© 2017 Dental Press Journal of Orthodontics Dental Press J Orthod. 2017 May-June;22(3):47-54 47 original article Fracture strength of orthodontic mini-implants Tatiana Feres Assad-Loss 1 , Flávia Mitiko Fernandes Kitahara-Céia 1 , Giordani Santos Silveira 1 , Carlos Nelson Elias 2 , José Nelson Mucha 1 Objective: This study aimed at evaluating the design and dimensions of five different brands of orthodontic mini- implants, as well as their influence on torsional fracture strength. Methods: Fifty mini-implants were divided into five groups corresponding to different manufactures (DEN, RMO, CON, NEO, SIN). Twenty-five mini-implants were subjected to fracture test by torsion in the neck and the tip, through arbors attached to a Universal Mechanical Testing Machine. The other 25 mini-implants were subjected to insertion torque test into blocks of pork ribs using a torquimeter and contra-angle handpiece mounted in a surgical motor. The shape of the active tip of the mini-implants was evaluated under microscopy. The non-parametric Friedman test and Snedecor’s F in analysis of variance (ANOVA) were used to evaluate the differences between groups. Results: The fracture torque of the neck ranged from 23.45 N.cm (DEN) to 34.82 N.cm (SIN), and of the tip ranged from 9.35 N.cm (CON) to 24.36 N.cm (NEO). Insertion torque values ranged from 6.6 N.cm (RMO) to 10.2 N.cm (NEO). The characteristics that most influenced the results were outer diameter, inner diameter, the ratio between internal and external diameters, and the existence of milling in the apical region of the mini-implant. Conclusions: The fracture torques were different for both the neck and the tip of the five types evaluated. NEO and SIN mini-implants showed the highest resistance to fracture of the neck and tip. The fracture torques of both tip and neck were higher than the torque required to insert mini-implants. Keywords: Orthodontics. Skeletal anchorage. TADs. Mini-implant. Dental materials. 1 Universidade Federal Fluminense, Department of Orthodontics (Niterói/RJ, Brazil). 2 Instituto Militar de Engenharia, Materials Engineering, Biomaterials Laboratory, Rio de Janeiro, RJ, Brazil. Contact address: Giordani Santos Silveira Av. Antônio Abrahão Caran, 820, sala 607, São José – Belo Horizonte/MG, Brasil CEP: 31.275-000 – E-mail: [email protected] DOI: https://doi.org/10.1590/2177-6709.22.3.047-054.oar How to cite this article: Assad-Loss TF, Kitahara-Céia FMF, Silveira GS, Elias CN, Mucha JN. Fracture strength of orthodontic mini-implants. Dental Press J Orthod. 2017 May-June;22(3):47-54. DOI: https://doi.org/10.1590/2177-6709.22.3.047-054.oar Submitted: April 26, 2016 - Revised and accepted: December 01, 2016 » The authors report no commercial, proprietary or financial interest in the products or companies described in this article. Objetivo: o objetivo do presente estudo foi avaliar o desenho e as medidas de cinco marcas diferentes de mini-implantes ortodônticos, e sua influência na resistência à fratura em torção. Métodos: cinquenta mini-implantes foram divididos em cinco grupos, correspondentes a diferentes fabricantes (DEN, Dentaurum; RMO, Rocky Mountain Orthodontics; CON, Conexão; NEO, Neodent; SIN, Sistema de Implantes Nacional). Vinte e cinco mini-implantes foram submetidos ao teste de fratura por torção no pescoço e na ponta, com mandris fixados a uma máquina universal de testes mecânicos. Os outros 25 mini-implantes foram submetidos ao teste de torque de inserção em blocos de costelas suínas, utilizando- -se um torquímetro e um contra-ângulo montado em motor cirúrgico. O formato da ponta ativa dos mini-implantes foi avaliado por microscopia. O teste não-paramétrico de Friedman e o teste F de Snedecor na análise de variância (ANOVA) foram utilizados para avaliar as diferenças entre os grupos. Resultados: o torque de fratura do pescoço variou de 23,45 N. cm (DEN) a 34,82 N.cm (SIN); e o da ponta, entre 9,35 N.cm (CON) e 24,36 N.cm (NEO). O valor do torque de inserção variou de 6,6 N.cm (RMO) a 10,2 N.cm (NEO). As características que mais influenciaram os resultados foram: diâmetro externo, diâmetro interno, razão entre o diâmetro interno e o externo, e a presença de fresagem na região apical do mini- -implante. Conclusões: os torques de fratura foram diferentes entre os cinco tipos avaliados, tanto no pescoço quanto na ponta. Os mini-implantes NEO e SIN foram os mais resistentes à fratura do pescoço e da ponta. Os torques de fratura tanto na ponta quanto no pescoço foram maiores do que o torque necessário para a inserção dos mini-implantes. Palavras-chave: Ortodontia. Ancoragem óssea. Mini-implante. Materiais dentários.

