C A R B O N 4 7 ( 2 0 0 9 ) 3 8 4 – 3 9 5
. sc iencedi rec t .com
ava i lab le at wwwjournal homepage: www.elsevier .com/ locate /carbon
Growth kinetics of MWCNTs synthesized by acontinuous-feed CVD method
Illayathambi Kunadiana, Rodney Andrewsa,*, Dali Qiana, M. Pinar Mengucb
aCenter for Applied Energy Research, University of Kentucky, 2540 Research Park Drive, Lexington, KY 40511-8410, USAbDepartment of Mechanical Engineering, University of Kentucky, 269 Ralph G. Anderson Building, Lexington, KY 40506, USA
A R T I C L E I N F O
Article history:
Received 14 January 2008
Accepted 7 October 2008
Available online 1 November 2008
0008-6223/$ - see front matter � 2008 Elsevidoi:10.1016/j.carbon.2008.10.022
* Corresponding author: Fax: +1 859 257 0220E-mail address: [email protected] (R
A B S T R A C T
Unlike two-step chemical vapor deposition (CVD) methods using pre-deposited catalyst
particles, in a continuous-feed CVD process, the liquid feed (consisting of catalytic precur-
sor and hydrocarbon source) is continuously supplied into the reactor causing catalyst par-
ticle formation, nucleation of carbon nanotubes (CNTs) and CNT growth to occur
simultaneously throughout the reaction period. In order to observe these processes, CVD
experiments were conducted for different durations (30 s to 3 h) and the product multi-
walled carbon nanotubes (MWCNTs) were characterized using scanning electron micros-
copy. It was found that the nanotubes did not grow in the vapor phase and that
substrates played an important role in the growth by providing a place for them to anchor
before growth took place. Based on transmission electron microscopy images, it has been
suggested that MWCNTs grew by root-growth mechanism from the catalyst particles that
were deposited on the substrate during the early stages. At long process times, continu-
ously supplied feed gas produced additional catalyst particles which were deposited mostly
on the growing nanotube mat. Due to weak catalyst–mat interaction, the additional nano-
tubes grew by tip growth. A comprehensive MWCNT growth model has been presented for
the continuous-feed CVD.
� 2008 Elsevier Ltd. All rights reserved.
1. Introduction
The study of the growth of carbon nanotubes started with the
study of growth of carbon filaments in the 1970s [1–3]. The
growth of carbon nanotubes and the type of carbon nano-
tubes (SWCNT or MWCNT) synthesized differs significantly
depending on the synthesis method used due to different
growth environments. Consequently, several growth mecha-
nisms have been proposed [4–9]. A number of theories have
been postulated for SWCNT growth, some from vapor phase
[10–12] and others from a condensed phase [13,14], with
either tip-growth [15,16] or root growth [13,14,17,18]. The
structure of the SWCNTs produced was found to be depen-
er Ltd. All rights reserved
.
. Andrews).
dent on the growth parameters such as reaction time, furnace
temperature, catalyst particles, promoters (S, Bi, or Pb), and
reaction gas [4,19,20].
Several groups [4,5,21–28] have studied the growth of well-
aligned MWCNT mats by CVD in an attempt to optimize the
process parameters. Sinnott et al. [4] have claimed formation
and growth of MWCNTs via CVD to be an extension of the
process described by Baker [2] and suggested a tip-growth (de-
tached particle) model for the growth of MWCNTs based on
transmission electron microscopy (TEM) images. Qian [5] sug-
gested a combined root-growth and tip-growth model for the
growth of MWCNTs via CVD. One theory has claimed sequen-
tial growth of various shells of the MWCNTs [29,30] where
.
C A R B O N 4 7 ( 2 0 0 9 ) 3 8 4 – 3 9 5 385
each following nanotube shell was formed by carbon adsorp-
tion at the previous shell surface. Still, another theory has
suggested simultaneous growth of the tube shells [31]. Vari-
ous studies have shown that the diameter and length of the
nanotubes depend on the size of the initial catalyst particles
formed on the substrates [4,5,32,33]. Studies have also shown
that the electric field influences the alignment of carbon
nanotubes [34,35].
Over the years, the growth of CNTs has been studied
extensively using several approaches. In situ observation of
the nanotube growth has been made by using an environ-
mental transmission microscope [36]. These tools are imprac-
tical to use due to high equipment cost and harsh operating
temperatures that could damage any diagnostic tool. They
may require major modifications to the existing experimental
setup. Optical characterization techniques based on laser-
beam attenuation and scattering [34,37] have also been used
in situ during the synthesis of the carbon nanotubes. Geohe-
gan et al. have used Febry–Perot interference fringes and
attenuation of a reflected HeNe laser beam to study the
growth rates and kinetics of MWCNT arrays [37]. Due to opti-
cal limitations, the system is not capable of capturing the
early stages of the growth of nanotubes. Computer simula-
tions like molecular dynamics simulations [8,38–41], and
computational fluid dynamics [42–44] have been used to mod-
el the CNT growth from the catalyst particles.
The growth of the CNTs has been successfully studied
using ex situ characterization of the product CNTs via electron
microscopy [4–9,15,32,33,35,45–49]. Fan et al. have predicted
the growth of CNT array using carbon isotope labeling method
involving labeling the nanotube array with tracing chemicals
and then detecting the isotope compositions of each section
in the nanotubes by a micro-Raman after growth [46]. Com-
pared to other methods, ex situ characterization techniques
are more cost effective for monitoring CNT growth because
this method allows for conducting CVD experiments using
available equipment.
