Download - TAR-1403-41_manuscript_1.pdf
1
Comperation of pulping and bleaching behaviors of some agricultural residues1
Saim ATEŞa, İlhan DENİZb, Hüseyin KIRCIb, Celil ATİKc, Onur Tolga OKANb,*2
aKastamonu University, Faculty of Forestry, Department of Forest Industrial3
Engineering, 37200 Kastamonu, Turkey.4
bKaradeniz Technical University, Faculty of Forestry, Department of Forest Industrial5
Engineering, 61080 Trabzon, Turkey.6
cIstanbul University, Faculty of Forestry, Department of Forest Industrial Engineering,7
34473 Istanbul, Turkey.8
9
10
11
12
13
14
15
16
17
18
19
20
*Corresponding author at; Karadeniz Technical University, Faculty of Forestry,21
Department of Forest Industrial Engineering,61080 Trabzon, Turkey. Tel: +90 462 37722
15 14; fax: +90 462 3257499. E-mail addresses: [email protected] (Onur T.23
OKAN).24
2
Abstract1
In the present study, the characteristics of bleaching and beating of annual plants and2
agricultural waste, which constitute important raw material potential for the pulp and3
paper industry in Turkey, were determined, and the effects of this process on some paper4
properties were examined. First, chemical contents were determined for each raw material,5
and then evaluated for use in the pulp and paper industry. All raw materials studied were6
found to be suitable for use in the pulp and paper industry, according to the determined7
chemical content. Subsequently, the pulps obtained with different properties were first pre-8
treated with enzyme xylanase, and then bleached using with Elementary Chlorine Free9
(ECF) method, utilizing the DEpD bleaching sequence, which is both easy to apply, and10
highly effective. The bleaching behavior of each material was then determined. The11
highest ISO brightness value of 98.3% was obtained using soda-AQ pulps deriving from12
rye straw. This is followed by wheat straw (92.0%), reed (88.6%), corn stalks (87.6%),13
and rice straw (87.5%). Each unbleached pulp sample was beaten at a constant 300014
revolutions PFI (9000 rev. for hemp) and changes in freeness properties were15
determined. The hardest material to beating is hemp fibers, followed by reed, rye, corn,16
and cotton stalks. The best beatable pulps were rice straw, tobacco, wheat, sunflower,17
and barley stalks. Paper sheets from both unbleached and bleached pulps were tested.18
Keywords: Annual plants, Enzyme, ECF bleaching, Paper properties, Soda-AQ pulping19
20
21
22
23
24
3
Introduction1
The use of agricultural residues in the paper industry, as a source of cellulose, is2
supported by many institutions, due in part to increasing environmental pressures3
(Camarero et al. 2004). The principal aim of those incentives is to minimize the4
environmental damage of the cellulose industry, in addition to reducing raw material5
pressure placed on forests (Pan et al., 1999). Moreover, another reason which makes the6
use of agricultural residues in the cellulose industry attractive is the fact that some7
countries have limited forest resources (Jimenez, 1999). When those countries that have8
an agricultural-dependent economy and limited forest sources are considered, the use of9
agricultural residues, and either cultured or uncultured annual stalks, for manufacturing10
pulp will offer a significant solution to the raw material problem (Okan et al, 2013).11
Being an agricultural-dependent country with limited forest resources, Turkey is still far12
away from utilizing the current potential of agricultural residues in the cellulose13
industry. In total, 38,247 hectares of agricultural fields are cultivated in Turkey. Of this14
cultivated area, the potential number of stalks (which include wheat, barley, corn, rye,15
cotton, and rice straw), usable for cellulose industry over last three years (2011, 2012,16
and 2013), is estimated at approximately 94 thousand metric tons. The worldwide17
tendency of increased demand-to-paper-and-cardboard-products persists, a constraint18
will occur in the production of wood-derived cellulose, and it will be inevitable to use19
the high growth potential of agricultural fibers in the cellulose industry in order to20
overcome this limitation (Fillat et al., 2012).21
Another important problem encountered by the paper industry concerns22
minimizing environmental pollution and developing technologies that create less23
pollution. After it was discovered that chlorine-containing components (for bleaching24
4
pulp using conventional methods) react with the lignin (a residue in the pulp), which get1
converted into environmentally hazardous chlorinated phenolic compounds and2
poisonous carcinogenic compounds (such as dioxine and furan groups), exist in the3
waste water of bleaching process, social pressures were born to limit use of compounds4
containing chlorine: such as chlorine, chlorine dioxide, hypochloride, and chloride. All5
these facts led the pulp industry to develop new technologies which do not cause6
environmental problems in the production of bleached paper (Okan, 2013). However,7
the bleaching process of pulps (which are derived from annual plants) is difficult due to8
anatomic and chemical characteristics, therefore modern totally chlorine-free (TCF)9
bleaching procedures are not enough to reach a high brightness level in this type of pulp10
(Camamero et al., 2004). For this purpose, when it is compared with other11
environmentally friendly technologies used for bleaching pulps derived from annual12
plants, enzymatic procedures offer low-cost solutions by limiting the chlorine dioxide13
capacity (Stafford, 2000). The xylanase is a commercially available enzyme that is most14
often used for pretreatment of pulp bleaching. In a study with the bleaching stages15
determined as DC(EOP)(DED)(D:Chloride, C:Chlorine, E: Alkaline extraction, O:16
Oxygen, P:Peroxide), the total amount of chlorine could be reduced at rate of 15-23%17
