influence of gasification reaction of coke on sliding and

ISIJ International, Vol. 60 (2020), No. 7

© 2020 ISIJ1401

ISIJ International, Vol. 60 (2020), No. 7, pp. 1401–1408

* Corresponding author: E-mail: [email protected]: https://doi.org/10.2355/isijinternational.ISIJINT-2019-190

1. Introduction

Coke is charged with iron ore from the top of the blast furnace to maintain the permeability of the moving bed in the furnace. A coke bed is formed between the cohesive zone and the deadman at the bottom of the blast furnace, and the molten iron and slag formed at the cohesive zone descend to the coke bed. However, the hot blast gas blown from the tuyeres rises through the vacancy in the coke bed, so a counterflow of liquid and gas occurs. When hold-up of liquid is formed in the packed bed, liquid fills the space of the bed, and, thus, gas permeability decreases. Enhance-ment of the descent of the liquid droplet in the coke bed is therefore desirable. Because the hold-up of liquid remark-ably decreases the gas permeability of the packed bed, many studies have been carried out to investigate this phenom-enon. Formulas for the amount of hold-up in a packed bed have been reported,1,2) obtained in experiments using a cold model. Ohgusu et al. derived a formula of static hold-up of CaO–SiO2–Al2O3–MgO melt from experiments at a higher temperature.3) It was shown by a numerical simulation that the amount of static hold-up depends on the wettability.4) When the liquid wets the solid of the packed bed, a liquid hold-up is formed in the vicinity of the contact point of packed bed materials.5,6) However, when liquid does not wet the solid, liquid hold-up forms in the bottleneck of the vacancy in the packed bed.7,8) As described above, the hold-up of the liquid is influenced by the surface tension, the wetting angle, and the packing-layer structure.

For a system similar to the wetting phenomena of coke

Influence of Gasification Reaction of Coke on Sliding and Dynamic Contact Angles of Droplets in a Blast Furnace

Shinsuke OGYU,1) Lichun ZHENG,2) Xu GAO,3) Shigeru UEDA,3)* Sohei SUKENAGA3) and Shin-ya KITAMURA3)

1) Institute of Multidisciplinary Research Advanced Material, Tohoku University. Now at NIPPON STEEL Stainless Steel Corpo-ration (NSSC), 3434 Shimada, Hikari, Yamaguchi, Japan.2) School of Metallurgy, Northeastern University, 3-11, Wenhua Road, Heping District, Shenyang, P.R. China.3) Institute of Multidisciplinary Research Advanced Material, Tohoku University, 1-1 Katahira 2 Aoba-ku Sendai, 980-8577 Japan.

(Received on March 26, 2019; accepted on May 27, 2019)

To enhance the descent of droplets in the coke bed of a blast furnace, the sliding angle of the water droplet and the advancing and receding contact angles at the time of sliding were measured. Coke used as a reducing agent in a blast furnace was employed as a substrate. Because the shape of the coke sur-face varies with the gasification reaction with CO2, the coke substrate was treated with heat (1 273 K) in a CO/CO2 atmosphere. Irregularities of approximately several micrometers were formed on the coke sur-face by the gasification reaction, and the sliding angle of the droplet decreased.

KEY WORDS: coke; dynamic contact angle; droplet motion; dripping zone; blast furnace; surface roughness.

and slag, measurements on the surface tension of molten oxides and the wettability of molten oxides with carbona-ceous materials have been reported.9,10) In recent years, mea-surement of the contact angle of slag and coke considering the influence of the ash on the wetting phenomena has been done.11,12) The contact angle of coke and molten iron was reported to be 60°–130°,13) and it is influenced by concentra-tions of C and S in the iron. In addition, the contact angle of the melt of the CaO–SiO2–Al2O3 system and carbonaceous material has a wide range of 20° to 160°, and that is varied with contacting time and reaction. In systems containing Fe2O3, the contact angle is decreased by the reduction reac-tion. However, slag containing no iron oxide is not wet with carbonaceous material, and the angle is more than 90°.14) In addition to the effect of ash, the wetting of coke and molten slag and iron are influenced by the surface properties, reac-tion at the interface, and motion state of the liquid.

