Bab 2 & 3 Materials, Manufacturing, Welding
Piping system Integrity
1
BAB 2 & 3PIPE MATERIALS,
MANUFACTURING AND WELDING
2
PENDAHULUANBAGIAN I
1. UMUMBERDASARKAN DATA YANG ADA, 30% DARI MODALYANG DIALOKASIKAN UNTUK INDUSTRI KIMIA PROSES, DITUJUKAN UNTUK: KATUP, FITTINGS DAN KOMPONEN2 LAIN YANG BERHUBUNGAN DENGAN PEMIPAAN
2. FUNGSI- KONSTRUKSI- MENYALURKAN/MENGALIRKAN FLUIDAPARAMETER: T, P DAN v
- MENERUSKAN DAYAPARAMETER: Mt dan μ
- MENTRANSFER/MEMINDAHKAN PANAS
![Page 2: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/2.jpg)
2
3
3. STANDAR:BAIK UNTUK PIPA, KOMPONEN-KOMPONENNYA MAUPUN MATERIAL DAN PENGENDALIAN KOROSI;- ASME- API- ASTM- ANSI/AWWA- TEMA- HEI- NACE
CATATAN:A. STANDAR: MERUPAKAN DOKUMEN YANG
BERFUNGSI SBG MODEL DALAM PENGUKURAN SIFAT ATAU PENETAPAN PROSEDUR. TERDIRI DARI: SPESIFIKASI, METODA UJI DAN REC.PRACTICE
4
B. SPESIFIKASIPERNYATAAN PERSYARATAN TEKNIK DANKOMERSIL YG HARUS DIPENUHI OLEH SUATUPRODUK
C. METODA UJIKUMPULAN INSTRUKSI UNTUK MENGIDENTIFIKASIMENGUKUR ATAU MENGEVALUASI SIFAT2 MATERIAL
D. RECOMMENDED PRACTICEKUMPULAN INSTRUKSI UTK MELAKSANAKAN SATUATAU LEBIH OPERASI ATAU FUNGSI SELAINMENGIDENTIFIKASI, MENGUKUR ATAU MENGEVALUASI.
![Page 3: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/3.jpg)
3
5
E. KODESUATU STANDAR ATAU KUMPULAN PERATURANYANG HARUS DIADOPSI.
6
CONTOH SPESIFIKASI MATERIAL MENURUT ASTM:
![Page 4: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/4.jpg)
4
7
ASTM SPEC FOR METALLIC PIPE:
-C-STEEL………………….....A53 (welded and seamless)A106 (seamless pipe)
A105 (FORGINGS)
A181 (FORGED FLANGES)
A234 (FITTINGS)
-INCONEL 600 B167 (SEAMLESS PIPE)
-ALUMINUM B241 (SEAMLESS PIPE)
-COPPER B43 (SEAMLESS PIPE)
-TITANIUM B337 (SEAMLESS PIPE)
8
CHEMICAL COMPOSITION OF METALLIC PIPING MATERIALS
C Cr Cu Fe Mn Mo Ni Si
![Page 5: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/5.jpg)
5
9
CONTOH SISTEM AISI-SAE
10
![Page 6: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/6.jpg)
6
11
SISTEM YANG DIKEMBANGKAN OLEH DIN DANAFNOR:• BAJA KARBON:
- St.37; kadang2 ditulis St.370. Namun saat ini ditulisSt.285
- St.42.11- St.OO
• BAJA UNTUK PERLAKUAN PANAS- C45 (BANDINGKAN DENGAN S45C PADA JIS)- Ck 45
• BAJA PADUAN RENDAH (U.P KURANG DARI 5%)- UNTUK UNSUR2: Cr, Co, Mn, Ni, Si; ANGKA YANG
ADA HARUS DIBAGI 4; UNTUK Mo, W DAN V 100CONTOH: 100Cr6; 16MnCr5
12
• BAJA PADUAN TINGGI DINYATAKAN DENGAN ADANYA HURUF X DIDEPAN DESIGNASI. ANGKA YANG TERAKHIR TIDAK PERLU DIBAGI 4 ATAU 100CONTOH: X30Cr12
BEBERAPA PENGERTIAN DARI SPESIFIKASIPIPA:
1. SPESIFIKASI PIPA YANG UTAMA ADALAH API 5L; MERUPAKAN KOMBINASI DARI API 5L, 5LX DAN 5LS. PEMILIHAN “GRADE”NYA TERGANTUNG PADA RASIO KEKUATAN TERHADAP BERAT (STRENGTH TO WEIGHT)