with the use of the enzyme xylanase, without changing pulp quality in production plant18
conditions (Manji, 2006).19
In a current study, it was investigated whether the residual annual plants, which20
are cultivated all around Turkey, can be feasibly used as raw material in the paper21
industry. The resulting pulps, showing different characteristics, first exposed to pre-22
bleaching with the enzyme xylanase, followed by an easy to use, and remarkably more23
efficient ECF (Elementary chlorine-free bleaching) bleaching sequence (DEpD)24
5
(D:Chloride, Ep: Alkaline-peroxide extraction). The bleaching characteristics of the1
resulting annual plant pulps were revealed. Also, the beating degrees of raw material2
were examined. Physical and optical properties of trial papers, which were made from3
those pulps, were determined. Thus, each annual plant or agricultural waste material4
will be evaluated in a production plant, either separately or altogether.5
6
2. Materials and methods7
2.1. Material8
2.1.1. Raw Materials9
Cultivated areas were studied for each raw material, considering the location and10
potential of study areas in Turkey. The wheat, rye and barley straw were supplied from11
Konya, Cotton stalk was supplied from Adana, Tobacco and corn stalk were supplied12
from Samsun, Sunflower stalk was supplied from Tekirdağ, Rice straw was supplied13
from Çorum, Reed supplied was from Afyon and finally Hemp was supplied from14
Kastamonu province for this study. Initially, annual stalk samples were cleaned of15
leaves, root, soils, and other contaminants. Then, stalks were cut into 4-5cm pieces16
using a cutter. Raw material experiments were then conducted on the whole stalk. For17
hemp, only phloem fibers were used.18
19
20
21
22
23
24
6
2.2. Method1
2.2.1 Analysis of raw material2
Annual plant samples were ground up and 60-80 mesh fractions were selected to3
determine the chemical composition, according to TAPPI T 264 om-88. Samples were4
first placed in a Soxhlet extraction, with alcohol-benzene extraction, according to T 2045
cm-97, then an acetone extraction according to SCAN CM:49-03. Holocellulose content6
was determined by Wise’s sodium chlorite method (Wise and Murphy 1946), and7
cellulose content according to Kurscher and Hoffner’s nitric acid method (Rowell8
1984). In addition, alpha cellulose (T 203 cm-99), lignin (T 222 om-02), silica (T 2079
CM-99), and ash (T 211 OM-93) contents were determined. Determination of 1%10
sodium hydroxide and water (hot and cold) solubility of annual plants were carried out11
following the standard procedures described in T 212 om-98 and T 212 OM-8812
respectively.13
2.2.2. Methods used for production and chemical analyses of pulp14
Kappa number described as the remaing lignin amount in pulp as a percentage of15
the total lignin content of the raw material. Easily bleachable pulp means the kappa16
number is below 15 (Danielewicz and Šlusarska 2006). In order to ensure the kappa17
numbers of pulps are within the category of easily and moderately bleachable pulps,18
previous studies were referenced (Jimenez et al.,1995; Lopez et al; 1996; Lopez et al.,19
2005; Rodriguez et al., 2008; Akgül and Tozluoğlu, 2009; Shakhes et al. 2011; Jahan20
and Rahman, 2012). Soda-AQ pulping method, the most suitable for agricultural21
residues (Eroğlu 1990), was choosed and applied to cooking plan as can be seen in22
Table 1.23
Table-124
7
Cooking trials were performed in a thermostatically controlled, rotary, laboratory-1
type reactor characterized by a capacity of 15 liters, electrically heated, resistant to2
pressure of 25kg/m2, 4 rpm, with an automated temperature control table. The reactor3
was manually loaded and unloaded, and 600g of completely dry cut stalks were used for4
all of the cooking procedures. Determination of the kappa numbers and viscosities of5
pulp samples were carried out using the standard procedures described in T 236 om-996
and Scan-C 15:62 respectively.7
Handsheets of 60g/m2 were formed, and their some properties were evaluated in8
accordance with the TAPPI standard methods. The handsheets were conditioned in9
accordance with T 402 sp-98. The burst index of handsheets was measured by method T10
403 om-97, the tensile index of handsheets were determined by method T 404 cm-9211
and tear index was carried out by standard procedure described in T 414 om-98. ISO12
Brightness, yellowness, and opacity were calculated to the, ISO 2470-1, ASTM E313,13
ISO 2470 respectively, and the amount of bleaching yield was calculated using the dry14
solids content of the pulps.15
16
2.2.3 Pulp bleaching17
2.2.3.1. Xylanase pretreatment (enzymatic procedure)18
A commercially available enzyme called endo-xylanase was used for the19
preliminary biological process prior to the elementary chlorine-free (ECF) bleaching20
sequence of pulps. Endo-xylanase was supplied from Sigma, and its activity was21
determined according to the DNS method (Bailey, 1988). The diluted sample of enzyme22
(30µl) was incubated in 300µl of 1% (w/v) common beech wood-xylane solution for 2023
minutes at 40°C. Activity of 1U xylanase was calculated as the enzyme catalyzed by24
8
1mmol xylose per minute. Xylanase, 2 IU/g at ratio of 7:1 (solution/stalk), was applied1
to each pulp sample, which was obtained following the production of paper pulp, and2
was applied for 2 hours at pH = 4.8 and 48°C.3
4
2.2.3.2. Elementary chlorine-free (ECF) bleaching procedure5
It was aimed to determine the bleachability characteristics of raw materials by6
applying DED bleaching sequence (D: Chloride, Ep : Alkaline-peroxide extraction)7
according to the easy to use and remarkably efficient conventional ECF (Elementary8
Chlorine-Free) bleaching method, following preliminary biological bleaching.9