Upload: dinhtuyen

Post on 28-Aug-2018

213 views

Category:

Documents


0 download

TRANSCRIPT

Page 1: Fracture strength of orthodontic mini-implants - … · 2017 Dental Press ournal of Orthodontics 47 Dental Press Orthod. 2017 Maune22(3)4754 original article Fracture strength of

© 2017 Dental Press Journal of Orthodontics Dental Press J Orthod. 2017 May-June;22(3):47-5447

original article

Fracture strength of orthodontic mini-implants

Tatiana Feres Assad-Loss1, Flávia Mitiko Fernandes Kitahara-Céia1, Giordani Santos Silveira1, Carlos Nelson Elias2, José Nelson Mucha1

Objective: This study aimed at evaluating the design and dimensions of five different brands of orthodontic mini-implants, as well as their influence on torsional fracture strength. Methods: Fifty mini-implants were divided into five groups corresponding to different manufactures (DEN, RMO, CON, NEO, SIN). Twenty-five mini-implants were subjected to fracture test by torsion in the neck and the tip, through arbors attached to a Universal Mechanical Testing Machine. The other 25 mini-implants were subjected to insertion torque test into blocks of pork ribs using a torquimeter and contra-angle handpiece mounted in a surgical motor. The shape of the active tip of the mini-implants was evaluated under microscopy. The non-parametric Friedman test and Snedecor’s F in analysis of variance (ANOVA) were used to evaluate the differences between groups. Results: The fracture torque of the neck ranged from 23.45 N.cm (DEN) to 34.82 N.cm (SIN), and of the tip ranged from 9.35 N.cm (CON) to 24.36 N.cm (NEO). Insertion torque values ranged from 6.6 N.cm (RMO) to 10.2 N.cm (NEO). The characteristics that most influenced the results were outer diameter, inner diameter, the ratio between internal and external diameters, and the existence of milling in the apical region of the mini-implant. Conclusions: The fracture torques were different for both the neck and the tip of the five types evaluated. NEO and SIN mini-implants showed the highest resistance to fracture of the neck and tip. The fracture torques of both tip and neck were higher than the torque required to insert mini-implants.

Keywords: Orthodontics. Skeletal anchorage. TADs. Mini-implant. Dental materials.

1 Universidade Federal Fluminense, Department of Orthodontics (Niterói/RJ, Brazil).

2 Instituto Militar de Engenharia, Materials Engineering, Biomaterials Laboratory, Rio de Janeiro, RJ, Brazil.

Contact address: Giordani Santos SilveiraAv. Antônio Abrahão Caran, 820, sala 607, São José – Belo Horizonte/MG, Brasil CEP: 31.275-000 – E-mail: [email protected]

DOI: https://doi.org/10.1590/2177-6709.22.3.047-054.oar

How to cite this article: Assad-Loss TF, Kitahara-Céia FMF, Silveira GS, Elias  CN, Mucha JN. Fracture strength of orthodontic mini-implants. Dental Press J Orthod. 2017 May-June;22(3):47-54. DOI: https://doi.org/10.1590/2177-6709.22.3.047-054.oar

Submitted: April 26, 2016 - Revised and accepted: December 01, 2016

» The authors report no commercial, proprietary or financial interest in the products or companies described in this article.

Objetivo: o objetivo do presente estudo foi avaliar o desenho e as medidas de cinco marcas diferentes de mini-implantes ortodônticos, e sua influência na resistência à fratura em torção. Métodos: cinquenta mini-implantes foram divididos em cinco grupos, correspondentes a diferentes fabricantes (DEN, Dentaurum; RMO, Rocky Mountain Orthodontics; CON, Conexão; NEO, Neodent; SIN, Sistema de Implantes Nacional). Vinte e cinco mini-implantes foram submetidos ao teste de fratura por torção no pescoço e na ponta, com mandris fixados a uma máquina universal de testes mecânicos. Os outros 25 mini-implantes foram submetidos ao teste de torque de inserção em blocos de costelas suínas, utilizando--se um torquímetro e um contra-ângulo montado em motor cirúrgico. O formato da ponta ativa dos mini-implantes foi avaliado por microscopia. O teste não-paramétrico de Friedman e o teste F de Snedecor na análise de variância (ANOVA) foram utilizados para avaliar as diferenças entre os grupos. Resultados: o torque de fratura do pescoço variou de 23,45 N.cm (DEN) a 34,82 N.cm (SIN); e o da ponta, entre 9,35 N.cm (CON) e 24,36 N.cm (NEO). O valor do torque de inserção variou de 6,6 N.cm (RMO) a 10,2 N.cm (NEO). As características que mais influenciaram os resultados foram: diâmetro externo, diâmetro interno, razão entre o diâmetro interno e o externo, e a presença de fresagem na região apical do mini--implante. Conclusões: os torques de fratura foram diferentes entre os cinco tipos avaliados, tanto no pescoço quanto na ponta. Os mini-implantes NEO e SIN foram os mais resistentes à fratura do pescoço e da ponta. Os torques de fratura tanto na ponta quanto no pescoço foram maiores do que o torque necessário para a inserção dos mini-implantes.

