NO.5601 10-P-0053_E (1/7)

Super thin double-coated adhesive tape

No.5601

Outline

Nitto Denko No. 5601 is 0.01mm thick double-coated adhesive tape. The tape has a #2 polyester film as a base coated on both sides with acrylic adhesive and offers superior bonding performance to plastic films and moldings. The tape facilitates thinner electronic equipment, as tape thickness is 0.01mm. Also, it is has an excellent converting and working performance by using #2 polyester film.

Structure

Features

●Tape thickness is 0.01mm. Can be used for bonding in limited spaces or clearances.

●Excellent thickness uniformity by using polyester film.

●Uses thin #2 polyester film for superior conversion prior to use and offers less blocking and oozing.

●Excellent bonding performance to plastic material.

●The tape minimizes dust emission by using polyester release liner and plastic core.

●The six hazardous materials restricted by the RoHS directive are not compounded. Applications

●Fixing of reflective sheets and optical waveguide films used for LCD backlight modules such as

digital camera and cellular phone.

●Fixing of film for compact electronics.

●Fixing of thin layered films, splicing and fixing for metal foil end. Standards size

Tape thickness (mm) Widths (mm) Length (m)

0.01 50, 100, 230 50

For more information, please contact us.

Acrylic adhesive

Polyester film (#2) Acrylic adhesive

Release liner (Polyester film)

No.5601 【Tape thickness: 0.01 ㎜】

Plastic core

No.20131024092056-41536

NO.5601 10-P-0053_E (2/7)

Properties

●180 peeling adhesion by substrate

Substrate No.5601

ABS plate 7.0

Polystyrene plate 8.5

Acrylic plate 8.0

Polycarbonate 9.0

Polyester film 7.8

Stainless steel plate 8.3

Aluminum plate 6.6

Glass plate 7.8

(Unit: N/20 mm) Backing: PET#25

Peeling speed: 300 mm/min

Peeling angle: 180 Pressure application condition: *1pass back and forth with 2kg

Substrate: Stainless steel plate

〈Test method〉

PET#25

Substrate

No.5601

180° peeling adhesion by substrate

Adh

esio

n [

N/2

0mm

]

Substrate

ABS Polystyrene Acrylic Polycarbonate Polyester Stainless steel

Aluminum Glass

No.20131024092056-41536

NO.5601 10-P-0053_E (3/7)

Properties

●180°peeling adhesion by temperature

●Holding power

Temperature No.5601

10℃ 7.0

23℃ 8.3

40℃ 7.8

60℃ 6.2

80℃ 6.1

Temperature No.5601

40℃ 0.3

80℃ 0.6

(Unit: N/20 mm) Backing: PET#25

Peeling speed: 300 mm/min

Peeling angle: 180 Measurement temperature: 10C, 23C, 40C, 60C, 80C,

*Application under various temperatures

→Measurement under various temperatures

Substrate: Stainless steel plate

(Unit：mm/hr) Measurement temperature: 40, 80℃

Tape area: 10mmｘ20mm

Load: 4.9N（500g）

Substrate: Bakelite plate

No.5601

PET#25

ｗ

Bakelite plate

〈Test method〉

180° peeling adhesion by temperature

Adh

esio

n [

N/2

0mm

]

Temperature

No.20131024092056-41536

NO.5601 10-P-0053_E (4/7)

Properties

●Shear strength

●180°Peeling adhesion by pressure

Temperature No.5601

23℃ 450

Pressure No.5601

0.1kg 4.6

0.5kg 7.0

2kg 8.3

5kg 8.4

(Unit：N／20mm) Backing: PET#25

Peeling speed: 300mm/min

Peeling speed: 180°

Measurement condition: 23℃ｘ50%RH

Pressure application condition *1 pass back with forth with 0.1 kg、0.5kg、2kg、5kg

(Unit: N/20 mm x 20mm) Substrate:Acrylic plate / Acrylic plate

Tape area: 20mm x 20mm

Peeling speed: 50 mm/min

Measurement condition: 23C x 50%RH

Measurement method:

A specimen is prepared and shear strength is

measured after allowing it to set 30 minutes.