Procedures of the bleaching sequence and application levels are given in detail in Table10
2.11
Table-212
2.2.4 Refining Process13
According to pre-trial results, reasonable PFI beating revolution was determined14
as 3000 for annual plants and also 9000 for hemp fibers. Each sample of unbleached15
pulp was beated totally 3000 revolution in the PFI beater under low load conditions, and16
beating characteristics were examined by SR° (Schopper Riegler degree) of the pulp.17
Because SR° value of hemp fibers were normally very low those fibers were beated18
with PFI as 9000 revolution.19
20
2.2.5. Production of handsheets21
Paper samples obtained from pulp by using Rapid Köthen, which were made from22
different types of agricultural residues, were conditioned for 24 hours in an air-23
9
conditioned room according to ISO 287 standards, and then some optical, and physical1
properties of each paper were determined according to TAPPI standard.2
3
3. Results and discussion4
3.1. Chemical composition of raw material5
The average composition of raw materials is given in Table 3. Holocellulose is6
defined as the total content of carbohydrate materials. High holocellulose content,7
therefore, is considered desirable for the pulp and paper industry because it has been8
correlated with higher pulp yield (Shakhes et al., 2011).9
Table-310
The holocellulose content of wheat straw, barley, corn, tobacco, cotton, and11
sunflower stalks was similar to each other. Furthermore, there was a nearly identical12
holocellulose content of rye, rice straw, and reed. The holocellulose content of hemp13
was found to be higher than the other agricultural residues in this study. The14
holocellulose content in wheat straw, barley, corn, tobacco, cotton, and sunflower stalks15
are very close to those reported for wood species such as Pinus pinaster, Fagus16
sylvatica L, and Pinus sylvestris L (Alonso, 1976; Inari et al., 2007). The holocellulose17
content in rye, rice straw, and reed was similar to other wood species such as poplar and18
spruce (Law et al., 2001; Bertaud and Holmbom, 2004). The holocellulose content of19
rye (Secale cereale L), hemp (Cannabis sativa L.), sunflower (Helianthus annuus L),20
tobacco (Nicotiana tabacum L.), barley (Hordeum vulgare), and corn stalks (Zea mays L.)21
were close to that found in published literature (Lopez et al., 1996; Akgül and22
Tozluoğlu, 2009; Shakes et al., 2011). The lowest holocellulose contents were observed23
in wheat straw (Triticum aestivum L) and cotton stalks (Gossypium hirsitum L), while the24
10
highest holocellulose contents were observed in rice straw, compared to that found in1
published literature (Deniz et al 2004; Rodriguez et al., 2008). The highest cellulose2
content was observed in hemp, but the lowest cellulose content was observed in cotton3
stalks and sunflower stalks. Additionally, the cellulose content of these raw materials4
was nearly identical to each other, with the exception of hemp. The amount of alpha5
cellulose, namely the fraction that is insoluble in 17.5% NaOH, was determined to be6
above 35%. According to Shakes et al (2010), the presence of 35% alpha cellulose7
content has a satisfactory effect on paper strength properties. Furthermore, the pulp8
yield strongly correlated with both holocellulose and alpha cellulose content. When9
examined Table 3, it can be seen that alpha cellulose content of wheat straw, barley, rye,10
corn, and sunflower stalks are significant differences compared to rice straw and reed.11
The alpha cellulose content of hemp was 72.29%, which was higher than the other12
agricultural residues samples.13
The desirable lignin content level is below 30%, because lignin was considered to14
be an undesirable polymer, and the removal during pulping and bleaching requires a15
high amount of energy and chemicals (Shakes et al., 2011). The lignin content of hemp16
was fairly low compared to other agricultural residues samples in this study, but no17
significant difference in lignin content was found in most other agricultural residues18
studied.19
Overall, high silica and ash content were found in agriculture samples. Compared20
to wood, this type of raw material commonly has silica and ash contents, which can21
cause problems in the manufacturing process. Ash content in trace elements also makes22
lower bleaching efficiency (Dutt et al. 2009).23
11
The alcohol-benzene and acetone solubility of hemp and rice straw are lower than1
the other agricultural samples in this study. In the other eight agricultural samples,2
alcohol-benzene and acetone solubility contents were found to be very similar.3
According to Table 3, the content of 1% NaOH,hot and cold water solubilitytions4
of hemp was found to be fairly lower than the other agricultural residues samples.5
Barley, sunflower, tobacco, and wheat straw contain a significantly higher content of6
soluble compounds in both hot and cold water, and also 1% NaOH. Generally, the7
presence of extractives in wood increased the pulping effluent load and consumption of8
pulping reagents, and reduced the pulp yield (Azizi et al. 2010). For instance, as9
examined in Table 4, total yield of rye and rice straw is higher than wheat straw and10
barley stalk, although all cooking methods are the same. The reason for this is that11
wheat straw and barley stalk contain a considerably higher content of soluble12
compounds in 1% NaOH and hot and cold water, as compared to rye and rice straw.13
14
3.2. Pulp properties obtained from annual plants with soda-AQ cooking method15
Screened yield, kappa numbers and viscosity values of bleachable (kappa number16
≤ 15) pulps, which are derived from annual plants using soda-AQ method, are given in17
Table 4.18
Table 419
It is obvious that cooking conditions vary when the cooking plan of each annual20
plant is examined. This fact is an important piece of criteria for the availability of21
