Available online at www.worldscientificnews.com
WSN 28 (2016) 30-40 EISSN 2392-2192
Biogenic production of zinc oxide nanoparticles from aqueous extracts of Duranta erecta L.
C. P. Ravindran, M. Manokari, Mahipal S. Shekhawat*
Biotechnology Laboratory, Department of Plant Science, M.G.G.A.C. Mahe, Pondicherry - 673 311, India
*E-mail address: [email protected]
ABSTRACT
The present communication reports the biosynthesis of zinc oxide nanoparticles using aqueous
extracts of leaves, stem, root, flowers and fruits of Duranta erecta L. This plant gains horticultural and
medicinal importance due to its various biological activities. Zinc Nitrate Hexahydrate [Zn
(NO3)2·6H2O] solution was used as a precursor to synthesize Zinc oxide nanoparticles. The various
plant (leaves, stem, roots, flowers, fruits) extracts played as reducing agents. The leaf extract showed
strong absorbance peak at 302 nm, stem and flower peaks were located at 299 nm, roots at 293 nm and
fruit extract solution peak observed at 317 nm.
Keywords: Bioreduction, Zinc oxide nanoparticles, Duranta erecta L, Characterization
1. INTRODUCTION
The quasi-zero-dimensional nanomaterials from plant source have been effectively
proved in controlling the various endemic diseases without adverse effects. The natural
phytochemicals such as alkaloids, steroids flavonoids, tannins, saponins and other nutritional
compounds derived from various parts of plants like leaves, stems, roots, flowers, fruits,
World Scientific News 28 (2016) 30-40
-31-
seeds and barks are studied to synthesize nanoparticles (Mittal et al., 2013; Kuppusamy et al.,
2014).
Biogenic production of metal oxide nanoparticles from plants, particularly zinc oxide
nanoparticles (ZnO NPs) received global attention due to ample applications in medicines and
agriculture.
Zinc oxide nanoparticles are reported efficiently to protect over a broader UV range
than any of the molecular UV-absorbers, photocatalytic degradation of environment
pollution, biocompatibility in drug delivery mechanisms and as nanofertilizers and
nanopesticides (Devalapally et al., 2007; Kulkarni and Muddapur, 2014; Sabir et al., 2014).
Extracts of a diverse range of plant species have been successfully used to synthesize
nanoparticles (Vidya et al., 2013; Shekhawat et al., 2014). Different methods of particle
characterization and its potential applications in medicine are widely discussed by many
researchers (Kuppusamy et al., 2014).
(A)
World Scientific News 28 (2016) 30-40
-32-
(B) (C)
Fig. 1A. Morphology of the plant Duranta erecta.
Fig. 1B. Shoots with flowers.
Fig. 1C. Branches with fruits.
The present study concerns with biological production of zinc oxide nanoparticles from
whole plant extract of Duranta erecta L.
Duranta erecta (syn. Duranta repens) is a horticultural plant with immense medicinal
properties, a member of the family Verbenaceae. It is popularly known as Golden dewdrop,
pigeon berry or skyflower and cultivated as an ornamental plant in tropical and subtropical
gardens throughout the world (Anis et al., 2001). It is a shrub, attaining the height of 3 m, the
leaves are pale-green, and flowers are lavender, produced in tight clusters. The fruit is
globose orange berry. (Fig. 1A-C).
D. erecta is used medicinally for a wide variety of ailments. The whole plant is utilized
as insect repellent, vermifuge, diuretic, antidote to treat itches, infertility, pneumonia, malaria,
intestinal worms, abscesses and neuralgic disorder (Castro et al., 1996; Whistler, 2000;
Rahmatullah et al., 2011). This plant exhibits antioxidant, antibacterial and antimicrobial
activities against human pathogens (Bangou et al., 2012; Prabhakar et al., 2015). It is
endowed with several iridoid glycosides as durantosides and lamiide, flavonoids, alkaloid,
saponnins, acetosides and tannins (Anis et al., 2000; Ahmed et al., 2009; Khanal et al., 2014).