2. GRADE “LOW STERNGTH” ADALAH GRADE A DAN B (30 DAN 35 KSI YS MIN).
![Page 7: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/7.jpg)
7
13
3. GRADE “EXTRA STRENGTH (X)” ADALAH X42 S/D X70X42 BERARTI: PIPA DGN MIN YS 42 KSI. YANG PALINGUMUM DIGUNAKAN ADALAH X52KEKUATAN MAKS YANG DAPAT DICAPAI MELALUICOLD EXPANSION TANPA PENAMBAHAN UNSURPADUAN.
PENAMBAHAN UNSUR PADUAN DIMAKSUDKAN UNTUK:
• MENGONTROL KEKUATAN• MEMPERBAIKI MAMPU LAS• MEMPERBAIKI NOTCH TOGHNESS.
14
FUNGSI UNSUR PADUAN DAN BATAS2NYA:1. KARBON:
0.20% UTK API X60-X72; 0.26% UTK X520.08% UTK MENGHINDARI PWHT.
2. SILIKON: 0.13 – 0.33%3. MANGAN: 0.8 – 1.6%
RASIO Mn/C = 4/1; UTK NOTCH TOUGHNESS YANGBAIK.RASIO Mn/Si= 3/1 UTK MENINGKATKAN MAMPU LASMAKIN TINGGI Mn; MAMPU LAS SEMAKIN RENDAH.
4. V DAN Nb (Cb); PENGHALUS BUTIR (X60)5. Ti DAN Zr SEBAGAI PENGHALUS BUTIR6. Mo < 0.2% UNTUK MEMINIMIZE M DAN UB.
![Page 8: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/8.jpg)
8
15
KLASIFIKASI PIPA DIDASARKAN PADA PENGGUNAANNYA:1. STANDARD PIPE:
A. Standard weight pipe (black & galvanized)B. Extra strong pipeC. Double extra strong pipe
8. LINE PIPE:A. Gas LineB. Oil linesC. Water transmission linesD. Slurry lines.
13. PRESSURE PIPING:A. High Pressure steam/chemical linesB. Hot oil lines.
16
17. OIL COUNTRY TUBULAR PRODUCT/GOODS(OCTP/OCTG);A. Oil Well CasingB. Oil Well TubingC. Drill PipeD. Drive Pipe
18. PRESSURE TUBES19. OIL STILL TUBE20. HEAT EXCHANGER AND CONDENSER
TUBES21. MECHANICAL TUBES22. STAINLESS STEEL PIPE AND TUBES.
![Page 9: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/9.jpg)
9
17
CATATAN UNTUK OCTG:1. METODA MANUFAKTUR:
- Seamless- ERWUmumnya disambungkan dengan “coupling” (bukanpengelasan); jadi material yang digunakan lazimnyaadalah:
- Baja C-tinggi- Low alloy steel for SSC resistance- Cr and high alloy steels for CO2 resistance andCO2/SSC resistance (AISI 420)
- Jika ada H2S dan CO2; 13%Cr menjadi sensitif thdSSC----22-25%Cr duplex SS atau High Ni base alloy
18
2. LINE PIPE:A. TIPE DAN METODA PRODUKSI:
- Gathering lines: mengalirkan crude oil dan naturalgas hasil well
` - Flow lines: mengalirkan crude oil dan natural gaske dehydration/gas treatment/refining plants atauplatforms. Pipa FL diexpose pada lingkungan yangkorosif; diameter kecil dan heavy wall seamless.