relevant raw material. It is well known that the more lignin content in the pulp means22
the more bleaching chemicals and energy for removing it. When Table 4 is examined, it23
can be speculated that wheat, barley, rye, and rice straw are easily cooked raw materials,24
12
while corn stalk is a moderately hard to cook material. Tobacco, cotton, and sunflower1
stalks are hard to cook raw materials. In bleaching, the term hard cooking conditions2
when used for a given pulping process, refers to the amount of lignin remaining in the3
unbleached pulp. Therefore cooking conditions have a remarkable effect on kappa4
numbers and viscosity. When figure 1 is examined, the lowest kappa values were5
obtained with rye (10.0), corn (10.14), reed (10.88), rice (11.2), wheat (12.60), and6
barley straw (12.7), among pulps which were cooked under the same conditions. When7
the viscosity value, indicating the depolimerization degree of cellulose, is examined, it8
was observed that easily cooked pulps have similar viscosites. However, harder cooking9
conditions were applied to obtaining economically bleachable pulps from tobacco,10
cotton, and sunflower stalks, which are among hard to cook pulps, and in conclusion11
this approach showed that the viscosities of those pulps were low (5.79cp, 6.07cp and12
7.49cp, respectively).13
Figure 114
15
In a study conducted with tobacco stalks, it was found that for soda-AQ pulps16
which applied 20% active alkaline solution, 170°C, 90 minute cooking and 0.1% AQ17
conditions, the kappa number was 28.7 and viscosity was 46.0 cp, and it was not18
possible to bleach those pulps in an economic manner (Ateş et al., 2010). In another19
study conducted for producing economically bleachable paper pulp, it was found that20
for tobacco stalks, which were manufactured in conditions of 25% active alkali ratio,21
165°C pulping temperature, 180 minutes pulping time with the addition of 0.2% AQ,22
the kappa number was 20 (Shakhes et al., 2012). Based on cooking studies conducted23
on cotton stalks under various conditions, the kappa number was 33.1 and viscosity was24
13
31.0 cp in the following conditions: 18% active alkali ratio, 0.075% AQ, solution to1
stalk ratio of 4:1, and 165°C (Ali et al., 2001). In a study conducted for obtaining2
bleachable pulps from sunflower stalk under different cooking conditions, the kappa3
number of pulps obtained from stalks was 25, under conditions of 16% active alkali,4
170°C with the addition of 0.13% AQ soda-AQ cooking (Khristova et al., 1998). In5
another study conducted for production bleachable soda-AQ pulp from corn stalks with6
or without preliminary hydrolysis, corn stalks applied a cooking procedure in different7
alkaline conditions (150°C, stalk/solution ratio of 6:1, AQ rate of 0.1%, and cooking8
time of 60 minutes). Based on those cooking conditions, the kappa number was 27.49
when 14% alkaline was applied, 24.8 when 16% alkaline was applied, and 21 when10
18% alkaline was applied (Jahan and Rahman, 2012).11
12
3.3. Some physical properties of papers obtained from bleached and unbleached13
pulps14
Schopper Riegler degree (SR°), viscosity, gramage, and some physical and optical15
properties of paper obtained at an equal PFI beating stages of pulp papers, which are16
derived from annual plants with the soda-AQ method, are given in Table 5.17
Table 518
A comparison of pulps obtained from annual plants and agricultural residues,19
using the soda-AQ method, with regards to pulp freeness, is given in Figure 2. When20
Figure 2 is examined, the hardest material to beating is hemp fibers, followed by reed,21
rye, corn, and cotton stalks. The best beatable pulps are rice straw, tobacco, wheat,22
sunflower, and barley stalks. Therefore, pulps obtained from this group can be beat23
together.24
14
Figure 21
In regards to Table 5, it is also observed that unbleached pulps can be more2
difficult to beat in comparison to bleached pulps. The underlying reason is that amount3
of xylane is low in pulps which have applied enzymatic pretreatment (Fillat, 2012). In4
other words, bleaching causes fibers to become more individual, and therefore cause5
more difficulty in beating. In studies investigating the effect of xylanase on beating the6
pulp, other investigators have found similar results (Wong et al., 1997; Roncero et al.,7
2003; Valls et al., 2010).8
The changes observed in the breaking length, burst, and tearing resistances of the9
handsheets (obtained from pulp after bleaching is performed) are demonstrated in10
Figure 3. As the figure indicates, resistance values were adversely influenced after11
pulps, obtained from hemp, cotton stalks, and reed fibers, were bleached. A mean12
reduction of 3.8 units was observed in the tearing index of hemp phloem, which is13
directly proportional to the length of the fiber. This is followed by reed with a reduction14
of 2.08 units, and cotton stalks with a reduction of 0.71 unit. Moreover, hemp, cotton,15
and tobacco stalks have higher rankings in terms of lignin residue in the paper pulp, and16
it is possible to speculate that when the lignin is removed from the stalks, the physical17
properties are adversely affected.18
An increase was observed in the resistance properties of paper pulps made from19
wheat straw, barley, rye, and rice straw (among cereal stalks) as well as corn, tobacco20
and sunflower stalks, when the pulp was bleached. Breaking length, burst, and tearing21
resistances increased at rates of 15.12%, 34.5% and 18.0%, respectively, as a22
consequence of the ECF bleaching method with pretreatment of xylanase (X+DEpD),23
particularly for the pulps obtained from rice straw.24
15
Figure 31
Degradation occurs when bleaching is made under alkaline conditions. This leads2
to significant reduction on the viscosity (Camarero et al., 2004). Physical properties of3