No.5601

Peeling speed

50mm/min

Acrylic plate

〈Test method〉

Acrylic plate

Adhesive adhesion by pressure

Adh

esio

n [

N/2

0mm

]

Pressure

No.20131024092056-41536

NO.5601 10-P-0053_E (5/7)

Properties

●180°Peeling adhesion after application(increase)

●180°peeling adhesion(change after application)

Temperature Time No.5601

23℃

0.5hrs 8.3

4hrs 8.3

12hrs 8.4

24hrs 8.5

48hrs 8.9

72hrs 8.9

Temperature Time No.5601

23℃

1 day 8.5

14 days 9.2

30 days 9.4

40℃92％RH

1 day 8.5

14 days 9.5

30 days 9.8

50℃

1 day 8.8

14 days 10.1

30 days 10.4

70℃

1 day 9.2

14 days 11.5

30 days 11.4

(Unit：N/20mm) Backing: PET#25

Peeling speed: 300mm/min

Peeling angle: 180°

Measurement condition: 23℃ｘ50%RH

Substrate: stainless steel plate

180 peeling adhesion after application (increase)

(Unit：N/20mm) Backing: PET#25

Peeling speed: 300mm/min

Peeling angle: 180°

Measurement condition: 23℃ｘ50%RH

Substrate: stainless steel plate

Time

Adh

esio

n [

N/2

0mm

]

No.20131024092056-41536

NO.5601 10-P-0053_E (6/7)

Properties

●Unevenness (Observe the unevenness on applied metal foil)

*Super thin, No.5601 does not stand out the unevenness where the tape applied.

〈Test method〉 ・Metal foil : Rolled cooper foil #35

・Substrate: Acrylic plate

・Size: 50mm×70mm

・Tape area:20mm width x 70mm

Metal foil

Tape

Acrylic plate

〈No.5601〉 〈0.10mm-thick double coated tape〉

Tape mark Tape mark

Tape mark Tape mark

No.20131024092056-41536

NO.5601 10-P-0053_E (7/7)

Precautions when using

●Remove all oil, moisture and dirt from the surface of the substrate before applying.

●The tape employs pressure-sensitive adhesive. Be sure to apply pressure with a roller or press when applying. Failure to do so could affect properties or appearance.

●The tape may not adhere well to significantly uneven or distorted surfaces. Level off the surface as much as possible before applying.

●Because it is very thin, you should avoid applying large loads for at least several hours following application.

Precautions when storing

●Be sure to keep the tape in its box when not using. ●Keep in a cool dark place not exposed to direct sunlight.

Safety precautions

●Make sure the product is suitable for the application (objective and conditions) before attempting to

use. The tape may come off depending on the substrate to which it is applied or conditions under

which it is applied.

●Use in combination with another method of joining if there is possibility of an accident.

Published in October 2013

！ WARNING

No.20131024092056-41536

No.5603,No.5603BN 10-P-0170_E (1/6)

Double-coated adhesive tape

No.5603, No.5603BN Outline

Nitto Denko No. 5603 and No. 5603BN are 0.03mm thickness double-coated adhesive tapes. The tapes have a #4 polyester film as a base coated on both sides with acrylic adhesive, and offer superior bonding to plastic films and moldings. A mere 0.03-mm thick, the tape facilitates thinner electronic equipment. The double-coated adhesive tapes also offer superior adhesion to rough surfaces.

Structure

Features

●Tape thickness is 0.03 mm. Can be used for bonding in limited spaces or clearances.

●Uses thin #4 polyester film for superior conversion prior to use.

●Offers strong bonding to PC housing, optical waveguide plates and reflective sheets used for LCD backlight modules.

