inhibition of co2 corrosion by formate fluids in high temperature environments
DESCRIPTION
Presentation to the Royal Society of Chemistry's "Chemicals in the Oilfield" conference, November 2005 The paper describes how formate brines protect steels against CO2 corrosion. It also shows the results of stress corrosion cracking tests on CRA steel samples exposed to high-density completion brines containing oxygen at 160 deg C. The 13Cr, 22Cr and 25Cr steels all cracked in the presence of calcium bromide brine containing oxygen.TRANSCRIPT
Inhibition of Carbon Dioxide Corrosion by Formate Brines in High Temperature Environments
John D. Downs, Alan Carnegie and William Benton,Cabot Specialty Fluids LtdHåkon Leth-Olsen, Norsk Hydro ASA, Corporate Research Centre
Chemistry in the Oil Industry IX, EOSCA, Royal Society of ChemistryManchester 1th November 2005
04357 • Page: 2 •
Gas-injection tubing with NaCl completion
fluid. CO2 leakage
Chlorine SCCof AISI 316L pipe
What worries a corrosion engineer
Localised corrosion Stress Corrosion Cracking (SCC)
04357 • Page: 3 •
Outline
General corrosivity of halide and formate brines
CO2 corrosion test in K/Cs-formate and CaBr2
SCC tests in K/Cs-formate and CaBr2 brines with O2 influx
Summary
04357 • Page: 4 •
Corrosivity in halide brines Halide well brines:
NaCl Max SG: 1.2 NaCl-NaBr Max SG: 1.5 CaCl2 Max SG: 1.39 CaBr2 Max SG: 1.70 CaCl2–CaBr2 Max SG: 1.8 ZnBr2 Max SG: 2.3 Mixes
NaCl, CaCl2, CaBr2 basically non-corrosive Neutral salts Not oxidising
Disadvantageous: ZnBr2 : Acid salt. Corrosive! SCC of CRAs in chloride brines if oxygen or CO2 influx Localised corrosion in CaBr2:
– If acidified with acid gas? (no buffer effect)– If oxygen influx?
04357 • Page: 5 •
Corrosivity in formate brines (without CO2 influx)
Three basic formate well brines: Na formate: HCOONa Max SG: 1.3 K formate: HCOOK Max SG: 1.57 Cs formate: HCOOCs Max SG: 2.3 Mixes of the three
Basically low corrosivity against all relevant well materials Not oxidising High pH (9-10) Low halide contents (< 3000 ppm) Highly buffered (soluble carbonate and bicarbonate)
– Maintains a high pH - usually not acidified with acid gas No reported failures in the field due to corrosion in formate brines
04357 • Page: 6 •
Concerns with formate brines
Corrosivity if acidified due to influx of large amounts of acid gass Not likely under drilling and short term use Theoretical possibility in packer fluid
SCC of CRAs if formate brine contaminated with chloride? With O2 influx? With CO2 influx?
Concerns addressed in recent and ongoing test programs
04357 • Page: 7 •
Relevant materials
Material Specification Cr (%) Ni (%) Mo (%) Mn (%) C (%) Other (%)
C-steel ST-37-2 - - - - < 0.20 -
13Cr L80 13.0 0.4 0.09 1.67 Co: 0.8 V: 0.38
S13Cr (Hypo II)
NT-CRSS-110
12.2 5.73 2.1 0.44 0.02 Cu: 1.4 Si: 0.3
22Cr 22.0 5.0 3.2 - - N : 0.18
25Cr 25.0 7.0 4.0 - - N: 0.3
04357 • Page: 8 •
CO2 corrosion test in K-formate [1]
