Download - Ordering Number: LAST
Ordering Number: LAST
Techniques to Evaluate
Long-Term Aging of Systems
Prepared by:
Quanterion Solutions Incorporated
100 Seymour Rd.
Suite C101
Utica, NY 13502-1311
Prepared for:
Reliability Information Analysis Center (RIAC)
100 Seymour Rd.
Suite C101
Utica, NY 13502-1311
The information and data contained herein have been compiled from government
and nongovernment technical reports and from material supplied by various
manufacturers and are intended to be used for reference purposes. Neither the
United States Government nor Quanterion Solutions Incorporated warrant the
accuracy of this information and data. The user is further cautioned that the data
contained herein may not be used in lieu of other contractually cited references and
specifications.
Publication of this information is not an expression of the opinion of the United
States Government or of Quanterion Solutions Incorporated as to the quality or
durability of any product mentioned herein and any use for advertising or
promotional purposes of this information in conjunction with the name of the United
States Government or Quanterion Solutions Incorporated without written
permission is expressly prohibited.
ISBN-10: 1-933904-34-8 (Download)
ISBN-13: 978-1-933904-34-4 (Download)
Copyright © 2011 by Quanterion Solutions Incorporated. This publication was developed by Quanterion Solutions Incorporated, in support of the prime contractor (Wyle Laboratories) in the operation of the Department of Defense Reliability
Information Analysis Center (RIAC) under Contract HC1047-05-D-4005. The Government has a fully paid up perpetual
license for free use of and access to this publication and its contents among all the DOD IACs in both hardcopy and electronic versions, without limitation on the number of users or servers. Subject to the rights of the Government, this document
(hardcopy and electronic versions) and the content contained within it are protected by U.S. Copyright Law and may not be copied, automated, re-sold, or redistributed to multiple users without the express written permission. The copyrighted work
may not be made available on a server for use by more than one person simultaneously without the express written permission.
If automation of the technical content for other than personal use, or for multiple simultaneous user access to a copyrighted work is desired, please contact 877.808.0097 (toll free) or 315.732.0097 for licensing information.
Techniques to Evaluate Long-Term Aging of Systems (LAST)
100 Seymour Rd., Suite C101, Utica, NY 13502-1311 877.808.0097 i
Table of Contents
1
1
1. Introduction
2. General Design Considerations for In-Service Conditions 2
2
4
5
6
2.1.1 2.1.2 2.1.3 2.1.4 2.1.5
Temperatures
Solar Radiation (UV)
Dust (Airborne and Ground)
Thermal Temperature Cycling
Humidity 6
7
7
2.1.62.1.72.1.8 7
2.2 7
7
8
9
9
2.2.12.2.22.2.32.2.4 2.2.5
Temperature
Solar Radiation (UV)
Dust (Airborne and Ground)
Thermal Cycling
Humidity 9
2.2.6 Chemical 11
2.2.7 Compatibility 11
2.2.8 Interactions 12
2.3 12
2.3.1 Temperature 12
2.3.2 Solar Radiation (UV) 12
2.3.3 Dust (Airborne and Ground) 13
2.3.4 Thermal Cycling 13
2.3.5 Humidity 14
2.3.6 Chemical 14
2.3.7 Compatibility 15
2.3.8 Interactions 15
3. Aging Factors Related to Ferrous and Non-Ferrous Metals 15
3.1 Properties of Metals 15
3.1.2 Metal Basics 15
3.2 Failure Modes and Mitigation Techniques 18
3.2.1 Yielding 18
3.2.2 Elastic Deformation 21
3.2.3 Brinelling 21
3.2.4 False Brinelling 22
ChemicalCompatibilityInteractions
2.1
Tropical Environments
Arctic Environments
Desert Environments
Techniques to Evaluate Long-Term Aging of Systems (LAST)
ii Quanterion Solutions Incorporated
3.2.5 Brittle Fracture 23
3.2.6 Ductile Fracture 24
3.2.7 Buckling 25
3.2.8 Creep 25
3.2.9 Galling 26
3.2.10 Spalling 27
3.2.11 Wear 28
3.2.12 Fatigue 29
3.2.13 Corrosion 32
3.2.13.1 Uniform Corrosion 33
3.2.13.2 Galvanic Corrosion 36
3.2.13.3 Crevice Corrosion 42
3.2.13.4 Pitting Corrosion 44
3.2.13.5 Stress Corrosion Cracking 47
3.2.13.6 Corrosion Fatigue 55
3.2.13.7 Intergranular Corrosion 57
3.2.13.8 Selective leaching 59
3.2.13.9 Erosion corrosion 60
3.2.13.10 Exfoliation 61
3.2.13.11 Microbiological Influenced Corrosion (MIC) 62
3.2.13.12 Filiform Corrosion 64
3.2.13.13 Hydrogen Damage 65
3.2.13.14 Hot Corrosion 65
4. Polymers 69
4.1 What is a Polymer 69
4.1.1 Monomers and Macromolecules 70
4.1.2 Thermoplastics, Thermosets and Elastomers 71
4.1.2.1 Blends 72
4.1.2.2 Crystalline or Amorphous 72
4.1.2.3 Molecular Weight 73
4.1.2.4 Formation Process 73
4.1.2.5 Process Considerations for Curing Thermosets 74
4.1.2.6 Glass Transition 74
4.1.2.7 Stress-Strain 75
4.1.3 Fluids 80
4.1.4 Thermal Conductivity 81