the pulp are not only related to the amount of cellulose, but also to the ratio of hemi-4
cellulose. High amounts of cellulose usually give strong pulps, and a low ratio of5
cellulose to hemicellulose reduces the resistance of paper. (Brannvall, 2004). Briefly,6
the reactions of different annual plants to a bleaching sequence, which is applied under7
same conditions, are derived from the change of their effects on chemical compounds8
and fiber morphologies.9
3.4. Optical properties of papers as a result of ECF bleaching10
The brightness values of handsheets bleached in accordance with the XDEpD X11
(Xylanase) + D (chlorine dioxide) + Ep (Alkaline peroxide) + D (Chlorine dioxide)12
sequence, are given in Table 6.13
Table 614
Soda-AQ pulps produced from different annual plants under different cooking15
conditions (optimum, should the resultant kappa number be the same) were pretreated16
with enzyme xylanase, followed by bleaching with a DEpD bleaching sequence.17
Changes in brightness values of thepulps after the bleaching procedure is fully complete18
are given in Figure 4 and Table 6. When examining the table, it is shown that no19
remarkable change is observed in brightness properties. However, the effects of20
pretreatment with the enzyme can be clearly seen at the end of next bleaching stage. In21
other words, the results of this enzymatic procedure have small but remarkable effects22
on the brightness. When the literature is examined, it is found that this is similar to a23
16
study conducted on the effects of pretreatment with xylanase on the brightness of paper1
pulp (Stafford et al., 2000; Ateş et al., 2008).2
Figure 43
When Table 6 is examined, it is obvious that brightness increases as long as4
bleaching advances. ISO Brightness values for fully bleached annual plant pulps are5
given in Figure 4. Accordingly, the highest ISO brightness value of 98.3% is obtained6
from soda-AQ pulps deriving from rye straw. This is followed by wheat straw (92.0%),7
reed (88.6%), corn (87.6%), and rice straw (87.5%). The weakest reaction to the8
XDEpD bleaching sequence was obtained from cotton, tobacco, and sunflower stalks,9
and the corresponding ISO brightness values were 61.0%, 68.4% and 71.9%,10
respectively.11
In a study conducted on wheat straw, which underwent a DEpD bleaching12
sequence with xylanase pretreatment, it was found that brightness increased as long as13
the bleaching stages advanced. ISO brightness of fully bleached wheat straw pulp was14
approximately 85%. It was reported in the same study that the XDEpD bleaching15
sequence is the best alternative to the DEpD bleaching sequence in terms of brightness16
and optical properties (Jimenez et al., 1995). Similar brightness values were determined17
in another bleaching study which involved the enzymatic pretreatment of paper pulps18
obtained from wheat straw pulps using the Biokraft method (Ateş et al., 2008a).19
4. Conclusions20
As a consequence of different cooking procedures for obtaining bleachable pulps21
from each of the primary agricultural residues, it was determined that tobacco, cotton,22
and sunflower stalks are not appropriate for obtaining bleachable pulp. When23
agricultural residues were examined with regards to beatability using the ECF bleaching24
17
method with xylanase pretreatment, it was found that bleached pulps were usually more1
difficult to beat than unbleached pulps. It is understood that among all raw materials2
used, rice straw was the best type with regards to beatability. However, it can be3
speculated that reed, hemp, and cotton stalks are not suitable for ECF bleaching with4
enzymatic pretreatment. Generally no positive change was observed in the physical5
properties of agricultural residues after bleaching was completed. However, it was6
found that the ECF bleaching method with enzymatic pretreatment, similar to the7
beating process, was not a suitable method for reed, hemp, and cotton stalks due to the8
reduction in physical properties after bleaching was completed. When the brightness9
value was examined after the ECF method with enzymatic pretreatment was completed,10
an increase was observed for all types of pulps. However, considering bleaching11
efficiency, the best reaction to the XDEpD bleaching sequence was given by cotton12
(216%), wheat (167%), sunflower (154%), and reed (131%), while the weakest reaction13
to bleaching (as indicated by comparison to baseline unbleached brightness) was given14
by hemp, corn, and rye pulps, as indicated by corresponding increases at rates of 80, 99,15
and 160%, respectively.16
In brief, it was found that the type of agricultural residues appropriate for xylanase17
pretreated using ECF bleaching included rice, barley, wheat straw, and corn (in18
descending order) and unfavorable types were cotton, hemp, and reed.19
20
Acknowledgment: The authors are grateful to Foundation for The Scientific and21
Technological Research Council of Turkey (TUBITAK) (Project No: 108 O 594) for22
financial support of this work.23
24
18
References1
Akgül M, Tozluoğlu A (2009). A comparison of soda-AQ pulps from cotton2
stalks. African J of Biotechnol 8:6127-6133.3
Ali M, Byrd M, Jameel H (2001). Soda-AQ pulping of cotton stalks, in: TAPPİ4
Fall Techincal Conferences (CD version).5
Alonso L, (1976). In: INIA (Ed.), Ana’lisis quı’mico de maderas de diferentes6
especies forestales. Ministerio de Agricultura, Madrid, Spain.7
Ateş S, Akgül M, Deniz İ, Tutuş A, Okan OT, Tozluoğlu A (2010). Investigation8
of the effects of soda and modified soda methods on pulps obtained from tobacco stalks.9
In: Proceedings of III. Ulusal Karadeniz Ormancılık Kongresi, 20-22 Mayıs 2010;10
Artvin, Türkiye: Artvin Çoruh Üniversitesi Orman Fakültesi, Cilt V, pp.1976-1984.11
Ateş S, Atik C, Ni Y, Gümüşkaya E (2008). Comparison of different chemical12
