Download - TiO2 Photo Catalysis [Compatibility Mode]
![Page 1: TiO2 Photo Catalysis [Compatibility Mode]](https://reader034.vdocuments.site/reader034/viewer/2022051515/55262551550346126f8b4beb/html5/thumbnails/1.jpg)
1
TiO2 particles - Fundamentals and Applications as photocatalyst
Most information taken from TiO2 photocatalysis – Fundamentals and Applications by Akira Fujishima, Dr. Kazuhito Hashimoto, and Dr. Toshiya Watanabe
TiO2 particles
• Used in paints and cosmetics
• Consumption exceeds 3 million tons
• a semiconductor – can be chemically activated by light energy
• Paint chalking – stabilisers or/and additives are added to solve the problems
![Page 2: TiO2 Photo Catalysis [Compatibility Mode]](https://reader034.vdocuments.site/reader034/viewer/2022051515/55262551550346126f8b4beb/html5/thumbnails/2.jpg)
2
Synthesis and Functionalisation
EnvironmentEnergyHealth Care
17.5
cm
Nanomagnetite
Protective Layer
Magnetic Core
Antigen Detection
Shape Recognition
Biocompatibility
FluorescentSignaling
Linkers
WO3Pt/WO3
WO3
TiO2
TiO2
Clean Water
Fresh Air
Self cleaning super - surface
Renewable Energy
Harnessing Solar Energy through Photocatalysis
![Page 3: TiO2 Photo Catalysis [Compatibility Mode]](https://reader034.vdocuments.site/reader034/viewer/2022051515/55262551550346126f8b4beb/html5/thumbnails/3.jpg)
3
Photocatalyst
Self cleaning
Self sterilising
Decomposition by powerful oxidising action
light
TiO2
sun
Solar Induced Photocatalysis
• Need for ecologically clean chemical processes and technology - solar induced photocatalysis
• Low quantum efficiency- less than 1% of the input electrical energy is effectively utilised by UV-photocatalytic systems
.
![Page 4: TiO2 Photo Catalysis [Compatibility Mode]](https://reader034.vdocuments.site/reader034/viewer/2022051515/55262551550346126f8b4beb/html5/thumbnails/4.jpg)
4
• Two requirements:
Substance to be degraded need to be brought into contact with TiO2
Light needs to reach the surface
CB
VB
TiO2 Semiconductor Photocatalyst
UVOrganic matter oxidation
Org + h+ → Intermediates → CO2 + H2O
Org + OH• → Intermediates → CO2 + H2O
Hole
h+ + H2O → H+ + OH•
h+ + OH- → OH•
Electron
e- + O2→ O2-•
O2-• ⇒ OH•
Light less than 380nm
![Page 5: TiO2 Photo Catalysis [Compatibility Mode]](https://reader034.vdocuments.site/reader034/viewer/2022051515/55262551550346126f8b4beb/html5/thumbnails/5.jpg)
5
• Electrons and holes are generated
• For metals, these two are immediately recombined
• On semiconductors, they survive for longer periods of time
• Holes have greater oxidising power than the reducing power of the excited electrons.
• Destructive power is stronger than chlorine, ozone, hydrogen peroxide – so in theory it can decompose almost all hydrocarbon organic compounds to C, H, O
• Energy has been quantised - it means regardless of the intensity level – energy of each photon is the same
• Energy of photons of light – equivalent to greater than 30,000 oC in thermal energy
![Page 6: TiO2 Photo Catalysis [Compatibility Mode]](https://reader034.vdocuments.site/reader034/viewer/2022051515/55262551550346126f8b4beb/html5/thumbnails/6.jpg)
6
![Page 7: TiO2 Photo Catalysis [Compatibility Mode]](https://reader034.vdocuments.site/reader034/viewer/2022051515/55262551550346126f8b4beb/html5/thumbnails/7.jpg)
7
Germ Killer
• E.Coli
• Methicilin-resistant Staphylococcus aureus (MRSA) – resistant to most commonly used antibiotics
• Pseudomonas aeruginosa
• 1 hour illumination at 1000 lux – 99% of the three bacteria are killed
![Page 8: TiO2 Photo Catalysis [Compatibility Mode]](https://reader034.vdocuments.site/reader034/viewer/2022051515/55262551550346126f8b4beb/html5/thumbnails/8.jpg)
8
Antimicrobial Tiles
• TiO2 was applied onto the tiles by spray coating – The tile is then heated at 800oC.
• For tiles where the light is harder to reach –could deposit metal such as Ag (antimicrobial metal particles) onto the tiles . Ag metals could be deposited onto the TiO2 by illumination.
![Page 9: TiO2 Photo Catalysis [Compatibility Mode]](https://reader034.vdocuments.site/reader034/viewer/2022051515/55262551550346126f8b4beb/html5/thumbnails/9.jpg)
9
• After installing photocatalytic tiles –numbers of bacteria on the wall surfaces and number of airborne bacteria dropped.
• Could be used to reduce the unpleasant odour from public toilet facilities – (pets and rats)
• In addition to its antibacterial properties, it has the ability to combat viruses, molds and algae.
• Decomposing Endotoxin as well as killing the bacteria
• Endotoxin – toxin released when E.coli cells die – can cause more problems than E.coli itself
![Page 10: TiO2 Photo Catalysis [Compatibility Mode]](https://reader034.vdocuments.site/reader034/viewer/2022051515/55262551550346126f8b4beb/html5/thumbnails/10.jpg)
10
0
20
40
60
80
100
0 10 20 30 40 50 60
Time (min)
E.C
oli S
urvi
val (
%)
Dark (P25)
UV
P25
HPC
MPC
Self cleaning transparent glass
Development:
• Coating a transparent TiO2 thin film on glass
• When coated onto a common sheet glass (soda-lime glass) – activity drops
• WHY?????
