Presses and Equipment for Sheet Metal dies
POWER PRESS TYPES
The types of power presses available for metal-cutting and forming
operations are varied, the selection depending upon the type of operation.
Not all types of presses will be described because of space limitations. The
basic types of presses and press mechanisms will be described to give the
beginner the necessary background for designing press tooling.
Presses are classified by (1) type of frame, (2) source of
power, (3) method of actuation of slides, (4) number of slides incorporated,
and (5) intended use. Most presses are not classified by only category one but
several. For example, a straight-side press may be mechanically or
hydraulically driven and may be either single or double acting.
Classification by frame type: The frame of a press is fabricated by
casting or by welding heavy steel plates. Cast frames are quite stable and
rigid but expensive. Cast frame construction also has the advantage of placing
a mass of material where it is needed most. Welded frames are generally
less expensive and are more resistant to shock loading because of the greater
toughness of steel plate.
The general classification by frame includes the gap frame and the
straight side. The gap frame is cut back below the ram to form the shape of a
letter C. This allows feeding a strip from the side. Some gap-frame presses
have an open back to permit strip feeding from front to back or ejection of
finished parts out the back. Gap-frame presses are manufactured with solid
frames fixed in a vertical or inclined position. Others are manufactured with a
separate frame mounted in a base, which allows the frame to be inclined at
an angle in three different positions.
The reason for inclining the press is to allow parts to fall through the
open back by gravity. The three-position inclinable press is frequently
referred to as an open-back inclinable (OBI) press (see Fig. 3-1). Solid gap-
frame presses are obtainable in higher tonnages than inclinable ones because
of the rigid base and solid construction.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
2/153
2
The OBI press is the most common press in use today. It ranges from
a small 1-ton bench press to floor presses rated up to 150 tons. Its main use
is for blanking and piercing operations on relatively small work pieces,
although bending, forming, and drawing operations can also be done.
Fig, 3-2 shows the major components of an OBI press, as follows:
1) A rectangular bed, the stationary and usually horizontal part of the
press, serving as a table to which a holster plate is mounted.
2) A bolster plate, consisting of a flat steel plate from 50 mm. to 125
mm. thick, secured to the press for locating and supporting the die
assembly.
3) The ram, sometimes called the slide, which reciprocates within the
press frame and to which the punch or upper-die assembly is
fastened.
4) A knockout, consisting of a crossbar through a slot in the ram that
contacts a pin in the die to eject the work piece.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
3/153
3
5) The flywheel, which absorbs energy from the motor continuously and
delivers its stored energy to the work piece intermittently, making it
possible to use a smaller motor.
6) The pitman, consisting of a connecting rod to convey motion andpressure from the main shaft or eccentric to the press slide.
Fig. 3-3Single action straight side eccentric shaft mechanicalpress.
The straight slide press incorporates a slide or ram, which travels up
and down between two straight sides or housing and commonly used for large
and heavy work. The size of the press is limited to some extent because
reduce the working area. However the frame construction does permit large
bed areas and longer strokes. The drive mechanism is generally located
above the bed, The straight slide press incorporates a slide or ram, which
-
7/30/2019 Presses and Equipment for SheetMetal Dies
4/153
4
travels up and down between two straight sides or housing and commonly
used for large and heavy work. The size of the press is limited to some extent
because reduce the working area. However the frame construction does
permit large bed areas and longer strokes. The drive mechanism is generally
located above the bed, although under drive presses may be obtained with
the drive mechanism located below the bed. Straight side presses are
classified as single, two or four point suspension, depending upon the number
of connection between the slide and the main drive shaft. Fig, 3-3 shows a
typical straight slide press.
Classification by source of power: The great majority of presses
receive their power mechanically or hydraulically. A few manually operated
presses are hand operated through levers or screws, but they are hardly
suited for high production.
Mechanical presses use a flywheel driven system to obtain ram
movement. The heavy flywheel absorbs energy from the motor
continuously and delivers its stored energy to the work piece
intermittently. The motor returns the flywheel to operating speed between
strokes. The permission slowdown of the flywheel during the work period is
about 7 to 10 percent in nongeared presses and 10 to 20 percent in
geared presses. The flywheel is attached directly to the main shaft of the
press (non geared), or, it is connected to the main shaft by a gear train.
Nongear drives are used on presses of low tonnage and short strokes. The
number of strokes per minute on nongear drives is usually quite high.
Gear driven presses transmit the energy of the flywheel through a single or
double reduction gear. The single reduction gear drive is suited for heavier
blanking operations or shallow drawing. The double-gear drive is used on large,
heavy presses where it is necessary to move large amounts of mass at slower
speeds. The double reduction greatly reduces the strokes per minute without
reducing the flywheel speed.
Basic types of mechanical press drives
a) Nongeared
-
7/30/2019 Presses and Equipment for SheetMetal Dies
5/153
5
b) Single geared
c) Single reduction gear
d)Double reduction
Fig. 3-5Typical double action hydraulic presswith a Die cushion
Hydraulic presses have a large cylinder and piston, coupled to a hydraulic pump.
The piston and press ram are one unit. The tonnage capacity depends upon the
cross-sectional area of the piston (or pistons) and the pressure developed by the
pump. The cylinder is double acting in order to move the ram in either direction.
The advantage of a hydraulic press is that it can exert its full tonnage at any
position of the ram stroke. In addition, the stroke can be varied to any length
within the limits of the hydraulic-cylinder travel. The speed and pressure are also
-
7/30/2019 Presses and Equipment for SheetMetal Dies
6/153
6
constant throughout the entire stroke Fig. 3-5 shows a typical hydraulically driven
press.
Classification by method of slide actuation: The flywheel of a press drives the
main shaft, which in turn changes the rotary motion of the flywheel into the linear
motion of the slide or ram. This is generally accomplished by incorporating
crankpins or eccentrics into the main drive shaft, as shown in Fig, 3-4. The
number of points of suspension of the slide determines the number of throws or
eccentrics on the main shaft. Points of suspension are places where pressure is
transmitted by connection to the slide. Press connections, called connecting rods
or pitman, are usually adjustable in length so that the shut height of the press can
be varied.
The most common driving device is the crankshaft, although many
newer presses use the eccentric for ram movement. The main advantage
of the eccentric is that it offers more surface area for bearing support for
the pitman and main disadvantage is its limitations on the length of
stroke. Therefore, presses having longer strokes generally utilize the
crankshaft.
In addition to eccentrics and crankpins, cams, toggles, rack andpinions, screws, and knuckles actuate slides. Space does not permit
discussion of these mechanisms in this text. Information may be obtained
by referring to the various die-design and press handbook.
3.1.4 Classification by the number of slides incorporated: The
number of slides incorporated in a single press is called the action, i.e. the
number of rams or slides on the press. Thus a single-action press has one
slide. A double-action press has two slides, an inner and an outer slide
(see Fig. 3-5). This type of press is generally used for drawing operations
during which the outer slide carries the blank holder and the inner slide
carries the punch. The outer, or blank-holder, slide, which usually has a
shorter stroke than the inner, or punch-holder slide, dwells to hold the
blank while the inner slide continues to descend, carrying the draw punch
to perform the drawing operation.
A triple-action press is the same as a double-action with the
addition of a third ram, located in the press bed, which moves upward in
the bed soon after the other two rams descend. All three-slide movements
-
7/30/2019 Presses and Equipment for SheetMetal Dies
7/153
7
are properly synchronized for triple-action drawing, redrawing, and
forming.
GENERAL PRESS INFORMATION
The tool designer must know certain fundamentals of press
operation before he can successfully design press tooling.
Press tonnage: The tonnage of a press is the force that the press ram is
able to exert safely. Press slides exert forces greater than the rated
tonnage because of the built-in safety factor, but this is not a license to
overload.
The tonnage of hydraulic presses is the piston area multiplied by
the oil pressure in the cylinder. Changing the oil pressure varies the
tonnage. The tonnage of mechanical presses is determined by the size of
the bearings for the crankshaft or eccentric and is approximately equal to
the shear strength of the crankshaft metal multiplied by the area of the
crankshaft bearings. The tonnage of a mechanical press is always given
when the slide is near the bottom of its stroke because it is greatest at this
point.
Stroke: The stroke of a press is the reciprocating motion of a press
slide, usually specified as the number of inches between terminal points of
the motion. The stroke is constant on a mechanical press but adjustable on
a hydraulic press.
Shutheight: The shut height of a press is the distance from the
top of the bed to the bottom of the slide with the stroke down and the
adjustment up. The thickness of the bolster plate must always be taken
into consideration when determining the maximum die height. The shut
height of the die must be equal to or less than the shut height of the
press. The shut height of a press is always given with the adjustment up.
Lowering the adjustment of the slide may decrease the opening of the
press from the shut height down, but it does not increase the shut height.
Thus the shut height of a die must not be greater than the shut height of
the press. It may be less, because lowering the adjustment can reduce the
die opening in the press.
