![Page 1: Lecture 24 - Stanford Universitydionne.stanford.edu/.../Lecture24_ppt.pdf · Photolithography: Process flow 1. Apply photon sensitive polymer film to wafer via spin coating:-Positive](https://reader033.vdocuments.site/reader033/viewer/2022043015/5f3829023e76cc53f5774ce5/html5/thumbnails/1.jpg)
Lecture 24Lecture 24
Top‐down and bottom up fabrication
![Page 2: Lecture 24 - Stanford Universitydionne.stanford.edu/.../Lecture24_ppt.pdf · Photolithography: Process flow 1. Apply photon sensitive polymer film to wafer via spin coating:-Positive](https://reader033.vdocuments.site/reader033/viewer/2022043015/5f3829023e76cc53f5774ce5/html5/thumbnails/2.jpg)
Lithography (“lithos” –stone / “graphein” – to write)
Cit f d lith h City of words lithograph (Vito Acconci, 1999)
1930’s lithography press
![Page 3: Lecture 24 - Stanford Universitydionne.stanford.edu/.../Lecture24_ppt.pdf · Photolithography: Process flow 1. Apply photon sensitive polymer film to wafer via spin coating:-Positive](https://reader033.vdocuments.site/reader033/viewer/2022043015/5f3829023e76cc53f5774ce5/html5/thumbnails/3.jpg)
Photolithography
)(2 NA
d
NA=numerical aperture
![Page 4: Lecture 24 - Stanford Universitydionne.stanford.edu/.../Lecture24_ppt.pdf · Photolithography: Process flow 1. Apply photon sensitive polymer film to wafer via spin coating:-Positive](https://reader033.vdocuments.site/reader033/viewer/2022043015/5f3829023e76cc53f5774ce5/html5/thumbnails/4.jpg)
Electron-beam Lithography
![Page 5: Lecture 24 - Stanford Universitydionne.stanford.edu/.../Lecture24_ppt.pdf · Photolithography: Process flow 1. Apply photon sensitive polymer film to wafer via spin coating:-Positive](https://reader033.vdocuments.site/reader033/viewer/2022043015/5f3829023e76cc53f5774ce5/html5/thumbnails/5.jpg)
Photolithography: Process flow
1. Apply photon sensitive polymer film to wafer via spin coating:
-Positive resist: a polymeric resin and radiation sensitive molecules. Exposure causes chemical change to the sensitizer which Exposure causes chemical change to the sensitizer which
promotes dissolution of the exposed resist in aqueous developer solution
l l k h-Negative resist: sensitizer promotes polymer cross-linking in the resin, making exposed resist region insoluble to the developer
2. Soft bake: resist baked for 1/2hr at 80-90 °C to drive off excess solvent in resist and to improve adhesion to the wafer
3. Mask alignment: most semiconductor deices are currently manufactured using deep UV projection photolithography
![Page 6: Lecture 24 - Stanford Universitydionne.stanford.edu/.../Lecture24_ppt.pdf · Photolithography: Process flow 1. Apply photon sensitive polymer film to wafer via spin coating:-Positive](https://reader033.vdocuments.site/reader033/viewer/2022043015/5f3829023e76cc53f5774ce5/html5/thumbnails/6.jpg)
Lithography: Process flow
4. Development: resist-covered wafer is placed in contact with developer solution Different dissolution rates of exposed and masked resist solution. Different dissolution rates of exposed and masked resist
regions
d b k d d l d l h5. Hard bake: Hardens developed resist layer ~12hr at 150 °C
6. Etching or deposition of material in regions of removed resist. Etching g p g gshould remove the underlying layer more quickly than the resist
