulation system. Cracks are prevented because of good chemical corrosion resistance and high warp and weft strength～Distortions insulation system from high impact are

minimized because the directions.

Application(1) ALKALI-RESISTANT FIBERGLASS MESH is widely used in wall

reinforcement,out –side wall heat insulation,roof waterproof,wall corner. (2) It can also reinforce cement,plastic,bitumen,plaster,marble,mosaic etc (3) It is an ideal engineering material in construction

Mesh size

2.5mm×2.5mm, 4mm×4mm,5mm×5mm, 6mm×6mm, 7mm×7mm, 8mm×8mm,

10mm×10mm,12mm×12mm

The unit grams 60g/m2to 580g/m2

Width 10cm to 3m

Length 50m/roll to 1500m/roll

ColorWhite,yellow,blue,green,win

e red,orange.etc

Raw Materialc-glass yarn or e-glass

yarn

Packing:Plastic bag+carton+pallet

Technical Specification:

Spec. widthResin mark

Resin content

(%)

Alkali Resistant Properties

(%)

Tensile Strength

(N)

Range Of Weight

Warp--Weft Yarn

4x4mm,75g/m2

100cm

BASF +factory

glue

18 ≥50 ≧740 75g±5g 60×2--120

4x4mm,90g/m2

100cm 18 ≥50 ≧910 90g±5g 72×2--140

4x4mm,110g/m2

100cm 18 ≥50 ≧1100 110g±5g 88×2--176

4x4mm,145g/m2

11cm-300cm

18 ≥50 ≧1500 145g±5g 116×2--232

4x4mm,160g/m2

11cm-300cm

18 ≥50 ≧1585 160g±5g 128×2--256

Reinforcement material

Product Name

Fiber Type

Fiber Strengt

h(Mpa)

Fiber Stiffne

ss(Gpa)

Areal Weight(g/m2)

Fabric Thick-ness

(mm)*

Style

YC-N200

high strength carbon

4,900 230 200 0.111Woven

UD

YC-N300

high strength carbon

4,900 230 300 0.166Woven

UD

YC-H300

Intermediate modulus carbon

4,600 340 300 0.166Woven

UD

CARBON WRAP SYSTEM

ARAMID WRAP SYSTEM

Product Name

Fiber Type Fiber

Strength(Mpa)

Fiber Stiff-ness

(Gpa)

Areal Weight(g/m2)

Fabric Thick-ness

(mm)*

Style

YC-A280

Kevlar 2,880 100

280 0.194Woven

UD

YC-A415

415 0.288Woven

UD

YOU CHANG

• APPLICATION

Multi-axial Fabric

YOU CHANG

PRODUCT FEATURES：1.No binder used;2.Fast wet-out;3.High strength in a specific direction;4.Increase the properties of laminated FRP in terms of ultimate

tensile strength, delaminating resistance under stress and flexural strength;

5.Reduce the weight of FRP;6.Make FRP surface smoother;7.Simplify the operation of Hand Lay-up and improve productivity.

Chopped Strand Mat

TYPE OF GLASS E GLASS

Filament diameter 11-12Micron

Sizing of roving Silcane

Blinder type Emulsion or powder

Wet out speed 3-4Min

Chopped strand length 50mm

Weight(g/m2) 100,250,300,450,600,900

Width(mm) 30,60,1250,1050,1020,3200

YOU CHANG

• APPLICATION

Chopped CF & Chopped strand

YOU CHANG

Chopped CF

Compatible with cement for constructing bridge and road.

TYPE USED YARNCHOPPING

LENGTH

ThermosettingTOHO

YARN

3mm,6mm,

8mm,12mmThermoplastic

Chopped Strand

1. E-Glass Chopped Strands for BMC are widely used in transportation, construction, electronics,chemical industry.

2. E-Glass Chopped Strands for Thermoplastics are mainly used in injection and compression molding processes

Waste carbon fiber

for making carbon chopped or recycle to make carbon material.