Palavras-chave: Ortodontia. Ancoragem óssea. Mini-implante. Materiais dentários.

Page 2: Fracture strength of orthodontic mini-implants - … · 2017 Dental Press ournal of Orthodontics 47 Dental Press Orthod. 2017 Maune22(3)4754 original article Fracture strength of

© 2017 Dental Press Journal of Orthodontics Dental Press J Orthod. 2017 May-June;22(3):47-5448

Fracture strength of orthodontic mini-implantsoriginal article

INTRODUCTIONMini-implants have been an effective anchorage

method,1 being very well tolerated by patients,2 creat-ing new possibilities for orthodontic treatment that requires minimal cooperation and maximum aesthet-ics results, particularly in adults.3 Unlike osseointe-grated dental implants made of commercially pure ti-tanium, mini-implants are manufactured with the al-loy Ti6Al4V (ASTM grade 5).4,5 This alloy has higher mechanical strength than pure titanium6 and it is best suited to the small diameter of mini-implants. It also presents bioactive characteristics inferior to pure tita-nium, thus facilitating removal because it promotes lower osseointegration.4,5

The mini-implant installation is simple, and it can be inserted in various sites because of its reduced size,1,7,8 including those between the roots of teeth using mono or bicortical anchor,9 alone or connected by an inter-changeable structure.10 On the other hand, the small size of mini-implants empowers an increase of fracture during insertion, deformation or fracture during its re-moval.4 Bicortical anchorage adds a new challenge to the fracture resistance of orthodontic mini-implants especially in the tip region, which has a smaller diam-eter. Another risk of fracture could occur when mini-implants are placed in the external oblique ridge area of the mandible because of the thickness and hardness of the cortical bone in this area.10

Mini-implants can be found in the market with different shapes, designs, diameters, lengths, degree of

titanium alloy purity and surface treatments.5 How-ever, mini-implants with similar dimensions have different design that may influence the fracture resis-tance and are relied upon by the various manufactur-ers to improve clinical performance.6,11 The  fracture resistance of the mini-implants is a decisive aspect to assist the clinician in choosing the most appropriate and safe device.

Therefore, the main objective of this study was to evaluate the design, to measure the insertion torque and to quantify the maximum fracture torque resistance of five different orthodontic mini-implants.

MATERIAL AND METHODSFifty orthodontic self-perforating mini-implants

from five different manufacturers (DEN: Dentaurum, Ispringen, Baden-Württemberg, Germany; RMO: Rocky Mountain Orthodontics, Seoul, South Ko-rea; CON: Conexão, Arujá, São Paulo, Brazil; NEO: Neodent, Curitiba, Paraná, Brazil; and SIN: Sistema de Implantes Nacional, São Paulo, São Paulo, Brazil) simi-lar in size dimension, were divided into five groups, as shown in Tables 1 and 2.

The surface morphology and chemical composition of the mini-implants in each group was analyzed by scanning electron microscope (SEM; Jeol JSM-5800LV) at 20kV and observed at 500x magnification and 50 μm away, by energy dispersive spectroscopy  (EDS). Fig-ure  1 illustrates SEM microphotographs of the mini-implants for each group.

GroupsApical

millingTrade name

Manufacturer

and lotOrigin

Chemical

composition

Diameter

(mm)

Length

(mm)

Profile

(mm)

DEN YesTomas

Ref 302-106-10

Dentaurum

394727Ispringen, Germany Ti

6Al

4V 1.6 6 ND*

RMO Yes

Dual-top Anchor

System

Ref Goo213

Rocky Mountain

Orthodontics

022367

Seoul, South Korea Ti6Al

4V 1.6 6 ND*

CON YesOrtoimplante

Ref P9900099

Conexão

8081468146

Arujá, SP

BrazilTi

6Al

4V 1.5 6 1

NEO No

Implante Ancora-

gem Ortodôntica

Ref 109496

Neodent 2788897 Curitiba PR, Brazil Ti6Al

4V 1.6 7 1

SIN NoWire Dynamic

Ref POTC 1616

SIN – Sistema de

Implantes Nacional

F60556

São Paulo SP, Brazil Ti6Al

4V 1.6 6 1

Table 1 - Groups code, milling in the apical region, trade name, manufacturer, source, chemical composition, nominal diameter, length and transmucosal profile of mini-implants used in the study.