Die space:Die space is the area available for mounting dies in the press.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
8/153
8
Introduction to Die Cutting Structure
THE FUNDAMENTALS OF DIE-CUTTING OPERATIONS
While there are many die-cutting operations, some of which are very
complex, they can all be reduced to the following simple fundamentals.
Fig. 4-1 Drop-through Blanking Die Fig. 4-2 Piercing Die Assembly
Plain blanking: Fig. 4-1 shows a simple operation of this type. The
material used is called the stockand is generally a ferrous or nonferrous
strip. During the working stroke the punch goes through the material, and
on the return stroke the material is lifted with the punch and is removed
by the stripper plate. The stop pin is a gage for the operator. In practice,
he feeds the stock by hand and locates the holes to be punched as shown.
The part that is removed from the strip is always the work piece (blank) in
a blanking operation.
4.1.2 Piercing: This operation consists of simple hole punching. It differs
from blanking in that the punching (or material cut from stock) is the scrap and
the strip is the work piece. Piercing is nearly always accompanied by a blanking
operation before, after, or at the same time. Fig. 4-2shows a typical piercing
die assembly.
4.1.3 Lancing: This is a combined bending and cutting operation along a
line in the work material. No metal is cut free during a lancing operation.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
9/153
9
The punch is designed to cut on two or three sides and bend along the
fourth side. Fig. 4-3 and 4-4 show the principle of the lancing operation.
Fig. 4-3 lancing action Fig. 4-4 Strip lanced for free metal for
forming
4.1.4 Cutting off and parting: A cutoffoperation separates the work
material along a straight line in a single-line cut (Fig. 4-5). When the
operation separates the work material along a straight line cut in a double-
line cut, it is known asparting (Fig. 4-6) . Cutting off to separate the work
piece from the scrap strip. Cutting off and parting usually occur in the final
stages of a progressive die. Cutting off is also used to chop up the scrap
strip skeleton as it leaves the die. This makes the scrap much easier to
handle. Fig. 4-7 shows the basic principles of cutting off and parting.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
10/153
10
Fig. 4-5 Cutoff action Fig. 4-7 Layout for making blanks by
Cutoff
4.1.5 Notching: This operation removes metal from either or both edges
of the strip. Notching serves to shape the outer contours of the workspace
in a progressive die or to remove excess metal before a drawing or
forming operation in a progressive die. The removal of excess metal allows
the metal to flow or from without interference from excess metal on the
sides. Fig. 4-8 shows a typical example of notching
Fig. 4-8 Notching Fig. 4-9 Shaving
4.1.6 Shaving: Shaving is a secondary operation, usually following
punching, in which the surface of the previously cut edge is finished smoothly
to accurate dimensions. The excess metal is removed much as a chip is
formed with a metal-cutting tool. There is very little clearance (close to zero)
between the punch and die, and only a thin section of the edge is removed
from the edge of the work piece. Fig. 4-9described the shaving operation.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
11/153
11
Fig. 4-10 Trimming a horizontal flange
4.1.7 Trimming: This operation removes the distorted excess metal from
drawn or formed parts and metal that has been needed in a previousoperation. It also provides a smooth edge. Fig. 4-10 shows tooling for
Trimming a horizontal flange on a drawn shell in a separate operation.
After scrap from a sufficient number of trimmed shells has accumulated,
the piece of scrap at the bottom is severed at each stroke of the press by
scrap cutter shown in this figure and falls clear.
CUTTING ACTION IN PUNCH AND DIE OPERATIONS
The cutting action that occurs in blanking or piercing is quite similarto that of chip formation ahead of a cutting tool. The punch contacts the
work material supported by the die and a pressure buildup occurs. When
the elastic limit of the work material is exceeded, the material begins to
flow plastically (plastic deformation). The punch penetrates the work
material, and the blank, or slug, is displaced into the die opening a
corresponding amount. A radius is formed on the top edge of the hole and
the bottom edge of the slug, or blank, as shown in Fig. 4-11a. The radius
is often referred to as rollover and its magnitude depends upon the
ductility of the work material. Compression of the slug material against
the walls of the die opening burnishes a portion of the edge of the blank,
as shown in Fig. 4-11b. At the same time, the plastic flow pulls the
material around the punch, causing a corresponding burnished area in the
work material. Further continuation of the punching pressure then starts
fractures at the cutting edge of the punch and die (see Fig. 4-11c). Under
ideal cutting conditions, the fractures will meet and the remaining portion
of the slug edge will be broken away. A slight tensile burr will be formed
along the top edge of the slug edge will be broken away. A slight tensile
burr will be formed along the top edge of the slug and the bottom edge of
the work material (see Fig. 4-11d).
-
7/30/2019 Presses and Equipment for SheetMetal Dies
12/153
12
Fig. 4-11 Cutting action progression when blanking
and piercing metal
-
7/30/2019 Presses and Equipment for SheetMetal Dies
13/153
13
Fig. 4-12 Characteristic appearance of edges of parts produced
by piercing and blanking
Fig. 4-12 Shows the characteristic appearance of the edges of parts
produced by blanking and piercing operations in detail. The edge radius
(or rollover) is produced during the initial stage of plastic deformation.
The edgeradius is more pronounced with soft materials.
The highly burnished band is the result of the materials being forced
against the walls of the punch and die and rubbing during the final stages
of plastic deformation. The sum of the edge radius depth and the
burnished depth is referred to aspenetration, i.e., the distance the punch
penetrates into the work material before fracture occurs. Penetration is
usually expressed as a percent of material thickness, and it depends upon
the properties of the work material. As the work material becomes
harder, the percent of penetration decreases. For this reason, harder
materials have less deformation and burnished area.
The remaining portion of the cut is the fractured area, or break. The
angle of the fractured area is the breakout angle. The tensile burr is
adjacent to the break. The burr side of blank or slug is toward the punch,
and the burr side of the work material is toward the die opening.
Die Clearance: Clearance is defined as the intentional space between the
punch cutting edge and die cutting edge. Clearance is always expressed as the
-
7/30/2019 Presses and Equipment for SheetMetal Dies
14/153
14
amount of clearance per side. Theoretically, clearance is necessary to allow the
fractures to meet when break occurs, as shown in Fig. 4-13. The amount of
clearance depends upon the kind, thicknessand hardness of the work material.
Excessive clearance allows a large edge radius (rollover) and
excessive plastic deformation. The edges of the material tend to be drawn
or pulled in the direction of the working force, and the break is not
smooth. Large burrs are present at the break edge.
Fig. 4-13 The effect of clearance (a) too little clearance: fracture do
not meet(b) Correct clearance: fracture do meet
Insufficient cutting clearance caused the fractures to miss and
prevents a clean break, as shown in Fig. 4-13a. A partial break occurs,
and a secondary break connects the original or main fractures. This is
often referred to assecondary shear. The secondary break does not allow
separation of the material without interference, and a second burnished
ring is formed, as shown in Fig. 4-13b. The burnished ring may appear as
a slight step around the outside edge of the blank or around the inside
edge of the hole. Insufficient clearance increase pressure on the punch
and die edge and has a marked effect on die life.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
15/153
15
Authorities disagree on the correct amount of clearance for a given
work piece material. One reference may recommend 6 percent of stock
material thickness per side, while another may recommend 12 percent for
the same material. The difference is probably in the end result each is
striving for. The designer should consider the application of the pierced or
blanked work piece. When the purpose is only to make a hole, as in the
case of structural steel, wide clearances may be used to increase die life.
Blanked work pieces that assemble as an integral part of a mechanism
require tighter clearances. Fig. 4-14 shows various edges for
stampings with a description and use of each. Note that the
recommended clearance varies from 2 to 21 percent for mild steel.
The diameter of the blank or pierced hole is determined by
measurement of the burnished area. Since the burnished area on the
blank is produced by the walls of the die, the diameter of the blank will be
the same as the diameter of the die (disregarding a slight expansion after
the blank is pushed from the die). The same principle applies to the
diameter of the pierced hole. The burnished area in the hole is caused by
the punch; thus the diameter of the pierced hole will be the same as the
punch. Therefore, die clearance is either placed on the punch or the die,
depending upon whether the pierced hole or the blank will be the desired
work piece. If the blank is to become the work piece, the die diameter is
made to the work piece size and the punch is reduced in size an amount
equal to the die clearance. If the pierced hole is to become part of the
work piece, the punch is made to the correct hole size and the die
opening is made oversize an amount equal to the die clearance. In simple
terms, the die controls blank size and the punch controls hole size
-
7/30/2019 Presses and Equipment for SheetMetal Dies
16/153
16
Angular clearance is necessary to prevent backpressure caused by
blank or slug buildup especially when the punches or die block are fragile.