- Trunk lines: mengalirkan dehydrated oil & gas keconsuming centers. Diameternya besar, UOE danlongitudinal seam welding pipe.
![Page 10: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/10.jpg)
10
19
B. MATERIAL:
KARENA LINE PIPE DISAMBUNGKAN DENGAN CARA DILAS; MAKA DIPERLUKAN MATERIAL YANG “WELDABLE”, HIGH STRENGTH DAN CORROSION RESISTANCE
- C-STEEL DENGAN TOUGHNESS YANG TINGGI (DARI BAHAN PELAT BAJA HASIL TMCP)
- Cr AND HIGH ALLOY STEELS FOR CO2 AND CO2/SSCRESISTANCE
- HIGH GRADE OCTG
20
BAGIAN IIPROSES PEMBUATAN PIPA
A. WELDING PROCESS:
1. BUTT WELD PROCESSES(1/8 INCH TO 4 INCHES NOMINAL DIAMETER)
![Page 11: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/11.jpg)
11
21
22
![Page 12: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/12.jpg)
12
23
II. ELECTRIC WELD PROCESSES:
A. ELECTRIC RESISTANCE WELD (ERW)B. ARC WELDING PROCESSES (SMAW/MMA; SAW;
FCAW).
TO PRODUCE THE ENTIRE SIZE RANGE OF PIPE, TUBE AND LINE PIPE.
24
![Page 13: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/13.jpg)
13
25
26
B. SEAMLESS PROCESS
I. PIERCING PROCESSES: ROLL AND DISC PIERCINGARE USED TO MAKE PIPES AND TUBES UP TO 26INCHES IN DIAMETER.A. HOT FINISHED (TO 26” OD)B. COLD DRAWN (ANY SIZE UP TO 10 ¾” OD)C. COLD EXPANDING (SIZES 16” TO 26” OD)
II. VERTICAL PIERCING PROCESSTO MAKE TUBES AND CYLINDERS, 3 TO 20” ODHOT DRAWN (FINISH).
III. EXTRUSION PROCESS (SMALL SIZES ONLY)
![Page 14: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/14.jpg)
14
27
28
![Page 15: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/15.jpg)
15
29
30
![Page 16: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/16.jpg)
16
31
32
PENGENDALIAN KUALITAS YANG DILAKUKAN:
1. PEMERIKSAAN PELAT BAHAN PIPA DENGAN METODA ULTRASONIK
![Page 17: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/17.jpg)
17
33
2. PEMERIKSAAN LAS-LASAN PADA PIPA UOE DAN ERW.
METODA PEMERIKSAAN: UT DAN X-RAY
34
![Page 18: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/18.jpg)
18
35
3. PEMERIKSAAN KUALITAS PIPA SEAMLESS DENGAN METODA EDDY CURRENT, ELECTROMAGNETIC; MAGNETIC DAN UT
36
![Page 19: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/19.jpg)
19
37
PENERAPAN COATING;
1. EXTERNAL COATING:
BAHAN: POLYETHYLENE UNTUK PIPA DENGAN DIAMETER YANG KECIL DAN MEDIUM
* GENERAL UNDERGROUND SERVICE
* HIGHLY CORROSIVE SOIL SERVICE
* UNDERWATER SERVICE
NOMINAL DIAMETER: ½ - 24 IN.
PIPE LENGTH: 20 – 40 FT
STANDARD COATING THICKNESS: 0.06 – 0.1 IN
38
![Page 20: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/20.jpg)
20
39
UNTUK DIAMETER PIPA YANG BESAR COATING DILAKUKAN DENGAN CARA: HELICALLY WRAPPED.
NOMINAL DIAMETER: 16 – 64 IN.
PIPE LENGTH: 20-62 FT
STANDARD COATING THICKNESS: 0.1 – 0.12 IN
BAHAN PELAPIS LAIN YANG DIGUNAKAN ADALAH:
FUSION BONDED EPOXY POWDER. LAZIM DITERAPKAN PADA PIPA DENGAN DIAMETER YANG BESAR.