Most of the existing growth models describe the CNT
growth mechanism for the two-step CVD method. However,
the continuous-feed CVD growth mechanism is more compli-
cated than the two-step CVD method because catalyst parti-
cle formation, nucleation of CNTs and their growth all take
place simultaneously throughout the reaction period as the li-
quid feed (consisting of catalytic precursor and hydrocarbon
source) is continuously fed into the reactor. It is possible to
control the diameter of the nanotubes grown via two-step
CVD by controlling the diameter of the pre-deposited catalyst
particles. In contrast to this, in a continuous-feed CVD, it is al-
most impossible to control the diameter of the nanotubes
grown due to lack of methods to control the diameter of the
catalyst particles generated in the reactor. The growth models
available for the continuous-feed CVD method [2,4,47,50–52]
do not contain sufficient experimental evidence of the inter-
mediate stages that lead to the formation of MWCNT-mat. It
is also unclear whether the nanotubes were initially formed
in the gas phase or if the substrates played a role on the for-
mation of aligned carbon nanotubes.
This paper describes the various stages of growth of
MWCNTs starting from catalyst particle formation, then
MWCNT formation from catalyst particles, MWCNT growth
and organization to form regular arrays of aligned MWCNT-
mats on the surface of a quartz substrate. The experimental
work was accomplished by conducting CVD runs at different
reaction times and performing ex situ characterization of the
products later. Gas chromatography (GC) was performed on
the exhaust gas samples in order to study the major hydrocar-
bons produced. The results were compared with those avail-
able for the CVD method using pre-deposited catalyst particles.
2. Experimental setup and procedure
The CVD experiments were conducted using the same reactor
system previously described by Andrews et al. [25]. The feed
solution consisted of ferrocene which was used as the precur-
sor for producing Fe catalyst particles and xylene which was
used as the hydrocarbon source. Approximately 6.5 mol% of
ferrocene was dissolved in xylene to obtain feed solution with
�0.75 at% Fe/C ratio. The liquid feed was pumped into the pre-
heater zone of the two-stage reactor where it was preheated to
�240 �C prior to its entry into the furnace. The liquid was
immediately volatilized and swept into the reaction zone of
a furnace maintained at 700 �C, under a reducing atmosphere
(90% Ar/10% H2). The reactor was operated at a modest over-
pressure, 250 Pa, at all times to prevent any oxygen influx.
The experiments were conducted at different reaction times
starting from the point where the feed gas just entered
the reaction zone to about 3 h afterward. The MWCNTs were
grown on small quartz substrates (1 cm · 1 cm) which were
placed in the furnace area of the tubular reactor. The sub-
strates were removed at the end of the reaction and were later
characterized using SEM.
3. Experimental results
Fig. 1a shows the SEM images of the MWCNTs grown at differ-
ent reaction times: initial, 30 s, 1 min, 3, 5, and 15 min. The
term ‘‘initial’’ denotes the period when the feed gas just en-
tered the reaction zone of the CVD reactor. The injection of
the feed stock material was immediately stopped and the
reactor was purged with Argon. The reactor was left to cool
down while the quartz substrate on which the reaction prod-
ucts were formed was removed and characterized using SEM.
CVD experiments were then repeated at different reaction
times. The reaction times were calculated immediately after
the feed gas entered the reactor.
3.1. Initial stages of MWCNT growth
During the initial stage, small particles were observed spar-
sely deposited on the surface of the substrate. The size of
these particles ranged from 20 to 100 nm, coinciding with
the various outer diameters of the nanotubes as shown in
previous studies [4,5,25,32,33]. This variability of the sizes of
the Fe catalyst particles deposited accounts for the wide
range of CNT diameters observed. At this stage, the chemical
composition of the catalyst particles could not be evaluated
due to the extremely small sizes of the particles. Regardless,
even when the Fe catalyst particles had some carbon content,
they did not possess any filamentous structure.
Fig. 1 – (a) SEM images of MWCNT growth and (b) plot of MWCNT and catalyst particle count on substrate surface with
change in reaction time.
386 C A R B O N 4 7 ( 2 0 0 9 ) 3 8 4 – 3 9 5
At 30 s, the substrate was covered densely with free cata-
lyst particles. Some short nanotubes that could have nucle-
ated from the metal catalyst particles were also observed.
After the first minute of the process, the substrate was den-
sely covered with particles and sparsely covered with nano-
tubes of different lengths. This indicated that while catalyst
particles were being deposited on the substrate, some
MWCNTs began to nucleate from the catalyst particles and
others that had already nucleated began to grow longer. At
3 min, MWCNTs appear to have grown in random directions
on the substrate due to low carbon nanotube areal densities.
Some catalyst particles also were found on the substrate,
which indicated that particle deposition was still taking place
at that stage. At 5 min, most of the substrate area was covered
with nanotubes. As the areal number density increased,
growth in random directions ceased and the MWCNTs were
forced to grow vertically, perpendicular to the substrate due
to geometric constraints. (Einarsson et al. have reported that
vertical growth of SWCNTs was caused when the density of
the nanotube array impeded the growth in all directions par-
allel to the substrate surface [45]). At 15 min, the entire sub-
strate area was covered with MWCNTs. Some catalyst
particles deposited on top of the growing MWCNTs and
formed additional tubes. As the reaction time progressed,
the array density and the thickness of the mat continued to
increase.