Recommended angular clearance varies from to 2 per side, depending
upon the material and the shape of the work piece. Soft materials and
heavy-gage materials require greater angular clearance. Larger angular
clearance may be necessary for small and fragile punches.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
17/153
17
Fig. 4-15 The use of angular clearance
Stripping: The forces that cause the blank to grip inside the die
walls also cause the stock material to grip around the punch. The stock
material will rise as the press ram is raised unless some means of
stripping the stock material from the punch is provided. Fig. 4-15 shows
the two basic types of stripping device.
Fig. 4-15 Basic types of stripping devices (a) Fixed type and
(b) Spring loadedtype
The amount of pressure required to strip the stock material from the
punch varies from 5 to 20 percent of the cutting-force requirements.
This is only a rough estimate, as many variables affect stripping
pressure. For example some materials cling more than others. Thicker
-
7/30/2019 Presses and Equipment for SheetMetal Dies
18/153
18
materials require more stripping force because more material is in
contact with the punch. Holes punched close to the strip edge do not
require as much stripping force because there is less backing and the
metal can give. Punches with polished sidewalls tend to strip easier
than those with rough surfaces. More force is also required to strip
punches that are close together.
Cutting forces: The force required to penetrate the stock material
with the punch is the cutting force. If the die contains more than one
punch that penetrates t he stock material simultaneously, the cutting
force for that die is the sum of the forces for each punch. Knowledge of
cutting forces is important in order to prevent overloading the press or
failure to use it to capacity.
The formula for determining cutting forces takes into account the
thickness of the stock material, the perimeter of the cut edge and the
shear strength of the stock material. The shear strength of the stock
material is the force necessary to sever 1 sq. in. of the material by
direct shearing action.
It sometimes becomes necessary to reduce cutting forces to
prevent press overloading. One method of reducing cutting forces is to
step punch lengths, as shown in Fig. 4-16. Punches or groups of punches
progressively become shorter by about one stock-material thickness. A
second method is to grind the face of the punch or die at a small shear
angle with the horizontal. This has the effect of reducing the area in shear
at any one time. Shear also reduces shock to the press and smoothes out
the cutting operation. The shear angle chosen should provide a change in
punch length of from 1 to 1 times the stock thickness. Shear that is
equal to or greater than the stock thickness is called full shear. Cutting
forces are reduced by approximately 30 percent when full shear is applied
-
7/30/2019 Presses and Equipment for SheetMetal Dies
19/153
19
Methods of reducing cutting forces:
a) Stepping punches
b) Single shear on punch
c) Single shear on die
d) Double shear on punches
e) Double shear on punches
f) Convex & concave shear
Scrap Strip Trip Layout For Blanking
In designing parts to be blanked from strip material, economical stock
utilization is of high importance. The goal should be at least 75 per cent
utilization. A very simple scrap-strip layout is shown in Fig. 6-1.
SCRAP ALLOWANCE
-
7/30/2019 Presses and Equipment for SheetMetal Dies
20/153
20
A scrap-strip layout having insufficient stock between the blank and the strip
edge, and between blanks, will result in a weakened strip, subject to breakage
and thereby causing misfeeds. Such troubles will cause unnecessary die
maintenance owing to partial cuts, which defect the punches, resulting in nicked
edges. The following formulas are used in calculating scrap-strip dimensions for all
strips over 0.8 mm. thick.
t = specified thickness of the material
B = 1.25 t when C is less than 64 mm
B = 1.5 t when C is 64 mm or longer
C = L + B, or lead of the die
Example: A rectangular part, to be blanked from 1.5 mm thick steel
(Manufacturers Standard) is 10 X 27 mm. If the scrap strip is developed as in Fig.
6-2, the solution is
t = 1.5 mm
B = 1.25 X 1.5 = 1.875 mm
C = 10 + 1.875 = 11.875 mm
W = 27 + 3.75 = 30.75 mm
Nearest commercial stock is 32 mm. Therefore, the distance B will equal
2.3mm. This is acceptable since it exceeds minimum requirements.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
21/153
21
Minimum Scrap-Strip Allowance: If the material to be blanked is 0.6
mm thick or less, the formulas above should not be used. Instead, dimension B is
to be as follows:
Strip width W Dimension B
0 - 75 mm 1.3 mm
76 150 mm 2.4 mm
150 300 mm 3.2 mm
Other Scrap-Strip Allowance Applications:
Figure 6-3, 6-4 and 6-5 illustrates special allowances for one-pass layouts:
-
7/30/2019 Presses and Equipment for SheetMetal Dies
22/153
22
View D. For layouts with sharp corners of blanks adjacent, B = 1.25 t.
Fig. 6-4 Allowances for one-passlayouts.
Percentage of Stock Used: If the area of the part is divided by the area
of the scrap strip used, the result will be the percentage of stock used.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
23/153
23
If A = total area of strip used to produce a single blanked
part, then
A = CW (Fig. 3-35), and a = area of the part = LH.
If C = 11.5 mm and W = 32 mm then A = 11.5 X 32 = 368
mm
If L X 9.5 mm and H = 27 mm then a = 29.5 X 27 = 256.6
mm
Percentage of stock used:
a 256.5
= = 70% approx.A 368
EVOLUTION OF A BLANKING DIE
In the planning of a die, the examination of the part print immediately
determines the shape and size of both punch and die as well as the working area
of the die set.
Die Set Selection
-
7/30/2019 Presses and Equipment for SheetMetal Dies
24/153
24
A commercially available standardized two-post die set with 150 mm overall
dimensions side-to-side and front-to-back allows the available 76 mm. wide stock
to be fed through it. It is large enough for mounting the blanking punch on the
upper shoe (with the die mounted on the lower shoe) for producing the blank
shown in Fig. 6-6, since the guideposts can be supplied in lengths of from 100 to
225 mm.
Since the stock, in this case was available only in a width of 76 mm the length
of the blanked portions extended across the stock left a distance between the
edges of the stock and the ends of the blank of 6 mm or twice the stock
thickness; this allowance is satisfactory for the 3.2 mm stock.
Die Block Design
By the usual rule-of thumb method previously described, die block thickness
(of tool steel) should be a minimum of 20 mm for a blanking perimeter up to 75
mm and 25 mm for a perimeter between 75 and 100 mm. For longer perimeters,
die block thickness should be 32 mm. Die blocks are seldom thinner than 22 mm
finished thickness to allow for grinding and for blind screw holes. Since the
perimeter of the blank is approximately 178 mm a die block thickness of 38 mm
was specified, including a 6 mm grinding allowance.
There should be a margin of 32 mm around the opening in the die block; its
specified size of 150 x 150 mm allows a margin of 45 mm in which four M10 cap
screws and dia. 10 mm dowels are located at the corners 20 mm from the edges
of the block.
The wall of the die opening is straight for a distance of 3.2 mm (stock
thickness); below this portion or the straight, an angular clearance of 1 allows
the blank to drop through the die block without jamming. The dimensions of the
die opening are the same as that of the blank; those of the punch are smaller by
the clearance (6 per cent of stock thickness, or 2 mm), which result in the
production of blanks to print (and die) size.
The top of the die was ground off a distance equal to stock thickness (Fig. 6-7)
with the result that shearing of the stock starts at the ends of the die and
progresses towards the center of the die, and less blanking pressure is required
than if the top of the die where flat.
Punch Design
-
7/30/2019 Presses and Equipment for SheetMetal Dies
25/153
25
The shouldered punch (57 mm) long is held against a 6 mm thick hardened
steel backup plate by a punch plate 20 mm thick) which is screwed and doweled
to the upper shoe. The shut height of the die can be accommodated by a 32-ton
(JIC Standard) open-back inclinable press, leaving a shut height of 240 mm. For
the conditions of this case study, shear strength S = 42 kg/mm, blanked
perimeter length L = 178 mm approx. and thickness T = 3.2 mm.
From the equation P = SLT
The pressure P = 42 kgs. X 178 mm X 3.2 = 23.92 tons.
This value is well below the 32-ton capacity of the selected
press.
The shut height (Fig. 6-7) is 178 mm less the 1.6 mm
travel of the punch into the die cavity.
print immediately determines the shape and size of both punch and
die as well as the working area of the die set.
Die Sheet Selection
-
7/30/2019 Presses and Equipment for SheetMetal Dies
26/153
26
A commercially available standardized two-post die set with 150 mm
overall dimensions side-to-side and front-to-back allows the available 76 mm.
wide stock to be fed through it. It is large enough for mounting the blanking
punch on the upper shoe (with the die mounted on the lower shoe) for producing
the blank shown in Fig. 6-6, since the guideposts can be supplied in lengths of
from 100 to 225 mm.
Since the stock, in this case was available only in a width of 76 mm the
length of the blanked portions extended across the stock left a distance between
the edges of the stock and the ends of the blank of 6 mm or twice the stock
thickness; this allowance is satisfactory for the 3.2 mm stock.