As described above, the relationship between the con-tact angle and the hold-up in the packed bed and the static wettability on the smooth carbonaceous material has been extensively studied; however, for considering the droplet motion in the coke-packed bed, it is necessary to investigate the behavior of droplets in packed a bed with a surface that is not smooth.

The relation between the wettability and the falling angle of droplets has been studied in the field of surface science.15–22) Many studies have been conducted on the lotus and rose petal effects caused by the hierarchical roughness. However, the falling and flow of droplets in a packed bed of coke composed of a nonuniform and nonsmooth surface have not been sufficiently studied.

In a previous work, the relationship between the transfer resistance of triple circles around droplets on coke and the


© 2020 ISIJ 1402

surface structure of coke with the gasification reaction was reported.23) The relationship between the sliding angle and the dynamic contact angle of the droplets staying in the packed bed was not sufficiently examined in that study.

In the present study, considering the motion of molten slag and iron on the coke surface, the relationship between the sliding angle and dynamic contact angles of water drop-lets on a nonsmooth coke surface was investigated. The surface structure of coke was modified by a gasification reaction with CO2. The relationship between the surface structure and sliding angle was investigated.

2. Experimental Procedure

2.1. Sample PreparationMetallurgical coke used in blast furnace operation is

employed as a material of substrate. The composition of the coke substrate obtained through a proximate analysis is shown in Table 1. Coke was cut as substrates with dimen-sions of 40 × 30 × 4 mm. The surface was polished with #400 emery paper. A mullite tube of φ40 (O.D.) × 600 mm was installed as a reaction tube to a horizontal electric resistance furnace. The atmosphere in that was controlled with a gas mixture of N2/CO/CO2 using mass flow controllers.23) Coke was placed in the hot zone in the furnace, heated to 1 273 K in N2, and then reacted with CO2 gas in a CO/CO2 = 1/1 mixture at 1 273 K. The gas flow was 200 ml/min, and the holding time was 2, 4, or 8 h. The substrate was then removed from the furnace and cooled in a N2 stream. In the heat treatment, the gasification reaction of carbon progresses at the surface of the coke, and, thus, the surface structure changes.

According to the above procedure, samples of various conditions of gasification reaction as unreacted coke and reacted coke for 2, 4, and 8 h in a CO/CO2 atmosphere were prepared, and the surface of the sample was observed. The relationship between gasification reaction condition and reaction ratio of coke was reported elsewhere.23) Water wets with the coke and penetrates the inside of the coke. In order to form droplets and clarify the influence of surface shape on dynamic contact angle, fluorine-based water repellent (FLUORO SURF) was impregnated, while care was taken not to change the surface shape of the sample; it was dried for 24 h at room temperature. As a flat and smooth sample, a glass plate with a water-repellent material was employed. Pure water was used as the liquid sample.

2.2. Analysis of Surface Structure of CokeBefore subjecting the sample to water-repellent treat-

ment, the surface structure of the sample was observed using electron probe micro analyzer (EPMA) and an optical microscope capable of measuring the surface shape of the sample. The fine surface condition and element distribution were measured by EPMA, and the optical microscope was used for observation of the surface roughness and sharpness.

2.3. Measurement of Sliding Angle and Advancing and Receding Angles

As shown in Fig. 1, a metal stage was installed on a smoothly rotatable table with a horizontal axis, and a clip for fixing the coke substrate was placed on it. To capture the shape of the specimen on the tilted coke, the camera was installed at the height of the stage in the direction of the rotation axis. An arbitrary amount (10 to 100 ml) of distilled water was placed on the coke from the top side to form droplets. While photographs were taken with the camera, the tilt of the stage was increased slowly until the droplet fell. As shown in Fig. 2, the slope α of the substrate at the time of falling, the advancing contact angle θA, and the receding contact angle θR of the droplet just before the fall were measured, respectively, based on the image taken. The static contact angle and contact surface radius of the droplet on the horizontal substrate were also derived.