Fig. 1b shows the number of carbon nanotubes and metal
catalyst particles counted in a square area on the surface of
the substrates plotted against the reaction time. The catalyst
particles illustrated here refers to the free Fe catalyst particles
which had not become part of the growing MWCNTs. The par-
ticle count was higher than the nanotube count during the
initial time indicating that the deposition of metal particles
took place before the formation of MWCNTs. The nanotube
count increased while the free particle count on the surface
of the substrate dropped steadily. This could mean that the
C A R B O N 4 7 ( 2 0 0 9 ) 3 8 4 – 3 9 5 387
metal particles that were deposited on the surface of the sub-
strate became part of the MWCNTs that nucleated from them.
The number of free catalyst particles decreased to zero once
all the particles were used up to form MWCNTs and there
was no room left on the substrate for further deposition of
metal particles. Particle deposition continued to take place
on top of the growing MWCNTs.
3.2. Role of substrate on the growth of MWCNTs
Fig. 2 shows MWCNTs grown on a quartz substrate that was
non-uniformly sputter coated with gold. It was observed that
the MWCNTs did not grow on the gold surface but grew from
quartz surfaces beneath the gold layer as if their bases were
anchored to the quartz substrate. This indicated that there
must have been some strong interaction between the
MWCNTs and the substrate, possibly when the catalyst parti-
cles were deposited during the initial stages. Once the catalyst
particles established a bond with the substrate, the carbon
nanotubes nucleated and grew from them. If the MWCNTs
were formed in the vapor phase, they would have appeared
lying on top of the gold surface. This confirmed the hypothe-
sis that carbon nanotube growth does not take place in the
vapor phase and that the substrate played an important role
in the initiation of nanotube growth [25]. Li et al. [17] have also
shown the importance of the presence of a solid substrate
interface for the growth of carbon nanotubes.
3.3. Transmission electron microscopy of MWCNTs
Transmission electron microscopy (TEM) and high resolution
transmission electron microscopy (HRTEM) were performed
on the MWCNTs (Fig. 3) in order to determine the mecha-
nisms that governed the growth process. The TEM/HRTEM
images revealed that a majority of the MWCNTs contained
Fig. 2 – SEM images of MWCNT growth on quartz su
catalyst particles at the root end. The MWCNTs with catalyst
particles at the root end likely grew from the catalyst particles
that were deposited on the substrate during the initial stages
where catalyst–substrate interaction was highly favorable.
The catalyst particles at the root end exhibited a neck like re-
gion and traces of the catalyst were found along the inner
core of the tubes (Fig. 3a). As shown in Fig. 3c, some MWCNTs
did not contain catalyst particles due to losses from scraping
the nanotubes off the substrate prior to microscopy. The
growing end of the nanotube exhibited a closed-capped struc-
ture which is known to be energetically more stable than
open-ended structures [39]. Catalyst particles were also ob-
served on the tip–end of the nanotubes. These nanotubes
with catalyst particles at the tip end likely grew from catalyst
particles that were deposited at a later stage on top of the
growing nanotube mat. The weaker catalyst interaction with
the nanotube mat likely caused the nanotubes to grow by
tip-growth. Additionally, catalyst particles were observed on
the tip and root ends of the nanotubes. Perhaps this was
caused by the splitting of catalyst particles: while the lower
part of the catalyst was firmly attached to the substrate the
upper part was lifted off along with the growing end of the
nanotube. This theory is supported by the presence of traces
of catalyst particles observed along the inner core of the
tubes. Secondary branching of the nanotubes was also ob-
served arising from the splitting of catalyst particles present
at the growing end of the nanotubes.
3.4. Growth of MWCNT mats with reaction time
Fig. 4 shows SEM images of MWCNT mats grown at different
reaction times taken at 65� angle from the surface of the sub-
strate. The thickness of the mat increased steadily with reac-
tion time. The MWCNTs were well aligned in the vertical
direction perpendicular to the substrate [5]. They appeared
bstrate non-uniformly sputter coated with gold.
Fig. 3 – TEM/HRTEM images of MWCNTs: (a) catalyst at root end with neck region, black arrows showing catalyst inclusions
within the tube core, (b) catalyst at root, (c) open-ended root-end with catalyst removed, (d) and (e) closed-capped growing tip
end, (f) catalyst particle at tip end, (g) catalyst particle at tip and root ends, (h) and (i) secondary-branching of nanotubes,
arrows show catalyst inclusions within tube core.
388 C A R B O N 4 7 ( 2 0 0 9 ) 3 8 4 – 3 9 5
to be tilted to the left in the SEM images due to displacement
where lines were marked on the substrate using a scriber. The
MWCNTs appeared to be randomly oriented on the top sur-
face of the mat which may have been due to two reasons: (i)
during the initial stages of growth, the low array density
caused the nanotubes to grow in random directions on the
substrate. As the reaction time progressed, nanotube crowd-
ing forced the nanotubes to grow in an aligned manner per-
pendicular to the substrate that carried the coiled
nanotubes above it (as described by Fan et al. [46]); (ii) the con-
tinuous supply of feed gas produced additional catalyst parti-
cles that deposit randomly on the growing nanotubes and
grew into randomly oriented nanotubes on the surface of
the nanotube mat.
