323
AdvancesinProductionEngineering&Management ISSN1854‐6250
Volume14|Number3|September2019|pp323–332 Journalhome:apem‐journal.org
https://doi.org/10.14743/apem2019.3.330 Originalscientificpaper
Effect of aluminium and chromium powder mixed dielectric fluid on electrical discharge machining effectiveness
Modi, M.a,*, Agarwal, G.b
aDepartment of Mechanical Engineering, Acropolis Institute of Technology and Research, Indore, Madhya Pradesh, India
bDepartment of Mechanical Engineering, Malaviya National Institute of Technology, Jaipur, Rajasthan, India
A B S T R A C T A R T I C L E I N F O
Thisarticlestudiedtheimpactsofusingdifferentpowdersontheproductivityof electro discharge machining (EDM) of Nimonic 8OA alloy. The powdersused for experiments are chromium (Cr) and aluminium (Al), though thesepowders are in contrasts in their thermo‐physical characteristics.With themixingofthesepowders indielectric fluid,effectonsurfaceroughness(SR),materialremovalrate(MRR),andmechanismofthemachiningprocesshavebeen studied in this researchwork.On going through the results of experi‐ments, itwasobserved that evenvolumetricproportionofpowders, size ofmolecules, its density, electric resistance, andheat conductivityof additiveswerevitalparameters thataltogether influenced theproductivityofpowdermixed‐electrodischargemachining(PMEDM)process.Withadditionofprop‐erratioofpowdersindielectricfluid,itenhancedthematerialremovalrate,and consequently, reduced the surface roughness.Under a similarmoleculevolumetricproportiontests,theminutessuspendedmoleculesizeofpowderprompted the largest material removal rate and consequently, the surfaceroughness increased.Conclusion is thataddingchromiumpowder improvesto the highest material removal rate, but poor surface finish while addingaluminiumpowderhasthereverseeffects.
©2019CPE,UniversityofMaribor.Allrightsreserved.
Keywords:Powdermixed‐electrodischargemachining(PMEDM);Aluminiumpowder;Chromiumpowder;Dielectricfluid;Productivity;Materialremovalrate(MRR);Surfaceroughness;Nimonic80Aalloy
*Correspondingauthor:[email protected](Modi,M.)
Articlehistory:Received12April2019Revised13September2019Accepted15September2019
1. Introduction
Electricaldischargemachining(EDM)hasbeenanessentialprocedureforthedieandtoolmak‐ingenterprisesforalongtime.Thismachiningprocedureisfindinggrowingutilizationinindus‐tries due to the feasibility of machining geometrically intricate shapes irrespective of thehardnessofmaterialsthatareverytoughbyutilizingthetraditionalmachiningprocedures[1].In EDM,managed distinct electrical sparks between the electrode and thework‐piece wouldproducearcing,i.e.concentrationofsparkwhenanexcessiveamountofscatteredtinymaterialremainsintheinter‐electrodegapinlightoftheinabilitytoclearscatteredtinymaterial.Arcingoccurswhenasuccessionofsparksstrikesmorethanonceonasimilarspot.