3. Results and Discussion

3.1. Sliding of Water Droplet on a Water-repellent Smooth Substrate

Figure 3 shows the relationship between weight and sliding angle of a water droplet on a water-repellent glass plate. The sliding angles were, respectively, 70° and 30° for droplets of approximately 0.01 and 0.05 g, and the sliding angle decreased with increasing droplet weight. The advancing and receding contact angles at this fall are shown in Fig. 4. The static contact angle of water on this

Fig. 1. Schematic of experimental apparatus. (Online version in color.)

Table 1. Composition of coke.

mass%Fixed carbon Volatile Ash Water

87.66 0.26 12.08 0.28 Fig. 2. Measurement of dynamic angles. (Online version in color.)


© 2020 ISIJ1403

substrate was approximately 100°. However, the advancing contact angle was slightly larger, and the receding contact angle was smaller. It was also found that contact angle hysteresis, which is the difference between the advancing and the receding contact angles, was large in the range of 0.02–0.04 g, where the weight of the droplet was small, and the hysteresis decreased with increasing weight of the droplet. This might be a result of the balance of the contact width and drop weight, the relation between droplet size and hysteresis is discussed in 3.2.2.

3.2. Sliding of Water Droplet on Water-repellent Coke3.2.1. Measurement Result

The relationship between the weight of the water droplet and the sliding angle is shown in Fig. 5. Figures 5(a)–5(d) indicate the result for coke with a gasified reaction for 0, 2, 4, and 8 h, respectively. The sliding angle decreased with increasing droplet weight on all substrates. Comparing nongasified and gasified coke, the sliding angle of the water droplet on gasified coke is significantly small.

Figure 6 shows advancing and receding contact angles just before sliding. Figures 6(a)–6(d) indicate the result on coke with a gasified reaction for 0, 2, 4, and 8 h, respec-tively. The change in advancing and receding angles due to the size of the droplet is small. The advanced contact angle on unreacted coke is clearly larger than the receding contact angle; however, the difference of angles is small on coke with the heat treatment. This difference corresponds to the force which the droplet receives at the time of falling.

The relationship between the weight of the droplet and the sliding angle on smooth glass, unreacted coke, and coke with gasification reactions for 2 and 8 h is shown in Fig. 7. Figures 6 and 7 show that the hysteresis of the contact

Fig. 3. Sliding angle of water droplet on flat substrate.

Fig. 4. Advancing and receding contact angles of water droplet on flat substrate.

Fig. 5. Relationship between weight of droplet and sliding angle. (a) Non-heat treated, (b) 2 h, (c) 4 h, (d) 8 h.


© 2020 ISIJ 1404

angle on the gasified coke was small, and the sliding angle on the coke was smaller than on glass and nontreated coke. Moreover, the sliding angle on unreacted coke was larger than that on a smooth substrate.

3.2.2. Validity of Application of Furmidge’s Equation to Droplet Behavior on a Nonsmooth Surface

The sliding angle of the droplet on the smooth surface can be calculated from the advancing and receding contact angle of the droplet by using a formula proposed by Furmidge. Moreover, by rearranging it for the sliding angle, it can be written as in Eq. (1).

sing

w

mcos cos�

�� glR A( ) .................. (1)

where cosθR–cosθA denotes the difference of receding contact angle θR and receding contact angle θA, namely, the contact angle hysteresis. Moreover α, γ gl, w, m, and g

respectively indicate sliding angle of the droplet, the sur-face tension, the projected contact width in the direction of movement, the weight of the liquid, and the gravitational acceleration. In the analysis, the diameter of the contact circle during static contact was substituted for w. Changes in the length and width of droplets have been studied.19,20) In this study, the droplet on the water-repellent substrate slides at a low angle, so it was assumed that there was no clear difference between the diameter of the static contact circle and the width of the contact surface at the fall.

Figure 8 shows the relationship between the contact angle hysteresis and the sliding angle of the water droplet on the water-repellent glass, untreated coke, 2-h-gasified coke, and 8-h-gasified coke. The straight line in the figure represents a line taking the value of γ gl/g of 0.0074 [g/mm] following Eq. (1) as a slope. The value was obtained using

Fig. 6. Relationship between weight of droplet, and advancing and receding contact angles. (a) Non-heat treated coke, (b) 2 h, (c) 4 h, (d) 8 h.