Three separate growth experiments were conducted at dif-
ferent reaction times and the average thickness of the
MWCNT mat was measured and plotted against the reaction
time (Fig. 5). The maximum variability in the mat thickness
was less than 5 lm, which showed the consistency of our
CVD experiments. The mat growth rate curve exhibited a sig-
moidal shape, although different in magnitude, as previously
obtained by Baker [2]. The growth curve showed an initial
acceleration period, a constant growth period and a final
slowing-down period. A sudden burst in the mat growth dur-
ing the initial acceleration period may have been due to the
availability of optimal conditions that were conducive for
the growth of CNTs such as temperature, open areas on the
substrate, and feed gas concentration. The final slowing-
down period may have been caused either when the substrate
became saturated with CNTs or when the catalyst particles
were completely covered with carbon layers. This conclusion
was based on the assumption that the root-growth
Fig. 4 – SEM images of growth of MWCNT mat at different reaction times: 5, 10, 20, 30, 60 and 180 min.
Fig. 5 – Growth rate curve of MWCNT mat.
C A R B O N 4 7 ( 2 0 0 9 ) 3 8 4 – 3 9 5 389
mechanism dominated the growth process of MWCNTs and
the growth of nanotubes via tip-growth (from the catalyst par-
ticles that were deposited on the growing mat) was relatively
insignificant.
3.5. Deposition pattern of MWCNTs across the CVDreactor
MWCNT deposition pattern across the CVD reactor was inves-
tigated by taking SEM images in the radial direction (x-axis) of
the substrate and the number of particles and nanotubes per
square area at different locations on the substrate were plot-
ted as shown in Fig. 6. It was observed that the catalyst parti-
cle and MWCNT number density was greater at the center
than in the region close to the walls of the CVD reactor. Com-
mercially available computational fluid dynamics (CFD) soft-
ware, Fluent 6.3, was used to investigate the velocity profiles
43
2
1
5
6
7
Middle
Left Extreme Right Extreme
x
y
z
(a)
6µm 6µm
6µm
6µm
6µm
6µm
6µm
0
10
20
30
40
50
60
1 2 3 4 5 6 7
Cou
nt (
#)
Location across reactor
Catalyst particlesMWCNTs
(b)
0
0.1
0.2
0.3
0.4
0.5
1 2 3 4 5 6 7
Velo
city
(m
/s)
Location across reactor
(c)
Fig. 6 – (a) SEM images of MWCNTs in the radial direction of the reactor. Catalyst particles and MWCNTs are denser in middle
than toward the extreme edges in the x-direction of the reactor, (b) MWCNT and catalyst particle count at different location in
the radial direction of the reactor. MWCNT and particle count is maximum in the center and decreases toward the reactor
walls, (c) velocity magnitude (m/s) of feed gas generated by CFD analysis: velocity is maximum at the center and decreases
toward the walls.
390 C A R B O N 4 7 ( 2 0 0 9 ) 3 8 4 – 3 9 5
of the feed gas inside the CVD reactor. The fluid dynamics
model adopted was based on 2-D, laminar, steady-state flow
with both gas-phase and surface chemical reactions. The in-
let gas velocity (�1.5 m/s) used in the CFD calculations was
based on the flow rate of argon (675 sccm) and hydrogen
(75 sccm) and the feed rate of xylene/ferrocene mixture
(1 ml/h). The velocity contours of the feed gas inside the
CVD reactor predicted by CFD calculations (Fig. 6c) indicated
that the feed gas velocity attained a maximum value at the
center of the reactor and decreased to zero at the walls. Since
the availability of feed material acted as the driving force for
the diffusion of carbon into the catalyst particles leading to
CNT growth, higher feed gas velocity in the center of the reac-
tor could have led to the increase in the CNT formation in that
zone when compared to the region that was closer to the
walls.
3.6. Analysis of exhaust gas using gas chromatography
The exhaust gases from the CVD reactor that used both the
two-step CVD method and the one with continuous-feed each
were collected at different reaction times (5, 15, 40 and
60 min) using gas bags and were submitted for GC analysis
for measurement of CmHn concentration. Mass spectra analy-
sis of the exhaust gas from the CVD method with pre-depos-
ited catalyst particles (Fig. 7a) showed that the larger C8H10
and C7H8 accounted for more than 94% of the total hydrocar-
bon molecules in the tail gas. However, the concentrations of
smaller molecules including benzene, methane and propane
were only about 6% in the tail gas. The analysis of the gas
samples collected from the continuous-feed CVD method
(Fig. 7b) showed that the larger C8H10 and C7H8 molecules ac-
counted for about 80% of the total hydrocarbon molecules in
0
20
40
60
80
100
0
Com
poun
d (w
t.%)
Reaction Time (Minutes)
Xylene TolueneXylene MethaneBenzene Propane
(a)
0
20
40
60
80
100
Com
poun
d (w
t%)
Reaction Time (minutes)
m+p-Xylene TolueneMethane Benzeneo-Xylene EthylbenzeneButane Ethane
(b)
20 40 60
0 20 40 60
Fig. 7 – CnHm molecule concentration in the tail gas from: (a)
a two-step CVD method involving pre-deposited catalyst
particles and (b) continuous-feed CVD method measured by
a mass spectrometer at different reaction times.
