miscellaneous dental materials

23
MISCELLANEOUS DENTAL MATERIALS BY DR KHAWAJA RASHID HASSAN HEAD SCIENCE OF DENTAL MATERIALS DEPARTMENT W.M.D.C ABBOTTABAD

Upload: badu

Post on 24-Feb-2016

161 views

Category:

Documents


1 download

DESCRIPTION

MISCELLANEOUS DENTAL MATERIALS. BY DR KHAWAJA RASHID HASSAN HEAD SCIENCE OF DENTAL MATERIALS DEPARTMENT W.M.D.C ABBOTTABAD. MISCELLANEOUS DENTAL MATERIALS. Materials used in MAXILLOFACIAL SURGERY. Materials used in ENDODONTICS. Materials used in PERIODONTICS. Maxillofacial materials. - PowerPoint PPT Presentation

TRANSCRIPT

Page 1: MISCELLANEOUS DENTAL MATERIALS

MISCELLANEOUS DENTAL MATERIALS

BYDR KHAWAJA RASHID HASSAN

HEAD SCIENCE OF DENTAL MATERIALS DEPARTMENTW.M.D.C

ABBOTTABAD

Page 2: MISCELLANEOUS DENTAL MATERIALS

MISCELLANEOUS DENTAL MATERIALS

Materials used in MAXILLOFACIAL SURGERY.

Materials used in ENDODONTICS. Materials used in PERIODONTICS.

Page 3: MISCELLANEOUS DENTAL MATERIALS

Maxillofacial materialsINTRODUCTION

Maxillofacial materials are used to correct facial defects.

CAUSES OF FACIAL DEFECTS Cancer surgeries. Accidents. Congenital deformities.

NOSES, EARS, EYES, ORBITS & OTHER PARTS OF HEAD AND NECK REGION

ARE REPLACED BY THESE PROSTHESES

Page 4: MISCELLANEOUS DENTAL MATERIALS

MAXILLOFACIAL PROSTHESES

PROSTHETIC EYE PROSTHETIC EAR

Page 5: MISCELLANEOUS DENTAL MATERIALS

MAXILLOFACIAL PROSTHESESPROSTHETIC NOSE

Page 6: MISCELLANEOUS DENTAL MATERIALS

Maxillofacial materials Following materials are used for the

fabrication of maxillofacial prostheses.1) POLYMETHYLMETHACRYLATE.2) POLYURETHANE.3) ROOM TEMPERATURE-VALCUNIZED

SILICONES.4) OTHER ELASTOMERS.

Page 7: MISCELLANEOUS DENTAL MATERIALS

Maxillofacial materials1) POLYMETHYLMETHACRYLATE: P.M.M.A was once commonly used for

maxillofacial prostheses. Still used occasionally to make artificial

facial parts. Look quiet realistic once properly

pigmented.Hardness & stiffness of P.M.M.A is

the main disadvantage.

Page 8: MISCELLANEOUS DENTAL MATERIALS

Maxillofacial materials2) POLYURETHANE:

a) Used as maxillofacial materials.b) Formed by the reaction of

diisocyanate & polyol in the presence of an initiator.

c) Reaction must be carried out in a dry atmosphere or carbon dioxide will result.

d) Processing temperature of 100 ̊C is reasonable.

Page 9: MISCELLANEOUS DENTAL MATERIALS

Maxillofacial materials3) ROOM TEMPERATURE VALCUNISED

SILICONES:a) Because of good physical & mechanical

properties & favorable processing characteristics RTV-Silicones have become popular maxillofacial materials.

b) Used more often than any other material for fabrication of maxillofacial prosthesis.

c) They are easy to color.

Page 10: MISCELLANEOUS DENTAL MATERIALS

Maxillofacial materials4) OTHER ELASTOMERS:a) Several elastomers have been

investigated for use as maxillofacial materials, including

b) Aliphatic polyurethanes.c) Chlorinated polyurethane.d) Organophosphazenes.e) Silicone poly(methyl meth acrylate)

block polymers.

Page 11: MISCELLANEOUS DENTAL MATERIALS

ENDODONTIC MATERIALSEndodontics is concerned

with the physiology, morphology & pathology of the human dental pulp &

periradicular tissuesTreatments include:a) Capping of exposed vital

pulp.b) Sealing of root canal space

after removal of infected pulp.

c) Reconstruction with endodontic post & core systems in case of badly broken down tooth.