Die Block Design
By the usual rule-of thumb method previously described, die block
thickness (of tool steel) should be a minimum of 20 mm for a blanking perimeter
up to 75 mm and 25 mm for a perimeter between 75 and 100 mm. For longer
perimeters, die block thickness should be 32 mm. Die blocks are seldom thinner
than 22 mm finished thickness to allow for grinding and for blind screw holes.
Since the perimeter of the blank is approximately 178 mm a die block thickness of
38 mm was specified, including a 6 mm grinding allowance.
There should be a margin of 32 mm around the opening in the die block;
its specified size of 150 x 150 mm allows a margin of 45 mm in which four M10
cap screws and dia. 10 mm dowels are located at the corners 20 mm from the
edges of the block.
The wall of the die opening is straight for a distance of 3.2 mm (stock
thickness); below this portion or the straight, an angular clearance of 1 allows
the blank to drop through the die block without jamming. The dimensions of the
die opening are the same as that of the blank; those of the punch are smaller by
the clearance (6 per cent of stock thickness, or 2 mm), which result in the
production of blanks to print (and die) size.
The top of the die was ground off a distance equal to stock thickness (Fig.
6-7) with the result that shearing of the stock starts at the ends of the die and
progresses towards the center of the die, and less blanking pressure is required
than if the top of the die where flat.
Punch Design
-
7/30/2019 Presses and Equipment for SheetMetal Dies
27/153
27
The shouldered punch (57 mm) long is held against a 6 mm thick hardened
steel backup plate by a punch plate 20 mm thick) which is screwed and doweled
to the upper shoe. The shut height of the die can be accommodated by a 32-ton
(JIC Standard) open-back inclinable press, leaving a shut height of 240 mm. For
the conditions of this case study, shear strength S = 42 kg/mm, blanked
perimeter length L = 178 mm approx. and thickness T = 3.2 mm.
From the equation P = SLT
The pressure P = 42 kgs. X 178 mm X 3.2 = 23.92 tons.
This value is well below the 32-ton capacity of the selected
press.
The shut height (Fig. 6-7) is 178 mm less the 1.6 mm
travel of the punch into the die cavity.
Stripper Design
The stripper that was designed is of the fixed type with a channel or slot
having a height equal to 1.5 times stock thickness and a width of 80 mm to allow
for variations in the stock width of 75 mm. The same screws that hold the die
block to the lower shoe fasten the stripper to the top of the die block.
If, instead of 3.2 mm stock, thin (0.8 mm) stock were to be blanked, a
spring-loaded stripper would firmly hold the stock down on top of the die block
and could, to some extent, flatten out wrinkles and waves in it.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
28/153
28
A spring-loaded stripper should clamp the stock until the punch is
withdrawn from the stock. The pressure that strips the stock from the
punch on the upstroke is difficult to evaluate exactly. A formula frequently
used is
Ps = 2.5 x L x t kgs.
Where Ps = stripping pressure, in kgs.
L = perimeter of cut, in mm.
t = stock thickness, in mm.
Spring design is beyond the scope of this book; die spring
data are available in the catalogues of spring manufacturers.
Stock Stops
The pin stop pressed in the die block is the simplest method for stopping
the hand-fed strip. The right-hand edge of the blanked opening is pushed against
the pin before descent of the ram and the blanking of the next blank. The 4-8 mm
depth of the stripper slot allows the edge of the blanked opening to ride over the
pin and to engage the right-hand edge of every successive opening.
The design of various types of stops adapted for manual and automatic
feeding is covered in a preceding discussion.
A spring-loaded stripper should clamp the stock until the punch is
withdrawn from the stock. The pressure that strips the stock from the punch on
the upstroke is difficult to evaluate exactly. A formula frequently used is
Ps = 2.5 x L x t kgs.
Where Ps = stripping pressure, in kgs.
L = perimeter of cut, in mm.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
29/153
29
t = stock thickness, in mm.
Spring design is beyond the scope of this book; die spring
data are available in the catalogues of spring manufacturers.
Stock Stops
The pin stop pressed in the die block is the simplest method for stopping
the hand-fed strip. The right-hand edge of the blanked opening is pushed against
the pin before descent of the ram and the blanking of the next blank. The 4-8 mm
depth of the stripper slot allows the edge of the blanked opening to ride over the
pin and to engage the right-hand edge of every successive opening.
EVOLUTION OF A PROGRESSIVE BLANKING DIE
Figure 6-8 gives the blanked dimensions of a linkage case cover of cold
rolled steel, stock size 3.2 x 60 x 60 mm. Production is stated to be 200 parts
made at one setup, with the possibility of three or four runs per year.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
30/153
30
Step 1, Part Specification
1. The production is of medium class; therefore a second-class die willbe used.
2.
Tolerances required: Except for location of the slots, alldimensions are in fractions. The slot locations, though specified in
decimals, are not very close. Thus a compound die is not
necessary; a two or three-station progressive die will be adequate.
3. Type of press to be used: Available for this production are pressesof 5-ton, 8-ton, or 10-ton capacity, with a shut height of 175 or
200 mm.
4. Thickness of material: Specified as 32 mm standard cold rolledsteel.
Step 2, Scrap-Strip Development
From the production requirements, a single-row strip will
suffice. After several trials, the scrap strip shown in Fig. 6-9 was
decided upon. Owing to the closeness of the holes it was decided to
make a four-station die.
The scrap strip would be fed into the first finger stop, and the center hole would
be pierced. The strip would then be moved in to the second finger stop, and the
two holes would then be pierced. At the third stage and third finger stop, a pilot
-
7/30/2019 Presses and Equipment for SheetMetal Dies
31/153
31
would locate the strip and the four corner holes would then be pierced. At the
fourth and final stage, a piloted blanking punch would blank out the finished part.
Step 3, Press Tonnage
It is now in order to determine the amount of pressure needed. Only the
actual blanking in the fourth stage need be calculated, since the work in the first
three stages will be done by stepped punches.
From Table, the shear strength S of cold rolled steel is 40 kgs/mm. The
length L of the blanked perimeter equals 60 x 4 = 240 mm. The depth of cut
(stock thickness t) equals 3.2 mm. From the equation P = S L t
P = 40 kgs./mm x 240 mm x 3.2 mm = 30,720 kgs.
Or 30.7 tons.
This tonnage is greater than can be handled by the available presses. To
lower the pressure, shear is ground on the blanking punch to reduce the needed
pressure by on third. This, ? x 30.7 = 30.7 - 10.2 = 20.5 tons. A punch press of
25-ton capacity would do, but there is reported available only a 30-ton press with
a 190 mm shut height and a 50 mm stroke. This press is selected. The bolster
plate is found to be 300 mm deep, 140 mm from centerline of ram to back edge
of bolster, and 600 mm wide. Shank diameter is 64 mm.
Step 4, Calculation of the Die
(a) The die. The perimeter of the cut equals 240 mm and therefore the
thickness of the die must be 25 nm. The width of our scarp-strip opening is 60
mm with 32 mm extra material on each side of the opening, it will be 60 mm + 64
mm = 124 mm or 130 mm width. The distance from the left side of the opening in
stage 4 to the edge of the opening in stage 1 equals 3 C + 30 + 6 = 192 + 30 + 6
= 228 mm and plus 62 mm = 290 mm or 296 mm long. Therefore the die should
be 2.5 x 130 x 296 mm long.
(b) The die plate. As a means of filling in between the die and the die shoe, a
die plate of machinery steel is used. To secure the die plate to the die shoe M12
cap screws and dowels are used. A minimum of twice the size of the cap screw for
the distance from the edge of the die to the edge of the die plate is needed, which
will equal 25 mm. Twice this distance = 50 mm and 50 mm added to the size ofthe die will result in a die plate of 25 x 180 x 346 mm. Figure 6-10 shows the die
-
7/30/2019 Presses and Equipment for SheetMetal Dies
32/153
32
and die plate fitted together, and with the holes, which show the sharpening
portion and the relief portion.
Step 5, Calculation of Punches
Good practice requires 10 per cent of the metal thickness to be removed
from the basic dimension of the blanking punch. This same value is used on the
die opening, since holes are to be pierced in the blank. The clearance rule will be
applied to the die opening in Stages 1, 2, and 3, and to the punch in Stage 4 (see
fig6-11).
For Stage 4: Blank to be 60 mm square,
Stock thickness = 3.2 mm; 10% = 0.32 mm.
Punch = 60 0.32 = 59.68 mm.
Therefore the die opening will equal 60.01 to 60 mm and
the punch will equal 59.68 to 59.67 mm.
For Stage 2: Slot to be 8 mm wide by 34 mm long.
Die = 8 + 0.32 + 8.32 mm long = 34.32 to 34.33 mm.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
33/153
33
Punch will equal 3.99 to 8.00 mm. wide, and 33.99 to
34.00 mm. long.
