NA62 SILICON PIXELS DETECTOR
VIBRATIONS MEASUREMENT1Vittore Carassiti - INFN FENA62 GTK Meeting
08.02.2011, CERN
2Vittore Carassiti - INFN FENA62 GTK Meeting 08.02.2011, CERN
MEASURING INSTRUMENT
MTN/VM120 VIBRATION METER
Constant current type accelerometer (10 mV/g sensitivity)
RMS and peak to peak detection of acceleration (g) , velocity (mm/s) and displacement (μm)
Reduction of the wide band noise by a low pass filter; filter selection : 1-5-10 KHz
3Vittore Carassiti - INFN FENA62 GTK Meeting 08.02.2011, CERN
THE DETECTOR CONSTRAINTS
THREE POINTS BY 50 μm THICKNESS KAPTON FOIL
4Vittore Carassiti - INFN FENA62 GTK Meeting 08.02.2011, CERN
MEASURED VIBRATIONS
Tested parts Deflection(μm)RMS
Velocity(mm/s)
RMS
Acceleration (g)
RMS
Filter(KHz)
Room floor 20 - - 1
Test bench 20 - - 1
Supports 20 - - 1
Vessel no flow
20 - - 1
VesselFrom 1 to 8 m^3/h
20(no vibrations
inside)
6,4 0,05 1-5-10
5Vittore Carassiti - INFN FENA62 GTK Meeting 08.02.2011, CERN
PROTECTIVE RUBBER TEST
TWO TYPES OF RUBBER HAVE BEEN TESTED IN LIQUID NITROGEN (3 DAYS) :
3140 RTV COATING (SILICONE RUBBER)
186 SILICONE ELASTOMETER (BICOMPONENT)
NO CRACKS ; NO LOSS OF ELASTICITY
6Vittore Carassiti - INFN FENA62 GTK Meeting 08.02.2011, CERN
NEXT STEPS
MAKING A BOARD FOR THE WIRE BONDS TEST
FRONT BACK
7Vittore Carassiti - INFN FENA62 GTK Meeting 08.02.2011, CERN
NEXT STEPS
OPTIMIZATION BY SIMULATIONS OF THE NITROGEN GUIDE CHANNELS
TEST AIMING TO VERIFY THE EFFECTIVE TEMPERATURE DISTRIBUTION ON THE DETECTOR
DESIGN OF THE NITROGEN SUPPLY SYSTEM