High Performance Styrene Acrylic Polymerfor 2K Waterproofing Mortars
ORGAL® Hydroflex 57
Important Notice: This information is based on our present state of knowledge and is intended to provide general notes on Organik Kimya Products and their uses. It should not therefore be construed as a guaranteeing specific properties ofthe products described or their suitability for a particular application. Any existing industrial property rights must be observed. The quality of our products is guaranteed under our General Conditions of Sale.
ORGAL® Hydroflex 57Styrene Acrylic Copolymer for Flexible Cementitious Systems
APEO FreeBroad Formulation Capability
Excellent Water & Alkali ResistanceExcellent Crack Bridging PerformanceHigh Flexibility with Excellent Recovery
Orgal® Hydroflex 57 is an APEO, ammonia and formaldehyde free, low Tg, styrene acrylic copolymer emulsion that forms a clear, elastic and slightly tacky film when
dried above 0°C. It is highly compatible with cement mixtures.Orgal® Hydroflex 57 provides better mortar rheology, reduces crack formation of
mortars and after curing, it improves adhesion, flexibility, water resistance and crack bridging ability. Orgal® Hydroflex 57 can be used in drinking water contact systems.
Appearance
Solid Content (%+_1)
Viscosity RVT 3/60
pH
Density (25°C, g/cm3) ± 0.01
MFFT (°C)
Tg (°C)
Storage Stability
White Emulsion
57
700 cps max.
7.0 - 9.0
1.04
< 0
-10
Protect from freezing
2K Waterproofing Mortar Formulation
CEM II 42,5R100-800 µm Silica SandTylose MH 6000 YP4ORP® 7365 HPFloset AD3Total
*Powder: Liquid ratio is 2:1 in weight
Component Key FunctionUsage Amount (%)BinderFillerWater Retention AgentPerformance ModifierPlasticizer
30.0066.70
0.203.000.10
100.00
Powder Component
Orgal® Hydroflex 57WaterAgitan 230Acticide MVTotal
Component Key FunctionUsage Amount (%)Binder
DefoamerBiocide
Supplier
Shin-EtsuOrganik KimyaSNF
SupplierOrganik Kimya
Münzing ChemieThor
80.0019.70
0.200.10
100.00
Liquid Component
Overall Performance
Orgal® Hydroflex 57 has the best overall performance.
Crack Bridging Ability
Crack Bridging Test - According to EN 14891
Competitor ACompetitor BOrgal® Hydroflex 57
CrackBridging (mm) @+23°C
1.781.821.86
@-5°C1.261.211.19
@-20°C0.910.860.96
Water Impermeability
Water Impermeabiliy Test - According to EN 14891
Water Impermeability(Positive, 1.5 bars, 7 days)
Competitor ACompetitor BOrgal® Hydroflex 57
No leakageLeakage on 5th dayNo leakage
Crack Formation Resistance
Competitor ACompetitor BOrgal® Hydroflex 57
Crack Formation210
0: No Crack 5: Worst
Crack Formation Test in 2K Waterproofing Formulation
Competitor ACompetitor BOrgal Hydroflex 57
Tensile Elongation
Competitor ACompetitor BOrgal® Hydroflex 57
MaximumTensile Strength
(N/mm²)
1.020.890.97
Elongationat Break (%)
206.35202.12219.56
ElasticModulus(N/mm²)
3.802.793.68
Adhesion on Concrete
Competitor ACompetitor BOrgal® Hydroflex 57
Adhesion on Concrete(EN 1348 N/mm²)
AfterHeat
Aging
1.311.281.31
AfterWater
Immersion
0.871.121.15
AfterFreeze Thaw
Cycles
1.461.511.54
0
1
2
3
4
5
Tensile Elongation Test - According to EN 527
Workability
Flexibility
Crack BridgingWater Resistance
Adhesion
High Performance Styrene Acrylic Polymerfor 2K Waterproofing Mortars
Important Notice: This information is based on our present state of knowledge and is intended to provide general notes on Organik Kimya Products and their uses. It should not therefore be construed as a guaranteeing specific properties ofthe products described or their suitability for a particular application. Any existing industrial property rights must be observed. The quality of our products is guaranteed under our General Conditions of Sale.
ORGAL® Hydroflex 57Styrene Acrylic Copolymer for Flexible Cementitious Systems
APEO FreeBroad Formulation Capability
Excellent Water & Alkali ResistanceExcellent Crack Bridging PerformanceHigh Flexibility with Excellent Recovery
Orgal® Hydroflex 57 is an APEO, ammonia and formaldehyde free, low Tg, styrene acrylic copolymer emulsion that forms a clear, elastic and slightly tacky film when
dried above 0°C. It is highly compatible with cement mixtures.Orgal® Hydroflex 57 provides better mortar rheology, reduces crack formation of
mortars and after curing, it improves adhesion, flexibility, water resistance and crack bridging ability. Orgal® Hydroflex 57 can be used in drinking water contact systems.
Appearance
Solid Content (%+_1)
Viscosity RVT 3/60
pH
Density (25°C, g/cm3) ± 0.01
MFFT (°C)
Tg (°C)
Storage Stability
White Emulsion
57
700 cps max.
7.0 - 9.0
1.04
< 0
-10
Protect from freezing
ORGAL® Hydroflex 57
Overall Performance
Orgal® Hydroflex 57 has the best overall performance.
Crack Bridging Ability
Crack Bridging Test - According to EN 14891
Competitor ACompetitor BOrgal® Hydroflex 57
CrackBridging (mm) @+23°C
1.781.821.86
@-5°C1.261.211.19
@-20°C0.910.860.96
Water Impermeability
Water Impermeabiliy Test - According to EN 14891
Water Impermeability(Positive, 1.5 bars, 7 days)
Competitor ACompetitor BOrgal® Hydroflex 57
No leakageLeakage on 5th dayNo leakage
Crack Formation Resistance
Competitor ACompetitor BOrgal® Hydroflex 57
Crack Formation210
0: No Crack 5: Worst
Crack Formation Test in 2K Waterproofing Formulation
Competitor ACompetitor BOrgal Hydroflex 57
2K Waterproofing Mortar Formulation
CEM II 42,5R100-800 µm Silica SandTylose MH 6000 YP4ORP® 7365 HPFloset AD3Total
*Powder: Liquid ratio is 2:1 in weight
Component Key FunctionUsage Amount (%)BinderFillerWater Retention AgentPerformance ModifierPlasticizer
30.0066.70
0.203.000.10
100.00
Powder Component
Orgal® Hydroflex 57WaterAgitan 230Acticide MVTotal
Component Key FunctionUsage Amount (%)Binder
DefoamerBiocide
Supplier
Shin-EtsuOrganik KimyaSNF
SupplierOrganik Kimya
Münzing ChemieThor
80.0019.70
0.200.10
100.00
Liquid Component
Tensile Elongation
Competitor ACompetitor BOrgal® Hydroflex 57
MaximumTensile Strength
(N/mm²)
1.020.890.97
Elongationat Break (%)
206.35202.12219.56
ElasticModulus(N/mm²)
3.802.793.68
Adhesion on Concrete
Competitor ACompetitor BOrgal® Hydroflex 57
Adhesion on Concrete(EN 1348 N/mm²)
AfterHeat
Aging
1.311.281.31
AfterWater
Immersion
0.871.121.15
AfterFreeze Thaw
Cycles
1.461.511.54
0
1
2
3
4
5
Tensile Elongation Test - According to EN 527
Workability
Flexibility
Crack BridgingWater Resistance
Adhesion