The punch and the die opening will have straight sides for at least 3-
11 also shows a 3 mm shear for the die at Stage 4 and a 3 mm shear for thepunches of Stage 2, and also the stepped arrangement of the punches for all
stages
Step 6, springs
A solid stripper plate can be used for this job.
Step 7, Piloting
Figures 6-9 and 6-11 illustrate the arrangement for piloting. In this case it
is direct piloting. However, if the part did not have a center hole, and the slots
and other holes were too small, indirect piloting would have to be provided.
Step 8, Automatic Stops
Finger stops will act as stops when a new scrap strip is being inserted but,
after that, an automatic spring drop stop must be used to halt the scrap strip.
Figures 6-12 illustrate details of the completed drawing of the die.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
34/153
34
Die Design
WIRE METHODOFLOCATING THE CENTEROF PRESSURE:
The center of pressure of a blank contour may be located mathematically, but
it is a tedious computation. Location of the center of pressure within 12 mm
of true mathematical location is normally sufficient.A simple procedure
accurate within such limits is to bend asoft wire to the blank contour. By
balancing this frame acrossa pencil, in two coordinates, the intersection ofthe two axes of balance will locate the desired point. As an example of the
marked influence this factor may have on tool design, a rather unusual blank
is shown in Fig. 5-1. Here, the center of pressure is near one end of the
blank, and will require the indicated imbalance in the press tool design.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
35/153
35
Die clearance is the space between the matting members of a die set. Proper
clearance between cutting edges enables the fractures to meet and the
fractured portion of the sheared edge has a clean appearance. For optimum
finish of a cut edge, proper clearance is necessary and is a function of the
kind, thickness and temper of the work material.
At Fig. 5-2, which shows clearance C for blanks of a given size, make die to
size and punch smaller by total clearance 2C. At B, which shows clearance for
holes of given size, make punch to size and die larger by the amount of the
total clearance 2C
-
7/30/2019 Presses and Equipment for SheetMetal Dies
36/153
36
The application of the clearance for holes of irregular shape is diagrammed in
Fig. 5-13; at B the hole will be of punch size, while at A the blank will be of
the same dimensions as the die.
DIE BLOCK GENERAL DESIGN:
Overall dimensions of the die block will be determined by the minimum die
wall thickness required for strength and by the space needed for mounting
screws and dowels and for mounting the stripper plate.
Wall thickness requirements for strength will depend on the thickness of the
stock to be cut. Sharp corners in the contour may lead to cracking in heat
treatment, and so require greater wall thickness at such points.
Two, and only two, dowels should be provided in each block or element thatrequires accurate and permanent positioning. They should be located as far
apart as possible for maximum locating effect, usually near diagonally
opposite corners. Two or more screws will be used, depending on the size of
the element mounted. Screws and dowels are preferably located about 1
times their diameters from the outer edges or the blanking contour.
Die block thickness (see Table 5-1) is governed by the strength necessary to
resist the cutting forces, and will depend on the type and thickness of the
material being cut. On very thin materials 13 mm. thickness should be
-
7/30/2019 Presses and Equipment for SheetMetal Dies
37/153
37
sufficient but, except for temporary tools, finished thickness is seldom less
than 22 mm., which allows for blind screw holes and also builds up the tool to
a narrower range of shut height for press room convenience.
DIE BLOCK CALCULATIONS:
Method 1 (Rule of Thumb). Assuming a die block of tool steel its thickness
should be 20 mm. minimums for a blanking perimeter of 75 mm. or less 25
mm. thick for perimeters between 75 mm. and 250 mm. and 32 mm. thick for
larger perimeters. There should be a minimum of 32 mm. margins around the
opening in the die block.
The die opening should be straight for a maximum of 3 mm; the opening
should then angle out at to 1 to the side(draft). Thestraight sides
provide for sharpenings of the die; the tapered portion enables the blanks to
drop through without jamming.
To secure the die to the die plate or die shoe, the following rules provide
sound construction:
1) On die blocks up to 175 mm square, use two M10 cap screws and two
dowels of dia. 10 mm.
2) On sections up to 200 mm. square, use three cap screws and two dowels .
3) For blanking heavy stock, use cap screws and dowels of dia 12-mm.
diameter. Counterbore the cap screws 3.2 mm. deeper than usual, to
compensate for die sharpening.
Method 2. This method of calculating the proper size of the die was derivedfrom a series of tests, whereby die plates were made increasingly thinner untilbreakage became excessive. From these data the calculation of die thicknesswas divided into four steps:1) Die thickness is provisionally selected from Table 5-1. This table takesinto account the thickness of the stock and its ultimate shear strength (seeTable 4-1).
Table 5-1. DIE THICKNESS PER TON OF PRESSURE
Stock Die Stock Die
-
7/30/2019 Presses and Equipment for SheetMetal Dies
38/153
38
thickness
mm.
thickness
cm.
thickness
mm.
thickness
cm. *
0.25
0.50
0.7
5
1.00
1.2
5
*
0.
118
0.236
0.
335
0.433
0.
512
1.5
1.8
2.0
2.3
2.5
0.590
0.649
0.7
08
0.748
0.7
87
* For each ton per sq. cm. of shear strength.
Table 5-2. FACTORS FOR CUTTING EDGES EXCEEDING 50-
mm.
Cutting perimeter mm. Expansion Factor
50 to 75
75 to 150150 to 300
300 to 500
1.25
1.51.75
2.0
2) The following corrections are then made:
a) The die must never be thinner than 8 mm. to 10 mm.
b)Data in Table 5-1 apply to small dies, i.e. those with acutting perimeter of 50-mm. or less. For larger dies, the
thickness listed in Table 5-1 must be multiplied by the
factors in Table 5-2.
c) Data in Tables 5-1 and 5-2 are for die members of tool-
steel, properly machined and heat-treated. If a special alloy
of steel is selected, die thickness can be decreased.
d) Dies must be adequatelysupported on a flat die plate or die
shoes. Thickness data above do not apply if the die is placed
-
7/30/2019 Presses and Equipment for SheetMetal Dies
39/153
39
over a large dopening or is not adequately supported.
However, if the die is placed into a shoe, the thickness of
the member can beDecreased up to 50 percent.
e) A grinding allowance up to 0.25 to 0.5 mm must be added
to the calculated die thickness.
3) The critical distance A, Fig. 5-4, between the cutting edge and
the die border must be determined. In small dies, A equals 1.5
to 2 times the die thickness; in larger dies it is 2 to 3 times the
die thickness.
Table 5-3 MINIMUM CRITICAL AREA
Criticaldistance A must not less than 1.5 to 2 times die
thickness.
The critical area between the die hole and the die border
must be checked against minimum values in Table 3-4 and
die thickness B corrected if necessary.
4) Finally, the die thickness must be checked against the empirical
rule that the cross-sectional area A x B (Fig. 5-4) must bear a
certain minimum relationship to the impact pressure for a die
put on a flat base. In Table 5-3 impact pressure equals
thickness times the perimeter of the cut times ultimate shearing
strength. If the die height, as calculated by steps 1and 2, does
-
7/30/2019 Presses and Equipment for SheetMetal Dies
40/153
40
not give sufficient area for the critical distance A (Fig. 5-4), the
die thickness must be increasedaccordingly.
With the die block size determined, the exact size of the die
opening can now be determined. Assuming a clearance of
approximately 10 percent of the metal thickness, and by the rule-of-
thumb method.
Metal thickness = 1.6 x 10% = 0.16 mm.
If the finished die opening is 25 mm. dia., then add 0.16 mm.,
giving 26.16 0.025 mm. If the blank were made according to size,
the clearance would be applied to the punch.
PUNCH DIMENSIONING:The determination of punch dimension has been generally
based on practical experience. When the diameter of a pierced round
hole equals stock thickness, the unit compressive stress on the punch
is four times the unit shear stress on the cut area of the stock, from
the formula.
The diameter of most holes are greater than stock thickness; a
value for the ratio d / tof 1.1 is recommended. The maximum
allowable length of a punch can be calculated from the formula.
This is not to say that holes having diameters less than stock
thickness cannot be successfully punched. The punchingof such holes can be
facilitated by:
1. Punch steels of high compressive strengths
2. Greater than average clearances
3. Optimum punch alignment, finish, and rigidity
4. Shear on punches or dies or both
5. Prevention of stock slippage
6. Optimum stripper design
The determination of punch dimension has been generally based on practicalexperience. When the diameter of a pierced round hole equals stockthickness, the unit compressive stress on the punch is four times the unitshear stress on the cut area of the stock, from the
METHODS OF PUNCH SUPPORT:
-
7/30/2019 Presses and Equipment for SheetMetal Dies
41/153
41
Following figure presents a number of methods to support punches to meetvarious production requirements:
-
7/30/2019 Presses and Equipment for SheetMetal Dies
42/153
42
-
7/30/2019 Presses and Equipment for SheetMetal Dies
43/153
43
-
7/30/2019 Presses and Equipment for SheetMetal Dies
44/153
44
STOCK STOPS:
Finger Stops:
In its simplest form, a stock stop may be a pin or small block, against which
an edge of the previously blanked opening is pushed after each stroke of the
press. With sufficient clearance in the stock channel, the stock is momentarily
lifted by its clinging to the punch, and is thus released from the stop. Figure
6-23 shows an adjustable type of solid block stop which can be moved along a
-
7/30/2019 Presses and Equipment for SheetMetal Dies
45/153
45
support bar in increments up to 25 mm to allow various stock lengths to be
cut off.
