As an innovative formulator Axson Technologies is keen to customized systems and formulations tomeet composites market requirements in different industries, in addition to the traditional EPOLAMEPOXY range, we are working in formulations based on a new PU for RTM process, supportingmass production applications combining short cycle times and high mechanical performances.Axson Technologies formulates EP systems with dispersed Nano particles/additives to enhancedurability properties for composites like: toughness, impact resistance, ... without compromising thethermo-mechanical properties.Axson Technologies is committed to supporting the growing demand for a lower carbon footprint,CO2 reduction and the rise of greener systems by developing few formulations in this area.
MASTER MODEL/PLUG
Extrudable pastes, machinableboards Epoxy & PU boardsLaminating pastes/putties
This initial step consists of producing themost accurate master model in anydimension and any shape. AXSONhas developed several methods toachieve this step due to new millingfacilities and Cad Cam software.
COMPANY SUMMARYAxson Technologies has been formulating tailor-madepolyurethane and epoxy systems for the past 70 years for avariety of highly demanding markets on a worldwide basis.Today, Axson offers high end value composite resins inautomotive, aerospace, marine, general industry and wind millindustries. Axson Technologies maintain a cohesive andcompetitive advantage from plugs to parts through its globalnetwork of 12 direct subsidiaries, 6 manufacturing sites, R&Dcenters and more than 50 exclusive dealers.
MOULD MAKING
High temperature epoxy resins GelcoatsWoven and multiaxial fabricsHoneycomb panelsPrepregs
Fundamental phase, where exact mouldproduction produces exact replicationquality and repeatability under vacuum,pressure and temperature for allprocesses.- Infusion and wet lay-up hightemperature systems
- Low curing temperature/high end useprepregs
PART PRODUCTION
Epoxy systems solutions featuring:- High temperature resistance- Germanischer Lloyd's and LloydsRegister approvals
- Self extinguishing properties- Compliancy with wet lay up, infusion, RTM, pultrusion and filament winding processes
This final step produces what is visibleand used generally in severeenvironment applications - wind, heat,shock and/or exposure to chemicals...
Axson Technologies resins can be segmented into the following groups:
INTEGRATED PRESENCE
CUSTOMIZED AND INNOVATIVE SOLUTIONS
Ref. Main features Density(g/cm3)
Compressivestrength (Mpa)
CTE 10-6 k-1
Max servicetemp (C°)
PU
LABELITE 25PU foamed boards. Different densitiesand thickness for backup and reinforce-ments constructions.
.25 3.80 60 75
LABELITE 35 .35 7 60 70
LABELITE 45 .45 10 55 65
PROLAB 65 Medium density for Prototyping andlight tooling or strong reinforcements.
.65 28 75 85
Epox
y LAB 973 Dimensional and thermal resistance.Good surface finish.
.75 50 40 125
LAB 975 .70 50 40 115
Ref. Main features
LABELITE GLUE Adhesive for Labelite boards with similar foam aspect.
H 8973 For bonding LAB 973 / LAB 975.
H9951 For bonding any large surfaces.
A 77 P Polyester mastic for rapid repair.
EC 85 Epoxy coating for machinable boards.
M 175/380/390 Epoxy repair mastic for extrudable pastes.
Ref. Main features Density(g/cm3)
Hardness(shore)
Tg (°C)DSC
CTE 10-6 k-1
SC 175 Multipurpose. Good surface aspect. Easy to process. Good adhesion and thixotropy.
.65 53D 80 68
SC 380 Excellent hardness/density balance.Elevated thermal properties.
.82 67D 85 60
SC 390 Very good surface aspect. Good sag resistanceon vertical support up to 30 mm.
1.05 75D 90 60
Machinable boards
Extrudable pastes
Ancilliary products
MASTER MODELPlugs and master models are an essential and primary phase of any composite construction. Newlyimproved CNC and Cad Cam abilities enable Axson Technologies to offer a wide variety of machinableproducts in the shape of finished boards or pastes. These products have been designed to meet mechanicalspecifications, offer higher dimensional stability as well as improving ease of use and set up.
