SYSWELD database
heat_treatment_quenching
Material
17CrNiMo6
Additional info from the database
NOM : HT 17CrNiMo6 thermometal_enth mm
COMMENTAIRES :
Disclaimer:
Whilst this database has been carefully written and subject to intensive review,it is the users responsibility to take all necessary steps to ensure thatthe assumptions and results from any finite element analysis which is madeas a result of using this data are correct. Neither ESI GROUP nor the authors
can accept any liability for incorrect analysis.
Date: 19-02-06
Composition - basic material:
% C 0.17% Si 0.29% Mn 0.54% Ni 1.62% Cr 1.68% Mo 0.28% V 0.01
Phases:
1: Ferrite / Pearlite2: Upper Bainite (soft)3: Martensite4: Lower Bainite (hard)5: Not used - reserved for tempering6: Austenite
TS = 1450, TL = 1507, LF = 250000 J/kg
Typical applications:
Case hardening steelSteel for cold extrusion
About the properties:
Enthalphy: Average values of not and low alloyed steelsUnit J/kgPhase transformation enthalphy includedMelting enthalphy included
Thermal conductivity: Individual propertiesUnit W/mmAustenite: Average values of austenitic steels
Density: Average values of not and low alloyed steelsUnit kg/mm3Austenite: Average values of austenitic steels
Heating: Individual AC1 and AC3
CCT-diagram: Heat Treatment CCT diagram. It is important to understand thatthe CCT diagram needs to be adjusted with a Jominy test
-
8/11/2019 Sysweld CCT Description
2/16
Properties formatted for wizards usageComposition
% C 0.17% Si 0.29% Mn 0.54% Ni 1.62
% Cr 1.68% Mo 0.28% V 0.01
EndCompositionPhases
1 : Ferrite2 : Bainite3 : Martensite4 :5 :6 : Austenite
EndPhases
-
8/11/2019 Sysweld CCT Description
3/16
SYSWELD database
heat_treatment_quenching
Material
18CD4
Additional info from the database
NOM : HT 18CD4 thermometal_enth mm
COMMENTAIRES :
Disclaimer:
Whilst this database has been carefully written and subject to intensive review,it is the users responsibility to take all necessary steps to ensure thatthe assumptions and results from any finite element analysis which is madeas a result of using this data are correct. Neither ESI GROUP nor the authors
can accept any liability for incorrect analysis.
Date: 19-02-06
Composition:
0.15-0.22 % C0.80-1.20 % Cr0.60-0.90 % Mn0.15 % Ni0.10-0.40 % Si0.15-0.25 % Mo
-
8/11/2019 Sysweld CCT Description
4/16
-
8/11/2019 Sysweld CCT Description
5/16
SYSWELD database
heat_treatment_quenching
Material
18CrNiMo7-6
Additional info from the database
NOM : HT 18CrNiMo7-6 thermometal_enth mm
COMMENTAIRES :
Disclaimer:
Whilst this database has been carefully written and subject to intensive review,it is the users responsibility to take all necessary steps to ensure thatthe assumptions and results from any finite element analysis which is madeas a result of using this data are correct. Neither ESI GROUP nor the authors
can accept any liability for incorrect analysis.
Date: 19-02-06
Composition - basic material:
0.17-0.18 % C0.50-0.58 % Mn0.26-0.32 % Si1.55-1.68 % Ni1.63-1.71 % Cr0.26-0.29 % Mo0.005-0.009 % V
Phases:
1: Ferrite / Pearlite2: Upper Bainite (soft)3: Martensite4: Not used - reserved for tempering5: Not used - reserved for tempering6: Austenite
TS = 1450, TL = 1507, LF = 250000 J/kg
Typical applications:
Case hardening steelSteel for cold extrusion
About the properties:
Enthalphy: Average values of not and low alloyed steelsUnit J/kgPhase transformation enthalphy includedMelting enthalphy included
Thermal conductivity: Individual propertiesUnit W/mmAustenite: Average values of austenitic steels
Density: Average values of not and low alloyed steelsUnit kg/mm3Austenite: Average values of austenitic steels
Heating: Individual AC1 and AC3
CCT-diagram: Heat Treatment CCT diagram. It is important to understand thatthe CCT diagram needs to be adjusted with a Jominy test
-
8/11/2019 Sysweld CCT Description
6/16
Properties formatted for wizards usageComposition
% C 0.18% Si 0.29% Mn 0.54% Ni 1.62
% Cr 1.68% Mo 0.28% V 0.01
EndCompositionPhases
1 : Ferrite2 : Bainite3 : Martensite4 :5 :6 : Austenite
EndPhases
-
8/11/2019 Sysweld CCT Description
7/16
SYSWELD database
heat_treatment_quenching
Material
100Cr6
Additional info from the database
NOM : HT 100Cr6 thermometal_enth mm
COMMENTAIRES :
Disclaimer:
Whilst this database has been carefully written and subject to intensive review,it is the users responsibility to take all necessary steps to ensure thatthe assumptions and results from any finite element analysis which is madeas a result of using this data are correct. Neither ESI GROUP nor the authorscan accept any liability for incorrect analysis.