A starting stop, used to position stock as it is initially fed to a die, is shown in
Fig. 5-23, view A. Mounted on the stripper plate, it incorporates a latch, which
is pushed inward by the operator until its shoulder (1) contacts the stripper
plate. The latch is held in to engage the edge of the incoming stock; the first
die operation is completed, and the latch is released.
Automatic Stops:
The starting stops shown at view B, mounted between the die
shoe and die block, upwardly actuates a stop plunger to initially
position the incoming stock. Compression springs return the manually
operated lever after the first die operation is completed.
Trigger stops incorporated pivoted latches (1, Fig. 5-24, viewsA
and B). At the rams descent, these latches are moved out of the
blanked-out stock area by actuating pins, 2. On the ascent of the ram,
springs, 3, control the lateral movement of the latch (equal to the side
relief) which rides on the surface of the advancing stock, and drops
into the blanked area to rest against the cut edge of the cut-out area.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
46/153
46
When feeding the stock strip from one stage to another, some method must
be used to correctly locate and stop the strip. Automatic stops (trigger stops)
register the strip at the final die station. They differ from finger stops in that
they stop the strip automatically, the operator having only to keep the strip
pushed against the stop in its travel through the die. A typical automatic stop
designs shown in figure 5-24. In this lever end is raised by the trip screw as
punch descends and cut the blank. On the return stroke end of lever drops
and lever end would drop it former position if it were not for the endwise
action o the lever, which causes the lever end to drop onto the top surface of
the stock instead of into blank space. The mounting of the finger on the pivot
is loose enough to allow for this endwise movement.
When feeding the stock strip from one stage to another, some method must
be used to correctly locate and stop the strip.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
47/153
47
Automatic stops (trigger stops) register the strip at the final die station. They
differ from finger stops in that they stop the strip automatically, the operator
having only to keep the strip pushed against the stop in its travel through the
die.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
48/153
48
Cropping:
An unusual stop that requires no moving mechanisms is known
as the French stop or Cropping as shown in fig. 5-26. It operates on
the principle of cutting a shoulder in the edge of the stock strip, which
acts as stop. A strip wider than necessary is inserted into the strip
channel until it contacts the shoulder built into back gage. The first hit
of the press performs the first station operation and at the same time
punches from the side of the strip a section of metal equal to the
length of the pitch. This operation leaves a shoulder in the side of the
strip. The strip is then advanced until the strip shoulder contacts the
shoulder on the back gage on the return stroke of the ram.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
49/153
49
The advantage of the cropping is its accuracy and speed of
operation. It is especially well suited to the light-gage materials that
are easily distorted when pushed or pulled against a stop pin. Its main
disadvantages are the extra cost of tooling and extra stock scrap.
PILOTS:
Since pilot breakage can result in the production of inaccurate parts and the
jamming or breaking of die elements, pilots should be made of
good tool-steel, heat-treated for maximum toughness and to
hardness of Rock-well C57 to 60.
Press-fit Pilots:
Press-fit pilots (Figs. 5-28 and 5-29, view C), which may out of the punch
holder, are not recommended for high-speed dies but are often used in low-
speed dies. For holes 20 mm in diameter or larger, the pilot may be held
-
7/30/2019 Presses and Equipment for SheetMetal Dies
50/153
50
by a socket-head screw shown at B. A typical press-fit type is shown at C.
Pilots of less than 6 mm diameter may be headed and secured by a socket
setscrew, as shown at D.
Indirect Pilots:
Designs of pilots that enter previously pierced holes in the strip as shown in
Fig. 5-27. This practice provides more support under the strip. It helps to
locate the pitch and prevent distortion.
Spring-loaded pilots:
Spring-loaded pilots should be used for stock exceeding 1.5 mm thickness
sheet as shown in Fig. 5-30. This allows the pilot to retract in case of misfeed.
Tapered slug-clearance holes through the die and lower shoe should be
provided, since indirect pilots generally pierce the strip during a misfeed.
Spring-loaded pilots are not necessary on thinner material because the pilot
will pierce the strip rather than break in the event of misfeed. In this case
tapered slug-clearance holes through the die and lower shoe should be
provided.
Misfeed detector:
Fig. 5-31 shows a precision misfeed detector used in a manner similar to that
of a pilot. The detector senses out-of-register position of stock and actuates a
switch to cut off the electric power to the press.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
51/153
51
-
7/30/2019 Presses and Equipment for SheetMetal Dies
52/153
52
STRIPPERS:
Strippers are of two types, fixed or spring-operated. The primary
function of either type is to strip the work piece from a cutting or non-cutting
punch or die. A stripper that forces a part out of a die may also be called a
knockout, an inside stripper, or an ejector. Besides its primary function, a
stripper may also hold down or clamp, position, or guide the sheet, strip, or
work piece.
Fixed strippers:
The stripper is usually of the same width and length as the die block.
In the simpler dies, the stripper may be fastened with the same screws
and dowels that fasten the die block, and the screw heads will be
counter bored into the stripper. In more complex tools and with
sectional die blocks the die block screws will usually be inverted, and
the stripper fastener will be independent. Following fig. 5-32 is will
make clear picture of fixed type stripper plate.
The stripper thickness must be sufficient to withstand the force required to
strip the stock from the punch, plus whatever is required for the stock strip
channel. Except for very heavy tools or large blank areas, the thickness
required for screw head counter bores, in the range of 10 to 16 mm will be
sufficient.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
53/153
53
The height of the stock strip channel should be at least 1 times the stock
thickness. This height should be increased if the stock is to be lifted over a
fixed pin stop. The channel width should be the width of the stock strip, plus
adequate clearance to allow for variations in the width of the strip as cut, as
follows:
Stock thickness mm Add to strip width in mm
Up to 1 2.0
1 to 2 2.4
2 to 3 2.8
Above 3 3.2
If the stripper length has been extended on the feed end for better
stock guidance, a sheet metal plate should be fastened to the underside of the
projecting stripper to support the stock. This plate should extend slightly in
for convenience in inserting the strip. The entry edges of the channel should
be beveled for the same reason.
5.9.2 Spring-operated strippers:
-
7/30/2019 Presses and Equipment for SheetMetal Dies
54/153
54
Where spring-operated strippers are used as shown in fig. 5-33, the force
required for stripping is 35000 times cut perimeter times the stock thickness.
It may be as high as 20 per cent of the blanking force, which will determine
the number and type of springs required. The highest of these values should
be used.
Selection of stripper springs:
Die springs are designed to resist fatigue failure under severe service conditions. They are
available in medium, medium-heavy and heavy-duty grades, with corresponding permissible
deflections ranging from 50 to 30 percent of free length. The number of springs for which space is
available and the total required force will determine which grade is required. The required travel
plus the preload deflection will be the total deflection, and will determine the length of spring
required to stay within allowable percentage of deflection limits. As the punch is re-sharpened,
deflections will increase, and should also be allowed for.
To retain the stripper against the necessary preload of the springs, and
to guide the stripper in its travel, a special type of shoulder screw known as a
stripper bolt is used.
Choice of the method of applying springs to stripper plates depends on
the required pressure, space limitations, shape of the die and the nature of
the work, and production requirements. The stripping pressure may be from 5
to 20 percent of the cutting pressure. The amount of pressure needed to hold
thin firmly while it being cut must also be considered when selecting springs.
With so many variable factors involved, exact results cannot be expected from
formulas, although they may be useful as guides. The Metal Handbook gives
the following formula for stripping force:
L = KA
Where
L = Stripping force
K = Stripping
constant, Kg / cm.2
A = Area of cut
surface, cm.2
Approx. values for K, as determined by experiment: 105 for sheet
metal thinner than 1.6 mm. when cut is near an edge or near a
preceding cut; 150 for other cuts in sheet metal thinner than 1.6
mm; and 210 for sheet metal more than 1.6 mm. thick.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
55/153
55
(stockthickness xlength of cut)
Die springs are available in various service grades with corresponding
permissible deflections ranging from 25 to 50 percent of free length. For
example, DME Spring catalogue lists four load ratings. Based upon max. (See
fig. 5-34)
50% deflection = medium pressure (MP)
37% deflection = medium high pressure (MHP)
30% deflection = high pressure (HP)
25% deflection = extra high pressure (XMP)
An important feature of these springs is that they are similar
dimensioned thus are interchangeable. The steps in selecting die
springs are as follows:
1) Estimate the stripping force required according to formula.