Fig. 7. Comparison of sliding angles on various substrates.

Fig. 8. Relationship between hysteresis of contact angle and slid-ing angle.


© 2020 ISIJ1405

the surface tension of water and gravitational acceleration.The measured value and the value obtained from Eq. (1)

are close to each other. However, focusing on the result for the non-heat-treated coke, when the hysteresis is large, the sliding angle by measurement tends to be slightly larger than the line following Eq. (1). The effect of surface structure on the relationship is not clear. Overall, because there is no considerable difference in the relationship between the hys-teresis and sliding angle owing to the difference in substrate, it is shown that the relationship of Eq. (1) can be applied to some extent regardless of the surface texture.

3.3. Evaluation of Variation of Coke Surface by Gasifi-cation Process

The appearances of samples with different gasification treatments are shown in Fig. 9. Figures 9(a), 9(b), and 9(c) are substrates with no treatment and heat treatment for 2 and 8 h, respectively. As the gasification time becomes longer, the surface of the coke sample turns a brighter color.

Figure 10 shows the coke sample surface observed by scanning electron microscopy. Figures 10(a) and 10(b), respectively, show the surface of untreated coke and the coke with gasification treatment for 2 h. Pores of various sizes coexist in Figs. 10(a) and 10(b) from several hun-dred micrometers to pores of 10 μm or less. Regarding the distribution of pores of about several hundreds of microm-eters, there is no clear difference between Figs. 10(a) and 10(b); however, in Fig. 10(a), smooth parts can be visually observed among vacancies and holes, while, in Fig. 10(b), fine irregularity exists in the portion corresponding to the

smooth parts in Fig. 10(a). This fine irregularity is attribut-able to the fact that the surface properties have formed as a result of the progress of the following reaction.

CO g C(s) CO(g)2 2( )� � ...................... (2)

Figures 11(a) and 11(b) show the concentration of ele-ments of the surface of the untreated coke and that gasified for 2 h observed by EPMA, respectively. Panels show a secondary electron image, backscattered electron image, and concentration of C, Si, S, and O near the sample surface. Comparing Figs. 11(a) and 11(b) shows that concentrations of Si and O were increased, and the gangue particles are exposed on the surface by the gasification process for coke. This phenomenon is one factor that causes changes in the surface properties of the coke.

A stereoscopic image of a certain area on the surface of the coke substrate was taken with a digital microscope, and the surface shape was measured. Figure 12 shows an example of a stereoscopic image of the surface shape of the coke without heat treatment. For the three arbitrary straight lines on the substrate surface shown in the figure, the surface roughness on each line was analyzed. Three arbitrary lines avoiding large pores were selected, and the results of line analysis were averaged to obtain the roughness of the sur-face texture. In this analysis, two kinds of objective lenses of 10 times and 20 times different magnification ratios were used, and the observation regions were 1 960 × 1 960 and 245 × 245 μm. Here, for a region of 1 960 × 1 960 μm, a stereoscopic image was formed with a pitch of 12.1 μm in the vertical direction, and the pitch was 0.859 μm in the vertical direction for the region of 245 × 245 μm.

Figures 13(a), 13(b), and 13(c), respectively, show the analysis results of a line of 1 960-μm width in the nonre-acted coke substrate and those with gasification reactions for 2 and 8 h. There was a difference in shape depending on the measurement position. With large irregularities, there was more than a 100-μm variation in the depth direction, while fine changes of a few micrometers were not detected. The surface roughness was evaluated by the arithmetic average of the roughness profile, Ra (μm). Ra was derived according to JIS B 0601. The reference length was 1 960 μm of the observation width. In this experiment, the Ra of the mea-surement position of each substrate in the 1 960-μm-width region was 18.8 μm for unreacted coke, 22.1 μm for 2-h-gasified coke, and 17.8 μm for 8-h-gasified coke. Ra

Fig. 10. SEM images of coke surface. a) non-heat treated, b) heated in CO/CO2 for 2 hs.

