ceramic coated separator for lithium-ion batteries

1
Product Data Sheet Ceramic Coated Separators Product Properties: Material = Polyethylene with Aluminum Oxide Coating (Both Sides) Montreal Head Office 18105 Transcanadienne, Kirkland, Quebec H9J 3Z4 Canada Tel.: +1 514 695 8095 Fax.: +1 514 695 0593 E-mail: [email protected] www.targray.com PDS Targray Ceramic Coated Separators Rev 1 8 Oct 2013 | Pg 1 of 1 Item Unit 12 15 18 22 Width mm ≤ User Spec ± 0.5 ≤ User Spec ± 0.5 ≤ User Spec ± 0.5 ≤ User Spec ± 0.5 Thickness µm 7 + 2.5/2.5 9 + 3/3 12 + 3/3 16 ± 3/3 Length mm 1000 + 10/-0 1000 + 10/-0 1000 + 10/-0 1000 + 10/-0 Permeability (Gurley Type) sec/100ml 160 ± 50 200 ± 50 200 ± 50 250 ± 50 Porosity % 50 ± 5.0 45 ± 5.0 Break Strength MD kgf/cm ≥1600 ≥1200 ≥1700 ≥1700 TD ≥1800 ≥1200 ≥1100 ≥1700 Break Elongation MD % ≤52 ≤120 ≤120 ≤120 TD ≤60 ≤120 ≤120 ≤120 Puncture Strength gf ≥350 ≥400 ≥400 ≥500 Heat Shrinkage 105 ºC/1 hr MD % ≤0.5 ≤0.7 ≤5.0 ≤1.0 TD ≤0.2 ≤0.4 ≤3.0 ≤1.0 Heat Shrinkage 130 ºC/1 hr MD % ≤0.5 ≤0.5 ≤2.0 ≤2.0 TD ≤1.0 ≤0.0 ≤2.0 ≤2.0 Heat Shrinkage 150 ºC/1 hr MD % ≤1.0 ≤1.0 ≤3.0 ≤3.0 TD ≤1.0 ≤1.0 ≤3.0 ≤3.0 Shut-down Temp (actual) ºC 150 150 150 150 Shut-down Temp (DSC) ºC 136 ~ 140 136 ~ 140 136 ~ 140 136 ~ 140

Upload: targray

Post on 17-Jan-2017

97 views

Category:

Science


4 download

TRANSCRIPT

Page 1: Ceramic Coated Separator for Lithium-Ion Batteries

Product Data Sheet

Ceramic Coated Separators

Product Properties:Material = Polyethylene with Aluminum Oxide Coating (Both Sides)

Montreal Head Office18105 Transcanadienne, Kirkland, Quebec H9J 3Z4 CanadaTel.: +1 514 695 8095 • Fax.: +1 514 695 0593E-mail: [email protected] • www.targray.com

PDS Targray Ceramic Coated Separators Rev 1 8 Oct 2013 | Pg 1 of 1

Item Unit 12 15 18 22

Width mm ≤ User Spec ± 0.5 ≤ User Spec ± 0.5 ≤ User Spec ± 0.5 ≤ User Spec ± 0.5

Thickness µm 7 + 2.5/2.5 9 + 3/3 12 + 3/3 16 ± 3/3

Length mm 1000 + 10/-0 1000 + 10/-0 1000 + 10/-0 1000 + 10/-0

Permeability (Gurley Type) sec/100ml 160 ± 50 200 ± 50 200 ± 50 250 ± 50

Porosity % 50 ± 5.0 45 ± 5.0

Break StrengthMD

kgf/cm≥1600 ≥1200 ≥1700 ≥1700

TD ≥1800 ≥1200 ≥1100 ≥1700

Break ElongationMD

%≤52 ≤120 ≤120 ≤120

TD ≤60 ≤120 ≤120 ≤120

Puncture Strength gf ≥350 ≥400 ≥400 ≥500

Heat Shrinkage 105 ºC/1 hrMD

%≤0.5 ≤0.7 ≤5.0 ≤1.0

TD ≤0.2 ≤0.4 ≤3.0 ≤1.0

Heat Shrinkage 130 ºC/1 hrMD

%≤0.5 ≤0.5 ≤2.0 ≤2.0

TD ≤1.0 ≤0.0 ≤2.0 ≤2.0

Heat Shrinkage 150 ºC/1 hrMD

%≤1.0 ≤1.0 ≤3.0 ≤3.0

TD ≤1.0 ≤1.0 ≤3.0 ≤3.0

Shut-down Temp (actual) ºC 150 ↓ 150 ↓ 150 ↓ 150 ↓

Shut-down Temp (DSC) ºC 136 ~ 140 136 ~ 140 136 ~ 140 136 ~ 140