*ND = Not disclosed.

Page 3: Fracture strength of orthodontic mini-implants - … · 2017 Dental Press ournal of Orthodontics 47 Dental Press Orthod. 2017 Maune22(3)4754 original article Fracture strength of

© 2017 Dental Press Journal of Orthodontics Dental Press J Orthod. 2017 May-June;22(3):47-5449

original articleAssad-Loss TF, Kitahara-Céia FMF, Silveira GS, Elias CN, Mucha JN

Figure 1 - Microphotograph illustrating the superficial aspects and superficial finish quality of five types of mini-implants used (DEN, RMO, CON, NEO, SIN).

Figure 2 - Linear measurements made in pictures of the mini-implants in opti-cal microscope with an increase of 1.6 x. Pitch of the threads (a), total length or active tip of the mini-implant (b), the external diameter of mini-implant (c), steps for calculating the taper of the mini-implant (d), and internal diameter of the mini-implant (d’).

Figure 3 - Linear and angular measurements made in pictures of the mini-implants in optical microscope with an magnification of 1.6 x. Angle of the screw thread (e), the free length of thread (f), and the length of the bottom fillet of the thread (g) of the screw thread pitch (h).

Mini-implants design evaluationPictures of the mini-implants were obtained under

optical microscope (Zeiss Stemi 2000-C, Zeiss) ob-served at 1.6 x magnification. The pictures of the sur-faces were analyzed with Axio Vision program (Zeiss) which were made of linear and angular measurements, as shown in Figures 2 and 3.

Mini-implant insertion torqueSix frozen pig ribs, from the same animal, were pre-

pared to be used as material for insertion of the mini-implants. After slaughter, the ribs were cleaned to re-move tissue and stored in normal saline at 4°C for 24 hours. Then, they were cut transversely to obtain 60 bone blocks of 2 x 2 cm and stored again in physiologi-cal saline at 4°C until assay insertion occurred between the first and the third day.

Table 2 - Values of linear measurements (µm) and angle (degrees) of mini-implants.

Feature evaluatedGroups

DEN RMO CON NEO SIN

Length of tip 6.006,01 5,329.59 5,926.47 6,812.51 6,090.93

Outside diameter 1.607,96 1,539.77 1,482.95 1,630.72 1,562.59

Inside diameter 1.079,55 1,028.42 772.75 1,107.97 1,164.77

Number of threads 6 7 12 9 7

Step of threads 888,09 735.39 464.49 732.32 756.49

Angle of the screw thread (degrees) 140,22 137.69 128.85 135.31 128.46

Length of the thread franc 381,96 384.78 232.11 360.58 292.79

Length from the bottom of the screw thread 395,63 327.65 239.77 323.86 376.89

Taper (ratio= b-a/2xD) 0,11 0.07 0.09 0.1 0.1

Percentage between diameters 67% 67% 52% 68% 75%

Page 4: Fracture strength of orthodontic mini-implants - … · 2017 Dental Press ournal of Orthodontics 47 Dental Press Orthod. 2017 Maune22(3)4754 original article Fracture strength of

© 2017 Dental Press Journal of Orthodontics Dental Press J Orthod. 2017 May-June;22(3):47-5450

Fracture strength of orthodontic mini-implantsoriginal article

Each pork rib bone block was randomly picked among the 60 bone blocks and was attached to an ad-justable piece of metal, for size and shape standardiza-tion. This piece of metal was attached to the digital torque meter (Lutron TQ-8800 torque meter) con-nected to a computer and pre set to prevent any move-ment during the test.

Tests on insertion of the mini-implant were carried out without performing any preliminary drilling, using the mini-implant coupled to the switch for short contra angle for each specific group of mini-implants, fitted to a hand piece with reduced speed (20:1) at 50 rpm (An-thogyr Instruments) with MC -101 surgical drill, and Omega II Dentscler motor. Each mini-implant was in-serted in the block located in the central portion of pork ribs perpendicular to the cortical bone (Fig 4).