C A R B O N 4 7 ( 2 0 0 9 ) 3 8 4 – 3 9 5 391
the tail gas which indicated that about 20% of the larger mol-
ecules were converted into smaller molecules. This difference
signified greater catalytic activity during the continuous CVD
process, whether on the surface, or, in the gas phase.
4. Comprehensive growth model
Based on the SEM, TEM, and HRTEM images of the MWCNTs
synthesized by the continuous-feed CVD method the follow-
ing growth mechanisms have been proposed as shown in
Fig. 8.
4.1. Root-growth mechanism
The first step in the growth of nanotubes involves the thermal
decomposition of ferrocene to produce clusters of Fe atoms.
During the initial stages, the open areas on the quartz sub-
strate favor strong catalyst–substrate interactions, and fea-
ture growth by the root-growth mechanism as shown in
Fig. 8a. The pyrolysis of xylene produces carbon atoms which
are extremely mobile on metal surfaces leading to rapid diffu-
sion over and through the metal particles. Carbon diffuses
along the concentration gradient and precipitates crystalline
graphite around and below the bisecting diameter of the cat-
alyst particles. The basal planes of the graphite crystallites
are oriented tangential to the curved surface of the catalyst
particle [4] (the details of the crystallographic structure and
orientation of the iron catalyst particles encapsulated in the
CNTs can be obtained elsewhere [44]). The large radius of cur-
vature resulting from the extremely small diameters of the
metal particles imposes a large strain on the basal planes of
the crystallites forcing them to take the continuous filamen-
tous surface form of the carbon nanotubes. Several concen-
tric cylindrical structures are formed in a nested fashion
from the catalyst particle. Since the basal planes of the graph-
ite crystallites are oriented tangential to the curved surface of
the catalyst particle, at a critical radius of curvature of the ex-
posed catalyst particle, further formation of a cylindrical
structure becomes almost impossible due to a significant in-
crease in the strain of the basal planes. This results in the for-
mation of a hollow core in the interior of the MWCNTs.
As the reaction progresses, the dissociated Fe atoms may
diffuse into the old catalyst particles that are part of the grow-
ing tubes resulting in an increase in the diameter of the cata-
lyst particles. As more carbon atoms diffuse into these
enlarged catalyst particles, additional tube walls may be
formed resulting in coarsening of the nanotube near the
root-end. While this portion of the nanotube is being ex-
truded, if the catalyst particle continues to increase in diam-
eter, the nanotube near the base will broaden a little more
with a diameter slightly greater than the region above it. As
these sequence of events are repeated tapered nanotube
structures are formed [5]. The growing end of the MWCNTs
exhibits a closed-capped structure due to the high dangling
bond energy required to keep it open (it has been theoretically
shown that the closed-capped form of nanotube growth is
energetically more favorable than the open-ended growth
[39]). As the nanotube increases in length the catalyst particle
at the root initially forms a neck which breaks off leaving
traces of catalyst particles within the inner core of the tubes
as evident in the TEM/STEM images in Fig. 3. The growth of
these nanotubes stops when the catalyst particle is com-
pletely covered with layers of carbon. The encapsulation of
the carbon nanotubes with catalyst particles has also been
shown by previously by Xiang et al. [18]. They have shown
that the bottom ends of the carbon nanotubes act as active
growth sites and the entrained catalyst particles move bot-
tom–up as the nanotubes increase in length [18].
4.2. Tip-growth mechanism
The growing nanotube mat may also act as a substrate for
nanotube growth. The tip-growth may occur from the newly
formed catalyst particles that are deposited on the growing
nanotube mat as shown in Fig. 8b. The weak interaction of
the catalyst particles with the nanotube mat causes the cata-
lyst particles to lift off with the concentric cylindrical struc-
tures formed below it. As explained earlier, at the critical
radius of curvature of the catalyst particle, further formation
of cylindrical structures is prevented and a hollow core is pro-
duced. With the base of the nanotube anchored to the nano-
tube mat, the tip carrying the catalyst particle grows toward
the region of higher feed gas concentration (this type of
growth is also referred to as the ‘‘kite mechanism’’ in which
the active end of the nanotube floats while the section close
to the original site where the catalyst was deposited forms
the van der Waals contacts with the substrate [6]). The diffu-
sion of carbon and Fe atoms takes place through the exposed
Fig. 8 – Schematic of (a) root growth: (I) Fe catalyst particle formation, (II) diffusion of carbon into catalyst, (III) formation of
nested MWCNT structure, (IV) enlargement of catalyst particle, (V) formation of neck and trapping of catalyst inside nanotube
core, (VI) catalyst covered with carbon layers and growth stoppage; (b) tip growth: (I) Deposition of Fe catalyst particle on
growing mat, (II) diffusion of carbon into catalyst, (III) lift-off of catalyst particle due to weak interaction with mat, (IV)
diffusion of Fe atoms on exposed end of catalyst, (V) catalyst covered with carbon layers and growth stoppage; and (c)
combined root-tip-growth mechanisms: (I) Fe catalyst particle formation, (II) diffusion of carbon into catalyst, (III) splitting of
catalyst particle, (IV) upper portion of catalyst particle carried away on growing tip of nanotube, (V) catalyst covered with
carbon layers and growth stoppage or (V(a) and (b)) further splitting of catalyst particle and formation of secondary branches.
392 C A R B O N 4 7 ( 2 0 0 9 ) 3 8 4 – 3 9 5
portion of the catalyst particle. As the catalyst particle moves
away from the mat, a portion of the catalyst breaks off and
gets trapped within the inner core of the tube. The tip growth
stops when the catalyst particle is covered with carbon layers
or when the supply of feed gas is cut off.