World Scientific News 28 (2016) 30-40
-33-
Recently Patil and Hooli (2015) explored D. erecta in biogenic production of silver
nanoparticles, and evaluated its antimicrobial activity.
The present investigation concentrates on synthesis of metal oxide zinc nanoparticles
(ZnO) and their characterization with the aid of UV-Visible spectrophotometry using
horticultural and medicinal important plant D. erecta.
2. MATERIALS AND METHODS
2. 1. Collection of plant material
D. erecta is mostly cultivated as ornamental plant. The plant material was collected
from the coastal area of Pondicherry, India. The whole plant was harvested and fresh green
leaves, stem, roots, flowers and fruits were collected during the months of July to December,
2014. All the plant parts were washed with distilled water and finely chopped into small
pieces (Fig. 2AB - 6AB).
D. erecta is mostly cultivated as ornamental plant. The plant material was collected
from the coastal area of Pondicherry, India. The whole plant was harvested and fresh green
leaves, stem, roots, flowers and fruits were collected during the months of July to December,
2014. All the plant parts were washed with distilled water and finely chopped into small
pieces (Fig. 2AB - 6AB).
2. 2. Preparation of broth solution
The broth solution (plant extracts) were prepared using 5 gm each of washed and
chopped leaves, stem, roots, flowers and fruits in a 250 ml Erlenmeyer flask with 50 ml of
sterile double distilled water and then boiling the mixture for 5 min. The aqueous herbal
extracts were collected in separate conical flasks by standard filtration method and stored at 4
°C in a refrigerator for further experimentation.
2. 3. Preparation of precursor
Zinc Nitrate Hexahydrate [Zn (NO3)2·6H2O] (Merck, Mumbai) was used as a precursor
to synthesize ZnO nanoparticles from D. erecta in the present study. 1 mM Zinc nitrate
solution was prepared using sterile double distilled water and stored in brown bottle at 4 °C
for further use to synthesize ZnO nanoparticles from leaf, stem, roots, flowers and fruits of D.
erecta.
2. 4. Synthesis of ZnO nanoparticles
Three boiling tubes were used to synthesize ZnO nanoparticles, one containing 10 ml of
1 mM Zinc nitrate solution and the second one containing 10 ml of aqueous plant extract and
the third one containing 9 ml of 1 mM Zinc nitrate solution and 1 ml of plant extracts as test
solution. The reaction mixture from the third tube was centrifuged at 5000 rpm for 15 min to
obtain the pellet after 2 to 3 hrs. Supernatant is discarded and the pellet is dissolved in
deionized water.
World Scientific News 28 (2016) 30-40
-34-
Fig. 2A-C. Leaves and reaction mixtures.
Fig. 3A-C. Stems and reaction mixtures.
Fig. 4A-C. Roots and reaction mixtures.
2. 5. UV-VIS spectral analysis
The bioreduction of ZnO metal ions in solutions was monitored by measuring the UV-
VIS spectrum of the reaction medium. The UV-VIS spectral analysis of the sample was done
by using Systronics Double Beam spectrophotometer (Model 2202, Systronics Ltd. India) at
room temperature operated at a resolution of 1nm between 200 nm and 700 nm ranges.
2
4
3 C
C
C
B
B
B A
A
A
World Scientific News 28 (2016) 30-40
-35-
Fig. 5A-C. Flowers and reaction mixtures.
Fig. 6A-C. Fruits and reaction mixtures.
3. RESULTS AND DISCUSSION
The bioreduction of zinc oxide nanoparticles using leaf, stem, root, flowers and fruit
extracts of D. erecta was investigated in this study. After treating the extracts of D. erecta
with Zinc nitrate solution, the color change of the reaction mixture was visually observed in
cell free extracts of leaves, roots, flowers and fruits.
The reduction of Zinc nitrate ions into zinc nanoparticles during exposure to the plant
extract is followed by color change from colorless to pale yellow. Initially the color of cell
free extract of stem with metallic precursor was unchangeable, and turned into lemon yellow
when it was heated for 20 min (Fig. 2C-6C). Zinc nitrate is an organometallic precursor and
these color changes observed because of the excitation of surface plasmon vibrations in the
zinc nanoparticle.