The same calibrated operator performed the whole as-say. Initial tests were undertaken to verify the procedure and to maintain the strength standardized in relation to the long axis of the mini-implant. The insertion torques were recorded continuously by the Lutron 101 program, version V0011TW (Lutron Electronic Enterprise).

Maximum and minimum insertion torque values were considered as the largest and the smallest values, respectively. Each bone block, properly identified, was taken to the Optical Zeiss Stemi 2000-C Microscope (Zeiss) with 1.6x and 5x magnification for measurement

of cortical thickness of the bone at the site of insertion of the mini-implant. The images were captured in the cortical computer and sent to the Axio Vision program (Zeiss) where their thicknesses were measured.

MINI-IMPLANT FRACTURE TORQUEFive mini-implants in each group (DEN: Dentau-

rum, RMO: Rocky Mountain Orthodontics, CON: Conexão, NEO: Neodent; SIN: Sistema de Implantes Nacional) were submitted to fracture torsion testing. The maximum torque fracture was determined in the lower third of the active tip (tip) and the upper third of the active tip (neck). For this test, a device with two mandrels coupled to universal mechanical testing ma-chine (EMIC) with a 500N load cell was used.

In the fracture test, the key for short contra-angle surgical kit, specific for each group coupled to the head of the mini-implant, was attached to the mandrel, and the other mandrel was attached to the other end of the mini-implant. The left mandrel rotated by traction of a polymer strand attached to the shaft of the testing device and the load cell, thereby applying a torque on the mini-implant, once the right mandrel was fixed.

In the first mechanical testing, the fracture torque of the mini-implant tip was measured. In the second frac-ture testing, the maximum fracture torque of the region close to the neck was determined.

Figure 4 - Mini-implant position in pork rib (A) and cortical bone thickness of pork rib block used in the insertion test of mini-implants (B).

A B

Page 5: Fracture strength of orthodontic mini-implants - … · 2017 Dental Press ournal of Orthodontics 47 Dental Press Orthod. 2017 Maune22(3)4754 original article Fracture strength of

© 2017 Dental Press Journal of Orthodontics Dental Press J Orthod. 2017 May-June;22(3):47-5451

original articleAssad-Loss TF, Kitahara-Céia FMF, Silveira GS, Elias CN, Mucha JN

In order to calculate the fracture torque (N.cm) the maximum force was obtained from records of the Uni-versal Mechanical Testing Machine (EMIC), based on the following formula: T = F x 0.4, where T = Torque (N.cm), F = Force (N), and 0.4 cm is the radius of the shaft on which the polymer strand was wound.

STATISTICAL ANALYSISThe numerical results were presented as means and

standard deviations. The non-parametric Friedman test was used to assess torque values of fracture of the tip and the neck of the mini-implant. Snedecor’s F in analysis of variance (ANOVA) was used to evaluate the inser-tion torque and the thickness of cortical bone. The data obtained from all measurements were processed with SPSS software, version 13.0 (IBM, Chicago, Illinois, USA). The level of significance for all statistical tests was predetermined at 1%.

RESULTSTable 2 presents the results of mini-implants de-

sign and the measures corresponding to the length of tip, outer diameter, inner diameter, and the number of threads (Figs 2 and 3).The bone material used for the test was the pork rib, which has been used in other studies, as the thickness of cortical bone is similar to that found in the human jaw, around 0.5 to 1.0 mm.12 In this study the cortical thickness of the pork rib blocks showed a thickness average from 1.30 to 1.52 mm and no significant difference among groups was determined (Table 3). Therefore, it can be assumed that the bone material used to insert the mini-implants did not influ-ence the results. The average and standard deviations of the torque during insertion in the five groups and the average values and standard deviations for the thickness of the cortical bone blocks used as material for insertion were calculated (Table 3).

GroupsInsertion Cortical thickness

Mean ± SD F test, p Mean ± SD F test, p

DEN 7.80 ± 1.30AB

F = 4.66

p = 0.008*

1.52 ± 0.38

F = 0.43

p = 0.786 ns

NEO 10.20 ± 0.84A 1.50 ± 0.17

SIN 8.20 ± 1.79AB 1.30 ± 0.35

CON 7.40 ± 1.34B 1.30 ± 0.25

RMO 6.60 ± 1.52B 1.47 ± 0.56

Table 3 - Means and standard deviations (SD) of the insertion torque (N.cm) and cortical bone thickness (mm), Snedecor’s F test in ANOVA.

Table 4 - Means and standard deviations (SD) of fracture torque (N.cm) in the neck and tip of the five groups, tested with Snedecor’s F in ANOVA and XR2 non-parametric “Friedman” for comparison between groups (p < 0.01).

