ee 5340 semiconductor device theory lecture 5 - fall 2009 professor ronald l. carter [email protected]
TRANSCRIPT
EE 5340Semiconductor Device TheoryLecture 5 - Fall 2009
Professor Ronald L. [email protected]
http://www.uta.edu/ronc
L 05 Sept 08
Second Assignment
• Please print and bring to class a signed copy of the document appearing at
http://www.uta.edu/ee/COE%20Ethics%20Statement%20Fall%2007.pdf
2
L 05 Sept 08 3
Classes ofsemiconductors• Intrinsic: no = po = ni, since Na&Nd << ni,
ni2 = NcNve-Eg/kT, ~1E-13 dopant level !
• n-type: no > po, since Nd > Na
• p-type: no < po, since Nd < Na
• Compensated: no=po=ni, w/ Na- = Nd
+ > 0
• Note: n-type and p-type are usually partially compensated since there are usually some opposite- type dopants
L 05 Sept 08 4
n-type equilibriumconcentrations• N ≡ Nd - Na , n type N > 0
• For all N,no = N/2 + {[N/2]2+ni
2}1/2
• In most cases, N >> ni, so
no = N, and
po = ni2/no = ni
2/N, (Law of Mass Action is al-
ways true in equilibrium)
L 05 Sept 08 5
p-type equilibriumconcentrations• N ≡ Nd - Na , p type N < 0
• For all N,po = |N|/2 + {[|N|/2]2+ni
2}1/2
• In most cases, |N| >> ni, so
po = |N|, and
no = ni2/po = ni
2/|N|, (Law of Mass Action is al-
ways true in equilibrium)
L 05 Sept 08 6
Intrinsic carrierconc. (MB limit)
• ni2 = no po = Nc Nv e-Eg/kT
• Nc = 2{2m*nkT/h2}3/2
• Nv = 2{2m*pkT/h2}3/2
• Eg = 1.17 eV - T2/(T+)
= 4.73E-4 eV/K = 636K
L 05 Sept 08 7
Drift Current
• The drift current density (amp/cm2) is given by the point form of Ohm LawJ = (nqn+pqp)(Exi+ Eyj+ Ezk), so
J = (n + p)E = E, where
= nqn+pqp defines the conductivity
• The net current is SdJI
L 05 Sept 08 8
Drift currentresistance• Given: a semiconductor resistor with
length, l, and cross-section, A. What is the resistance?
• As stated previously, the conductivity,
= nqn + pqp
• So the resistivity, = 1/ = 1/(nqn + pqp)
L 05 Sept 08 9
Drift currentresistance (cont.)• Consequently, since
R = l/AR = (nqn + pqp)-1(l/A)
• For n >> p, (an n-type extrinsic s/c)R = l/(nqnA)
• For p >> n, (a p-type extrinsic s/c) R = l/(pqpA)
L 05 Sept 08 10
Drift currentresistance (cont.)• Note: for an extrinsic semiconductor
and multiple scattering mechanisms, since
R = l/(nqnA) or l/(pqpA), and
(n or p total)-1 = i-1, then
Rtotal = Ri (series Rs)
• The individual scattering mechanisms are: Lattice, ionized impurity, etc.
L 05 Sept 08 11
Net intrinsicmobility• Considering only lattice scattering
only, , 11
is mobility total the
latticetotal
L 05 Sept 08 12
Lattice mobility
• The lattice is the lattice scattering mobility due to thermal vibrations
• Simple theory gives lattice ~ T-3/2
• Experimentally n,lattice ~ T-n where n = 2.42 for electrons and 2.2 for holes
• Consequently, the model equation is lattice(T) = lattice(300)(T/300)-n
L 05 Sept 08 13
Net extrinsicmobility• Considering only lattice and
impurity scattering
impuritylatticetotal
111
is mobility total the
L 05 Sept 08 14
Net silicon extrresistivity (cont.)• Since = (nqn + pqp)-1, and
n > p, ( = q/m*) we have
p > n
• Note that since1.6(high conc.) < p/n < 3(low conc.), so
1.6(high conc.) < n/p < 3(low conc.)
L 05 Sept 08 15
Ionized impuritymobility function• The impur is the scattering mobility
due to ionized impurities
• Simple theory gives impur ~ T3/2/Nimpur
• Consequently, the model equation is impur(T) = impur(300)
(T/300)3/2
L 05 Sept 08 16
Figure 1.17 (p. 32 in M&K1) Low-field mobility in silicon as a function of temperature for electrons (a), and for holes (b). The solid lines represent the theoretical predictions for pure lattice scattering [5].
L 05 Sept 08 17
Exp. (T=300K) modelfor P, As and B in Si1
L 05 Sept 08 18
Exp. mobility modelfunction for Si1
Parameter As P Bmin 52.2 68.5 44.9
max 1417 1414 470.5
Nref 9.68e169.20e162.23e17
0.680 0.711 0.719
ref
a,d
minpn,
maxpn,min
pn,pn,
N
N1
L 05 Sept 08 19
Carrier mobilityfunctions (cont.)• The parameter max models 1/lattice
the thermal collision rate
• The parameters min, Nref and model 1/impur the impurity collision rate
• The function is approximately of the ideal theoretical form:
1/total = 1/thermal + 1/impurity
L 05 Sept 08 20
Carrier mobilityfunctions (ex.)• Let Nd
= 1.78E17/cm3 of phosphorous, so min = 68.5, max = 1414, Nref = 9.20e16 and = 0.711. – Thus n = 586 cm2/V-s
• Let Na = 5.62E17/cm3 of boron, so min
= 44.9, max = 470.5, Nref = 9.68e16 and = 0.680. – Thus p = 189 cm2/V-s
L 05 Sept 08 21
Net silicon (ex-trinsic) resistivity• Since = -1 = (nqn + pqp)-1
• The net conductivity can be obtained by using the model equation for the mobilities as functions of doping concentrations.
• The model function gives agreement with the measured (Nimpur)
Figure 1.15 (p. 29) M&K Dopant density versus resistivity at 23°C (296 K) for silicon doped with phosphorus and with boron. The curves can be used with little error to represent conditions at 300 K. [W. R. Thurber, R. L. Mattis, and Y. M. Liu, National Bureau of Standards Special Publication 400–64, 42 (May 1981).]
L 05 Sept 08 22
L 05 Sept 08 23
Net silicon extrresistivity (cont.)• Since = (nqn + pqp)-1, and
n > p, ( = q/m*) we have
p > n, for the same NI
• Note that since1.6(high conc.) < p/n < 3(low conc.), so
1.6(high conc.) < n/p < 3(low conc.)
L 05 Sept 08 24
Net silicon (com-pensated) res.• For an n-type (n >> p) compensated
semiconductor, = (nqn)-1
• But now n = N Nd - Na, and the mobility must be considered to be determined by the total ionized impurity scattering Nd + Na NI
• Consequently, a good estimate is = (nqn)-1 = [Nqn(NI)]-1
Figure 1.16 (p. 31 M&K) Electron and hole mobilities in silicon at 300 K as functions of the total dopant concentration. The values plotted are the results of curve fitting measurements from several sources. The mobility curves can be generated using Equation 1.2.10 with the following values of the parameters [3] (see table on next slide).
L 04 Sept 04 25
L 05 Sept 08 26
References
1Device Electronics for Integrated Circuits, 2 ed., by Muller and Kamins, Wiley, New York, 1986.– See Semiconductor Device Fundamen-
tals, by Pierret, Addison-Wesley, 1996, for another treatment of the model.
2Physics of Semiconductor Devices, by S. M. Sze, Wiley, New York, 1981.