poly jet tango family material sheet
TRANSCRIPT
For more information on any of our products or services please visit us
on the Web at:
www.dinsmoreinc.com
Email:[email protected]
SERVICES AVAILABLE Product Design
Rapid Prototyping
Stereolithography
HDSLA
PolyJet
SLS
DMLS
FDM
Plastic Casting
CNC Machining
Injection Mold Tooling
Rapid Tooling
Production Tooling
Injection Molding
Metal Casting
3020 Red Hill AvenueCosta Mesa, CA 92626Phone 714.641.7111
Fax 714.641.3111
PolyJet: TangoPlus, TangoBlack, TangoGray
Flexible, Rubber-like, Tough, Exceptional Elongation
that produces strong, tough, water-resistant, ABS-like parts. 11122 are nearly colorless, and look more like true, clear
the DSM Somos Oxetane Advantage™— an advanced water resistance and high dimensional stability.
that mimic traditional engineering plastics including ABS and PBT. automotive, medical and consumer electronics markets
TangoPlus, FullCure930 – expands the Tango family of rubber-like materials, offering exceptional elongation at break, excellent toughness and durability and high resistance to tearing. It addresses a broad range of applications requiring rubber-like flexibility and durability, such as gaskets and seals, hoses, athletic footwear, toys and more.
The new material offers unmatched combination of mechanical properties that sets a new standard in rubber-like performance. At 218%, the elongation at break of TangoPlus is more than double that of any other rapid prototyping material available on the market. It is highly resistant to tearing and has a Ross Flex measurement in excess of 150,000. Thus, TangoPlus offers outstanding resistance to deterioration, making it ideal for models that are likely to be exposed to long use or rough handling.
TangoBlack and TangoGray
TangoBlack and TangoGray rubber like flexible 3D modeling materials enable models that closely resemble the “feel” of flexible target products, opening new business opportunities for Eden systems. They are particularly ideal for many consumer electronics applications, shoes, toys, general industrial applications, and rapid tooling.
TangoBlack and TangoGray enable a realistic rubber/silicon feel, and easily stretch to fit onto other parts. TangoBlack provides high elasticity with hardness of 61 Shore Scale A. TangoGray is a slightly harder, but still flexible, material with hardness of 75 Shore Scale A, providing more controlled flexibility and elasticity.
Key Advantages
Rubber-like flexible material enables 3-dimensional parts to be used in the early design stages, shortening the product design cycle.
Very high elongation at break, specifically for TangoPlus, provides a realistic feel of rubber and silicon and enables model parts that stretch easily to fit with other parts.
Choice of flexibility and hardness levels - TangoBlack (Elongation at break of 47.7% and 61 Shore Scale A); TangoGray ((Elongation at break of 47% and 75 Shore Scale A); TangoPlus (Elongation at break of 218% and 27 Shore Scale A).
PolyJet: TangoPlus, TangoGray, TangoBlack
FullCure®930 TangoPlus
Property ASTM Results (Metric) Results (Imperial)
Tensile Strength at Break D-412 MPa 1.455 psi 211 Tenslie Modulus at 20% Strain D-413 MPa 0.146 psi 21 Tenslie Modulus at 30% Strain D-414 MPa 0.185 psi 27 Tenslie Modulus at 50% Strain D-415 MPa 0.263 psi 38
Elongation at Break D-412 % 218 % 218 Compressive Set, 22 Hr, 750C D-395 % 4.4 % 4
Shore A Hardness D-2240 Scale D 27 Scale D 27
Ross Flex D-1052 Above 150,000
Above 150,000
Tensile Tear Resistance D-624 Kg/cm 3.47 Lb/in 20
Tg
DSC
ºC -9.6 ºF 15 (-80ºC+100ºC)
FullCure®950 TangoGray
Property ASTM Results (Metric) Results (Imperial)
Tensile Strength D-412 MPa 4.36 psi 632
Elongation at Break D-412 % 47 % 47
Compressive Set D-395 % 1 % 1
Shore A Hardness D-2240 Scale A 75 Scale A 75
Tensile Tear Resistance D-624 Kg/cm 9.5 Lb/in 54
Tg
DSC
ºC 2.6 ºF 37 (-80ºC+100ºC)
FullCure®970 TangoBlack
Property ASTM Results (Metric) Results (Imperial)
Tensile Strength D-412 MPa 2 psi 290
Elongation at Break D-412 % 47.7 % 47.7
Compressive Set D-395 % 0.8 % 1
Shore A Hardness D-2240 Scale A 61 Scale A 61
Tensile Tear Resistance D-624 Kg/cm 3.8 Lb/in 21
Tg
DSC
ºC -10.7 ºF 13 (-80ºC+100ºC)
FOR MORE INFORMATION CALL 714.641.7111
Dinsmore & Associates, Inc. 3020 Red Hill Avenue, Costa Mesa, CA 92626 www.dinsmoreinc.com [email protected]