pulps from wheat straw and bleaching with xylanase pre-treated ECF method. Turk J13
Agric For 32: 561-570.14
Ates S, Ni Y, Atik C, İmamoğlu S (2008a). Pretreatment by Ceriporiopsis15
subvesmispora and Phlebia subserials of wheat straw and its impact on subsequent16
Soda-AQ and Kraft-AQ pulping. Romanian Biotech Letters 13:3914-3912.17
Azizi MA, Harun J, Fallah SR, Resalati H, Tahir MP, Ibrahim R, Zuriyzti MA18
(2010). A review of literature related to kenaf as alternative for pulpwoods. Agric J19
5:131-138.20
Bailey MJ (1988). A note on the use of dinitrosalyclic acid for determination the21
products of enzimatic reactions. Appl Microbiol Biotechnol 29:494-496.22
19
Bertaud F, Holmbom B (2004). Chemical composition of earlywood and latewood1
in Norway spruce heartwood, sapwood and transition zone wood. Wood Sci Technol2
38:245-256.3
Brannvall E (2004). Pulp Characterisation, In: Monica EK, editors. The Ljungberg4
Textbook in Pulp Technology. 3rd ed. Stockholm, Sweden pp.7-8.5
Camarero S, Garcia O, Vidal T, Colom J, Rio DCJ, Gutierrez A, Gras MJ, Monje6
R, Martinez JM, Martinez TA (2004). Efficient bleaching of non-wood high-quality7
paper pulp using laccase-mediator system. J Enz and Mic Tec 35:113-120.8
Danielewicz DD and Šlusarska SB (2006). Oxygen delignification of high-kappa9
number pine kraft pulp. Fibres and Textile in Eastern Europe 14:89-93.10
Deniz I, Kırcı H, Ates S (2004). Optimisation of wheat straw (Triticum durum)11
kraft pulping. Ind Crop and Prod 19:237-243.12
Dutt D, Upadhyay JS, Singh B, Tyagi CH (2009). Studies on Hibiscus cannabinus13
and Hibiscus sabdariffa as an alternative pulp blend for softwood. An optimization on14
Kraft delignification process. Ind Crop and Prod 29:16-26.15
Eroglu H, and Usta M (1989). Oxygen bleaching of soda-oxygen wheat straw16
pulp. TAPPI Non-wood plant fiber pulping, Progress report 17:133-135.17
Fillat U, Roncero MB, Sacỏn VM, Bassa A (2012). Integrating a xylanase18
treatment into an industrial-type sequence for eucalyptus kraft pulp bleaching. J Ind Eng19
Chem Res 51: 2830-2837.20
Inari, GN, Petrissans M, Gerardin P (2007). Chemical reactivity of heat-treated21
wood. Wood Sci Technol 41:157-168.22
20
Jahan SM, Rahman MM (2012). Effect of pre-hydrolysis on the soda-1
anthraquinone pulping of corn stalks and Saccharuö spontaneum (kash). Carbohyd2
Polym 88:583-588.3
Jimenez L, Martinez C, Perez I, Lopez F (1995). Biobleaching procedures for4
pulp from agricultural residues using Phanerochaete chrysosporium and enzymes. Proc5
Biochm 32: 297-304.6
Jimenez L, Navarro E, Ferrer JL, Lopez F, Ariza J (1999). Biobleaching of7
cellulose pulp from wheat straw with enzymes and hydrogen peroxide. J Proc Bio8
35:149-157.9
Khristova P, Gabir S, Bentcheva S, Dafalla S (1998). Soda-anthraquinone pulping10
of sunflower stalks. Ind Crop and Prod 9:9-17.11
Law KN, Kokta BV, Mao CB (2001). Fiber morphology and soda-sulphite12
pulping of switchgrass. Bioresour Technol 97:535-544.13
Lopez DS, Tıssot M, Delmas M, (1996). Integrated cereal straw valorization by an14
alkaline pre-extraction of hemicellulose prior to soda-anthraquinone pulping. Case15
study of barley straw. Biomass and Bioenerg 10:201-211.16
Lopez F, Eugenio ME, Diaz MJ, Nacimiento M, Garcia M, Jimenez L (2005).17
Soda pulping of sunflower stalks. Influence of process variables on the resulting pulp. J18
Ind Eng Chem 11:387-394.19
Manji AH (2006). Extended usage of xylanase enzyme to enhance the bleaching20
of softwood kraft pulp. Tappi J 5:23-26.21
Okan OT, Deniz İ, Yildirim İ (2013). Bleaching of Bamboo (Phyllostachys22
bambusoides) Kraft-AQ pulp with Sodium Perborate Tetrahydrate (SPBTH) after23
Oxygen Delignification. Bioresour 8:1332-1344.24
21
Pan JX, Sano Y, Ito T (1999). Atmospheric acetic acid pulping of rice straw II:1
Behavior of ash and silica in rice straw straw during atmospheric asetic acid pulping2
and bleaching. Holzforschung, 53:49-55.3
Rodriguez A, Moral A, Serrano L, Labidi J, Jimenez L, (2008). Rice straw straw4
pulp obtained by using various methods. 99:2881-2886.5
Roncero B, Torres AL, Colom J, Vidal T (2003). TCF bleaching of wheat straw6
pulp using ozone and xylanase. Part A: paper quality assesment. Biresour Technol7
87:305-314.8
Rowel R (1984). The chemistry of solid wood. In: Proceeding of based on short9
course and symposium sponsored by the division of cellulose, paper and textile10
chemistry at the 185th meeting of American Chemical Society, Seattle, Washington, 20-11
25 March 1983, 70-72.12
Shakhes J, Marandi MAB, Zeinaly F, Saraian A, Saghafi T (2011). Tobacco13
residuals as promising lignocellulosic materials for pulp and paper industry. Bioresour14
6:4481-4493.15
Shakhes J, Rezayati CP, Zeinaly F (2010). Evaluation of harvesting time effects16
and cultivars of kenaf on papermaking. Bioresour 5:1268-1280.17
Stafford M, Genco J, Ghanem A (2000). Effect of xylanase treatment on chlorine18
dioxide kinetics and alkaline extraction efficiency during pulp bleaching. In: Proceeding19
of Pulping / Process & Product Quality Conference.5-8 November 2000; Boston, MA,20
USA.21
Valls C, Gallardo O, Vidal T, Pator FIJ, Diaz P, Roncero MB (2010). New22
xylanase to obtain modified eucalypt fibers with high-cellulose content. Biresour23
Technol 101:7439-7445.24
22
Wise LE, Murphy M (1946). A chlorite holocellulose, its fractionation and1
bearing on summative wood analysis and studies on hemicelluloses. Paper Trade J2
122:35-43.3
Wong KKY, Jong ED, Saddler JN, Allison RW (1997). Mechanisms of xylanase4
aided bleaching of kraft pulp. Part 2: Targert substrates. Appita J 50:509-518.5
6
7
8
9
10
11
12
13
14
15
16
17
18
19
20
21
22
23
24
23
Tabels1
Table 1: Cooking plan applied to production of pulp which is characterized as2
bleachable and derived from annual plants based on preliminary trials3
Annual plantNaOH
%
Temp.