[1] H. Leth-Olsen, SPE 95072, Aberdeen , UK, 13 May 2005
C-steel Super 13%Cr Standard 13%Cr
1.53 SG K-formate10 bar CO2120 – 180°C
0.0
1.0
2.0
3.0
4.0
5.0
6.0
0 200 400 600 800 1000 1200
Time (hours)
Cor
rosi
on r
ate
(mm
/y)
0
50
100
150
200
Cor
rosi
on r
ate
(mpy
)
C-steel 13% Cr
120°C 140°C 160°C
180°C
150°C
120°C
Carbon steel
Iron carbonate
04357 • Page: 9 •
Results from earlier tests in CaBr2 [1]
[1] H. Leth-Olsen, SPE 95072, Aberdeen , UK, 13 May 2005
C-steel Standard 13%Cr Super 13%Cr LPR corrosion rates for C-Steel in CaBr2 , 10 bar CO2
0
0.5
1
1.5
2
0 200 400 600 800 1000 1200 1400 1600
Time (hours)
Corr
osio
n r
ate
(m
m/y
ear)
0
10
20
30
40
50
60
70
80
Corr
osi
on r
ate
(mpy)
UninhibitedInhibited
120oC 140o
C
160o
C
180o
C
150o
C
120oC
Localised corrosion
1.53 SG CaBr2
10 bar CO2
120 – 180°C
04357 • Page: 10 •
CO2 corrosion tests - experimental
Test solutions: K/Cs formate, 1.7 SG, fully buffered, pH 10.5 CaBr2, 1.7 SG , pH 5
Temperatures: 150°C and 175°C
Exposure times: Until stable LPR values (6 and 4 weeks)
Materials: C-steel, Standard 13Cr, Super 13Cr, Duplex 22Cr, Duplex 25Cr
CO2 pressure: 10 bar (autoclaves)
04357 • Page: 11 •
CO2 corrosion tests - experimental
Test methods: Visual, measurements of local corrosion depths Weight losses Linear Polarisation Resistance (LPR) – Real-time corr. measurements Scanning Electron Microscopy (SEM) of scales
Severe conditions – simulating the worst-case situation of buffer overwhelmed . Unlikely in service for the buffered formate brines More likely for the halide brines (no carbonate buffer)
04357 • Page: 12 •
Example LPR curve, K/Cs formate, 150°C, 10 bar CO2
04357 • Page: 13 •
Specimens, K/Cs-formate, 175°C, 10 bar CO2
04357 • Page: 14 •
Scales formed in K/Cs-formate, 175°C, 10 bar CO2
Super 13CrC-steel
04357 • Page: 15 •
Specimens, CaBr2, 175°C, 10 bar CO2
04357 • Page: 16 •
Result Example 2: CaBr2, 175°C, 10 bar CO2
Super 13CrC-steel
04357 • Page: 17 •
Long-term (LPR) corrosion rates – 150°C
04357 • Page: 18 •
Localised corrosion – 150°C
04357 • Page: 19 •
Long-term (LPR) corrosion rates – 175°C
04357 • Page: 20 •
Localised corrosion – 175°C
04357 • Page: 21 •
Summary CO2 corrosion tests
C-steel: High initial corrosion rates in both brines followed by build-up of protective scale Relatively low long-term rates at 150°C and 175°C in both brines Severe localised corrosion in CaBr2 at 175 °C (up to 5 mm/year)
Standard 13Cr Relatively low general corr. rates in both brines– Protective scale Localised corrosion in CaBr2 at 150°C
Super 13Cr Increasing general corrosion rates with temperature in K/Cs formate Low rates in bromide brine
Duplex 22Cr and 25Cr Low rates in both brines
04357 • Page: 22 •
Stress Corrosion Cracking tests
Test solutions: K/Cs formate, 1.7 SG, pH 10.5 , 10.000 ppm Cl- CaBr2, 1.7 SG , pH 5, no Cl- CaBr2, 1.7 SG , pH 5, 10.000 ppm Cl-
Materials: Super 13Cr, Duplex 22Cr, Duplex 25Cr, AISI 316L (ref.)