This,intheend,causesharmtothecathodeoftheapparatusandthework‐pieceifthecon‐trollerofthemachinedoesnotstopitquickly.TheEDMprocedureinthismannerendsupun‐steadyandineffective.ToenhancetheeffectivenessofEDmachining,itisnecessarytoupgradeprocesssteadiness.Thispresentlyremainsamajortoughtask.Kiyaketal.[2]conductedexper‐imentalworkonEDMwithAISIP20toolsteel.Theyexaminedtheimpactofprocessfactorsonsurface roughness (SR) in EDM and observed that littler values of ampere‐current, pulse‐on‐duration and proportionately greater value of pulse‐off‐duration produced a descent surface
Modi, Agarwal
324 Advances in Production Engineering & Management 14(3) 2019
finish (SF).Hasçalıketal. [3] did experimentalwork onEDMwithTi6Al4V anddifferent toolmaterials.TheyinvestigatedthattheMRR,SR,electrodewear,andaveragewhitelayerthickness(AWLT)ascendwith increment inampere‐currentandpulse‐on‐duration.Theyalsoexaminedthesurface‐integrityofworkwithEDMprocessfactors.Fondaetal.[4]conductedexperimentalworkonEDMwithTi6AL4Vwork‐pieceandreportedtheimpactofpropertiesofthematerialonEDMefficiency.Chowetal.[5]didexperimentsonmicro‐slitelectricaldischargemachining(MSEDM)with Ti6Al4Vworkpiece. They examined the impact of silicon carbide powder blendedwithdielectricfluid(DF)onMRR,SR,andgapsize(GS).Chowetal.[6]conductedexperimentsonEDMwithTi6Al4V.Theyobserved that thesilicon‐carbideandaluminiumpowderblendedwithkeroseneisliableforincreasingthegap‐sizeamongtheelectrodes.ThedevelopedGSesca‐latesthedebrisremovalrate(DRR),andmaterialremovaldepth(MRD).TheyalsoexaminedtheimpactofaddingthepowdersmoleculeindielectricfluidonMRDandontheSR.Zhaoetal.[7]didexperimentalworkonEDMwithsteelasaworkpieceandredcopperasatoolmaterial.TheydescribedthemechanismofEDM,andpowdermixedelectricaldischargemachining(PMEDM)process and found thatPMEDMprocessupgrades themachiningefficiencyandSF in contrastwithEDMprocessbypickingthesuitablefactorsset.Pecasetal.[8]performedtheexperimentsonPMEDMwithandwithoutsiliconpowderblendedDF.Theyreportedthatthemixingofpow‐der‐molecule inDFaltersfewprocessparametersandmakesthecircumstancestoaccomplishthepeaksurfacequalityinvastregions.Pecasetal.[9]conductedexperimentsonPMEDMwithAISI H13. They explained that silicon powder blended DF enhances the process polishing‐effectiveness and reduces thewhite layer thickness (WLT), depth, anddiameter of the cavity.Theyreportedthatexact‐controloftheflushing‐rateandvolumetricproportionofpowderistherequirement for achieving theadvancement in the shiningabilityofprocess.Kozaketal. [10]conductedexperimentsonEDMwithtoolsteel.Experimentswereconductedwithkeroseneandwithpowderblendeddemonizedwater.Theynarratedabout the impactofprocess factorsonMRRandSRwithvariousvolumetricproportionsofpowders indielectric liquids.Kansaletal.[11]narratedthatDFwithpowderinPMEDMprocessreducesthedielectricinsulating‐strengthandenhances the gap among the tool andwork.They also found that theadditionofpowderenhancestheprocess‐outcomes.Kansaletal.[12]didexperimentalworkonPMEDMofAISID2die‐steelwith silicon powder blendedDF. They found that the chosen process factors have aremarkableimpactonMR.Pecasetal.[13]carriedouttheexperimentsonEDMwithAISIH13workandcopperasanelectrodewithandwithoutsiliconpowderblendedDF.Theoutcomesoftheexperimentsaccomplishedconfirmastraightconnectionamongtheelectrodeareaandthesurface quality measures and also a noteworthy execution enhancement when the powderblendedDFisutilized.Modietal.[14]describedthedetailofEDMandPMEDMprocessandde‐veloped the mathematical models of process responses through dimensional analysis (DA)method.Modietal.[15]didtheexperimentsonEDDSGwithTi6AL4V.TheyreportedthatGrey‐TMmethodologyenhancesmachiningeffectiveness.