Same letters: no difference. Different letters: significant differences.* = Significant (p < 0.01) NEO X CON, p = 0.015, NEO x RMO, p = 0.013.ns = Non significant (p > 0.01).

Same letters: no difference. Different letters: significant differences.* = Significant (p < 0.01) DEN X SIN, p = 0.014, NEO x SIN, p = 0.011.ns = Non significant (p > 0.01).

Site

Groups NECK TIP

Mean SD Test Sig. Mean SD Test Sig.

DEN 23.45 A 3.08

F= 9.04 0

10.56 A 5.12

Xr2= 17.53 0.002

NEO 27.28 A 0.98 24.36 B 2.58

SIN 34.82 B 3.5 22.88 B 2.98

CON 25.70 A 5.01 9.35 A 3.22

RMO 32.41 AB 3.5 21.95 B 2.79

Page 6: Fracture strength of orthodontic mini-implants - … · 2017 Dental Press ournal of Orthodontics 47 Dental Press Orthod. 2017 Maune22(3)4754 original article Fracture strength of

© 2017 Dental Press Journal of Orthodontics Dental Press J Orthod. 2017 May-June;22(3):47-5452

Fracture strength of orthodontic mini-implantsoriginal article

The torque values of fracture on the neck region were higher than the torque values to obtain a fracture in the region of the tip in all groups (Table 4).

DISCUSSIONThe mini-implants diameter showed a variation

from 1,630.72 µm (NEO) to 1,482.95 µm (CON). The CON group, besides having the smallest diam-eter, also showed a lower torque value of fracture of the tip (9.35 N.cm) and the second lowest value of fracture torque on the neck (25.7 N.cm). A similar result was observed in mini-implants with a diameter less than 1.5 mm, which were more susceptible to fracture.13,14,15

The torque values of fracture on the neck and the tip region could indicate that the diameter of the frac-ture site is an important variable in fracture torque, because the small-diameter mini-implant is an impor-tant risk factor for fractures, especially in insertion or removal time.1,4,8,14,15,16,17 Although mini-implants with a reduced diameter have increased risk of fracture, the choice of mini-implants with a diameter that is too large can lead to bone necrosis through micro fractures in bone, and dental structures risks.15,16

In relation to the tip region, the lowest torque value of fracture was found in the CON group (9.35 N.cm), which was statistically significant (p <0.01) compared with the NEO (24.36 N.cm), SIN (22.88 N.cm), and RMO (21.95 N.cm) groups. These differences may be a consequence of the great difference among them in shape, in ratio of external to internal diameter and in the num-ber of threads, and consequently, in the step of threads.18

CON group presented the second lowest value of fracture torque in the neck (25.7 N.cm), and it is sta-tistically significant (p < 0.01) when compared with SIN (34.82 N.cm), which showed highest value of fracture torque. Additionally, when the internal di-ameter of mini-implant between these two groups was compared, great variation was found. The CON group exhibited the lowest mean (772.75 µm), while the SIN group presented the highest (1164.77 µm). The  inner diameter of the mini-implant is an important charac-teristic of susceptibility to fracture.19

Furthermore, the mini-implants in the CON group also showed the smallest external diameter (1482.95 µm), and a greater number of threads.7

The taper of CON group was smaller, which means it was a cylinder mini-implant. Mini-conical

implants would be most suitable because it could have the thickness thinner and a diameter more re-sistant immediately below the point of loading ap-plication.20 However, fractures occur less frequently during application of orthodontic force and more often during insertion or removal of the mini-im-plants.8 In the present study, the tip region was the most susceptible area to fracture.

The results showed that SIN and NEO exhibited the highest mean fracture resistance as referred else-where.21 The lower fracture torque on the neck was found in DEN (23.45 N.cm). In the tip region, the DEN presented the second lowest value of fracture torque (10.56 N.cm). Possibly this was due to differenc-es in relation to the steps of thread and taper. The DEN group had means values of thread steps and taper larger than the other groups, contradicting the fact that frac-ture strength can be increased with the conical design.22

The lowest torque fracture values was shown in the tip region of CON and DEN groups and were also the groups that had the apical milling. The presence of this lateral groove reduces the in-ternal diameter of the narrower region of the mini-implants which probably increased the fracture sus-ceptibility at the tip, which would justify the lower values of fracture torque found in these groups.

Mini-implants of these five groups were made with the Ti6Al4V alloy, as perceived by energy dispersive spectroscopy. However, the strength of the titanium alloy depends also on the microstructure, which is in-fluenced by the composition, heating treatment, and thermo-mechanical processing of the mini-implants.6 These variables must be evaluated in further studies.