Date: 19-02-06
Composition:
% C 1.04% Si 0.26% Mn 0.33% Ni 0.31% Cr 1.53% Mo 0.01% V 0.01
Phases:
1 : Pearlite (Ferrite)
2 : Bainite3 : Martensite4 : Not used - reserved for tempering5 : Not used - reserved for tempering6 : Austenite
TS = 1320, TL = 1450, LF = 210000 J/kg
Typical applications:
Ball and roller bearing steel
About the properties:
Enthalphy: Average values of not and low alloyed steelsUnit J/kgPhase transformation enthalphy includedMelting enthalphy included
Thermal conductivity: Individual propertiesUnit W/mmAustenite: Average values of austenitic steels
Density: Average values of not and low alloyed steelsUnit kg/mm3Austenite: Average values of austenitic steels
CCT-diagram: Heat Treatment CCT diagram. It is important to understand thatthe CCT diagram needs to be adjusted with a Jominy test
-
8/11/2019 Sysweld CCT Description
8/16
Properties formatted for wizards usageComposition
% C 1.04% Si 0.26% Mn 0.33% Ni 0.31
% Cr 1.53% Mo 0.01% V 0.01
EndCompositionPhases
1 : Ferrite2 : Bainite3 : Martensite4 :5 :6 : Austenite
EndPhasesInitial hardnessEndInitial hardnessEndProperties formatted for wizards usage
-
8/11/2019 Sysweld CCT Description
9/16
-
8/11/2019 Sysweld CCT Description
10/16
Properties formatted for wizards usageComposition
% C 0.37% Si 0.58% Mn 1.38% Ni 0.01
% Cr 0.22% Mo 0.01% V 0.00
EndCompositionPhases
1 : Ferrite2 : Bainite3 : Martensite4 :5 :6 : Austenite
EndPhases
-
8/11/2019 Sysweld CCT Description
11/16
SYSWELD database
heat_treatment_surface
Material
42CrMo4
Additional info from the database
NOM : HT 42CrMo4 thermometal_enth mm
COMMENTAIRES :
Disclaimer:
Whilst this database has been carefully written and subject to intensive review,it is the users responsibility to take all necessary steps to ensure thatthe assumptions and results from any finite element analysis which is madeas a result of using this data are correct. Neither ESI GROUP nor the authorscan accept any liability for incorrect analysis.
Date: 19-02-06
Composition:
% C 0.38% Si 0.23% Mn 0.64% Ni 0.08% Cr 0.99% Mo 0.16% V 0.01
Phases:
1 : Ferrite
2 : Pearlite3 : Bainite4 : Martensite5 : Not used, reserved for tempered martensite6 : Austenite
Typical applications:
Casting steelStructural steel
About the properties:
Enthalpy: Average values of not and low alloyed steelsUnit J/kgPhase transformation enthalphy includedMelting enthalphy included
Thermal conductivity: Individual propertiesUnit W/mmAustenite: Average values of austenitic steels
Density: Average values of not and low alloyed steelsUnit kg/mm3Austenite: Average values of austenitic steels
Heating: Individual AC1 and AC3
CCT-diagram: Heat Treatment CCT diagram. It is important to understand thatthe CCT diagram needs to be adjusted with a Jominy test, in case more then amartensite transformation is expected
-
8/11/2019 Sysweld CCT Description
12/16
Properties formatted for wizards usageComposition
% C 0.38% Si 0.23% Mn 0.64% Ni 0.08
% Cr 0.99% Mo 0.16% V 0.01
EndCompositionPhases
1 : Ferrite2 : Bainite3 : Martensite4 :5 :6 : Austenite
EndPhases
-
8/11/2019 Sysweld CCT Description
13/16
SYSWELD database
heat_treatment_surface
Material
CF35
Additional info from the database
NOM : HT CF35 thermometal_enth mm
COMMENTAIRES :
Disclaimer:
Whilst this database has been carefully written and subject to intensive review,it is the users responsibility to take all necessary steps to ensure thatthe assumptions and results from any finite element analysis which is madeas a result of using this data are correct. Neither ESI GROUP nor the authorscan accept any liability for incorrect analysis.
Date: 11-01-07
Composition:
0.35 % Carbone0.65 % Mn
0.25 % Si
Phases:
1 : Ferrite / Pearlite2 : Bainite3 : Martensite4 : Not used, reserved for tempered bainite5 : Not used, reserved for tempered martensite
6 : Austenite
Typical applications:
Heat treatable steelHigh temperature construction steel
About the properties:
Enthalpy: Average values of not and low alloyed steelsUnit J/kgPhase transformation enthalphy includedMelting enthalphy included
Thermal conductivity: Individual propertiesUnit W/mmAustenite: Average values of austenitic steels
Density: Average values of not and low alloyed steelsUnit kg/mm3Austenite: Average values of austenitic steels
Heating: Individual AC1 and AC3
CCT-diagram: Heat Treatment CCT diagram. It is important to understand thatthe CCT diagram needs to be adjusted with a Jominy test, in case more then amartensite transformation is expected
-
8/11/2019 Sysweld CCT Description
14/16
Properties formatted for wizards usageComposition
% C 0.35% Si 0.325% Mn 0.65% Ni 0.0
% Cr 0.0% Mo 0.00% V 0.00
EndCompositionPhases
1 : Ferrite2 : Bainite3 : Martensite4 :5 :6 : Austenite
EndPhases
-
8/11/2019 Sysweld CCT Description
15/16
SYSWELD database
heat_treatment_surface
Material
CK45
Additional info from the database
NOM : HT CK45 thermometal_enth mm
COMMENTAIRES :
Disclaimer:
Whilst this database has been carefully written and subject to intensive review,it is the users responsibility to take all necessary steps to ensure thatthe assumptions and results from any finite element analysis which is madeas a result of using this data are correct. Neither ESI GROUP nor the authorscan accept any liability for incorrect analysis.
Date: 19-02-06
Composition:
0.45 % Carbone
-
8/11/2019 Sysweld CCT Description
16/16
Properties formatted for wizards usageComposition
% C 0.45% Si 0.30% Mn 0.65% Ni 0.35
% Cr 0.35% Mo 0.05% V 0.00
EndCompositionPhases
1 : Ferrite2 : Bainite3 : Martensite4 :5 :6 : Austenite
EndPhases