Marashi etal. [16] reported the intensive review of the impact of powder addition on themechanism of EDM process, the most influential powder parameters, future patterns in thistechnology,andarelativesurveyofpowdermaterialsisadditionallyexhibitedinthisarticletofacilitateadeeperinsightintopowderselectionparametersforfutureinvestigations.Theyalsoportrayed thatmain factorswhichmust be considered in PMEDMare powder size, type, andconcentration. At last in this paper, PMEDM research patterns, gaps, findings, and industrialtroublesarediscussedextensively.Kalamanetal.[17]presentedthestudyabouttheintroduc‐tionandsurveyoftheresearchworkinPMEDM.Theinvestigationsconcerningmachiningeffi‐ciency, surface integrity, andgenerationof functional surfacesarepresentedanddiscussed inthe lightofcurrentresearchpatterns.Attemptsmade to improvebiocompatiblesurfaceswiththe utilization of the process additionally included clarifying the future patterns in PMEDM.Daneshmandetal.[18]conductedtheexperimentsonEDMwithCK45steeltoexaminetheim‐pacts of current, voltage, andpulse frequencyonSR. In this testwork, kerosene is utilized asdielectric fluid and copper as an electrode. Design of experimentswith non‐linear regressionmodelwasutilized to estimate theprocess response.Rajuetal. [19] carriedout an extensiveliteraturestudytoprovideatotaldescriptiononμ‐EDMprocess, itsnecessities,executionand
Effect of aluminium and chromium powder mixed dielectric fluid on electrical discharge machining effectiveness
Advances in Production Engineering & Management 14(3) 2019 325
applications.The experiment frame‐ups and its subsystems, trial studies andoptimizing tech‐niques,createdmicrofeatureanddifferentapplicationsareadditionallydescribedinthispaper.
Inspiteofthefavorableoutcomes,theEDMprocedurewithaddedsubstancesisnotyetuti‐lized broadly in industry. One of the essential reasons is that numerous key factors of thePMEDMprocedure,incorporatingthemechanismofmachiningwithdifferentaddedsubstances,which are not surely known. The complicated nature of this procedure, particularly from theimpacts of the thermo‐physical characteristic of added powders, subsequently, justifies theextrainvestigation.TheobjectiveofthearticleistomakeapreciseinvestigationoftheimpactsofpowderpropertiesinDFontheeffectivenessofEDMachiningwiththeendgoaltoimprovethe applicability of the procedure in the industry. The release‐transivity, particularly, deter‐minesthefrequencyofsparkingthatcontrolsthewholeMRR,thoughthepowder‐particlesstrik‐ingimpacthasaninsignificantcuttingimpactprovidingprimarilytotheenhancementoftheSF.
2. Materials, methods and experimental set‐up
ThispaperusesnomenclaturegiveninAppendixA.Nimonic 80A nickel‐chromium alloy is widely utilized in several industries due to its re‐
sistance against to corrosion and high strength applications because of excellent mechanicalproperties at eminent temperature. PMEDM is an efficient process formachining hard‐to‐cutmateriallikeNimonic80A.ThecompositionofNimonic80Ais19.82%Cr,2.59%Ti,1.57%Al,2.63%Fe,andbalance%Ni.ThePMEDMframe‐upcontainstheservoarrangementofZNCEDMmachine(ZNC50×30,diesinkingtype,EMTltd.,India)isutilizedtokeepupthepredeterminedseparationamongthetoolandwork,whosewidthrelyonthegapvoltage.Totaltestswerecon‐ducted on this frame‐upwithNimonic 80A as awork‐piece andbronze as an anode. For thisreason,an independent fittinghasbeenplannedandcreatedwithin theEDMtank;adifferentacrylictankhavingthecapacityof36litersofDFwassettledontheEDMtablewithbolts.Thedifferent stirrer and pump arrangement are settled in the acrylic tank. The stirrer and pumparrangementisutilizedforpropermixingandcirculationofpowderblendeddielectricliquidintheinter‐electrodegap.Theschematicdiagramofthisframe‐upisdisplayedinFig.1.
Table 1 displays the EDM process factors. The thermal characteristics of aluminim, andchromiumpowdermoleculesaredepicted inTable2.Fig.2(a)displays themechanismofma‐chininginPMEDMprocessandtheoccurrenceofseriesdischargeinPMEDMprocessisdepictedinFig.2(b).