![Page 11: TiO2 Photo Catalysis [Compatibility Mode]](https://reader034.vdocuments.site/reader034/viewer/2022051515/55262551550346126f8b4beb/html5/thumbnails/11.jpg)
11
TiO2
Sodium lime glass
SiO2Na+ Na+ Na+ Na+Na+ Na+
Na+ Na+ Na+
The one that works…………
Other examples
• Ventilation fan - 0.1mg/cm2/day – the use of black-light UV could decompose the grease to CO2.
• Tunnel light
• Exterior materials
![Page 12: TiO2 Photo Catalysis [Compatibility Mode]](https://reader034.vdocuments.site/reader034/viewer/2022051515/55262551550346126f8b4beb/html5/thumbnails/12.jpg)
12
Antifogging
Typical contact angle between water and inorganic materials, such as glass (20o to 30o)
• On a plastic – 70o to 90o
• On silicone resin and fluororesins – angle is higher than 90o
• Some water absorbing surfaces or activated with surfactants or detergents could show contact angle lower than 10o
• Superhydrophilicity – completely non water repellent
• A thin film of titanium dioxide combined with suitable additives – initial contact angle of water several tens of degrees
• UV illumination – water droplet spread out flat –giving contact angle approaching zero –superhydrophilicity
• When light is off, still retain contact angle of a few degrees for water for a few days – and eventually contact angle increases – hydrophobic again
• Superhydrophilicity properties can be recovered by exposing it with UV light.
![Page 13: TiO2 Photo Catalysis [Compatibility Mode]](https://reader034.vdocuments.site/reader034/viewer/2022051515/55262551550346126f8b4beb/html5/thumbnails/13.jpg)
13
Bare Glass
![Page 14: TiO2 Photo Catalysis [Compatibility Mode]](https://reader034.vdocuments.site/reader034/viewer/2022051515/55262551550346126f8b4beb/html5/thumbnails/14.jpg)
14
TiO2 coated glass
Anti Fogging
![Page 15: TiO2 Photo Catalysis [Compatibility Mode]](https://reader034.vdocuments.site/reader034/viewer/2022051515/55262551550346126f8b4beb/html5/thumbnails/15.jpg)
15
• How does it work? - Postulation – not exact answer
When TiO2 is illuminated with light – have “oxygen defects” on the surface of TiO2
Enabling water molecules to be attached on to the Ti structure
![Page 16: TiO2 Photo Catalysis [Compatibility Mode]](https://reader034.vdocuments.site/reader034/viewer/2022051515/55262551550346126f8b4beb/html5/thumbnails/16.jpg)
16
Superhydrophilicity vs Photocatalytic technology
• Photocatalytic technology – decompose the dirt, odourous compounds by oxiding the compounds
• Superhydrophilicity – altering the properties of the surface by photocatalytic action
• Both need “light”
Air purification
• Decomposition of malodorous pollutant (of low concentration – ppm levels)
• Indoor air cleaners
• Oxidation of SOx and NOx
• Limited to 0.01 ppm to 10 ppm levels
• Can be integrated with other process such as adsorption
![Page 17: TiO2 Photo Catalysis [Compatibility Mode]](https://reader034.vdocuments.site/reader034/viewer/2022051515/55262551550346126f8b4beb/html5/thumbnails/17.jpg)
17
Water Purification
• Treating recalcitrant organic matters in low concentrations
• Not suitable to treat high concentration of organic matters
• Suitable as a polishing method
• Application is still limited due to recovery of the photocatalyst
Magnetic TiO2 Photocatalyst
MAGNET
P
P
P
P
![Page 18: TiO2 Photo Catalysis [Compatibility Mode]](https://reader034.vdocuments.site/reader034/viewer/2022051515/55262551550346126f8b4beb/html5/thumbnails/18.jpg)
18
Magnetic Photocatalyst Synthesis
Magnetic Photocatalyst (TSM)
Magnetitein TMAOH
Sodium Silicate
Silica Coated Magnetite
(SM)
Titanium Tetrachloride
6 h hydrothermal at 90°C1 h calcination at 450°C
80°C
Transmission Electron Microscopy
40 mM TiCl4
Titania
SiO2 coated Fe3O4
Magnetite
Silica
![Page 19: TiO2 Photo Catalysis [Compatibility Mode]](https://reader034.vdocuments.site/reader034/viewer/2022051515/55262551550346126f8b4beb/html5/thumbnails/19.jpg)
19
Water splitting
• Electrolysis – (High School Chemistry experiments)– two electrodes (cathodes and anodes)
– A little salt, acid
– Apply a direct current
– What did you see?
• Honda and Fujishima – did experiments which water splitting can be carried out without the need of electricity
• Problems : – low H2 generation
– requires artificial light to be effective – ie extra energy
![Page 20: TiO2 Photo Catalysis [Compatibility Mode]](https://reader034.vdocuments.site/reader034/viewer/2022051515/55262551550346126f8b4beb/html5/thumbnails/20.jpg)
20
![Page 21: TiO2 Photo Catalysis [Compatibility Mode]](https://reader034.vdocuments.site/reader034/viewer/2022051515/55262551550346126f8b4beb/html5/thumbnails/21.jpg)
21
• Another application of TiO2 is
Dye sensitised solar cells (DSC)
• More applications out there perhaps you will be the engineer to put them into reality