STANDARD COATING THICKNESS: 14 MIL (350 MIKRON)
40
![Page 21: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/21.jpg)
21
41
UNTUK MEMELIHARA UJUNG PIPA (PIPE END); TERUTAMA UNTUK DIAMETER PIPA YANG BESAR, DILAKUKAN PEMASANGAN “BEVEL PROTECTOR”
UNTUK PIPA YANG KECIL DIPASANG VINYL SHEET COVER
42
2. INTERNAL COATING:
LAZIMNYA DITUJUKAN UNTUK MENURUNKAN GESEKAN ANTARA FLUIDA DAN DINDING PIPA BAGIAN DALAM
BAHAN YANG DIGUNAKAN: EPOXY RESIN, PHENOLIC DAN ATAU BAKED URETHANE
DIAMETER NOMINAL YANG LAZIM ADALAH: ½ - 56 IN.
PANJANG PIPA: 20-45 FT.
![Page 22: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/22.jpg)
22
43
C. CENTRIFUGAL CASTING:
44
D. PROSES PEMBUATAN PIPA YANG LAIN:
I. UOE PIPE (U-ING; O-ING AND EXPAND-ING)II. ERW PIPEIII. SPIRAL WELD (SP) PIPEIV. ROLL AND PRESS BENDING (RP) PIPE
![Page 23: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/23.jpg)
23
45
46
![Page 24: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/24.jpg)
24
47
48
![Page 25: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/25.jpg)
25
49
BAGIAN IIIMATERIAL PIPA
PENDAHULUAN:KLASIFIKASI/PENGELOMPOKAN MATERIAL:
SECARA UMUM; MATERIAL DIMANFAATKAN ATAS DASARSIFAT-SIFATNYA.
P0LIMERLOGAM
KERAMIK
KOMPOSIT
50
MATERIAL METALIK MASIH MERUPAKAN MATERIALYANGDOMINAN, KARENA:
• DAPAT DIUBAH SIFATNYA SECARA TERMAL• DAPAT DIDEFORMASI DAN DIFABRIKASI
MATERIAL METALIK TERDIRI DARI:
• MATERIAL FERRO: BAJA, BESI COR• MATERIAL NON-FERRO:
- ALUMINUM DAN PADUANNYA- TEMBAGA DAN PADUANNYA- NIKEL, DSB
![Page 26: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/26.jpg)
26
51
KLASIFIKASI, DESIGNASI DAN SPESIFIKASI BAJA:
BAJA DIKELOMPOKAN BERDASARKAN:• KOMPOSISI• KEKUATAN• BENTUK PRODUK
PADA DOKUMEN “PROCUREMENT” HARUS TERCANTUM:• SCOPE: MELIPUTI KLASIFIKASI PRODUK, UKURAN DAN
KONDISI• KOMPOSISI KIMIA• KUALITAS• PERSYARATAN KUANTITATIF• PERSYARATAN LAINNYA
52
SIFAT BAJA:1. SIFAT MEKANIK:
- KUAT- KERAS- ULET/LIAT- TANGGUH- TAHAN BENTUR, DSB
2. SIFAT FISIK:- TAHAN KOROSI- MASA JENIS- KONDUKTIFITAS PANAS DAN LISTRIK- DSB
3. SIFAT TEKNOLOGI:- MAMPU MESIN, MAMPU BENTUK, MAMPU LAS DSB
![Page 27: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/27.jpg)
27
53
MUNGKINKAH SIFAT-SIFAT TSB DAPATDIUBAH?