2) Determine the amount of space available for spring mounting.
3) Select the max. allowable number of springs, which will fit into
the available space and total required force, will determine
which grade of spring is required.
4) Determine the deflection. The required travel plus preload
deflection will be the total deflection and will determine the
length of spring required to stop within the allowable
percentage of deflection limits. Allowance should be made for
punch sharpening, which will increase deflections over a period
of time.
Select a spring from the lowest (greatest deflection) load rating series from
the table. It is important that the spring not be compressed beyond the
specific limit for the highest-pressure spring of corresponding length and
-
7/30/2019 Presses and Equipment for SheetMetal Dies
56/153
56
diameter. Then if the springs prove too light for the stripping force required,
each one is replaced with the next higher rated springs. This will provide more
stripping pressure without the need changing spring pockets, support rods
and the like.
KNOCKOUTS
Since the cut blank will be retained, by friction, in the die block, some means
of ejecting on the ram upstroke must be provided. A knockout assembly
consists of a plate, a push rod and a retaining collar. The plate is a loose fit
with the die opening contour, and moves upward as the blank is cut. Attached
to the plate, usually by rivets, is a heavy pushrod, which slides in a hole in the
shank of the die set. This rod projects above the shank, and a collar retains
and limits the stroke of the assembly. Now the assembly of the ram stroke, a
knockout bar in the press will contact the pushrod and eject the blank.
It is essential that the means of retaining the knockout assembly besecure, since serious damage would otherwise occur.
In the ejection of parts positive knockouts offer the following
advantages over spring strippers where the part shape and the die selections
allow their use:
-
7/30/2019 Presses and Equipment for SheetMetal Dies
57/153
57
1) Automatic part disposal; the blank, ejected near the top of the ram
stroke, can be blown to the back of the press, or the press may be
inclined and the same result obtained.
2) Lower die cost; knockouts are generally of lower cost than spring
strippers.
3) Positive action; knockouts do not stick as spring strippers
occasionally do.
4) Lower pressure requirements, since there are no heavy springs to
be compressed during the ram descent.
Fig. 5-35 shows a plain inverted compound die, is of the simplest type.
It consists of an actuating plunger, knockout plate and a stop collar
doweled to the plunger. Shedder D consists of a shouldered pin
backed by a spring, which is confined by setscrew
-
7/30/2019 Presses and Equipment for SheetMetal Dies
58/153
58
Scrap Strip Trip Layout For Blanking
In designing parts to be blanked from strip material, economical stock
utilization is of high importance. The goal should be at least 75 per cent
utilization. A very simple scrap-strip layout is shown in Fig. 6-1.
SCRAP ALLOWANCE
A scrap-strip layout having insufficient stock between the blank and
the strip edge, and between blanks, will result in a weakened strip, subject to
breakage and thereby causing misfeeds. Such troubles will cause unnecessary
die maintenance owing to partial cuts, which defect the punches, resulting in
nicked edges. The following formulas are used in calculating scrap-strip
dimensions for all strips over 0.8 mm. thick.
t = specified thickness of the material
B = 1.25 t when C is less than 64 mm
B = 1.5 t when C is 64 mm or longer
C = L + B, or lead of the die
-
7/30/2019 Presses and Equipment for SheetMetal Dies
59/153
59
Example: A rectangular part, to be blanked from 1.5 mm thick
steel (Manufacturers Standard) is 10 X 27 mm. If the scrap
strip is developed as in Fig. 6-2, the solution is
t = 1.5 mm
B = 1.25 X 1.5 = 1.875 mm
C = 10 + 1.875 = 11.875 mm
W = 27 + 3.75 = 30.75 mm
Nearest commercial stock is 32 mm. Therefore, the
distance B will equal 2.3mm. This is acceptable since it exceedsminimum requirements.
Minimum Scrap-Strip Allowance: If the material to be blanked is
0.6 mm thick or less, the formulas above should not be used. Instead,
dimension B is to be as follows:
Strip width W Dimension B
0 - 75 mm 1.3 mm
76 150 mm 2.4 mm
-
7/30/2019 Presses and Equipment for SheetMetal Dies
60/153
60
150 300 mm 3.2 mm
Over 300 mm 4.0 mm
Other Scrap-Strip Allowance Applications:
Figure 6-3, 6-4 and 6-5 illustrates special allowances for one-
pass layouts:
View D. For layouts with sharp corners of blanks adjacent, B =
1.25 t.
Fig. 6-4 Allowances for one-passlayouts.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
61/153
61
Percentage of Stock Used: If the area of the part is divided by the
area of the scrap strip used, the result will be the percentage of stock used.
If A = total area of strip used to produce a single
blanked part, then
A = CW (Fig. 3-35), and a = area of the part = LH.
If C = 11.5 mm and W = 32 mm then A = 11.5 X 32 =
368 mm
If L X 9.5 mm and H = 27 mm then a = 29.5 X 27 =
256.6 mm
Percentage of stock used:
a 256.5= = 70% approx.
A 368
-
7/30/2019 Presses and Equipment for SheetMetal Dies
62/153
62
EVOLUTION OF A BLANKING DIE
In the planning of a die, the examination of the part print immediately
determines the shape and size of both punch and die as well as the working
area of the die set.
Die Set Selection
A commercially available standardized two-post die set with 150 mm overall
dimensions side-to-side and front-to-back allows the available 76 mm. wide
stock to be fed through it. It is large enough for mounting the blanking punch
on the upper shoe (with the die mounted on the lower shoe) for producing the
blank shown in Fig. 6-6, since the guideposts can be supplied in lengths of
from 100 to 225 mm.
Since the stock, in this case was available only in a width of 76 mm the length
of the blanked portions extended across the stock left a distance between the
edges of the stock and the ends of the blank of 6 mm or twice the stock
thickness; this allowance is satisfactory for the 3.2 mm stock.
Die Block Design
By the usual rule-of thumb method previously described, die blockthickness (of tool steel) should be a minimum of 20 mm for a blanking
-
7/30/2019 Presses and Equipment for SheetMetal Dies
63/153
63
perimeter up to 75 mm and 25 mm for a perimeter between 75 and 100 mm.
For longer perimeters, die block thickness should be 32 mm. Die blocks are
seldom thinner than 22 mm finished thickness to allow for grinding and for
blind screw holes. Since the perimeter of the blank is approximately 178 mm
a die block thickness of 38 mm was specified, including a 6 mm grinding
allowance.
There should be a margin of 32 mm around the opening in the die
block; its specified size of 150 x 150 mm allows a margin of 45 mm in which
four M10 cap screws and dia. 10 mm dowels are located at the corners 20
mm from the edges of the block.
The wall of the die opening is straight for a distance of 3.2 mm (stock
thickness); below this portion or the straight, an angular clearance of 1
allows the blank to drop through the die block without jamming. The
dimensions of the die opening are the same as that of the blank; those of the
punch are smaller by the clearance (6 per cent of stock thickness, or 2 mm),
which result in the production of blanks to print (and die) size.
The top of the die was ground off a distance equal to stock thickness
(Fig. 6-7) with the result that shearing of the stock starts at the ends of the
die and progresses towards the center of the die, and less blanking pressure
is required than if the top of the die where flat.
Punch Design
The shouldered punch (57 mm) long is held against a 6 mm thick
hardened steel backup plate by a punch plate 20 mm thick) which is screwed
and doweled to the upper shoe. The shut height of the die can be
accommodated by a 32-ton (JIC Standard) open-back inclinable press, leaving
a shut height of 240 mm. For the conditions of this case study, shear strength
S = 42 kg/mm, blanked perimeter length L = 178 mm approx. and thickness
T = 3.2 mm.
From the equation P = SLT
The pressure P = 42 kgs. X 178 mm X 3.2 = 23.92
tons.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
64/153
64
This value is well below the 32-ton capacity of the
selected press.
The shut height (Fig. 6-7) is 178 mm less the 1.6 mm travel of the
punch into the die cavity.
Stripper Design
The stripper that was designed is of the fixed type with a channel or
slot having a height equal to 1.5 times stock thickness and a width of 80 mm
to allow for variations in the stock width of 75 mm. The same screws that
hold the die block to the lower shoe fasten the stripper to the top of the die
block.
If, instead of 3.2 mm stock, thin (0.8 mm) stock were
to be blanked, a spring-loaded stripper would firmly hold the
stock down on top of the die block and could, to some extent,
flatten out wrinkles and waves in it.
A spring-loaded stripper should clamp the stock until the punch is
withdrawn from the stock. The pressure that strips the stock from the
punch on the upstroke is difficult to evaluate exactly. A formula frequently
used is
Ps = 2.5 x L x t kgs.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
65/153
65
Where Ps = stripping pressure, in kgs.
L = perimeter of cut, in mm.
t = stock thickness, in mm.