Fig.1TheschematicdiagramofPMEDMframe‐up
Modi, Agarwal
326 Advances in Production Engineering & Management 14(3) 2019
(a) (b)
Fig.2(a)MechanismofmachininginPMEDMprocesses,(b)Occurrenceofseriesdischarge
Table1EDMprocessfactorsElectrode(+) Bronze(ϕ =10mm)Workpiece(‐) Nimonic80A(ϕ =20mm)Timeofmachining HalfhourDielectricfluid KeroseneFlowrateofdielectricfluid 4l/minPowder Aluminium,ChromiumPowdersizes 0.080‐0.090μmand15‐20μmVolumetricproportionofpowdermolecules(cm3/l) 0.30,0.60,1.20CurrentI(A) 2.0,5.0Ton(μs) 5,30,80Dutycycle 0.67
Table2Powdersproperties
PowderDensityρ,(kg/cm3)
Thermalconductivityλ,W/(cm·K)
Electricalresistivityρ,(Ω·cm)
Melting‐point‐temperatureTm,
(K)
SpecificheatC,
Cal/(kg·K)Chromium 7.1610‐3 0.67 2.60 2148 0.110103Aluminium 2.7010‐3 2.38 2.45 933 0.215103
Intheseexperiments,thelevelsofinputparametershavebeenselectedaftertheconductionofpilot experiments. TheMRR,GS, and SR have beenmeasured as the responses in this experi‐mental work.We conducted the various experiments on PMEDM setup andmade the graphsbetween the input variables and the output responses. From these graph, conclusions weredrawn.
3. Results and discussion
3.1 Impacts of powder properties on gap size
Fig.3displaystheeffectofmixingofAlandCrpowderparticlesintheDFontheGS.Itwasob‐servedthatthegapamongtheanodeandcathodewithAlpowderismarginallymorewhencon‐trastedwiththeCrpowderblendeddielectricliquidwasfoundattributabletoitslittlerelectri‐cal‐resistivity.ThislittlestGSwouldbeaccountableforextremegasblastpressurewithCrpow‐der.Furthermore,theCrpowderdensityisgreaterthantheAlpowderdensity,resultinginarc‐ing rather sparking. Consequently, SR is higher with Cr when contrasted with Al powder. AlpowderdeliveredthebetterSFtrailedbyCrpowder.
Effect of aluminium and chromium powder mixed dielectric fluid on electrical discharge machining effectiveness
Advances in Production Engineering & Management 14(3) 2019 327
Fig.3TheimpactofmixingofAl,andCrpowdersparticleonthegapsize(I=5A,DC=0.67,Volumetricproportion=0.60cm3/l)
3.2 Impacts of powder particle size on material removal rate
Fig.4demonstratestheimpactoftwoAlpowder‐moleculesizesatdifferentvolumetricpropor‐tionsonMRR.Itwasseenthattheappropriatemixingofpowder‐particlesimprovesthemachin‐ingproductivitybyadditionalsettlingoftheelectric‐release.Theenhancementinprocessdura‐bilityoccurredduetothefairlylargerGSininter‐electrodegap.Theoutcomesadditionallydis‐closedthattheriseinthesizeofthepowderparticleresultedinadecreaseintheenhancementoftheMRR.Thiscanbeascribedtobothlesserelectricalpowerdensityandamoreprobabilityofanomalousrelease.
Moreover,whenthesizeofthemoleculewasmorethanthespark‐gap(about06‐55μm),theefficiency of machining evidently decayed. The MRR outcomes for the minimal size of themolecule (80‐90nm)atdifferentvolumetricproportionsofpowderparticleswereevenmorethanthosewith(15‐20μm)moleculesizeofpowderparticles.Thisishappenedduetotheexist‐enceoflesssparkgapamongtheelectrodes.Forthecurrentat5A,andvolumetricproportionofmoleculemorethan0.60cm3/l,demonstratedanotablefallingtrendinMRR.Thiswasbecauseofthejoinedimpactsoflowerelectrical‐density,thelesserstrikingofpowderparticles,unevenlydistributionofparticles,andverylowgrowthintherelease‐transitivity.