BEBERAPA CARA MENGUBAH SIFAT BAJA:
• PEMADUAN• PENGERJAAN MEKANIK• PENERAPAN PERLAKUAN PERMUKAAN• PENERAPAN PERLAKUAN PANAS• PENGUBAHAN UKURAN BUTIR
54
STRUKTUR MIKRO BAJA KARBON:
• DEFINISI• DIAGRAM FASA Fe-C
![Page 28: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/28.jpg)
28
55
DIAGRAM FASA INI MENAMPILKAN:
1. LARUTAN PADAT (SOLID SOLUTION) SEPERTI:- FERIT (α)- AUSTENIT (γ)- DELTA (δ)SIFAT LP ADALAH “LUNAK”
2. SENYAWA (COMPOUND):- SEMENTIT (KARBIDA BESI/Fe3C)SIFAT SENYAWA ADALAH “KERAS”
JADI: DENGAN MENINGKATKAN KADAR C; KEKERASAN BAJA MENINGKAT TETAPI MAMPU LAS TURUN.
56
STRUKTUR KRISTAL DAN KLASIFIKASI BAJA KARBON:
• STRUKTUR KRISTAL
• KLASIFIKASI BAJA KARBON:- BAJA KARBON RENDAH- BAJA KARBON MEDIUM- BAJA KARBON TINGGI
![Page 29: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/29.jpg)
29
57
• STRUKTUR MIKRO BAJA KARBON PADA BERBAGAIKADAR KARBON:
58
![Page 30: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/30.jpg)
30
59
• STRUKTUR TIDAK SEIMBANG; SEBAGAI AKIBAT PENERAPAN PROSES PERLAKUAN PANAS.RUJUKAN: DIAGRAM CCT
- MARTENSIT- BAINIT (LOWER BAINIT)- TROSTIT (UPPER BAINIT)- PERLIT
60
![Page 31: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/31.jpg)
31
61
62
PROSES TEMPER:
• DEFINISI• DIAGRAM TEMPER
• FENOMENA TEMPER: TEMPER EMBRITTLEMENT DAN SECONDARY HARDENING
• STRUKTUR TEMPER: M-TEMPER; SORBIT, SFEROID.
![Page 32: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/32.jpg)
32
63
64
MATERIAL PIPA:
1. BAJA KARBON:A. DEFINISIB. SIFAT-SIFAT YANG DIKEHENDAKI:
- Sifat teknologi: weldability, Forgedability- Sifat mekanik- Sifat fisik
BAJA KARBON SECARA UMUM; CAPITAL COST RENDAH, TETAPI LIFE CYCLE COST TINGGI KARENA BIAYA OPERASI, MAINTENANCE, INSPECTION DAN SERVICE
![Page 33: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/33.jpg)
33
65
Baja karbon sering juga digunakan sebagai BACKING PIPE Pada PIPA BAJA KOMPOSIT; YAITU BAJA KARBON YANG DICLAD (DILAPISI) DENGAN 316, 316L; ALLOY 625 ATAU ALLOY 825. Pipa seperti ini termasuk kedalam katagori:PIPA CRA (CORROSION RESISTANCE ALLOYS).
DARI BERBAGAI STANDAR DISYARATKAN BAHWA PIPABAJA KARBON TIDAK BOLEH MENGANDUNG UNSUR-UNSUR DENGAN PROSENTASE LEBIH DARI:
Mn : 1.65%Si : 0.60%Cu : 0.60%
66
FUNGSI UNSUR-UNSUR:
• MANGAN:- SEBAGAI DEOKSIDAN- PENGIKAT S (Mn SE-KURANG2NYA 8X%S)- MENGHALUSKAN PERLIT
• SILIKON: SEBAGAI DEOKSIDAN• ALUMINUM: SEBAGAI DEOKSIDAN DAN PENGHALUS
BUTIR (PADA BAJA “KILLED”)• TEMBAGA: MEMPERBAIKI KETAHANAN KOROSI• S, P DAN N HARUS SERENDAH MUNGKIN.
INGAT: FeS BERTITIK CAIR RENDAH; Fe3P DAN N MENYEBABKAN PENGGETASAN
![Page 34: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/34.jpg)
34
67
DALAM KAITANNYA DENGAN PENGELASAN:
PERSAMAAN MIYANO:
M = (%Si+%Mn)(%P+%Zn) x 104
= 200 (JIS)= 150 (ES)
= 100 (API RBI 581)
PERSAMAAN INI DIADOPSI DALAM STANDAR API RBI581 SEBAGAI FAKTOR J.