4.3. Combined root-tip-growth mechanism
Larger catalyst particles form as a result of agglomeration of
smaller catalyst particles. The combined root-tip-growth re-
sults from the splitting of these larger catalyst particles
(Fig. 8c). With the lower portion of the catalyst firmly an-
chored to the quartz substrate, the upper portion breaks away
from the original catalyst and is lifted off along with the grow-
ing end of the nanotube. This sort of growth favors elongation
of the nanotubes. The growth of the nanotube stops when the
catalyst particle is completely covered with carbon layers.
Alternatively, additional Fe atoms could diffuse into the ex-
posed catalyst particle and cause it to enlarge. The catalyst
particle eventually splits and gives rise to secondary
branches. Certain portions of the catalyst particle break off
and get trapped within the inner core of the tubes.
4.4. Sequence of growth events on the substrate
Since the feed material is continuously supplied throughout
the reaction period in a continuous-feed CVD reactor, the for-
mation of the catalyst particles followed by the formation of
MWCNTs take place throughout the reaction period making
the growth process on the surface of the substrate chaotic.
Using SEM images and previous experimental observations,
a sequence of growth events is presented in Fig. 9. As ob-
served in the SEM images, the deposition of catalyst particles
takes place first. This is followed by the nucleation of carbon
nanotubes via diffusion of carbon atoms into the catalyst par-
ticles. With a lot of empty surface area on the substrate, the
Fig. 9 – Sequence of events of the growth of MWCNTs on the
quartz substrate in a continuous-feed CVD process: (a)
random deposition of metal catalyst particles of different
diameters on the substrate, (b) nucleation of carbon
nanotubes by diffusion of carbon atoms into the deposited
catalyst particles and further deposition of catalyst particles,
(c) random growth of MWCNTs via root-growth; catalyst
particle enlargement leading to tube coarsening near root-
end; catalyst particle-splitting, (d) crowding of MWCNTs
leading to vertical alignment; deposition of new particles on
the growing mat, part of catalyst carried away on the
growing end of the tubes, branching of tubes from catalyst
particles that were carried away on growing end, (e)
MWCNTs grow by ‘‘tip-growth’’ from catalyst particles
deposited on growing nanotube mat; vertically-aligned
MWCNT-mat.
C A R B O N 4 7 ( 2 0 0 9 ) 3 8 4 – 3 9 5 393
catalyst particles are generously deposited on the substrate
and establish a strong interaction with the quartz substrate,
favoring nanotube growth via root-growth mechanism. Ini-
tially, the nanotubes are sparsely distributed and grow in ran-
dom directions on the substrate. While the nanotubes
continue to grow in the axial direction, the tube walls close
to the catalyst particles begin to coarsen via epitaxial growth
leading to the formation of taper-shaped nanotubes [5]. The
continuously supplied feed gas produces more clusters of Fe
atoms. The crowding of the nanotubes prevents these newly
formed catalyst particles from reaching the substrate. These
catalyst particles get deposited randomly on the growing
mat and grow via tip-growth due to weaker interaction with
the mat. The larger catalyst particle split and the growing
nanotube carries a portion of the catalyst on the tip end. A
portion of the catalyst splits further and gives rise to addi-
tional branches. As the nanotube number density increases,
they begin to align themselves into regular arrays in the ver-
tical direction perpendicular to the substrate carrying the
coiled nanotubes on the growing end of the mat.
5. Conclusions
The various events that take place on the substrate starting
from the formation of catalyst particles to the evolution of
MWCNT-mats have been successfully studied using ex situ
characterization methods. Based on the SEM images during
the initial stages of growth, it has been shown that the
MWCNTs do not appear to have grown in the vapor phase
and that substrate played an important role in the nucleation
of the nanotube by providing an anchorage point for the nano-
tubes during growth. During the initial stages, the open areas
in the substrate made it possible for generous deposition of
free catalyst particles on the substrate and for strong cata-
lyst–substrate interaction. This led to the majority of the
growth to take place by root-growth. As the substrate filled in
with nanotubes and the availability of open areas on the sub-
strate decreased, the newly formed catalyst particles were
deposited on the growing nanotube mat. The weak catalyst
interaction with the mat forced the catalyst particles to lift
off while the MWCNT bases remained anchored to the mat in
a tip-growth mechanism. Geometric constraints forced the
nanotubes to grow vertically, perpendicular to the substrate.
The catalyst particles that were carried away on the grow-
ing tip of the nanotubes led to tube elongation and formation
of secondary branches. As predicted by CFD, higher flows at
the center led to increased surface diffusion. This led to in-
creased MWCNT deposition in the center compared to regions
close to the walls that had been observed in the experimental
results. The comprehensive growth model developed in this
work is expected to help researchers to have a better under-
standing of the growth of MWCNTs synthesized via continu-
ous-feed CVD and also to possibly achieve better control of
the diameter, length and quality of synthesized products
which might be used in different fields of nanotechnology.
R E F E R E N C E S
[1] Tibbetts GG. Why are carbon filaments tubular? J CrystGrowth 1984;66(3):632–8.
[2] Baker RTK. Catalytic growth of carbon filaments. Carbon1989;27:315–23.