Page 12: MISCELLANEOUS DENTAL MATERIALS
Page 13: MISCELLANEOUS DENTAL MATERIALS

ENDODONTIC MATERIALS

a) Vital pulp capping:Two types

Indirect pulp cappingDirect pulp capping

PULP CAPPING MATERIALS:1) Calcium hydroxide cement.2) Dentin bonding agents.

Page 14: MISCELLANEOUS DENTAL MATERIALS

ENDODONTIC MATERIALSb) ROOT FILLING MATERIALS:Most widely used root canal filling materials

are basically a combination of I. Obturating points

&II. Canal sealer cements.I) OBTURATING POINTSA) Gutta percha points.B) Metal points.

Page 15: MISCELLANEOUS DENTAL MATERIALS

ENDODONTIC MATERIALS(OBTURATING POINTS)

A) GUTTA PERCHA POINTS:

Gutta percha is a rubber obtained from the trees in Malaysia.

Was introduced in U.K IN 1843.

Thermoplastic material. Softens at 60-65 ̊C &

melts at about 100 ̊C. Cannot be heat

sterilized but can be disinfected.

Gutta percha when cooled rapidly forms a crystalline β phase whereas when cooled slowly a denser crystalline α phase is formed.α phase gutta percha has better thermoplastic characteristics and hence preferred to be used in hot gutta percha systems

Page 16: MISCELLANEOUS DENTAL MATERIALS

ENDODONTIC MATERIALS(OBTURATING POINTS)

OBTURA II OBTURA III

Page 17: MISCELLANEOUS DENTAL MATERIALS

ENDODONTIC MATERIALS(OBTURATING POINTS)

COMPOSITION OF GUTTA PERCHA POINTSCONSTITUANT AMOUNT (%) PURPOSE

GUTTA PERCHA

19-22 RUBBER

ZINC OXIDE 59-75 FILLERHEAVY METAL

SALTS1-17 RADIO-

OPACIFIERWAX or RESINS

1-4 PLASTICIZER

Page 18: MISCELLANEOUS DENTAL MATERIALS

ENDODONTIC MATERIALS(OBTURATING POINTS)

B) METAL POINTS: Metals including gold, tin, lead &

silver had been used as root canal filling materials.

Silver points were used mostly because of bactericidal effect.

Rigidity & ability to get corroded easily were the 2 main disadvantages of silver obturating points.

Page 19: MISCELLANEOUS DENTAL MATERIALS

ENDODONTIC MATERIALS(ROOT CANAL SEALER MATERIALS)IDEAL PROPERTIES OF ROOT CANAL SEALER

CEMENTS Should be biocompatible. Should be bacteriocidal or atleast bacteriostatic. Easy to use. Should be insoluble. Should be free of air bubbles when mixed. Floe to thin film thickness. Should adapt to the canal walls & obturating points. Should be radiopaque. Should be easily removed in case of failure.

Page 20: MISCELLANEOUS DENTAL MATERIALS

ENDODONTIC MATERIALS(ROOT CANAL SEALER MATERIALS)

ROOT CANAL SEALER MATERIALS: ZINC OXIDE EUGENOL. GLASS IONOMER CEMENT. CALCIUM HYDROXIDE CEMENT. POLY DI METHYSILOXANE.

Page 21: MISCELLANEOUS DENTAL MATERIALS

ENDODONTIC MATERIALS(POST & CORE SYSTEMS)

PREFABRICATED POSTS: Metal posts

1) Non threaded parallel sided posts.2) Threaded parallel sided posts.3) Non threaded tapered posts.4) Threaded tapered posts.

Fibre reinforced resin posts1) Carbon fibre reinforced posts.2) Glass fibre reinforced posts.

Ceramic posts1) Cosmopost.2) Biopost.3) Cetapost.

Page 22: MISCELLANEOUS DENTAL MATERIALS

PERIODONTAL MATERIALS1) Zinc oxide eugenol formulation.2) Zinc oxide fatty acid formulation.3) Formulation including polyacrylic acid,

poly ethyl methacrylate, zinc oxide, n-butylphthalate & alcohol.

Page 23: MISCELLANEOUS DENTAL MATERIALS

This Ends Your Science of Dental Materials Course

GOOD LUCK FOR YOUR

PROFESSIONAL EXAMZ