Ref. Main features Tg (°C)
Viscosity(mPas)
Pot Life(min)
EPOLAM 2025 R/H Thermal resistant system. 135 1400 60
EPOLAM 2050 R/H Simplified cure schedule. 125 2000 80
EPOLAM 2080 R/H High temperature resistance. 190 2000 150
Ref. Main features
APG 1750 Sprayable, epoxy compatible polyester gelcoat, max temp 200°C.
APF 7 Styrene free polyester repair putty, max temp 200°C.
Epoxy Gelcoats From 80 to 200°C Tg - Please consult us.
Ref. Main features Tg (°C)by DSC
Viscosity(mPas)
Pot Life(min)
EPOLAM 2019 R/H No curing required before demoulding.
110 250 95
EPOLAM 2031 R/2031 H/2032 H
Long pot life, low viscosity.1 hardener for wet lay-up.
140 350 110200
EPOLAM 2090 R/2026 H Highest Tg of the range. 215 650 850
Wet lay up
Infusion
Ancilliary products
Ref. Main features Initial cure temperature (°C)
outlife(days)
Tg (°C)
AmberTool HX32 Large moulds (boats, blades...) 65 15 150
AmberTool HX40Aerospace tools, caul plates...
55 10 210
AmberTool HX42 50 5 200
AmberTool HX50 Medium and small autoclaveparts. Fast cure / high Tg
40 3 180
Tooling prepregs from TenCate
MOULD MAKINGMoulds are an essential part of the composite program as once built they produce several parts. Therefore,the choice of components for the composite tools has to be precise in order to achieve best dimensionalstability, shape, processing, size and pattern. Axson Technologies has developed over the years a comprehensive range of epoxy systems allowing theproduction of stable, accurate and long lasting tools. Axson Technologies has also developed renownedskills in various processes such as vacuum assisted infusion and tooling prepregs.
Ref. Main features
EPOLAM 2017 R/2013 H/2017 H/2018 H
Good wetting of fibres and wood, quick setting.3 miscible hardeners.
EPOLAM 2020 R/H Quick setting for medium temperature resistant.
EPOLAM 2022 R/H High mechanical performance.
EPOLAM 2040 R/2017 H/2042 H/2047 H Low viscosity, good wetting properties, 3 miscibles hardeners.
EPOLAM 2500 R/H Self extinguishing properties. Airbus Eurocopter approved.
RSF 816 R/H UV resistant, clear system for transparent laminates.
Ref. Main features
EPOLAM 8056 R/8012 H Medium temperature and medium viscosity system. Tg up to 160°C.
EPOLAM 8056 R/8045 H/8090 C Medium viscosity moderate temperature epoxy-anhydride based system. Tg up to 155°C.
EPOLAM 8056 R/8046 H/8090 C Medium viscosity high temperature epoxy-anhydride based system. Tg up to 180°C.
EPOLAM 8056 R/8073 H Tg up to 190°C with a good thoughness and flexibility.
EPOLAM 8064 R/2026 H Low viscosity and long open time. Tg up to 140°C.
EPOLAM 8064 R/8012 H Medium temperature and low viscosity system. Tg up to 140°C.
EPOLAM 8064 R/8045 H/5X C Low viscosity moderate temperature epoxy-anhydride based system. Tg up to 155°C.
EPOLAM 8079 R/8045 H/8090 C Low viscosity high temperature epoxy-anhydride based system. Tg up to 205°C.
EPOLAM 8085 R/8012 H Tg up to 160°C with a good flexibility.
Ref. Main features
EPOLAM 8064 R/8011 H High reactivity system for optimized curing cycles.
EPOLAM 8064 R/8033 H Flexible and versatile systems, high flexibility, long open time.
Cold curing systems
Warm curing systems
Hot curing systems
PARTS MAKINGThe appl icat ion f ie lds of COMPOSITE MATERIALS is expanding every day from boat building towindmill blade production and from automotive parts to liquid gas storage. They bring exceptional strengthin relation to weight ratio, together with maximized function integration. AXSON TECHNOLOGIES proposesa unique set of epoxy systems developed to fit with your process and specifications.
FAR 25
PART
MA
KIN
GM
OU
LD M
AKI
NG
EPOXY SYSTEMS
Resin systems(R=resin/H=hardener/C=catalyst) Description Mix ratio
by weightMix Viscosity
at 23°C (mPa.s)Pot life at 23°C (min) 100 ml
WET LAY UP
EPOLAM 2025 R/H Good thermal and chemical resistance. 100: 28 1300 60
EPOLAM 2050 R/H Easy post cure condition to get max Tg. 100: 32 2000 80
EPOLAM 2080 R/H Thick layer possible for moulding. 100: 41 2000 150
INFUSIONEPOLAM 2019 R/H No pre curing required; medium temperature range. 100: 35 250 95
EPOLAM 2031 R/2031 H/2032 H
Thick laminate by infusion ; good wetting ability ; any mould dimension.
100: 26 350110
/200
EPOLAM 2090 R/2026 H Compatible wet lay up/infusion for thick composites parts. 100: 53 650 1500
WET LAY UP
EPOLAM 2017 R/2013 H/2017 H/2018 H
Fast setting system ; good wetting properties ; 3 miscible hardeners.
100: 30 5508
/35/160
EPOLAM 2020 R/H Multipurpose system ; reactivity can be adjusted (accelerate). 100: 34 550 135**
EPOLAM 2022 R/H High mechanical properties combined with good wetting ability. 100: 40 600 60
EPOLAM 2500 R/H Fire resistant ; product for aircraft applications. 100: 22 3500 90
RSF 816 R/H U.V resistance product ; transparent and high glossy aspect. 100: 40 500 28
INFUSIONEPOLAM 2040 R/2017 H
/2042 H/2047 H
Tolerent to moisture; low viscosity system ; high mechanical properties ; 3 miscible hardeners.
100: 32 220/28035/75/180
RTM
EPOLAM 8064 R/8033 H
/8011 H
/8012 H
Good balance between long open time, low viscosity, high flexibility and elongation at break.
100: 36 240 16 h
Very low viscosity and fast curing at elevated temperature. 100: 21 320 45
Good balance between low viscosity and thermal resistance. 100: 25 550 100-150
EPOLAM 8085 R/8012 H Good balance between viscosity and temperature resistance. 100: 24 1300 125
EPOLAM 8056 R/8012 H Good balance between temperature resistance and elongation atbreak.
100: 23 700 at 40°C 70 - 110*
EPOLAM 8056 R/8073 H High temperature resistance, high flexibility/toughness and longopen time.
100: 23 4500 35 h*
FILAMENT WINDING/PULTRUSIONEPOLAM 8064 R
/8045 H/5X C Latent anhydride based system. 100: 98: X 550 ≥ 48h
EPOLAM 8064 R /2026 H Alternative to anydride curing agents. Good balance between longopen time, chemical resistance and excellent hot/wet properties.
100: 95: X 1500 ≥ 48h
EPOLAM 8056 R/8045H/8090 C
Latent anhydride based system providing medium temperature resistance.
100: 90: X 300 at 40°C ≥ 48h
EPOLAM 8056 R/8046 H/8090 C
Latent anhydride based system providing medium to high temperature resistance.
100: 95: X 1500 ≥ 48h
EPOLAM 8079 R/8045 H/8090 C
High temperature resistant anhydride based system. Very low viscosity at room temperature.
100: 115: X 200 ≥ 48h
* 500 ml
SELECTOR GUIDE
Demoulding time(h) Typical curing cycle
Tensile Modulus (MPa)
Tensilestrength (MPa)
Elongation at break
(%)
Flexural strength (MPa)
Tg (°C)(DSC) Application
242 h/40°C + 2h/60°C + 2h/80°C
+ 2h/100°C + 3h/120°C3300 56 - 110 135 Thermal resistant mould.
24 to 36 8 to 12 h/100°C - 45 - 105 125 Mould and concrete manufacture.need pre cure
24h 45°C1 h/60°C + 1 h/80°C + 2 h/120°C
+ 4 h/160°C- 40 - 62 190 High temperature resistance mould.
24 2 h/60°C + 2 h/80°C + 4 h/100°C 3000 70 4 118 110 Composite and mould structures. need pre cure,
see TDS2h/60°C + 2h/80°C + 2h/100°C
+ 16h/140°C3600 80 & 70 6 & 4 130 & 125 140 Temperature resistance moulding.
need pre cure,see TDS
1h/60°C + 1h/80°C + 2h/120°C + 4h/180°C
- - - 50 215 High chemical and temperature re-sistance.
6/24/28
12 to 36 h/RT + 2 h/45°C + 2 h/60°C + 8h/80°C
3300/3700
70 5.6 108/132 83/89 Wood bonding. Marine parts.
483 h/40°C + 2 h/60°C + 2 h/80°C
+ 3 h/100°C3400 78 - 125 100** ** Without accelerator.
Sport and General industry.24 4 h/50°C + 2 h/80°C + 2 h/100°C 3600 56 - 110 100 Very stiff parts for Sport & Leisure.
16 1 h/60°C + 2 h/100°C - - - 90 100 Aeronautic application and repair.
16 16 h/23°C + 16 h/80°C 3300 60 5 115 75 Top coat for wind surf.
24/36 24 h/23°C + 16 h/70°C - 70/75 8/8.70 115/125 86/93 Wind mill, Marine, and General Industry.
Depends on process parameters
8 h/80°C 3000 70 7-9 110 60-80 General Industry.
15 min/80°C + 1 h/120°C 3400 72 4 110 120-123 General Industry.
15 min/120°C + 2 h/150°C 3000 78 4-6 130 130-140 General Industry, Sport & Leisure.
15 min/120°C + 2 h/150°C 3200 76 5-6 125 150-160 General Industry, Sport & Leisure.
15 min/120°C + 2 h/150°C 2900 70 5-5 135 150-160 General Industry, Sport & Leisure.
2 h/120°C + 2 h/140°C + 2 h/180°C
3500 75 6.5 115 185-195 General Industry.
Depends on process parameters
4 h/80°C + 4 h/120°C 3100 83 5 145 112-123
General Industry: Profiles & Hollow structures.
15 min/120°C + 2 h/150°C 2600 75 4-6 120 130-140
4 h/80°C + 4 h/160°C 3200 90 6 130 150-155
2 h/120°C + 8 h/160°C 2900 55 2 125 140-180
2 h/100°C + 4 h/180°C 3000 55 1.5-2.1 92-122 185-205
●●
●●
●●●●
●●
●●
●●
●● ●●
●●
●●●●
●●
●●
●●
●●
●●
●●
●●
●● ●●
●●
●●
●●●●
●●●●
●●
●●
●●
●●●●
6 PRODUCTION SITES& RESEARCH CENTERS
ChinaFranceJapanMexicoSlovakiaUSA
12 SUBSIDIARIESAROUND THE WORLD
50 DISTRIBUTORSWORLDWIDE
MORE THAN
ChinaFranceGermanyIndiaItalyJapan
MexicoSlovakiaSpainUKUSAU.A.E.
●
●
●
●●
●●
Axson FranceTel. +33 1 34 40 34 60axson@axson.com
Axson SlovakiaTel. +42 1 76 42 25 26axson.sk@axson.com
Axson SpainTel. +34 9 32 25 16 20spain@axson.com
Axson ItalyTel. +39 02 96 70 23 36axson@axson.it
Axson GermanyTel. +49 6 07 44 07 11-0verkauf@axson.com
Axson UKTel. +44 16 38 66 00 62sales.uk@axson.com
Axson JapanTel. +81 5 64 26 25 91sales.japan@axson.com
Axson ChinaTel. +86 21 58 68 30 37marketing.china@axson.com
Axson Middle EastTel. +971 7 2432227axsonmideast@axson.com
Axson IndiaTel. +91 20 25 56 07 10-11info.india@axson.com
Axson North AmericaTel. +15 1 76 63 81 91axsonmh@axson.com
Axson MexicoTel. +52 55 52 64 49 22marketing@axson.com.mx
WORLDWIDE PRESENCE
www.axson-technologies.com
ChinaFranceGermanyIndiaItalyJapanMexicoSpainSlovakiaU. A. E.UKUSA
●●
DO
C12
7 - P
hoto
grap
hs: A
xson
, Ten
Cat
e, D
uque
ine,
H2X
, Sot
ira, F
otol
ia, 1
23RF
- O
utdo
or A
ctio
n Fi
nlan
d O
y - D
esig
n : w
ww
.cre
a-la
ure.
com
top related