Fig. 9. Appearance of coke substrates after heat treatment. (a) No-heated (b) heated for 2 h (c) heated for 8 h. (Online version in color.)


© 2020 ISIJ 1406

was strongly influenced by the presence of large irregulari-ties and pores, and the resolution in the measurement in this region corresponds to 12 μm. Therefore, in this analyzing region, the variation in Ra because of a fine irregularity by

gasification reaction cannot be evaluated.Figures 14(a), 14(b), and 14(c), respectively, show the

results of analysis of a line of 245-μm width in the nonre-acted coke substrate and those with gasification reactions

Fig. 11. EPMA observation of surface of coke. a) non-heat treated, b) heated in CO/CO2 for 2 hs. (Online version in color.)

a)

b)


© 2020 ISIJ1407

for 2 and 8 h. There was a difference in shape depending on the measurement position. The surface of coke without a gasified reaction seems smooth; meanwhile, numerous irreg-ularities with a depth of approximately 5 μm exist on the substrate subjected to a gasified reaction. Moreover, irregu-larities of approximately 5 μm were formed on the surface of the inner side of larger pores. The Ra of each substrate was 0.7 μm for untreated coke, 2.0 μm for 2-h-gasified coke and 6.6 μm for 8-h-gasified coke. The roughness of the relatively smooth part of the surface increased with the gasification reaction time depending on the resolution of the analysis. The coke surface was formed from pores and irregularities of different sizes, so the evaluation of the roughness varied considerably depending on the resolution

and the sampling position at the time the surface roughness was measured. The change in the surface roughness that influences the wettability due to the gasification reaction on the coke surface was difficult to evaluate with irregularities of more than 20 μm; however, that changes in the range of Ra = 0.7–6.6 μm.

3.4. Influence of Irregularities of Coke Surface on Sliding Angle

As shown in Fig. 7, a large sliding angle was observed on the coke without heat treatment as compared with on the smooth glass surface. However, the sliding angle on the coke with heat treatment became small. On the surface of the non-heat-treated coke, larger pores of more than 100 μm were also observed, and the average roughness was 18 μm. However, because the average roughness of a relatively smooth position including no large pore was 0.7 μm, the value of the roughness varied significantly depending on the position to be evaluated. As with the results in the previ-ous sections, no change in the structure of larger pores was observed by the heat treatment, but the fine roughness of the relatively smooth part increased to 6.6 μm. The fine irregu-larity of the surface significantly decreased the sliding angle.

On the surface of the non-heat-treated coke, the scale of the unevenness of the smooth portion was small, and it was clearly different from the part with larger pores. Extrand reported that the roughness has no effect on the sliding angle on a smooth substrate with Ra of approximately 0.2 μm at the maximum, but that the nature of the surface and the contact angle determine the sliding angle;20) therefore, it can be assumed that the roughness of the smooth part may have a small influence on the sliding angle, and, with regard to the smooth portion on the untreated coke, a falling behavior similar to that for the smooth glass surface would be exhib-ited. However, the presence or absence of large pores was different between the non-heat-treated coke and the glass sur-

Fig. 13. Surface profiles of coke for 1 960 μm width. a) non-heat treated, b) heated in CO/CO2 for 2 hs and c) heated in CO/CO2 for 8 hs. (Online version in color.)

Fig. 12. Position of measurement of surface roughness on coke substrate. (Online version in color.)


© 2020 ISIJ 1408

face, and the large pores on the coke surface would increase the sliding angle in this experimental result. As described above, the fine irregularity and the large pores on the coke surface have different influences on the sliding angle of the droplet. For a detailed understanding of the liquid flow in the coke-packed bed, further research is required on the size of the pores that has an effect on the falling behavior.

4. Conclusions

In this study, the relationship between the sliding angle of droplets and the dynamic contact angles of water droplets on coke substrate was investigated. The influence of the shape on the coke surface on the sliding angle and the dynamic contact angle was obtained.

(1) The relationship between the sliding angle and hys-teresis of contact angles on a smooth surface was established for that on the surface of coke.