●Halogen-free type. (We do not use chloride compounds on purpose for this product.)

●The six hazardous materials restricted by the RoHS directive are not compounded.

Applications

●Fixing of reflective sheets used for LCD backlight modules for digital cameras and cellular telephones.

●Fixing of parts for compact home appliances

Standards Size

Tape thickness (mm) Widths (mm) Length (m)

0.03 50, 70 50

For more information, please contact us.

No.5603, No.5603BN* 【Tape thickness: 0.03mm】

Acrylic adhesive Polyester film (#4) Acrylic adhesive Release liner (Polyester film)

Plastic core ＊No. 5603BN is the black version of No. 5603.

Uses black polyester film.

No.20131024092147-41537

No.5603,No.5603BN 10-P-0170_E (2/6)

Properties

●180 peeling adhesion by substrate

<Test method>

被着体別180°引き剥がし粘着力

0.0

2.0

4.0

6.0

8.0

10.0

12.0

14.0

ABS ﾎﾟﾘｽﾁﾚﾝ ｱｸﾘﾙ ﾎﾟﾘｶｰﾎﾞﾈｰﾄ ﾎﾟﾘｴｽﾃﾙ ｽﾃﾝﾚｽ ｱﾙﾐ ｶﾞﾗｽ

被着体

粘着

力［N

/20m

m］

Substrate No.5603,No.5603BN

ABS plate 10.0

Polystyrene plate 10.8

Acrylic plate 11.0

Polycarbonate plate 10.1

Polyester film 11.4

Stainless steel plate 10.4

Aluminum plate 9.7

Glass plate 9.6

(Unit: N/20mm) Backing: PET#25 Peeling speed: 300mm/min Peeling angle: 180° Measurement condition: 23℃, 50%RH Pressure application conditions

* 1 pass back and forth with 2-kg roller

PET#25

Substrate

Tape

180° peeling adhesion by substrate

Adh

esio

n [

N/2

0mm

]

Substrate

ABS Polystyrene Acrylic Polycarbonate Polyester Stainless steel Aluminum Glass

No.20131024092147-41537

No.5603,No.5603BN 10-P-0170_E (3/6)

Properties

●180 peeling adhesion by temperature

温度別180°引き剥がし粘着力の変化

0.0

2.0

4.0

6.0

8.0

10.0

12.0

14.0

16.0

0℃ 10℃ 23℃ 40℃ 60℃ 80℃

温度

粘着

力［N

/20m

m］

●180 peeling adhesion at low temperatures (applied at 23C and measured at 0C and -10C)

Substrate Temperature No.5603,No.5603BN

Stainless steel plate 0℃ 12.4

-10℃ 12.0

Polyester film 0℃ 8.3

-10℃ 6.6

Temperature No.5603,No.5603BN

0℃ 12.1

10℃ 10.9

23℃ 10.4

40℃ 9.1

60℃ 7.4

80℃ 6.6

(Unit: N/20mm) Backing: PET#25 Peeling speed: 300mm/min Peeling angle: 180° Measurement temperature: 0℃, 10℃, 23℃, 40℃, 60℃, 80℃

Application under various temperatures →Measurement under various temperatures Substrate: Stainless steel plate

(Unit: N/20mm) Backing: PET#25 Peeling speed: 300mm/min Peeling angle: 180°

Measurement temperature: 0℃, -10℃

*Applied at 23c, 50% RH and measured at 0C and -10C

Substrate: Stainless steel plate

Polyester film

Adh

esio

n [

N/2

0mm

]

Temperature

180° peeling adhesion by temperature

No.20131024092147-41537

No.5603,No.5603BN 10-P-0170_E (4/6)