Ballistic Fabric

YOU CHANG

A. Kevlar/Twaron Ballistic Fabric

Kevlar / Twaron Ballistic Fabric for making bulletproof jackets, helmets, plates, etc.:Specification: 1.20 by 2.42M; 1.60 by 3.20M; or length 100M+Area Density: 225g/m2Ballistic Layers for NIJ IIIA: 24Mini order: 100 sq.m; sample is available and charged.Capacity: 10 kilo sq.m monthlyKevlar / aramid ballistic fabric is softer and more comfortable than UHMW-PE, but it is weaker on UV resistant, low moisture sensibility and not waterproof.Guarantee Period: the material are in 5 years warranty.Note: the material can be preserved under temperature 300 centigrade

B. UHMW-PE Ballistic Fabric

We supply UHMW-PE UD (unidirectional) fabric sheet which is for making bulletproof applications. It is a roll product consisting of two/four plies of unidirectional polyethylene fiber crossplied at 0/90 degree, sandwiched with a thermoplastic film. It features lightweight, soft, comfort, outstanding UV resistant, low moisture sensibility and waterproof, also is powerful protection capability and high specific energy absorption. Our supplying specifications'''' range is from 140g/m2, 150g/m2, 160g/m2 and 170g/m2; continuous roll of fabric sheet is available

C. Ballistic HPPE Plate

Our ballistic HPPE plates substitute the traditional hard steel, Kevlar or Aramid plates for inserts of bulletproof vests and vehicle armoring.We have ballistic HPPE plates on levels NIJ IIIA III and III+, and ceramic & PE composite plates Level NIJ IV, their sizes may be made under your requirement.The main material is UHMW-PE (Ultra High Molecular Weight Polyethylene) fiber which is the best ballistic raw material nowadays.

High Silica Products - 1200℃ :

YOUCHANG Silica cloth is a high performance textile fabric that has 96%

SiO2, flexible fabric designed for use where severe temperature conditions

exist.

It used for thermal insulating and heat protection. It will not burn, rot or

deteriorate and resist most acids. It will keep good state when it works at

1100℃ for a long time. It works at 1400℃ more than 15 minutes and works

at 1700℃ more than 15 seconds.

Applications：

• Used for heat preservation and thermal insulating.

• Welding/cutting, molten metal splash protection.

• Heat and flame shielding, stress relief.

• Hose and cable protection and emergency fire blankets

Main Specifications：

YOU CHANG

Silica fabric

Model Weave

Warp FillTensile Strength

minWeight Thickness Width

Per cm Per cm Fill Warp g/m2 mm m

0300P01 Plain 18 13 1200 1000 300 0.28 0.8-0.82

0300S028H

Stain18 13 1500 1200 600 0.6 0.914

0300S048H

Stain18 13 4400 3400 1200 1.4 0.914

SiO2 content ≤96%

Endurance of temperature 1200℃/1800℉

Instantaneous temperature 1700℃/3000℉

Surfacing Tissue mainly used in the surface layers of FRP products. It features even Fiber distribution, soft feel, level and smooth fiber surface, less glue

content, quick resin soak and good pattern fitness. It can improve the product surface property on corrosion resistance, compressive strength,

seepage resistance, and longer service life. It is also suitable for spraying; pattern pressing and other FRP pattern technology.

Applications：

• Imparts a reinforced resin - rich surface for general FRP products

• Suitable for hand lay-up or press moulding where intricate contours are present and also for pipe and tank winding application

• Multicompatibility binder results in softer and more flexible tissue and improved surface - laminate bonding

• Resin - rich surface prevents crack formation and improves visual appearance of final product

Main Specifications：

Fiberglass Surfacing Tissue

ApplicationDensity(g/m)

Moisture Content(%)

Binder Content(%)

Wetting Time(%)

Tensile Strength(N/5cm)

Filament Winding

20

<0.2

7 <8 ≥20

30 6 <10 ≥25

50 6 <16 ≥40

Hand lay

30 7 <10 ≥20

40 6 <15 ≥25

50 6 <20 ≥30

YOU CHANG

Product Features :

ㆍ Rapid and complete wet out, Good processing characteristics

ㆍ Low resin demand during processing

ㆍ High composite mechanical properties

Storage :This Product should be stored in dry, cool, clean and rain-proof area. Recommended temperature range of storage is between 15℃-35℃ and relative humidity between 35%-65%.

Main Specifications：

Direct Roving

YOU CHANG

Linear Density(Tex)

Size Content(%)

Moisture Content(%)

Stiffness(mm)

Net Weight(kgs)

Application

ISO1887 ISO3344 ISO3341

240,300,600,1200,2400,4400,4800

0.15±0.15 ≤0.10 ≥0.4015.6，17, 22

Weaving

Filament Winding

Pultrusion

Direct Roving for Filament Winding, Pultrusion, Weaving :Direct Roving is an E-glass roving produced by directly winding a certain

number of individual fibers from the bushing without twist. It is coated with a silane-based size and is designed for reinforcing unsaturated polyester,

epoxy, vinylester and phenolic resins.