oC
Time
min
AQ
(%)
Time to maximum
Temp (min.)
Wheat straw 16 160 40 0.1 60
Rice straw 16 160 40 0.1 60
Rye straw 16 160 40 0.1 60
Barley straw 16 160 40 0.1 60
Reed stalk 20 160 60 0.1 60
Corn stalk 16 160 60 0.1 60
Tobacco stalk 25 170 120 0.1 60
Cotton stalk 25 170 180 0.1 60
Sunflower stalk 20 170 180 0.1 60
Hemp 14 125 90 0.1 60
4
5
6
7
8
9
10
11
12
24
Table 2: Bleaching plan applied following preliminary biological bleaching1
Bleaching
Stages
Bleaching Conditions
Dosage Time
D1 %3 ClO2 120
EP
%1 NaOH
%0.5 MgSO4
%0.5 H2O2
180
D2 %1.5 ClO2 120
* Following assumptions were made: temperature is 75°C and the concentration is 72percent.3
45
6
7
8
9
10
11
12
13
14
15
16
17
18
19
25
Table 3: Chemical compositions of used agricultural residues.1
Whe
atst
raw
Bar
ley
stra
w
Rye
stra
w
Ric
e st
raw
Ree
d st
alk
Cor
n st
alk
Tob
acco
stal
k
Cot
ton
stal
k
Sunf
low
erst
alk
Hem
p
Components (%)
Holocellulose 69.84 66.01 76.95 79.39 78.85 69.92 64.29 62.79 66.85 86.08
Cellulose 50.70 49.30 51.65 55.30 56.65 55.70 50.95 47.30 47.80 80.70
α-cellulose 42.07 38.70 44.55 53.67 52.56 46.78 36.40 29.74 44.20 75.29
Lignin 22.33 19.47 17.25 23.77 22.79 18.16 15.15 23.79 14.43 6.42
Silica 7.33 6.88 2.07 15.67 1.23 2.98 0.94 0.34 0.44 1.24
Ash 11.63 10.97 4.01 15.44 4.17 7.75 14.44 4.99 7.99 3.62
Solubilities (%)
Acetone 5.37 5.39 4.51 3.02 2.98 8.10 5.58 3.84 4.86 1.62
Alcohol-
Benzene
9.33 8.71 7.44 2.21 3.26 8.57 8.06 8.36 7.48 1.59
1% NaOH 53.67 56.25 44.35 45.63 36.81 46.43 50.57 48.88 50.05 20.04
Hot water 14.71 16.25 15.72 13.81 9.80 16.82 21.56 17.91 24.26 5.85
Cold water 11.33 11.01 11.95 9.66 7.61 14.64 17.15 15.05 21.08 5.29
2
3
4
5
6
7
26
Table 4: Yield and chemical properties of pulps made from annual plants with soda-AQ1
method.2
Name ofsample
NaOH%
AQ%
Temp.oC
Time
min
ScreenYield(%)
Reject(%)
Totalyield(%)
Kappano
Visc.Cp
Wheat straw 16 0.1 160 40 37.1 0.8 37.9 12.6 24.62
Barley straw 16 0.1 160 40 32.6 1.4 34.0 12.7 24.92
Rye straw 16 0.1 160 40 43.5 0.4 43.9 10.0 28.88
Rice straw 16 0.1 160 40 41.2 1.4 42.6 11.2 26.75
Reed 20 0.1 160 60 42.3 0.2 42.5 10.8 37.48
Corn stalk 16 0.1 160 60 42.4 1.3 43.7 10.4 32.01
Tobacco stalk 25 0.1 170 120 22.9 2.4 25.3 13.4 5.79
Cotton stalk 25 0.1 170 180 17.8 1.4 19.2 17.6 6.07
Sunflower
stalk
20 0.1 170 180 31.1 0.5 31.6 13.7 7.49
Hemp 14 0.1 125 90 64.2 0.0 64.2 14.8 65.87
3
4
5
6
7
8
9
10
11
12
27
Table 5: SR°, viscosity, and some physical properties of pulps in constant beating stages1
RawMaterials
PFI (
rpm
)
SRo
Vis
cosi
ty(c
p)
Gra
mag
e(g
/m2 )
Den
sity
(kg/
m3)
Bul
kine
ss(g
/cm
3)
Tear
inde
x(m
Nm
2/g)
Bur
stin
dex
(kPa
m2/
g)B
reak
ing
leng
th(k
m)
Tens
ilein
dex
(Nm
/g)
Unbleached
Barley straw 3000 56.5 24.92 64.65 711.75 1.40 3.72 3.81 6.77 66.34
Hemp 9000 37.0 65.87 77.42 645.16 1.55 26.61 2.59 3.11 30.51
Sunflower
stalk3000 56.5 7.49 71.24 689.39 1.45 3.49 1.99 4.24 41.61
Rye straw 3000 35.3 28.88 72.45 679.18 1.47 6.47 3.38 6.03 59.14
Reed 3000 21.0 37.48 73.92 537.63 1.86 9.09 2.06 4.18 40.97
Tobacco stalk 3000 61.0 5.79 75.27 711.20 1.41 3.32 2.25 4.36 42.74