Fig.4TheimpactofparticlesizeandvolumetricproportionofaluminiumpowdersonMRR(Ton=30μs,DC=0.67)
Fig.5TheimpactofTonandvolumetricproportionof80‐90nmaluminiumpowdersmoleculeonMRR(DC=0.67)
Modi, Agarwal
328 Advances in Production Engineering & Management 14(3) 2019
Fig.6TheimpactofTonandvolumetricproportionof15‐20μmaluminiumpowdersmoleculeonMRR(DC=0.67)
3.3 Impacts of molecule concentration on material removal rate
Fig.4additionallydemonstratesthatMRRwasaffectedbythevolumetricproportionofalumini‐umpowders.ThereasonabledistinctioninMRRisobservedforthecurrentatahigherlevelbe‐causeof thegenerationofmoresparkenergyasdisplayed inFigs.4,5, and6. Itwasalsoob‐servedfromFig.4thatthehighestMRRisobtainedat5Acurrent,0.6cm3/lofAlpowders,Ton=30μs,andmoleculessizesunder95nm.Thisdemonstratesthatanidealsparkgapwasacquiredat this setting of the volumetric proportion of powder andTon, which delivered the optimumfactorssettingofpowerdensity,strikingofmoleculeandrelease‐transitivityintheEDMproce‐dure.
Figs.5and6demonstratethattheimpactsofthevolumetricproportionofmoleculeof80‐90nmand15‐20μmaluminiumpowdersparticlefluctuatedalongwiththeTon.AtthelesserTonof5μs,0.6cm3/lprovidethegoodMRR,trailedby1.2cm3/l,andwith0.30cm3/lbeingtheinferior.Though,itmaybefoundinFig.6thatatthe5.0Acurrent,whentheTonwasraisedto30μs,theimpactsbeguntoalterwith15‐20μmaluminiumpowdersparticle.Thevolumetricconcentra‐tionof0.6cm3/lstilldeliveredthegoodMRR,however,0.30cm3/lwassuperiorascomparedto1.2cm3/l.Thispatternproceededwith therise in theTon.Whenthe timewasraised to80μs,0.30 cm3/l exceed 1.2 cm3/l inMRR outcomes for both 80‐90 nm, and 15‐20 μm aluminiumpowders particle. Thiswas because of extrawarming impacts due to the rising theTon.Moreevacuatedmoltenmaterialswereconsequentlyproducedthatinthelongrundecreasedtheper‐formanceofthevolumetricproportionof1.2cm3/linimprovingtheproceduresteadiness.
Thepurposebehindtheprimaryoutcomeswith15‐20μmaluminiumpowdersparticlewasbelievedtobebecauseofthebiggermoleculesizeanditsimpacts.Itdemonstratedthatthebig‐germoleculesizeofaddedsubstancesamongthesparkgapwasincreasinglydelicatetoevacu‐atethetinyworkmaterialsproduction.
3.4 Impacts of molecule characteristics on material removal rate
Fig.7demonstratestheimpactsoftwovolumetricproportionsofAl,andCrpowdersparticleontheMRR.ThetestoutcomesdemonstratedthatchromiumgeneratedthebestMRR,andalumini‐umthe leastwhen thevolumetricproportionofpowderwas<1.2cm3/land I=5.0A.At thepoint,whentheampere‐currentwasat2.0A,thedistinctioninMRR turnedouttobelittlebe‐causeofthelessinputofenergy.Fig.3demonstratesthatthesparkgapforchromiumislesserthanthat foraluminiumasclarifiedalready. Inprinciple, therewasasomewhathigherpowerdensityandgasexplosionpressureforchromium.
Moreover, chromium powder density is double than the aluminium powder, ensuing in apowerfulpowder‐particlecollision.Additionally, theheatconductivityofaluminiumpowderisabout3timesbiggerascomparedtochromiumpowder,whichshowedthatmoreenergyistak‐enoutbythealuminiumpowderblendeddielectricliquid.Subsequently,CrcreatedthebiggestMRR.