7 Resist strip: combination of oxygen plasma etching and wet chemicals 7. Resist strip: combination of oxygen plasma etching and wet chemicals are used to remove the resist from the wafer
![Page 7: Lecture 24 - Stanford Universitydionne.stanford.edu/.../Lecture24_ppt.pdf · Photolithography: Process flow 1. Apply photon sensitive polymer film to wafer via spin coating:-Positive](https://reader033.vdocuments.site/reader033/viewer/2022043015/5f3829023e76cc53f5774ce5/html5/thumbnails/7.jpg)
Resist materials
PMMA (poly(methyl methacrylate))Positive resist
SU-8Negative resist
![Page 8: Lecture 24 - Stanford Universitydionne.stanford.edu/.../Lecture24_ppt.pdf · Photolithography: Process flow 1. Apply photon sensitive polymer film to wafer via spin coating:-Positive](https://reader033.vdocuments.site/reader033/viewer/2022043015/5f3829023e76cc53f5774ce5/html5/thumbnails/8.jpg)
Etching1. Wet etching:
– i.e., removal of SiO2 layers using HF/H2O –Wet etching tends to be isotropic
–Some etchants preferentially etch certain crystallographic a p a y a y a g applanes faster than others
2 Dry etching: 2. Dry etching: –Aniosotropic etching (vertical etch)
–Bombardment by energetic particles from the gas phase
1 μm1 μm
![Page 9: Lecture 24 - Stanford Universitydionne.stanford.edu/.../Lecture24_ppt.pdf · Photolithography: Process flow 1. Apply photon sensitive polymer film to wafer via spin coating:-Positive](https://reader033.vdocuments.site/reader033/viewer/2022043015/5f3829023e76cc53f5774ce5/html5/thumbnails/9.jpg)
Solution-based synthesis (metal & semiconducting nanoparticles)
While the specifics of each reaction differ greatly, the basic stages of solution chemistry are:
1. Solvate the reactant species and additives2. Form stable solid nuclei from solution
3. Grow the solid particles by addition of material until the reactant species are consumed
Basic Aim: Simultaneous formation of large numbers of stable nuclei. If further growth is to occur it should happen independent of the nucleation stepgrowth is to occur, it should happen independent of the nucleation step
Key Challenge: Ostwald ripening || Need to use stabilizers
![Page 10: Lecture 24 - Stanford Universitydionne.stanford.edu/.../Lecture24_ppt.pdf · Photolithography: Process flow 1. Apply photon sensitive polymer film to wafer via spin coating:-Positive](https://reader033.vdocuments.site/reader033/viewer/2022043015/5f3829023e76cc53f5774ce5/html5/thumbnails/10.jpg)
1857: Faraday - Reduction of [AuCl4]- with P in carbon disulfide produces a deep red solution
![Page 11: Lecture 24 - Stanford Universitydionne.stanford.edu/.../Lecture24_ppt.pdf · Photolithography: Process flow 1. Apply photon sensitive polymer film to wafer via spin coating:-Positive](https://reader033.vdocuments.site/reader033/viewer/2022043015/5f3829023e76cc53f5774ce5/html5/thumbnails/11.jpg)
Air-stable, water-soluble Au nanoparticles, diameters between 10 and 20 nm
Turkevich Metal Nanoparticle Synthesis
p
Single phase synthesis• Reduction of gold chloride with sodium tris-citrate in water
Nature, 1973
![Page 12: Lecture 24 - Stanford Universitydionne.stanford.edu/.../Lecture24_ppt.pdf · Photolithography: Process flow 1. Apply photon sensitive polymer film to wafer via spin coating:-Positive](https://reader033.vdocuments.site/reader033/viewer/2022043015/5f3829023e76cc53f5774ce5/html5/thumbnails/12.jpg)
Why are metal nanoparticles cool?