The insertion torques ranged from 6.6 N.cm (RMO) to 10.2 N.cm (NEO). All groups had val-ues that were within the recommended bound-ary24,28 between 5 and 10 N.cm, and the values of insertion torque could reach 15N.cm without ma-jor problems. All fracture torque resistance were higher than the insertion torque values in both the fracture tip region and the neck in all groups, showing that all mini-implants tested can be con-sidered safe from the risk of fracture in clinical use. The insertion values showed significant differ-ences among NEO (10.2 N.cm), CON (7.4 N.cm) and RMO  (6.6 N.cm). The difference in insertion torque among the groups was possibly due to the

Page 7: Fracture strength of orthodontic mini-implants - … · 2017 Dental Press ournal of Orthodontics 47 Dental Press Orthod. 2017 Maune22(3)4754 original article Fracture strength of

© 2017 Dental Press Journal of Orthodontics Dental Press J Orthod. 2017 May-June;22(3):47-5453

original articleAssad-Loss TF, Kitahara-Céia FMF, Silveira GS, Elias CN, Mucha JN

difference in design among the mini-implants. The mini-implants designs showed a large difference be-tween them in relation to the number of threads of screws, and consequently the pitch of the thread.

The NEO group had the second highest number of threads (n = 9) and was the group with the high-est insertion torque (10.20 N.cm). As the retention mechanism is based on fitting mechanical structure in cortical and not necessarily the concept of os-seointegration,4,5 the shape and length of the screw threads are fundamental to primary stability.20,22,25 Greater number of threads and closeness between them increase the mechanical stability and resis-tance in the insertion in the bone.5 However, there were significant differences between NEO and CON groups, which had the largest number of threads,7 and the second lowest value of insertion torque (7.4 N.cm). This result was probably due to the difference in diameter between these two groups. The diam-eter is significantly associated with stability.16 NEO and CON groups showed the highest (1,630.72 µm) and lowest (1,482.95 µm) outer diameter, respec-tively, among all groups. The outer diameter appears to be an important feature of variation of the inser-tion torque.26 NEO group, with the largest diame-ter (1,630.72 µm), had the highest value of insertion torque (10.20 N.cm), and RMO and CON groups, with smaller diameters, showed the lowest values.

During the insertion, control features should be used such as micro-motor with controlled torque,13 manual wrench1 or dynanometer27 to prevent this torque from approaching or reaching the fracture torque of mini-implants. Fracture toughness of mini-implants varies according to the manufacturer and type of mini-implant, so the operator should be aware of the characteristics of mini-implants that in-fluence the torque values of fracture before choosing one to be used, and the maximum torque that can safely be used clinically for the insertion.18

CONCLUSIONSMini-implants of different brands have different

design and morphology, and fracture torques resis-tance is determined by: outside diameter, internal diameter, ratio of inner and outer diameter, and milling in the apical region.

Among the mini-implants trademark evaluat-ed, NEO and SIN mini-implants have showed the highest resistance to fracture of the neck and tip.

The insertion values torques was always lower than the fracture torque resistance of both the tip and the neck in all groups tested.

Authors’ contributionConception/design of the study: TFAL, JNM.

Data acquisition, analysis or interpretation: TFAL, FMFKC, CNE. Writing of the article: TFAL, FMFKC, GSS. Critical revision of the article: GSS, CNE, JNM. Final approval of the article: GSS, JNM.

Page 8: Fracture strength of orthodontic mini-implants - … · 2017 Dental Press ournal of Orthodontics 47 Dental Press Orthod. 2017 Maune22(3)4754 original article Fracture strength of

© 2017 Dental Press Journal of Orthodontics Dental Press J Orthod. 2017 May-June;22(3):47-5454

Fracture strength of orthodontic mini-implantsoriginal article

1. Brandão LBC, Mucha JN. Grau de aceitação de mini-implantes por

pacientes em tratamento ortodôntico – estudo preliminar. Rev Dental

Press Ortod Ortop Facial. 2008 Set-Out;13(5):118-27.

2. Elias CN, Guimarães GS, Muller CA. Torque de inserção e de remoção de

miniparafusos ortodônticos. Rev Bras Implant. 2005;11(3):5-8.

3. Mah J, Bergstrand F. Temporary anchorage devices: a status report. J Clin

Orthod. 2005 Mar;39(3):132-6.

4. Araújo TM, Nascimento MHA, Bezerra F, Sobral M. C. Ancoragem

esquelética em Ortodontia com mini-implantes. Rev Dental Press Ortod

Ortop Facial. 2006 Jul-Ago;11(4):126-56.