Effect of aluminium and chromium powder mixed dielectric fluid on electrical discharge machining effectiveness
Advances in Production Engineering & Management 14(3) 2019 329
Fig.7Theimpactofampere‐currentandvolumetricproportionof15‐20μmaluminiumandchromiumpowdersmoleculeonMRR(DC=0.67,Ton=30μs)
3.5 Effects of particle size on surface roughness
Fig.8demonstrates the impactsof twoaluminiumandchromiumpowdermoleculesizeswithdifferentvolumetricproportionsonSR.ThebestsortsofpowdersforupgradingthesmoothnessofthesurfaceareAl,Cretc.Aluminiumpowder‐particlecreatesagoodsurfaceforallthemole‐culeproportions.Itispredominantlybecauseofthejoinedimpactsofsmallelectrical‐resistivity,adequatethermal‐conductivity,andless‐densityofaluminium.Lesselectrical‐resistivitymakesahighsparkgap,goodthermal‐conductivityremovesmoreheat,andless‐densityavoidthearcingamongtheelectrodes.Theseimpactsjointlyleadtolessdensityofelectricalsparkbringingthelow gas blast, in thisway just shallowholes are created on themachined surface. Al powderproducedthebestsurfacefinishfollowedbytheCrpowder.Thebestsurfacefinishisobtainedatthevolumetricproportionof1.2cm3/lofaluminiumpowderwith15‐20μmparticlesize.
Fig.8Theimpactofparticle‐sizeandvolumetricproportionofAlpowdersmoleculeonSR(DC=0.67,Ton=30μs)
3.6 Effects of particle concentration on surface roughness
AsappearedinFig.9,itwasseenthatatthe5Acurrent,thealuminiumpowdervolumetricpro‐portionofmoleculehasbuiltamajoreffectinSRduetothebiggerMR. Itwasnoticedthatthebiggestmoleculevolumetricproportionof1.20cm3/lprovidetheworstSFatTon=80μsdueto
Fig.9TheimpactofTonandvolumetricproportionof80‐90nmaluminiumpowdersmoleculeonSR(DC=0.67,I=5A)
Modi, Agarwal
330 Advances in Production Engineering & Management 14(3) 2019
itshighestreleasetransitivity.ItisalsonotedfromFig.9thatthevolumetricproportionofpow‐dermoleculewasnotthemainparametercontrollingtheSRintheEDMprocedure.Alternately,Tonseemedbyallaccount,tobethemostvitalparameter.
3.7 Impacts of molecule characteristics on surface roughness
Fig.10demonstratestheimpactofsevenmoleculevolumetricproportionlevelsofaluminium,andchromiumpowder‐particlesontheSR.ItwasseenthataluminiumpowderproducedthegoodSFthanthechromiumpowderparticleforboththe2Aaswellasat5Acurrent.ThishappensbecausetheevacuationofmoremoltenmaterialfromworksurfaceinpresenceofCrpowderascomparedtothepresenceofAlpowderinDF.Subsequently,CrgeneratedthebiggestSR.
Moreover, chromium powder density is double than the aluminium powder, ensuing in apowerful powder‐particle collision and result in arcing. Additionally, the heat conductivity ofaluminiumpowder is about3 timesbigger as compared to chromiumpowder,which showedthatmoreenergyistakenoutbythealuminiumpowderblendeddielectricliquid.
Fig.10Theimpactofampere‐currentandvolumetricproportionof15‐20μmaluminium,andchromiumpowdersmoleculeonSR(DC=0.67,andTon=30μs)
4. Conclusions
Inviewofthetestoutcomes,thefollowingconclusionsaredrawn:
Themoleculesize,volumetricproportionofpowders,itsdensity,electrical‐resistivity,andthermal‐conductivityarethesignificantattributesofpowdersinfluencingperformanceofEDMachiningprocess.