Exposure time: 3 months (inspection every 30 days)
Temperature: 160°C
Gas: 0.2 bar 02, 10 bar N2
Test methods: U-bends and C-rings, pre-stressed to yield
04357 • Page: 23 •
Formate + Chloride CaBr2 no Chloride CaBr2 + ChlorideSuper 13Cr OKDuplex 22Cr OKDuplex 25Cr OK OK OK
AISI 316L OK OK? OK
2 monthsFormate + Chloride CaBr2 no Chloride CaBr2 + Chloride
Super 13Cr SCC? (2/3) SCC (3/3) SCC (3/3)Duplex 22Cr OK SCC (3/3) SCC (3/3)Duplex 25Cr OK SCC (1/3) SCC (1/3)
AISI 316L SCC (1/1) SCC (1/1) SCC (1/1)
Formate + Chloride CaBr2 no Chloride CaBr2 + ChlorideSuper 13CrDuplex 22Cr OKDuplex 25Cr OK
AISI 316L
SCC results1 month
Formate + Chloride CaBr2 no Chloride CaBr2 + ChlorideSuper 13Cr OK SCC (3/3) SCC (3/3)Duplex 22Cr OK SCC? SCC (1/3)Duplex 25Cr OK OK OK
AISI 316L OK OK? OK
Formate + Chloride CaBr2 no Chloride CaBr2 + ChlorideSuper 13CrDuplex 22Cr OKDuplex 25Cr OK
AISI 316L
Formate + Chloride CaBr2 no Chloride CaBr2 + ChlorideSuper 13CrDuplex 22Cr OKDuplex 25Cr OK
AISI 316L
Formate + Chloride CaBr2 no Chloride CaBr2 + ChlorideSuper 13Cr OKDuplex 22Cr OKDuplex 25Cr OK OK OK
AISI 316L OK OK? OK
Formate + Chloride CaBr2 no Chloride CaBr2 + ChlorideSuper 13CrDuplex 22Cr OKDuplex 25Cr OK
AISI 316L
3 monthsFormate + Chloride CaBr2 no Chloride CaBr2 + Chloride
Super 13Cr SCC (2/3) SCC (3/3) SCC (3/3)Duplex 22Cr OK SCC (3/3) SCC (3/3)Duplex 25Cr OK SCC (2/3) SCC (2/3)
AISI 316L SCC (1/1) SCC (1/1) SCC (1/1)
04357 • Page: 24 •
SCC results – K/Cs formatewith 10000 ppm Cl-
Super 13Cr, 3 months
Duplex 22Cr3 months
Duplex 25Cr3 months
04357 • Page: 25 •
SCC results – K/Cs formate with 10000 ppm Cl-
Super 13Cr, 3 months
04357 • Page: 26 •
SCC results – CaBr2 without chlorides
Super 13Cr, 1 month Duplex 22Cr, 2 months Duplex 25Cr, 2 months
04357 • Page: 27 •
SCC results – CaBr2 without chlorides
Duplex 25Cr, 2 months
04357 • Page: 28 •
SCC results – CaBr2 with 1000 ppm Cl-
Super 13Cr, 1 month Duplex 22Cr, 2 months Duplex 25Cr, 2 months
04357 • Page: 29 •
Summary SCC test (160°C, oxygen present)
K/Cs formate with 10000 ppm chloride: SCC initiation of Super 13Cr after 3 months SCC of AISI 316L No SCC of duplex 22Cr and 25 Cr
CaBr2 without chlorides: Severe cracking of all CRAs (S13Cr, AISI 316L, Duplex 22Cr and Duplex 25Cr)
CaBr2 with 10000 ppm chlorides: Severe cracking of all CRAs (S13Cr, AISI 316L, Duplex 22Cr and Duplex 25Cr)
Ongoing work: K/Cs formate with 3000 ppm chloride, O2, 160°C K/Cs formate with 10000 ppm chloride, 10 bar CO2, oxygen free, 160°C CaBr2 with 10000 ppm chlorides, 10 bar CO2, oxygen free, 160°C
04357 • Page: 30 •
Summary
K/Cs formate with CO2 influx: Iron carbonate scale formed on C-steel and Standard 13Cr Increased corrosion of Super 13Cr at 175°C (0.4 mm/y) Duplex CRAs practically resistant
K/Cs formate + 10000 ppm Cl- with O2 influx: Signs of SCC cracks of Super 13Cr after 3 months No signs of SCC cracking of duplex CRAs
CaBr2 with CO2 influx: Relatively low long term general corrosion rates on all materials Localised corrosion on C-steel at 175°C and Standard 13Cr at 150°C
CaBr2 + 10000 ppm Cl- with O2 influx: Severe SCC cracking of all CRAs
04357 • Page: 31 •
Acknowledgements
Cabot Speciality Fluids Ltd. is acknowledged for financing the work and Gro Skåum and Ingmarie Liberger, Hydro Corporate Research Centre, is acknowledged for performing the experimental work.