20 nm
Reflection Transmission
2 nmLycergus Cup (Roman), 4th century AD:
Excitation of metal nanoparticles in goblet makes glass appear redgoblet makes glass appear red
![Page 13: Lecture 24 - Stanford Universitydionne.stanford.edu/.../Lecture24_ppt.pdf · Photolithography: Process flow 1. Apply photon sensitive polymer film to wafer via spin coating:-Positive](https://reader033.vdocuments.site/reader033/viewer/2022043015/5f3829023e76cc53f5774ce5/html5/thumbnails/13.jpg)
Metal nanoparticles support surface plasmons
20 μm
![Page 14: Lecture 24 - Stanford Universitydionne.stanford.edu/.../Lecture24_ppt.pdf · Photolithography: Process flow 1. Apply photon sensitive polymer film to wafer via spin coating:-Positive](https://reader033.vdocuments.site/reader033/viewer/2022043015/5f3829023e76cc53f5774ce5/html5/thumbnails/14.jpg)
Applications of metal nanoparticles: Cancer therapy
Atwater, “The Power of Plasmonics,” Scientific American
![Page 15: Lecture 24 - Stanford Universitydionne.stanford.edu/.../Lecture24_ppt.pdf · Photolithography: Process flow 1. Apply photon sensitive polymer film to wafer via spin coating:-Positive](https://reader033.vdocuments.site/reader033/viewer/2022043015/5f3829023e76cc53f5774ce5/html5/thumbnails/15.jpg)
Applications of metal nanoparticles: sensing
![Page 16: Lecture 24 - Stanford Universitydionne.stanford.edu/.../Lecture24_ppt.pdf · Photolithography: Process flow 1. Apply photon sensitive polymer film to wafer via spin coating:-Positive](https://reader033.vdocuments.site/reader033/viewer/2022043015/5f3829023e76cc53f5774ce5/html5/thumbnails/16.jpg)
CdS, CdSe, ZnS, ZnSe, CdTe, ZnO, TiO2, etc.
Semiconducting Nanoparticle Synthesis
2
Example: CdSeDimethylcadmium is dissolved in a mixture of trioctylphosphine (TOP) and
trioctylphosphine oxide (TOPO).y p p ( )Solution is heated and vigorously stirred
Selenium source – usually Se dissolved in TOP or TOPO – is injected quickly and at room temperature
widespread nucleation of TOPO-stabilized CdSe quantum dotsThe room-temperature Se-TOP solution prevents further nucleation or growth
Reaction can be heated for further growthg
![Page 17: Lecture 24 - Stanford Universitydionne.stanford.edu/.../Lecture24_ppt.pdf · Photolithography: Process flow 1. Apply photon sensitive polymer film to wafer via spin coating:-Positive](https://reader033.vdocuments.site/reader033/viewer/2022043015/5f3829023e76cc53f5774ce5/html5/thumbnails/17.jpg)
Electric Field Sensors (i e neuron sensing)
Semiconducting Nanoparticle Applications
Electric Field Sensors (i.e., neuron sensing)
J. Muller et al. Nano Letters 5 (2005), K. Becker et al. Nature Materials 5 (2006)
compressed tetrapod
1.4, 1.9, 3.1, 3.9, 4.8, 4.6, 2.8, 1.8 GPa
Optical Strain Sensors (i.e., cancer cell sensing)
uncompressed tetrapod
tetrapod
20 nm
C. Choi et al. Nano Letters (in press)
20 nm
![Page 18: Lecture 24 - Stanford Universitydionne.stanford.edu/.../Lecture24_ppt.pdf · Photolithography: Process flow 1. Apply photon sensitive polymer film to wafer via spin coating:-Positive](https://reader033.vdocuments.site/reader033/viewer/2022043015/5f3829023e76cc53f5774ce5/html5/thumbnails/18.jpg)
Nanowire Growth: VLS Methods
From Willander, Zhao, & Nur, SPIE 2007
![Page 19: Lecture 24 - Stanford Universitydionne.stanford.edu/.../Lecture24_ppt.pdf · Photolithography: Process flow 1. Apply photon sensitive polymer film to wafer via spin coating:-Positive](https://reader033.vdocuments.site/reader033/viewer/2022043015/5f3829023e76cc53f5774ce5/html5/thumbnails/19.jpg)
Carbon allotropes require extreme synthetic techniques:
Carbon-based nanomaterials (nanotubes, bucky balls, etc)
Carbon allotropes require extreme synthetic techniques:• Laser vaporization (fullerenes & nanotubes)
• Arc discharge methods (fullerenes & nanotubes)• Pyrolysis (fullerenes & nanotubes)h l d ( b )• Chemical vapor deposition (nanotubes)
The precursor (graphite) require significant dissociation energies prior to self-assembly (contains strong covalent bonds)(contains strong covalent bonds)