68
2. BAJA PADUAN:
a. UNSUR PADUAN:
- Larut pada besi:Untuk memperbaiki sifat fisik; yaitu meningkatkanketahanan korosi
- Membentuk senyawa dengan besi:Untuk memperbaiki sifat mekanik baik pada suhu tinggimaupun pada suhu rendah
UNSUR2 YANG DIPADUKAN: Si, Mn, Ni, Cr, Cu, Mo
![Page 35: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/35.jpg)
35
69
b. PERSYARATAN YANG HARUS DIPENUHI:
- CE:
%C+(1/6)%Mn+(1/5)(%Cr+%Mo+%V)+(1/15)(%Si+%Ni+%Cu).
ATAU:
%C+(1/6)%Mn+(1/5)(%Cr+%Mo+%V)+(1/15)(%Ni+%Cu)
- PREN%Cr+3.3%Mo+16%N
70
JENIS BAJA PADUAN YANG LAZIM DIGUNAKAN SEBAGAI BAHAN PIPA:
1. BAJA TAHAN KARAT:- TYPE 304, 304L- TYPE 316, 316L- TYPE 347SPESIFIKASI ASTM:- A312 (SEAMLESS AND WELDED)- A182 (FORGED FLANGES)- A403 (FITTINGS)
![Page 36: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/36.jpg)
36
71
2. CORROSION RESISTANT ALLOY (CRA)
- CLAD PIPE- DUPLEX SS:* 22% Cr (API 5L C65-2205)* 25% Cr (API 5L C65-2506)* PREN>40; SUPER DUPLEX
- 13% Cr (CENTRIFUGAL CASTINGS)
PENGGUNAAN DIAGRAM NKK UNTUK PEMILIHAN PIPA CRA:
72
![Page 37: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/37.jpg)
37
73
3. BESI COR (CAST IRON):
A. DEFINISIB. JENIS-JENIS BESI COR
C. CONTOH PIPA DARI BESI COR:DUCTILE IRON PIPE, CENTRIFUGALLY CAST(ANSI A21.52)
74
3. JENIS MATERIAL PIPA YANG LAIN:
- HASTELOY B DAN C- NIKEL 200, 201- MONEL 400- INCONEL 600 DAN 750X- ALUMINUM 3003, 6061 DAN 6063- CUPPER AND RED BRASS- TITANIUM- ZIRKONIUM- PLASTIK:* ASTM D2513 THERMOPLASTIC PRESSURE PIPE
AND FITTINGS* ASTM D2517 REINFORCED EPOXY RESIN
![Page 38: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/38.jpg)
38
75
PIPELINE FAILURE:
____________________________________________CAUSE NUMBER %
_____________________________________________________
OUTSIDE FORCE 3144 53.5
MATERIAL FAILURE 990 16.9
CORROSION 972 16.6
OTHER 437 7.4
CONSTRUCTION DEFECT 284 4.8
CONSTRUCTION OR MATERIAL 45 0.8
______________________________________________________DATA: SERVICE FAILURE 1970-1984
76
CAUSES OF CORROSION INCIDENTS:
- EXTERNAL CORROSION 40%
- INTERNAL CORROSION 27%
- STRESS CORROSION CRACKING 17%
- OTHER 16%
CAUSES OF OUTSIDE FORCE INCIDENTS:
- EQP OPERATED BY OUTSIDE PTY 67.1%
- EARTH MOVEMENT 13.3%
- WEATHER 10.8%
- EQP OPERATED BY, OR FOR,
PIPELINE OPERATOR 7.3%
- OTHER 1.5%
![Page 39: BAB 02-03 Material & Manufacturing](https://reader034.vdocuments.site/reader034/viewer/2022050722/5475dd16b4af9f9d0a8b5dbc/html5/thumbnails/39.jpg)
39
77
78