DuetotheinclusionofpowderparticleinDF,thegapforsparkwasincreased. Sparkgapvarieswiththemixingofpowdersofvarioussizesinthedielectricfluid.Spark
gap increaseswith increasingsizeofpowdermolecules.Theminimumrise in thegap isproducedwithasizeof80‐90nmpowdersandwith15‐20μmgeneratingthehighestgap.
HighestMRRwasobservedwithpowdersofsize80‐90nmandwith15‐20μmgeneratingthesmallest.FortheSF,theoppositepatternisnoticed.
Highersparkgapwasobservedbyaddingaluminiumpowderparticlesfollowedbyusingchromiumpowder.
BestMRRwas observedwith adding chromium followedby aluminiumpowder. ForSF,theoppositepatternwasnoticed.
Thevolumetricproportiononmixing thepowderwith thedielectric fluid in theratioof0.6cm3/lgivesbestMRRoutcomes.
With2A,and5Acurrent,resultsarequitehigherthantheimpactofmoleculesize,volu‐metricproportionofpowder,andotherfactors.
TheMRR and SR varywith different combination ofmolecule sizes, volumetric propor‐tionsofAl,andCrpowdersindielectricfluidinPMEDMprocess.
Experimentscanbeconductedbyusingdifferentcombinationofmaterials,dielectricflu‐ids,andalsovariouspowderstogetdifferentfindingsinthePMEDMprocess.
Effect of aluminium and chromium powder mixed dielectric fluid on electrical discharge machining effectiveness
References [1] Abu Zeid, O.A. (1997). On the effect of electrodischarge machining parameters on the fatigue life of AISI D6 tool
steel, Journal of Materials Processing Technology, Vol. 68, No. 1, 27-32, doi: 10.1016/S0924-0136(96)02523-X. [2] Kiyak, M., Çakır, O. (2007). Examination of machining parameters on surface roughness in EDM of tool steel,
Journal of Materials Processing Technology, Vol. 191, No. 1-3, 141-144, doi: 10.1016/j.jmatprotec.2007.03.008. [3] Hasçalık, A., Çaydaş¸ U. (2007). Electrical discharge machining of titanium alloy (Ti–6Al–4V), Applied Surface
Science, Vol. 253, No. 22, 9007-9016, doi: 10.1016/j.apsusc.2007.05.031. [4] Fonda, P., Wang, Z., Yamazaki, K., Akutsu, Y. (2008). A fundamental study on Ti–6Al–4V’s thermal and electrical
properties and their relation to EDM productivity, Journal of Materials Processing Technology, Vol. 202, No. 1-3, 583-589, doi: 10.1016/j.jmatprotec.2007.09.060.
[5] Chow, H.-M., Yang, L.-D., Lin, C.-T., Chen, Y.-F. (2008). The use of SiC powder in water as dielectric for micro-slit EDM machining, Journal of Materials Processing Technology, Vol. 195, No. 1-3, 160-170, doi: 10.1016/ j.jmatprotec.2007.04.130.
[6] Chow, H.-M., Yan, B.-H., Huang, F.-Y., Hung, J.-C. (2000). Study of added powder in kerosene for the micro-slit machining of titanium alloy using electro-discharge machining, Journal of Materials Processing Technology, Vol. 101, No. 1-3, 95-103, doi: 10.1016/S0924-0136(99)00458-6.
[7] Zhao, W.S., Meng, Q.G., Wang, Z.L. (2002). The application of research on powder mixed EDM in rough machining, Journal of Materials Processing Technology, Vol. 129, No. 1-3, 30-33, doi: 10.1016/S0924-0136(02)00570-8.
[8] Peças P., Henriques, E. (2003). Influence of silicon powder-mixed dielectric on conventional electrical discharge machining, International Journal of Machine Tools and Manufacture, Vol. 43, No. 14, 1465-1471, doi: 10.1016/ S0890-6955(03)00169-X.