Wheat straw 3000 57.5 24.62 67.20 896.06 1.12 3.58 4.84 7.95 78.00
Corn stalk 3000 41.5 32.01 68.68 735.89 1.36 5.36 3.16 5.92 58.01
Rice straw 3000 65.5 26.75 69.76 611.02 1.64 4.89 3.42 6.02 59.00
Cotton stalk 3000 45.0 6.07 75.40 591.40 1.69 4.75 2.11 3.79 37.13
X+DEpD Bleached
Barley straw 3000 43.5 22.22 68.95 759.10 1.32 4.02 4.47 6.74 66.08
Hemp 9000 11 32.49 58.06 483.87 2.07 22.81 1.60 2.13 20.84
Sunflower
stalk3000 41.5 7.15 70.56 682.88 1.46 3.55 2.08 4.56 44.73
Rye straw 3000 24.0 29.40 74.60 699.34 1.43 6.87 3.71 6.37 62.49
Reed 3000 15.0 16.13 73.79 536.66 1.86 7.01 1.34 3.02 29.60
Tobacco stalk 3000 45.0 5.76 67.61 638.81 1.57 3.05 2.32 4.84 47.47
Wheat straw 3000 45.0 25.00 69.35 924.73 1.08 4.28 4.93 8.16 80.00
28
Corn stalk 3000 30.0 29.66 71.10 761.81 1.31 5.42 3.50 6.19 60.66
Rice straw 3000 53.5 29.85 62.90 550.98 1.81 5.77 4.60 6.93 67.97
Cotton stalk 3000 26.5 5.85 92.34 724.23 1.38 4.04 1.69 3.22 31.61
1
2
3
4
5
6
7
8
9
10
11
12
13
14
15
16
17
18
19
20
29
Table 6: Brightness properties of annual plant soda-AQ pulps following XDEpD1
bleaching2
Raw material Control X stageX + D1
stage
X + D1 + Ep
stage
X + D1 + Ep +
D2 stage
Wheat straw 34.5 36.70 62.34 76.06 92.0
Barley straw 39.0 42.06 62.05 74.17 86.0
Rye straw 47.8 48.62 72.51 85.09 98.3
Corn stalk 44.0 43.41 60.74 70.12 87.6
Sunflower
stalk
28.325.72 34.85 55.79 71.9
Rice straw 40.7 40.27 54.40 66.18 87.5
Tobacco stalk 31.2 30.85 44.43 56.81 68.4
Cotton stalk 19.3 17.02 35.35 42.71 61.0
Hemp 44.4 38.55 56.83 78.41 80.1
Reed 38.3 37.78 53.46 75.75 88.6
3
4
5
6
7
8
9
10
11
30
Figures1
2
3
Figure 1: Kappa numbers and viscosity values of annual plant and agricultural waste4
soda-AQ pulps5
6Figure 2: PFI beating behaviors of annual plant and agricultural waste soda-AQ pulps7
Kappa No
010203040506070
Schopper (SR°)
30
Figures2
3
4
Figure 1: Kappa numbers and viscosity values of annual plant and agricultural waste6
soda-AQ pulps7
8Figure 2: PFI beating behaviors of annual plant and agricultural waste soda-AQ pulps9
Viscosity (cp)
30
Figures3
4
5
Figure 1: Kappa numbers and viscosity values of annual plant and agricultural waste8
soda-AQ pulps9
10Figure 2: PFI beating behaviors of annual plant and agricultural waste soda-AQ pulps11
Viscosity (cp)
31
1
Figure 3: Change in the physical properties of annual plant pulps depending on the2
bleaching3
4
5
Figure 4: ISO Brightness properties of fully bleached annual plant pulps6
-4
-3.5
-3
-2.5
-2
-1.5
-1
-0.5
0
0.5
1
1.5
Tear Index (mNm2/g)
Burst Index (kPam2/g)
Breaking length (Km)
50
60
70
80
90
100
110ISO Brightness
31
2
Figure 3: Change in the physical properties of annual plant pulps depending on the4
bleaching5
5
6
Figure 4: ISO Brightness properties of fully bleached annual plant pulps7
Tear Index (mNm2/g)
Burst Index (kPam2/g)
Breaking length (Km)
ISO Brightness
31
3
Figure 3: Change in the physical properties of annual plant pulps depending on the6
bleaching7
6
7
Figure 4: ISO Brightness properties of fully bleached annual plant pulps8