The time taken for the reaction mixture to change the color was varied with plant
extracts. Plant mediated zinc oxide nanoparticles are widely accepted in cosmetic industry
and agriculture (Mittal et al., 2013; Sabir et al., 2014). Plant mediated nanoparticle synthesis
using whole plant extract is reported in number of plants (Park et al., 2011).
5 C B A
6 C B A
World Scientific News 28 (2016) 30-40
-36-
7 B
World Scientific News 28 (2016) 30-40
-37-
7 C
7 D
World Scientific News 28 (2016) 30-40
-38-
Fig. 7A. Absorbance peak with leaves extract.
Fig. 7B. Absorbance peak with stem extract.
Fig. 7C. Absorbance peak with roots extract.
Fig. 7D. Absorbance peak with flowers extract.
Fig. 7E. Absorbance peak with fruits extract.
Environmentally benign Zinc oxide nanoparticles from plants extracts were reported
from Passiflora foetida (Shekhawat et al., 2014), Hemidesmus indicus (Shekhawat and
Manokari, 2015), Coriandrum sativum, Acalypha indica (Gnanasangeetha and Thambavani,
2013a; 2013b) and Calotropis procera (Singh et al., 2011) etc. due to its cost effective non-
hazardous procedures.
The reduction of zinc oxide nanoparticles were characterized by UV-Visible
spectrophotometer and the readings were recorded at regular intervals using Double Beam
spectrophotometer. UV-Visible spectroscopy is an important technique to monitor the
formation and stability of metal nanoparticle in aqueous solution. The biosynthesis of zinc
oxide nanoparticles from the reaction mixture in the third tube was confirmed by evaluating
its optical properties. This analysis showed an absorbance peak between 290 – 350 nm, which
was specific for ZnO nanoparticles. The aqueous reaction mixture of leaves showed strong
broad peak at 302 nm, stem and flowers peak were located at 299 nm, roots at 293 nm and
fruit at 317 nm (Fig. 7A-E). The biomolecules and bioreducing agents from the plants such as
7 E
World Scientific News 28 (2016) 30-40
-39-
enzymes, proteins, flavonoids, terpenoids and cofactors present in the plant parts are of
significant in converting nanoparticles (Mittal et al., 2013). The phytomolecules such as
glycosides, saponins and tannins present in D. erecta plant extracts can be used to reduce
metal ions to nanoparticles in a single-step green synthesis process. Zinc oxide nanoparticles
are emerging with huge application in crop protection and agriculture (Prez-de-Luque and
Rubiales, 2009; Nair et al., 2010; Khot et al., 2012). The use of zinc oxide nanoparticles in
antimicrobial food packaging has also been reported (Prez Espitia et al., 2012). This biogenic
reduction of zinc oxide nanoparticles is quite rapid, readily conducted at room temperature
and pressure, and easily scaled up.
4. CONCLUSION
The method for zinc oxide nanoparticle synthesis described in this paper is a green
procedure, using environmentally non-hazardous natural resources. Plant extracts act as a
reducing and stabilizing agents for the bioreduction reaction to synthesize zinc oxide with a
lot of advantages such as cost effective, biocompatibility allowing large scale commercial
production of the herbal nanoparticles. Thus, the study ascertains the value of D. erecta in
nano-field, which could be of considerable interest to the development of new drugs in
medical field and production of pesticides and nano-bio-fertilizers in revolutionizing
agriculture.
References
[1] A. K. Mittal, Y. Chisti, U. C. Banerjee, Biotechnology Advances 31 (2013) 346-356.
[2] P. Kuppusamy, M. M. Yusoff, G. P. Maniam, N. Govindan, Saudi Pharmaceutical
Journal, 2014 doi: 10.1016/j.jsps.2014.11.013.
[3] H. Devalapally, A. Chakilam, M. M. Amiji. Journal of Pharmaceutical Sciences 96
(2007) 2547-2565.