[9] Peças, P., Henriques, E. (2008). Effect of the powder concentration and dielectric flow in the surface morphology in electrical discharge machining with powder-mixed dielectric (PMD-EDM), International Journal of Advanced Manufacturing Technology, Vol. 37, No. 11-12, 1120-1132, doi: 10.1007/s00170-007-1061-5.
[10] Kozak, J., Rozenek, M., Dabrowski, L. (2003). Study of electrical discharge machining using powder-suspended working media, Proceedings of the Institution of Mechanical Engineers, Part B: Journal of Engineering Manufac-ture, Vol. 217, No. 11, 1597-1602, doi: 10.1243/095440503771909971.
[11] Kansal, H.K., Singh, S., Kumar, P. (2007). Technology and research developments in powder mixed electric dis-charge machining (PMEDM), Journal of Materials Processing Technology, Vol. 184, No. 1-3, 32-41, doi: 10.1016/ j.jmatprotec.2006.10.046.
[12] Kansal, H.K., Singh, S., Kumar, P. (2007). Effect of silicon powder mixed EDM on machining rate of AISI D2 die steel, Journal of Manufacturing Processes, Vol. 9, No. 1, 13-22. doi: 10.1016/S1526-6125(07)70104-4.
[13] Peças, P., Henriques, E. (2008). Electrical discharge machining using simple and powder-mixed dielectric: The effect of the electrode area in the surface roughness and topography, Journal of Materials Processing Technology, Vol. 200, No. 1-3, 250-258, doi: 10.1016/j.jmatprotec.2007.09.051.
[14] Modi. M., Jha, S. (2009). Modeling and analysis of powder mixed electric discharge machining, International Journal of Mechanical Engineering, Vol. 2, 219-223.
[15] Modi, M., Agarwal, G. (2013). Optimization of electro-discharge diamond surface grinding process parameters with multiple performance characteristics of Ti-6Al-4V using grey-Taguchi approach, Advanced Materials Re-search, Vol. 622-623, 14-18, doi: 10.4028/www.scientific.net/AMR.622-623.14.
[16] Marashi, H., Jafarlou, D.M., Sarhan, A.A.D., Hamdi, M. (2016). State of the art in powder mixed dielectric for EDM applications, Precision Engineering, Vol. 46, 11-33, doi: 10.1016/j.precisioneng.2016.05.010.
[17] Kalaman, S., Yaşar, H., Ekmekci, N., Opoz, T.T., Ekmekci, B. (2018). Powder mixed electrical discharge machining and biocompatibility: A state of the art review, In: Proceedings of the 18th International Conference on Machine Design and Production, Eskişehir, Turkey, 803-830.
[18] Daneshmand, S., Neyestanak, A.A.L., Monfared, V. (2016). Modelling and investigating the effect of input parame-ters on surface roughness in electrical discharge machining of CK45, Tehnički Vjesnik – Technical Gazette, Vol. 23, No. 3, 725-730, doi: 10.17559/TV-20141024224809.
[19] Raju, L., Hiremath, S.S. (2016). A state-of-the-art review on micro electro-discharge machining, Procedia Tech-nology, Vol. 25, 1281-1288, doi: 10.1016/j.protcy.2016.08.222.
Advances in Production Engineering & Management 14(3) 2019 331
Modi, Agarwal
Appendix A The following nomenclature is used in the paper:
AWLT Average white layer thickness DC Duty cycle DF Dielectric fluid DRR Debris removal rate EDDSG Electro discharge diamond surface grinding EDM Electrical discharge machining GRA Grey relational analysis GS Gap size I Current (A) MR Machining rate MRD Material removal depth MRR Material removal rate (mm3/min) MS EDM Micro-slit EDM PMEDM Powder mixed electrical discharge machining Ra Average roughness of surface (µm) SF Surface finish SR Surface roughness TM Taguchi method Ton Pulse on-time (µs) WEDM Wire electrical discharge machining WLT White layer thickness
332 Advances in Production Engineering & Management 14(3) 2019