[3] Baker RTK, Harris PS. Formation of filamentous carbon. In:Walker PL, Thrower PA, editors. Chemistry and physics ofcarbon, vol. 14. New York: Decker; 1978. p. 83–165.
394 C A R B O N 4 7 ( 2 0 0 9 ) 3 8 4 – 3 9 5
[4] Sinnott SB, Andrews R, Qian D, Rao AM, Mao Z, Dickey EC,et al. Model of carbon nanotube growth through chemicalvapor deposition. Chem Phys Lett 1999;315:25–30.
[5] Qian D. Multiwalled carbon nanotube CVD synthesis,modification, and composite applications. Ph.D. Thesis, 2001,Lexington KY USA, University of Kentucky.
[6] Huang S, Woodson M, Smalley R, Liu J. Growth mechanism oforiented long single walled carbon nanotubes using ‘‘Fast-heating’’ chemical vapor deposition process. Nano Lett2004;4:1025–8.
[7] Vinciguerra V, Buonocore F, Panzera G, Occhipinti L. Growthmechanisms in chemical vapor deposited carbon nanotubes.Nanotechnology 2003;14:655–60.
[8] Gavillet J, Loiseau A, Ducastelle F, Thair S, Bernier P, StephanO, et al. Microscopic mechanisms for the catalyst assistedgrowth of single-walled carbon nanotubes. Carbon2002;40:1649–63.
[9] Lee CJ, Park J. Growth model of bamboo-shaped carbonnanotubes by thermal chemical vapor deposition. Appl PhysLett 2000;77:3397–9.
[10] Guo T, Nikolaev P, Thess A, Colbert DT, Smalley RE. Catalyticgrowth of single-walled nanotubes by laser vaporization.Chem Phys Lett 1995;243:49–54.
[11] Bernholc J, Brabec C, Buongiorno Nardelli M, Maiti A, RolandC, Yakobson BI. Theory of growth and mechanical propertiesof nanotubes. Appl Phys A 1998;67(1):39–46.
[12] Maiti A, Brabec CJ, Roland CM, Bernholc J. Growth energeticsof carbon nanotubes. Phys Rev Lett 1994;73(18):2468–71.
[13] Yudasaka M, Yamada R, Sensui N, Wilkins T, Ichihashi T,Iijima S. Mechanism of the effect of NiCo, Ni and Co catalystson the yield of single-wall carbon nanotubes formed bypulsed Nd: YAG laser ablation. J Phys Chem B1999;103(30):6224–9.
[14] Kanzow H, Ding A. Formation mechanism of single-wallcarbon nanotubes on liquid–metal particles. Phys Rev B1999;60(15):11180–6.
[15] Lee YH, Kim SG, Tomanek D. Catalytic growth of single-wallcarbon nanotubes: an ab initio study. Phys Rev Lett1997;78:2393–6.
[16] Maiti A, Brabec CJ, Bernholc J. Kinetics of metal-catalyzedgrowth of single-walled carbon nanotubes. Phys Rev B1997;55(10):6097–100.
[17] Li X, Cao A, Jung YJ, Vajtai R, Ajayan PM. Bottom–up growth ofcarbon nanotube multilayers: unprecedented growth. NanoLett 2005;5(10):1997–2000.
[18] Xiang R, Luo GH, Qian WZ, Zhang Q, Wang Y, Wei F, et al.Encapsulation, compensation, and substitution of catalystparticles during continuous growth of carbon nanotubes. AdvMater 2007;19(17):2360–3.
[19] Choi YC. Controlling the diameter, growth rate, and densityof vertically aligned carbon nanotubes synthesized bymicrowave plasma-enhanced chemical vapor deposition.Appl Phys Lett 2000;76(17):2367.
[20] Kiang CH. Growth of large-diameter single-walled carbonnanotubes. J Phys Chem A 2000;104(11):2454–6.
[21] Singh C, Shaffer MSP, Koziol KKK, Kinloch IA, Windle AH.Towards the production of large-scale aligned carbonnanotubes. Chem Phys Lett 2003;372(5–6):860–5.
[22] Mayne M, Grobert N, Terrones M, Kamalakaran R, Ruhle M,Kroto HW, et al. Pyrolytic production of aligned carbonnanotubes from homogeneously dispersed benzene-basedaerosols. Chem Phys Lett 2001;338(2–3):101–7.
[23] Vivekchand SRC, Cele LM, Deepak FL, Raju AR, Govindaraj A.Carbon nanotubes by nebulized spray pyrolysis. Chem PhysLett 2004;386(4–6):313–8.
[24] Cao A, Ci L, Wu G, Wei B, Xu C, Liang J, et al. Effective way tolower catalyst content in well-aligned carbon nanotube films.Carbon 2001;39(1):152–5.
[25] Andrews R, Jacques D, Rao AM, Derbyshire F, Qian D, Fan X,et al. Continuous production of aligned carbon nanotubes: astep closer to commercial realization. Chem Phys Lett1999;303:467–74.
[26] Kamalakaran R, Terrones M, Seeger T, Kohler-Redlich P, RulheM, Kim YA, et al. Synthesis of thick and crystalline nanotubearrays by spray pyrolysis. Appl Phys Lett 2000;77:3385–7.
[27] Zhang X, Cao A, Wei B, Li Y, Wei J, Xu C, et al. Rapid growth ofwell-aligned carbon nanotube arrays. Chem Phys Lett2002;362(3–4):285–90.