Spring design is beyond the scope of this book; die
spring data are available in the catalogues of spring
manufacturers.
Stock Stops
The pin stop pressed in the die block is the simplest method for
stopping the hand-fed strip. The right-hand edge of the blanked opening ispushed against the pin before descent of the ram and the blanking of the next
blank. The 4-8 mm depth of the stripper slot allows the edge of the blanked
opening to ride over the pin and to engage the right-hand edge of every
successive opening.
The design of various types of stops adapted for manual and automatic
feeding is covered in a preceding discussion.
EVOLUTION OF A PROGRESSIVE BLANKING DIE
Figure 6-8 gives the blanked dimensions of a linkage case cover of cold
rolled steel, stock size 3.2 x 60 x 60 mm. Production is stated to be 200 parts
made at one setup, with the possibility of three or four runs per year.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
66/153
66
Step 1, Part Specification
1. The production is of medium class; therefore a second-class diewill be used.
2. Tolerances required: Except for location of the slots, alldimensions are in fractions. The slot locations, though specified
in decimals, are not very close. Thus a compound die is not
necessary; a two or three-station progressive die will be
adequate.
3. Type of press to be used: Available for this production arepresses of 5-ton, 8-ton, or 10-ton capacity, with a shut height
of 175 or 200 mm.
4. Thickness of material: Specified as 32 mm standard cold rolledsteel.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
67/153
67
Step 2, Scrap-Strip Development
From the production requirements, a single-row strip will suffice. After
several trials, the scrap strip shown in Fig. 6-9 was decided upon. Owing to
the closeness of the holes it was decided to make a four-station die.
The scrap strip would be fed into the first finger stop, and the center hole
would be pierced. The strip would then be moved in to the second finger
stop, and the two holes would then be pierced. At the third stage and third
finger stop, a pilot would locate the strip and the four corner holes would then
be pierced. At the fourth and final stage, a piloted blanking punch would blank
out the finished part.
Step 3, Press Tonnage
It is now in order to determine the amount of pressure needed. Only
the actual blanking in the fourth stage need be calculated, since the work in
the first three stages will be done by stepped punches.
From Table, the shear strength S of cold rolled steel is 40 kgs/mm.
The length L of the blanked perimeter equals 60 x 4 = 240 mm. The depth of
cut (stock thickness t) equals 3.2 mm. From the equation P = S L t
-
7/30/2019 Presses and Equipment for SheetMetal Dies
68/153
68
P = 40 kgs./mm x 240 mm x 3.2 mm = 30,720
kgs. Or 30.7 tons.
This tonnage is greater than can be handled by the available presses.
To lower the pressure, shear is ground on the blanking punch to reduce the
needed pressure by on third. This, ? x 30.7 = 30.7 - 10.2 = 20.5 tons. A
punch press of 25-ton capacity would do, but there is reported available only
a 30-ton press with a 190 mm shut height and a 50 mm stroke. This press is
selected. The bolster plate is found to be 300 mm deep, 140 mm from
centerline of ram to back edge of bolster, and 600 mm wide. Shank diameter
is 64 mm.
Step 4, Calculation of the Die
(a) The die. The perimeter of the cut equals 240 mm and therefore the
thickness of the die must be 25 nm. The width of our scarp-strip opening is 60
mm with 32 mm extra material on each side of the opening, it will be 60 mm
+ 64 mm = 124 mm or 130 mm width. The distance from the left side of the
opening in stage 4 to the edge of the opening in stage 1 equals 3 C + 30 + 6
= 192 + 30 + 6 = 228 mm and plus 62 mm = 290 mm or 296 mm long.
Therefore the die should be 2.5 x 130 x 296 mm long.
(b) The die plate. As a means of filling in between the die and the die shoe,
a die plate of machinery steel is used. To secure the die plate to the die shoe
M12 cap screws and dowels are used. A minimum of twice the size of the cap
screw for the distance from the edge of the die to the edge of the die plate is
needed, which will equal 25 mm. Twice this distance = 50 mm and 50 mm
added to the size of the die will result in a die plate of 25 x 180 x 346 mm.
Figure 6-10 shows the die and die plate fitted together, and with the holes,
which show the sharpening portion and the relief portion.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
69/153
69
Step 5, Calculation of Punches
Good practice requires 10 per cent of the metal thickness to be
removed from the basic dimension of the blanking punch. This same value isused on the die opening, since holes are to be pierced in the blank. The
clearance rule will be applied to the die opening in Stages 1, 2, and 3, and to
the punch in Stage 4 (see fig6-11).
For Stage 4: Blank to be 60 mm square,
Stock thickness = 3.2 mm; 10% = 0.32 mm.
Punch = 60 0.32 = 59.68 mm.
Therefore the die opening will equal 60.01 to 60 mm and
the punch will equal 59.68 to 59.67 mm.
For Stage 2: Slot to be 8 mm wide by 34 mm long.
Die = 8 + 0.32 + 8.32 mm long = 34.32 to 34.33 mm.
Punch will equal 3.99 to 8.00 mm. wide, and 33.99 to
34.00 mm. long.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
70/153
70
The punch and the die opening will have straight sides for at least
3-11 also shows a 3 mm shear for the die at Stage 4 and a 3 mm shear for
the punches of Stage 2, and also the stepped arrangement of the punches for
all stages
Step 6, springs
A solid stripper plate can be used for this job.
Step 7, Piloting
Figures 6-9 and 6-11 illustrate the arrangement for piloting. In this
case it is direct piloting. However, if the part did not have a center hole, and
the slots and other holes were too small, indirect piloting would have to be
provided.
Step 8, Automatic Stops
Finger stops will act as stops when a new scrap strip is being inserted
but, after that, an automatic spring drop stop must be used to halt the scrap
strip. Figures 6-12 illustrate details of the completed drawing of the die.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
71/153
71
Bending, Forming And Drawing Dies
BENDING DIES
Bending is the uniform straining of material, usually flat sheet or strip
metal, around a straight axis, which lies in the neutral plane and normal to
the lengthwise direction of the sheet or strip. Metal flow takes place within the
plastic range of the metal, so that the bend retains a permanent set after
removal of the applied stress. The inner surface of a bend is in compression;
the outer surface is in tension. A pure bending action does not reproduce the
exact shape of the punch and die in the metal; such a reproduction is one of
forming.
Terms used in bending are defined and illustrated in Fig. 7-1. The
neutral axis is the plane area in bent metal where all strains are zero.
Bend Radii: Minimum bend radii vary for the various metals;
generally most annealed metals can be bent to a radius equal to the thickness
of the metal without cracking or weakening.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
72/153
72
Bend Allowances: Since bent metal is longer after bending, its
increased length, generally of concern to the product designer, may also have
to be considered by the die designer if the length tolerance of the bent part is
critical. The length of bent metal may be calculated from the equation
A
B = 2 ( IR + Kt )
(7-1) 360
Where B = bend allowance in mm. (along neutral axis)
A = bend angle in deg.
IR = inside radius of bend in mm.
t = metal thickness in mm.
K = 0.33 when IR is less than 2t and is 0.50 when IR is more
than 2t.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
73/153
73
Bending Methods: Two bending methods are commonly made use of
in press tools. Metal sheet or strip, supported by a V block (Fig. 7-2A), is
forced by a wedge-shaped punch into the block. This method, termed V
bending, produces a bend having an included angle which may be acute,
obtuse, or of 90. Friction between a spring-loaded knurled pin in the vee of a
die and the part will prevent or reduce side creep of the part during its
bending.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
74/153
74
Edge bending (Fig. 7-2B) is cantilever loading of a beam. The bending punch,
step1, forces the metal against the supporting die, step 2 - The bend axis is
parallel to the edge of the die. The work piece is clamped to the die block by a
spring-loaded pad, step3, before the punch contacts the work piece to prevent
its movement during downward travel of the punch.
Bending Pressures: The pressure required for V bending is
K L S t
P = W
(7-2)
Where P = bending force, tons
K = die opening factor: 1.20 for a die opening of 16 times metal
thickness,
1.33 for an opening of 8 times metal thickness
L = length of part, cm.
S = ultimate tensile strength, tons per sq cm.
W = width of V or U die, cm.
-
7/30/2019 Presses and Equipment for SheetMetal Dies
75/153
75
For U bending (channel bending) pressures will be approximately twice
those required for V bending; edge bending requires about one-half those
needed for V bending.
Spring back:
After bending pressure on metal is released, the elastic stresses are also
released, which causes metal movement resulting in a decrease in the bend
angle (as well as an increase in the included angle between the bent
portions). Such a metal movement, termed spring-back, varies in steel
from to 5, depending upon its hardness; phosphor bronze may springback from 10 to 15.
V-bending dies customarily compensate for spring-back with V blocks and
wedge-shaped punches having included angles somewhat less than that
required in the part. The part is bent through a greater angle than that
required but it spri