(2) The contact angle hysteresis of a droplet on coke without a gasification reaction was larger than that on a smooth surface, and that on coke with a gasification reaction for more than 1 h was smaller than on a smooth surface.

(3) Fine irregularities on the scale of several microm-eters were formed on the coke surface by the gasification reaction of coke.

(4) After fine irregularities were formed, the hysteresis of the contact angle decreased as the gasification reaction time of coke increased; however, the change was small.

AcknowledgementAuthors thanks to the member of research group

Mechanisms and Control of Cohesive Zone Phenomena for Blast Furnace Permeability of ISIJ, for their appropriate advices.

REFERENCES

1) T. Sugiyama, T. Nakagawa, H. Sibaike and Y. Oda: Tetsu-to-Hagané, 73 (1987), 2044 (in Japanese).

2) T. Fukutake and V. Rajakumar: Trans. Iron Steel Inst. Jpn., 22 (1982), 355.

3) H. Ohgusu, Y. Sassa, Y. Tomita, K. Tanaka and M. Hasegawa: Tetsu-to-Hagané, 78 (1992), 1164 (in Japanese).

4) T. Kon, S. Natusi, S. Ueda, R. Inoue and T. Ariyama: ISIJ Int., 52 (2012), 1565.

5) Y. Endo, Y. Kosaka and M. Ishii: Kagaku Kogaku Ronbunshu, 19 (1993), 1128.

6) S. Kikuchi, S. Ueda, T. Kon, R. Inoue, S. Natsui and H. Nogami: ISIJ Int., 54 (2014), 1244.

7) K. Saito, K. Ohno, T. Miki, Y. Sasaki and M. Hino: ISIJ Int., 46 (2006), 1783.

8) H. L. George, B. J. Monaghan, R. J. Longbottom, S. J. Chew and P. R. Austin: ISIJ Int., 53 (2013), 1172.

9) K. Mukai and T. Ishikawa: J. Jpn. Inst. Met., 45 (1981), 147.10) L. R. Barrett and A. G. Thomas: J. Soc. Glass Technol., 43 (1959),

179.11) K. Ohno, T. Maeda, K. Kunitomo, T. Miyake and S.Tsurumaru:

CAMP-ISIJ, 27 (2014), 16, CD-ROM (in Japanese).12) S. Sukenaga, H. Shibata, T. Fuchigami, K. Yasutake, S. Rine, N.

Satito and K. Nakashima: CAMP-ISIJ, 27 (2014), 19, CD-ROM (in Japanese).

13) K. Ogino: Bull. Jpn. Inst. Met., 11 (1972), 323 and M. Humenik, D. W. Hall and R. L. Van Alsten: Met. Prog., 81 (1962), 101.

14) M. Hayashi, S. Sukenaga, K. Ohno, S. Ueda, K. Sunahara and N. Saito: Tetsu-to-Hagané, 100 (2014), 211 (in Japanese).

15) C. G. L. Furmidge: J. Colloid Sci., 17 (1962), 309.16) A. I. ElSherbini and A. M. Jacobi: J. Colloid Interface Sci., 299

(2006), 841.17) N. Nishikawa, H. Mayama, Y. Nonomura, N. Fujinaga, S. Yokojima,

S. Nakamura and K. Uchida: Langmuir, 30 (2014), 10643.18) R. N. Wenzel: J. Phys. Chem., 53 (1949), 1466.19) A. B. D. Cassie: Discuss. Faraday Soc., 3 (1948), 11.20) C. W. Extrand and Y. Kumagai: J. Colloid Interface Sci., 170 (1995),

515.21) M. Yamamoto, N. Nishikawa, H. Mayama, Y. Nonomura, S.

Yokojima, S. Nakamura and K. Uchida: Langmuir, 31 (2015), 7355.22) M. Nosonovsky and B. Bhushan: Microelectron. Eng., 84 (2007),

382.23) T. Kon, S. Sukenaga and S. Ueda: ISIJ Int., 57 (2017), 1166.

Fig. 14. Surface profiles of coke for 245 μm width. a) non-heat treated, b) heated in CO/CO2 for 2 hs and c) heated in CO/CO2 for 8 hs. (Online version in color.)