[28] Zhang ZJ, Wei BQ, Ramanath G, Ajayan PM. Substrate-siteselective growth of aligned carbon nanotubes. Appl Phys Lett2000;77(23):3764–6.
[29] Amelinckx S, Zhang XB, Bernaerts D, Zhang XF, Ivanov V,Nagy JB. A formation mechanism for catalytically grownhelix-shaped graphite nanotubes. Science1994;265(5172):635–9.
[30] Amelinckx S, Bernaerts D, Zhang XB, Van Tendeloo G, VanLanduyt J. A structure model and growth mechanism formultishell carbon nanotubes. Science 1995;267(5202):1334–8.
[31] Saito Y, Yoshikawa T, Okuda M, Fujimoto N, Sumiyama K,Suzuki K, et al. Carbon nanocapsules engaging metals andcarbides. J Phys Chem Solids 1993;54(12):1849–60.
[32] Ducati C, Alexandrou I, Chhowalla M, Amaratunga GAJ,Robertson J. Temperature selective growth of carbonnanotubes by chemical vapor deposition. J Appl Phys2002;92:3299–303.
[33] Bower C, Zhou O, Zhu W, Werder DJ, Jin S. Nucleation andgrowth of carbon nanotubes by microwave plasma chemicalvapor deposition. Appl Phys Lett 2000;77:2767–9.
[34] Kim D-H, Jang H-S, Kim C-D, Cho D-S, Jee J-G, Lee H-R. In situoptical characterization of the alignment and density ofcarbon nanotubes. Nanotechnology 2003;14:46–9.
[35] Chhowalla M, Teo KBK, Ducati C, Rupesinghe NL,Amaratunga GAJ, Ferrari AC, et al. Growth processconditions of vertically aligned carbon nanotubes usingplasma enhanced chemical vapor deposition. J Appl Phys2001;90:5308–17.
[36] Sharma R, Rez P, Treacy MMJ, Stuart SJ. In situ observation ofthe growth mechanisms of carbon nanotubes under diversereaction conditions. J Electron Micros 2005;54(3):231–7.
[37] Geohegan DB, Puretzky AA, Ivanov IN, Jesse S, Eres G, HoweJY. In situ growth rate measurements and length controlduring chemical vapor deposition of vertically alignedmultiwall carbon nanotubes. Appl Phys Lett 2003;83:1851–3.
[38] Ding F, Rosen A, Bolton K. Molecular dynamics study of thecatalyst particle size dependence on carbon nanotubegrowth. J Chem Phys 2004;121:2775–9.
[39] Charlier JC, De Vita A, Blase X, Car R. Microscopic growthmechanisms for carbon nanotubes. Science1997;275(5300):646–9.
[40] Shibuta Y, Maruyama S. Molecular dynamics simulation offormation process of single-walled carbon nanotubes byCCVD method. Chem Phys Lett 2003;382(3–4):381–6.
[41] Ding F, Bolton K, Rosen A. Nucleation and growth of single-walled carbon nanotubes: a molecular dynamics study. J PhysChem B 2004;108(45):17369–77.
[42] Kuwana K, Endo H, Saito K, Qian D, Andrews R, Grulke EA.Catalyst deactivation in CVD synthesis of carbon nanotubes.Carbon 2005;43:253–60.
[43] Kuwana K, Saito K. Modeling CVD synthesis of carbonnanotubes: nanoparticle formation from ferrocene. Carbon2005;43:2088–95.
[44] Endo H, Kuwana K, Saito K, Qian D, Andrews R, Grulke EA.CFD prediction of carbon nanotube production rate in a CVDreactor. Chem Phys Lett 2004;387:307–11.
C A R B O N 4 7 ( 2 0 0 9 ) 3 8 4 – 3 9 5 395
[45] Einarsson E, Edamura T, Murakami Y, Igarashi Y, MaruyamaS. A growth mechanism for vertically aligned single-walledcarbon nanotubes. Therm Sci Eng 2004;12:77–8.
[46] Fan S, Liu L, Liu M. Monitoring the growth of carbonnanotubes by carbon isotope labeling. Nanotechnology2003;14:1118–23.
[47] Pinault M, Mayne-L’Hermite M, Reynaud C, Pichot V, LaunoisP, Ballutaud D. Growth of multiwalled carbon nanotubesduring the initial stages of aerosol-assisted CCVD. Carbon2005;43:2968–76.
[48] Banerjee S, Wong SS. In situ quantum dot growth onmultiwalled carbon nanotubes. J Am Chem Soc2003;125(34):10342–50.
[49] Fan X, Buczko R, Puretzky AA, Geohegan DB, Howe JY,Pantelides ST, et al. Nucleation of single-walled carbonnanotubes. Phys Rev Lett 2003;90:145501.
[50] Bladh K, Falk LKL, Rohmund F. On the iron-catalysed growthof single-walled carbon nanotubes and encapsulated metalparticles in the gas phase. Appl Phys A 2000;70:317–22.
[51] Nasibulin AG, Moisala A, Brown DP, Jiang H, Kauppinen EI.A novel aerosol method for single walled carbon nanotubesynthesis. Chem Phys Lett 2005;402:227–32.
[52] Nasibulin AG, Moisala A, Brown DP, Kauppinen EI. Carbonnanotubes and onions from carbon monoxide usingNi(acac)2 and Cu(acac)2 as catalyst precursors. Carbon2003;41:2711–24.