kingfisher technical data file no. 0002 metallic …m7 c3 eutectic carbides austenite machinability...
TRANSCRIPT
K-CLAD 800 RANGEK-CLAD 801 - MILD STEEL BACKING PLATE FORTEMPERATURES UP TO 450 DEGREES TYPICAL HARDNESS 60 HRC
K-CLAD
801 (MILD STEEL)
S801 (STAINLESS STEEL)
As above but with 304L Stainless Steel Backing Plate
TYPICAL ANALYSIS OFHARDFACING LAYER
C : 5.0Mn : 0.7Cr : 30.0
TYPICALHARDNESS
60 HRC
STRUCTURE
Primary carbidesM7 C3 eutectic
carbidesAustenite
MACHINABILITY
Only by grinding
PROPERTIES & APPLICATIONS
Highly resistant to extremeabrasion and gouging at
temperatures up tp 450˚C.
Typical applications:dredge pump parts, hoppers,
wearplates, crusher rolls,screw conveyors, shovel
bucket teeth, palm oil expellerscrews, catalytic pipes, etc.
CARBON CHROME WITH MOLYBDENUM / WORKING TEMPERATURE UP TO 450˚C
TECHNICAL DATAFILE NO. 0002
K-CLAD
803 (MILD STEEL)
S803 (STAINLESS STEEL)
As above but with 304L Stainless Steel Backing Plate
TYPICAL ANALYSIS OFHARDFACING LAYER
C : 5.0Mn : 0.75
N : 5.0Cr : 30.0
TYPICALHARDNESS
59 HRC
STRUCTURE
Primary carbidesM7 C3 eutectic
carbides Austenite
MACHINABILITY
Only by grinding
PROPERTIES & APPLICATIONS
Resists corrosive wear andabrasive wear.
Typical applications: chutes, feeders, scrolls
CARBON CHROME NICKEL FOR CORROSIVE ENVIRONMENT / WORKING TEMPERATURE UP TO 450˚C
K-CLAD
802 (MILD STEEL)
S802 (STAINLESS STEEL)
As above but with 304L Stainless Steel Backing Plate
TYPICAL ANALYSIS OFHARDFACING LAYER
C : 5.0Mn : 0.7
Si : 0.5Mo : 7.0Nb : 7.0W : 2.0Cr : 22.0
TYPICALHARDNESS
20c:62 HRC550c:54 HRC650c:50 HRC
STRUCTURE
Austenitic matrix with various
complex carbides such as chromium
rich hexagonal primary carbides, complex eutectic
and globular niobium rich
carbides
MACHINABILITY
Only by grinding
PROPERTIES & APPLICATIONS
Resists severe high stressabrasion resistant at
temperatures up to 750˚C.Typical applications:
blast furnace bells andhoppers, sinter plant, cement
kilns, screens, exhaust fanblades, pearlite crushers, etc.
COMPLEX CARBIDE DEPOSIT OF CHROMIUM, MOLYBDENUM, NIOBIUM, VANADIUM & TUNGSTEN / WORKING TEMPERATURES UP TO 750˚C
K-CLAD 802 - STAINLESS STEEL BACKING PLATE FORTEMPERATURES UP TO 750 DEGREES TYPICAL HARDNESS 50-62 HRC
K-CLAD 803 - STAINLESS STEEL BACKING PLATE FORCORROSIVE ENVIRONMENTS
METALLIC TECHNICAL DATA
KingfisherTE
EM
ILD
S
K-C
LAD
800
K-CLAD 800 Wear Life Comparison
The information contained on this product information sheet is to be used as guidance only. The advice and technical data given is done so in good faith and does not constitute any warranty or guarantee on product performance or suitability. We hereby reserve the right to change the technical information herewith without notification or prior agreement.
T +44 (0)1384 410 777F +44 (0)1384 410 877E [email protected]
Kingfisher IndustrialCradley Business ParkOverend RoadCradley HeathWest MidlandsUnited Kingdom B64 7DW
Protecting Industry WorldwideKingfisher