4.1.5 Aging 81
4.2 Failure Modes and Special Environmental Considerations 82
4.2.1 Specific Design Considerations for Polymers in Out-of-Service Conditions 82
4.2.2 Specific Design Considerations for Polymers in In-Service Conditions 82
Techniques to Evaluate Long-Term Aging of Systems (LAST)
100 Seymour Rd., Suite C101, Utica, NY 13502-1311 877.808.0097 iii
4.2.2.1 High Temperature 82
4.2.2.2 Low Temperature 83
4.2.2.3 Solar Radiation (UV) 83
4.2.2.4 Thermal Temperature Cycling 83
4.2.2.5 Cyclic Mechanical Load Cycling 83
4.2.2.6 Humidity 84
5. General Reliability Design and Analysis Considerations 97
5.1 Understanding Life Cycle Cost Concepts 97
5.2 The System Design Process 110
5.3 Design for Reliability 114
5.4 Materials and Parts Selection and Control Strategies 115
5.5 Reliability Physics 122
5.6 Failure Modes, Effects and Criticality Analysis (FMECA) 125
5.7 Fault Tree Analysis (FTA) 135
5.8 Life Modeling and Testing 141
5.8.1 Acceleration Factors Used in Life Models 143
5.8.2 Accelerated Life Testing 150
5.8.3 Highly Accelerated Testing 159
5.8.3.1 Step-Stress Testing 160
5.8.3.2 Progressive Stress Testing 162
5.8.3.3 Highly Accelerated Life Testing (HALT) 163
5.8.3.4 Highly Accelerated Stress Test (HAST) 166
5.8.4 Design of Experiments 167
5.9 Reliability Testing 177
5.9.1 Reliability Growth Testing and Reliability Demonstration Testing 182
5.10 Data Collection and Analysis 200
5.10.1 Types and Sources of Data 215
5.11 Failure Analysis 217
5.11.1 Root Failure Cause Analysis 224
APPENDIX A: References Reviewed A-1
Techniques to Evaluate Long-Term Aging of Systems (LAST)
100 Seymour Rd., Suite C101, Utica, NY 13502-1311 877.808.0097 1
1. INTRODUCTION
The Reliability Information Analysis Center mission has continued to evolve over the years
(including its years as the Reliability Analysis Center (RAC)) with the greater recognition that
reliability, maintainability, and quality are critical military system and commercial product
attributes. Coincident with the evolution has been the recognition that these attributes have much
more encompassing impacts than their specific attained metrics. For example, where at one time
the measure of reliability called mean-time-between-failure (MTBF) was of interest in itself, now
management and system planners have expanded their interest because of how that MTBF impacts
such issues as sustainability and total ownership costs. Part of the refocusing of reliability-related
needs is the concern over long-term aging effects on systems in operation and in storage brought
about by systems having to last longer.
The objective of this report is to highlight the impact of long-term aging effects on parts,
assemblies and equipments by investigating characteristics of aging as they impact specific
material classes.
The report is broken down into the following sections:
Section 2 addresses general environmental design considerations for aging during
in-service conditions
Section 3 discusses aging factors as they relate to ferrous and non-ferrous metals
Section 4 provides an overview of aging as it applies to polymer materials
Section 5 covers general reliability design considerations and appropriate tasks/techniques
2. GENERAL DESIGN CONSIDERATIONS FOR IN-SERVICE CONDITIONS
Various environmental extremes can accelerate material failure mechanisms, thereby affecting the
aging of designs in which they are used. Some environments may introduce peculiar stress
conditions that may not be of major concern in any of the other environments.
Although the following sub-sections address individual components of environmental stress
parameters (temperature, humidity, UV, etc.) it must be recognized that many of these components
may act in concert with one-another. A failure to consider the potential combined effects of these
parameters can lead to a serious underestimation of their overall effect on material aging.
In the sections related to environment, the terms desert, arctic and tropical are used to identify
major, non-temperate terrestrial environments on earth that present extreme environmental
conditions that may impact material selections for a design.
The word ‘desert’ usually brings to mind the hot deserts such as the Sahara. Technically, however,
a desert is any land area that has an annual moisture deficit. Accordingly, the polar and tundra land
areas are also deserts and, in fact, constitute the majority of all desert area. In addition, the term hot
desert and ‘tropical desert’ are often used synonymously.
Due to the potential confusion of terms, and because the environments cannot be definitely
associated with boundaries, this guideline will loosely define the three environments as follows: