3 rd advanced graphite creep capsule (agc-3) irradiation
DESCRIPTION
3 rd Advanced Graphite Creep Capsule (AGC-3) Irradiation. Proceedings of the 2013 14 th International Nuclear Graphite Specialists Meeting INGSM-14 September 16 – 18 , 2013, Seattle, Wa. USA. Agenda. Graphite irradiation overview - PowerPoint PPT PresentationTRANSCRIPT
www.inl.gov3rd Advanced Graphite Creep Capsule (AGC-3) IrradiationProceedings of the 2013 14th International Nuclear Graphite Specialists MeetingINGSM-14
September 16 – 18, 2013, Seattle, Wa. USA
Agenda• Graphite irradiation overview• Advanced Test Reactor (ATR)
irradiation locations and details • Graphite specimens• Capsule and test train design• Control and monitoring systems• AGC-3 Experiment – Design – Irradiation
• Summary
ATR Core During Reactor Operation
2
Graphite Irradiation Experiments
Graphite material property database
• Irradiation creep
• Thermal changes
• Mechanical changes
• Physical changes
High dose tensile irradiation creep studies needed for pebble bed design
Database for previous nuclear graphite grades
900 ºC
1200 ºC
AGC - 2600 ºC
1500 ºC
AGC - 1
AGC - 4
AGC - 6
Dose (dpa)
1 3 4.5 6
HTV-1 HTV-2
AGC - 3
AGC - 5
• Historic nuclear grade graphites are no longer available due to loss of feedstock
• ATR experiments to be irradiated: – 600, 900 and 1200ºC– Up to 4 or 7 dpa (5.5 and
9.6 × 1021 n/cm2 for E > 0.1 MeV)
• AGC-1 was irradiated from September 2009 to January 2011
• AGC-2 was irradiated from April 2011 to May 2012
• AGC-3 will be irradiated from November 2012 to March 2014
3
• AGC-1 and AGC-2 were irradiated in the South Flux Trap position
• AGC-3 is being irradiated in the East Flux Trap of the ATR
• Use of ATR Flux Trap– Maximizes number of graphite
specimens, stacks/channels, loads, and combinations
– Flux rate minimizes irradiation time to meet NGNP program schedule
• Test trains rotated to minimize flux gradient across diameter
• Most of ATR core height (44” of 48”) used to maximize specimen numbers and provide spectrum of fast fluence damage levels
AGC Experiment Locations
I-1 I-2I-3
I-4
I-5
I-6
I-7
I-8
I-9I-10I-12 I-11I-13
I-14
I-15
I-16
I-17
I-18
I-19I-20
OS-1 OS-2
OS-3 OS-4 OS-5 OS-6 OS-7
OS-8 OS-9 OS-10 OS-11 OS-12
OS-13 OS-14 OS-15 OS-16 OS-17
OS-18 OS-19 OS-20 OS-21 OS-22
ON-1 ON-2
ON-3 ON-4 ON-5 ON-6 ON-7
ON-8 ON-9 ON-10 ON-11 ON-12
B1
B2
B3
B4B5
B6
B7
B8
B9
B10
B11
B12
I21
I22I23
I24
Fuel Elements
South Flux Trap Location for AGC-1 & 2
North
H Positions
I Positions
Small B Position
Control Drum
ATR Core Cross Section
East Flux Trap Location for AGC-3
4
• Some large and small specimens – Large – Ø ½” (12.3 mm) × 1” (25.4 mm) tall– Small – Ø ½” (12.3 mm) × ¼” (6.4 mm) tall
• New ‘intermediate’ size specimen container– Ø ½” (12.3 mm) × ½” (12.7 mm) tall
• 6 Perimeter Stacks– 18 large size specimens above core center– 18 large and 3 small size specimens below core center
• Center Stack – 152 small and 9 intermediate size specimens
• Flux wires in spacers between graphite specimens
Core Centerline
Full Size Unloaded Specimens
Compressive Load Push RodUnloaded Small
SpecimensLoaded Large Specimens
AGC-3 Graphite Specimens
Flux Monitor
Spacer
Small Specimen
Large Specimen
AGC-2 Specimen Stack5
AGC-3 Irradiation Requirements• 900ºC design temperature• Fast neutron damage up to 3 to 4 dpa• Compressive loads on specimens
– 2 stacks with 2 ksi (14 MPa) compressive load
– 2 stacks with 2.5 ksi (17 MPa) compressive load
– 2 stacks with 3 ksi (21 MPa) compressive load
• Loaded and unloaded companion specimens
• Lift specimens during reactor outages to verify specimen load condition
• Grab samples of temperature control gas to monitor for oxidation of specimens
AGC Being Inserted into the ATR
AGC Experiment
ATR Top Head
6
AGC Capsule Design Features• 6 specimen stacks around capsule
perimeter with compressive load on upper half of stack
• 7th specimen stack in center without compressive load
• Graphite holder to contain graphite specimen stacks and thermocouples (TCs)
• 12 TC locations with positions located throughout core height
• Insulating gas jacket to attain desired temperature
• Radiation heat shield to limit radiation heat transfer
AGC Capsule Cross Section
ThermocouplesSpecimen Holder
Graphite Specimens
Heat Shield/Gas Jacket Area
Temperature Control Gas Line
Lower Bellows Gas Line
7
Temperature Control• Utilize neutron capture and
gamma heating of specimens as heat source
• Manipulate temperature by adjusting ratio of conducting and insulating gases in insulating gas gap
• AGC irradiations use He and Ar to maximize control band for temperature control
• All AGC experiments utilize same temperature control system
• Distributed control system used for control and data collection
8
• Pneumatic rams provide compressive load on specimens in six peripheral stacks located above the ATR core centerline – no load on specimens below core centerline
• Load cells between pneumatic rams and push bars to monitor specimen load• Push bars translate and transmit compressive load to push rods located in smaller
circle directly over specimen stacks– Stainless steel push rods transition to graphite in higher temperature areas of experiment
• Gas bellows below core to lift top specimens during outages to verify load conditions– Position indicators attached to push bars to verify specimen movement during outages
• Compressive loads imposed on diametrically opposite specimen stack pairs to avoid eccentrically loading the graphite holder
AGC Test Train
Push RodPneumatic Ram Gas BellowsLoad CellPosition IndicatorsPush Bar Graphite
Specimens
Compressive Load System
9
AGC-2 Design Changes/Improvements
TC Pair Locations in AGC-2
TC Locations
• TC12 moved to same elevation as TC9 to provide temperature gradient across the whole experiment
• Replaced stainless steel with aluminum in some internal components to reduce weight– Load cell adapter, plates, push bars and
sleeves• Tungsten ‘gamma heaters’ added to
top and bottom of center channel• Zirconia gamma heaters added to the
bottom of peripheral channels• Removed spacers in specimen stacks
to increase number of specimens– 36 large and 14 to 18 small specimens in
peripheral stacks (vs. 29 and 14)– 170 (vs. 172) small specimens in center
stack due to tungsten heaters 10
• East Flux Trap vs. South Flux Trap – 15% lower nominal power– 20% power variation versus 10% for AGC-1
and AGC-2• Increased specimen creep from higher
design temperature (900ºC)– Slightly smaller diameter specimens – Additional stroke in pneumatic cylinders– Additional room at core center for creep in
specimens and housing• Elevated mean wall temperature in
pressure boundary from higher temperature• Five zones versus single vertical
temperature control zone– Significantly enhanced temperature control – Significantly improved axial temperature
distribution• Different gamma ‘heaters’
– Molybdenum vs. tungsten and zirconia
AGC-3 Design Challenges and Changes
AGC Capsule Cross Section
Thermocouples
Specimen Holder
Graphite Specimens
Heat Shield/Gas Jacket Area
Temperature Control Gas Line
Lower Bellows Gas Line
11
Lower Gas Bellows installed on test train
Outer shell with gas bellows installed inside
Gas Bellows before installation in outer shell• Design initiated – April 2011• Final design reviews – March 2012• Test train inserted in ATR – August 2012• Start of irradiation – November 2012– Moisture level during start-up– Excellent temperature control– Extremely flat axial temperature profile– Compressive load control system leakage
– Helium shortage– Loads reduced on stacks 2 and 5 to
replace/supplement stacks 1 and 4• End of first irradiation cycle – January
2013– Accumulated 51 EFPDs– Peak fast neutron damage – 1.0 dpa
• Removed for short high power operating cycle – January 2013
• Re-insertion in ATR – July 2013• Irradiation complete – March 2014
AGC-3 Schedule and Status
12
Temperatures During Irradiation
13
Compressive Loads During Irradiation
14
AGC-3 Experiment• Multiple design improvements and lessons
learned from AGC-1 and AGC-2 incorporated
• New design challenges from increased temperature and new irradiation position
• Irradiation started in November 2012– Significant improvement in temperature
control and axial temperature profile– Compressive load control system leakage– Accumulated 51 EFPDs– Peak fast neutron damage level – 1.0 dpa
• Removed in January 2013 with re-insertion completed in July 2013
• Irradiation complete in March 2014
AGC Experiment Installed in ATR
Summary
AGC Test Train
ATR Core
ATR Fuel
ATR Flux Trap Top Head Penetration
ATR Vessel
AGC Connections to Control Systems
15
Michael Davenport Idaho National [email protected] (208) 526-6214