[4] N. Kulkarni, U. Muddapur. Journal of Nanotechnology 1 (2014) 1-8.
[5] S. Sabir, M. Arshad, S. K. Chaudhari. The Scientific World Journal 10 (2014) 1-8
[6] C. Vidya, H. Shilpa, M. N. Chandraprabha, M. A. Lourdu Antonyrai, V. Indu, J.
Aayushi, B. Kokil, International Journal of Current Engineering and Technology
(2013) 118-120.
[7] M. S. Shekhawat, C. P. Ravindran, M. Manokari, International Journal of Green and
Herbal Chemistry 3 (2014) 518-523.
[8] I. Anis, E. Anis, S. Ahmed, G. Mustafa, A. Malik, Z. Amtul, Atta-ur-Rahman,
Helvetica Chimica Acta 84 (2001) 649-655.
[9] O. Castro, M. Barrios, M. Chinchilla, O. Guerrero, Revista de Biologia Tropical 44
(1996) 361-367.
[10] W. A. Whistler, Timber Press, Inc., Portland, OR. 2000.
World Scientific News 28 (2016) 30-40
-40-
[11] M. Rahmatullah, R Jahan, F. M. S. Azam, S. Hossan, M. A. H. Mollik, T. Rahman,
African Journal of Traditional Complementary and Alternative Medicine 8 (2011) 53-
65.
[12] M. J. Bangou, N. T. R. Meda, A. M. E. Thiombiano, M. Kiendrebeogo, B. Zeba,
Current Research Journal of Biological Sciences 4 (2012) 665-672.
[13] G. Prabhakar, P. Kamalakar, V. T. Ashok, K. Shailaja, European Journal of
Pharmaceutical and Medical Research 2 (2015) 411-419.
[14] I. Anis, S. Ahmed, A. Malik, A. Yasin, M. I. Choudary, Chemical and Pharmaceutical
Bulletin 50 (2000) 515-518.
[15] W. S. Ahmed, M. A. Mohamed, R. A. El-Dib, M. M. Hamed. Molecules 14 (2009)
1952-1965.
[16] D. P. Khanal, B. Raut, R. K. Majhi, A. Kaini, R. Basnet, P. K. Mahat, An International
Journal of Advances in Pharmaceutical Sciences 5(2014) 1958-1962.
[17] B. M. Patil, A. A. Hooli, Nano Trend: A Journal of Nanotechnology and Its
Applications 14 (2015) 13-18.
[18] Y. Park, Y. N. Hong, A. Weyers, Y. S. Kim, R. J. Linhardt, Nanobiotechnology 5
(2011) 69-78.
[19] M. S. Shekhawat, M. Manokari, International Journal of Research Studies in
Microbiology and Biotechnology (1) 2015 20-24.
[20] D. Gnanasangeetha, D. S. Thambavani, Journal of Chemical Biological and Physical
Sciences 4 (2013b) 238-246.
[21] D. Gnanasangeetha, D. S. Thambavani, Research Journal of Material Science 1 (2013a)
1-8.
[22] R. P. Singh, V. K. Shukla, R. S. Yadav, P. K. Sharma, P. K. Singh, A. C. Pandey,
Advanced Materials Letters 2 (2011) 313-317.
[23] L. R. Khot, S. Sankaran, J. M. Maja, R. Ehsani, E. W. Schuster, Crop protection 35
(2012) 64-70.
[24] R. Nair, S. H. Varghese, B. G. Nair, T. Maekawa, Y. Yoshida, D. S. Kumar, Plant
Science 179 (2010) 154-163.
[25] P. J. Perez Espitia, N. F. Ferreira Soares, J. S. Reis Coimbra, N. J. Andrade, R. S. Cruz,
E. A. Alves Medeiros, Food Bioprocess Technology 5 (2012) 1447-1464.
[26] A. Perez-de-Luque, D. Rubiales, Pest Managment Science 65 (2009) 540-545.
( Received 17 October 2015; accepted 31 October 2015 )