It is specially used to produce GRP FRP pipes, pressure vessels, gratings and profiles and, when converted into woven rovings, boats and chemical storage

tanks with filament winding, pultrusion and weaving process.

Fiberglass Plain Weaving Fabric mainly means the fabric woven by fiberglass

yarn in plain weaving.

Applications：

It is mainly used in vessel, building, electricity insulation(designated as E-

grade Fabric) and the production of various composite materials and

reinforced materials. It is widely used for manufacturing FRP sheets, pipe,

rods, car body, boat hull, fan blade and Varieties of profiles etc.

Product Features :

• Plain veave, even thickness and low fuzz;

• High strength in both warp and weft direction;

• Incombustibility, corrosion resistance and heat

resistance;

Main Specifications：

YOU CHANG

C glass fabric

ModelType of

Glass

Density(ends/cm)Area Weight

(GSM)Width (cm) WeaveWarp

Denisty

Weft

Denisty

CW100H C 10 9 90 90 Plain

CW105 C 8 8 105 124 Plain

CW140 C 7 6.8 131 90 Plain

CW180A C 8 7 145 90 Plain

CW180D C 6 5 145 90 Plain

CW260 C 12 8 260 100 Plain

EW100B E 20 20 100 100 Plain

EW140B E 16 12 140 100 Plain

EW200 E 8 7 200 100 Plain

HS2 and HS4 - are high strength glass fibers made from magnesium alumina

silicate system which meets the needs of military and other applications

where high strength and high performance is required.

S-Glass is generally used for polymer matrix composites that require

improved mechanical properties compared to E-glass based composites. This

is often the case when the material is operated under more extreme

conditions.

S-Glass will has the same working qualities as a standard E-glass, however

you will gain an approximate 25-30% increase in breaking strength. Used in

applications where the most possible strength is required while keeping

weight to a minimum.

Applications：

Aerospace, marine and arms industries due to its high tensile strength and higher modulus of elasticity when compared to e-glass.

Advantageous ：

• 30 to 40% better tensile strength

• 16 to 20% higher modulus of elasticity

• 100 to 150 degrees celsius better temperature endurance

• 10 fold higher fatigue resistance

• Excellent impact resistance because of the high elongation to breakage

• High ageing and corrosion resistance

• Quick resin wet-out properties

• Weight saving at the same performance

YOU CHANG

S glass fabric

Main Specifications for S Glass Woven Roving :

Main Specifications for High Strength S Glass Fiber Fabric :

Style No. Warp TexFill Te

xCount

(ends/cm)

Breaking Strength >

(N/25mm)

Weight (G/m2)

SWR260 240 240 W. 6.1 F. 4.7 1800 1400 260

SWR480 480 480 W. 5.0 F. 5.0 2799 2700 480

SWR600 1290 1290 W. 2.7 F. 1.9 4350 3050 610

SWR800 2033 2033 W. 2.0 F. 2.0 4570 4570 810

Style No.Warp Tex

Count (ends/cm)

Breaking Strength

(N/25mm)

Weight(G/m2

)

Weave Pattern

Warp Fill Warp Fill

SW80B-90b SC8-12 x 1 x 2 16 16 500 500 80 2/2 Twill

SW100A-90a SC8-12 x 1 x 2 20 20 550 550 100 Plain

SW110C-90a SC8-12 x 1 x 2 22 22 600 600 110 4HS

SW140B-90a SC8-12 x 2 x 2 14 14 900 900 140 2/2 Twill

SW140C-90a SC8-12 x 2 x 2 14 14 900 900 140 4HS

SW180D-90a SC8-12 x 2 x 2 18 18 1200 1200 180 5HS

SW210B-92a SC8-12 x 2 x 3 16 12 1600 1350 210 2/2 Twill

SW210A1-92a SC8-24 x 1 x 3 16 12 1600 1350 210 Plain

SW220B-90a SC8-12 x 2 x 3 18 14 1900 1600 240 2/2 Twill

SW220C-90a SC8-12 x 2 x 3 18 14 2000 1600 240 4HS

SW220D-90a SC8-12 x 2 x 3 18 14 2000 1600 240 5HS

SW220B-90b SC8-12 x 2 x 3 18 14 1900 1600 240 2/2 Twill

SW220C-90b SC8-12 x 2 x 3 18 14 1900 1600 240 4HS

SW240F-92a SC8-12 x 2 x 3 20 14 2700 1500 260 8HS

SW280F1-90a SC8-24 x 1 x 3 20 18 2000 1700 280 8HS

S glass Woven Roving & fabric

YOU CHANG