Properties

●Holding power

●Shear strength

●180 peeling adhesion by pressure

圧着力別粘着力

0.0

2.0

4.0

6.0

8.0

10.0

12.0

14.0

0.1kｇ 0.5kg 2ｋｇ 5ｋｇ

圧着力

粘着

力［N

/20m

m］

Temperature No.5603,No.5603BN

40℃ 0.3

80℃ 0.6

Temperature No.5603,No.5603BN

23℃ 600

Pressure No.5603,No.5603BN

0.1 kg 9.3

0.5 kg 9.9

2 kg 10.4

5 kg 10.6

(Unit: mm/hr) Measurement temperature: 40, 80℃ Application area: 10mmｘ20mm Load: 4.9N (500g) Substrate: Phenol resin plate

Tape

PET#25

ｗ

Phenol plate

<Test method>

(Unit: N/20mmx20mm) Substrate: Acrylic plate / acrylic plate Tape area: 20mm×20mm Peeling speed: 50mm/min Measurement temperature: 23℃, 50％RH Measurement method: A specimen is prepared and shear strength

is measured after allowing it to set 30 minutes.

<Test method>

Acrylic plate

Tape

Acrylic plate

Peeling speed

50mm/min

(Unit: N/20mm) Backing: PET#25 Peeling speed: 300mm/min Peeling angle: 180° Measurement condition: 23℃, 50%RH Pressure application conditions:

* 0.1kg, 0.5kg, 2kg, 5kg 1 pass back and forth with 2-kg roller

Adhesive adhesion by pressure

Adh

esio

n [N

/20m

m]

Pressure

No.20131024092147-41537

No.5603,No.5603BN 10-P-0170_E (5/6)

Properties

●180 peeling adhesion after application (increase)

貼付け後の180°引き剥がし粘着力－上昇性

0.0

2.0

4.0

6.0

8.0

10.0

12.0

14.0

0.5ｈｒｓ 4ｈｒｓ 12ｈｒｓ 24ｈｒｓ 48ｈｒｓ 72ｈｒｓ

時間

粘着

力［N

/20m

m］

●180 peeling adhesion (change after application)

No.5603,No.5603BN

23 ℃

0.5 hrs 10.4

4 hrs 10.5

12 hrs 11.0

24 hrs 11.4

48 hrs 11.9

72 hrs 11.9

Temperature Time No.5603,No.5603BN

23℃

1 day 11.4

14 days 11.9

30 days 12.7

40℃, 92％RH

1 day 11.5

14 days 12.4

30 days 13.2

50℃

1 day 11.7

14 days 12.8

30 days 13.6

70℃

1 day 12.0

14 days 13.8

30 days 15.0

(Unit: N/20mm) Backing: PET#25 Peeling speed: 300mm/min Peeling angle: 180° Measurement condition: 23℃, 50%RH

Substrate: Stainless steel plate

(Unit: N/20mm) Backing: PET#25 Peeling speed: 300mm/min Peeling angle: 180° Storage conditions: 23℃, 40℃×92％RH

50℃, 70℃ Measurement condition: 23℃, 50%RH Substrate: Stainless steel plate

180 peeling adhesion after application (increase)

Adh

esiv

e ad

hesi

on [N

/20m

m]

Time

No.20131024092147-41537

No.5603,No.5603BN 10-P-0170_E (6/6)

Precautions when using

●Remove all oil, moisture and dirt from the surface of the substrate before applying.

●The tape employs pressure-sensitive adhesive. Be sure to apply pressure with a roller or press when applying.

Failure to do so could affect properties or appearance. ●The tape may not adhere well to significantly uneven or distorted surfaces. Level off the surface as much as

possible before applying.

●Because it is very thin, you should avoid applying large loads for at least several hours following application. Precautions when storing

●Be sure to keep the tape in its box when not using. ●Keep in a cool dark place not exposed to direct sunlight.

Safety precautions

●Make sure the product is suitable for the application (objective and conditions) before attempting to use. The tape

may come off depending on the substrate to which it is applied or conditions under which it is applied.

●Use in combination with another method of joining if there is possibility of an accident.

Published in October 2013