5. Park YC, Choi YJ, Choi NC, Lee JS. Esthetic segmental retraction of

maxillary anterior teeth with a palatal appliance and orthodontic mini-

implants. Am J Orthod Dentofacial Orthop. 2007 Apr;131(4):537-44.

6. Wilmes B, Rademacher C, Olthoff G, Drescher D. Parameters affecting

primary stability of orthodontic mini-implants. J Orofac Orthop. 2006

May;67(3):162-74.

7. Kuroda S, Sugawara Y, Tamamura N, Takano-Yamamoto T. Anterior

open bite with temporomandibular disorder treated with titanium screw

anchorage: evaluation of morphological and functional improvement.

Am J Orthod Dentofacial Orthop. 2007 Apr;131(4):550-60.

8. Morarend C, Qian F, Marshall SD, Southard KA, Grosland NM, Morgan TA,

et al. Effect of screw diameter on orthodontic skeletal anchorage. Am J

Orthod Dentofacial Orthop. 2009 Aug;136(2):224-9.

9. Iijima M, Muguruma T, Brantley WA, Okayama M, Yuasa T, Mizoguchi I.

Torsional properties and microstructures of miniscrew implants. Am J

Orthod Dentofacial Orthop. 2008 Sept;134(3):333.e1-6.

10. Itsuki Y, Imamura E, Sugawara J. Temporary anchorage device with

interchangeable superstructure for mandibular tooth movement. J World

Fed Orthod. 2013;2(1):e19-29.

11. Kitahara-Ceia FMF, Assad-Loss TF, Mucha JN, Elias CN. Morphological

evaluation of five active types of six types of orthodontic mini-implants.

Dental Press J Orthod. 2013 Mar-Apr;18(2):36-41.

12. Kim JH, Ahn SJ, Chang YI. Histomorfometric and mechanical analyses of

the drill free screw as orthodontic anchorage. Am J Orthod Dentofacial

Orthop. 2005 Aug;128(2):190-4.

13. Miyawaki S, Koyama I, Inoue M, Mishima K, Sugahara T,

Takano-Yamamoto T. Factors associated with the stability of titanium

screws placed in the posterior region for orthodontic anchorage. Am J

Orthod Dentofacial Orthop. 2003 Oct;124(4):373-8.

14. Nova MFP, Carvalho FR, Elias CN, Artese F. Avaliação do torque de

inserção, remoção e fratura de diferentes mini-implantes ortodônticos.

Rev Dent Press Ortod Ortop Facial. 2008 Set-Oct;13(5):76-87.

REFERENCES

15. Hong SB, Kusnoto B, Kim EJ, BeGole EA, Hwang HS, Lim HJ. Prognostic

factors associated with the success rates of posterior orthodontic miniscrew

implants: a subgroup meta-analysis. Korean J Orthod. 2016 Mar;46(2):111-26.

16. Melsen B, Verna C. Miniscrew implants: the Aarhus anchorage system.

Semin Orthod. 2005 Mar;11(1):24-31.

17. Barros SE, Janson G, Chiqueto K, Garib DG, Janson M. Effect of mini-

implant diameter on fracture risk and self-drilling efficacy. Am J Orthod

Dentofacial Orthop. 2011 Oct;140(4):e181-92.

18. Smith A, Hosein YK, Dunning CE, Tassi A. Fracture resistance of commonly

used self-drilling orthodontic mini-implants. Angle Orthod. 2015

Jan;85(1):26-32.

19. Squeff LR, Simonson MBA, Elias CN, Nojima LI. Caracterização de

miniimplantes utilizados na ancoragem ortodôntica. Rev Dent Press Ortod

Ortop Facial. 2008 Set-Out;13(5):49-56.

20. Freire JN, Silva NR, Gil JN, Magini RS, Coelho PG. Histomorphologic and

histomophometric evaluation of immediately and early loaded miniimplants

for orthodontic anchorage. Am J Orthod Dentofacial Orthop. 2007

June;131(6):704.e1-9.

21. Consolaro A, Sant´Anna E, Francischone Jr CE, Consolaro MFM,

Barbosa BA. Mini-implantes: pontos consensuais e questionamentos sobre o

seu uso clínico. Rev Dent Press Ortod Ortop Facial. 2008 Set-Out;13(5):20-9.

22. Motoyoshi M, Hirabayashi M, Uemura M, Shimizu N. Recommended

placement torque when tightening an orthodontic mini-implant. Clin Oral

Implants Res. 2006 Feb;17(1):109-14.

23. Pithon MM, Santos RL, Derech CD, Elias CN, Ruellas ACO, Nojima LI. In vitro

evaluation of torsional strength of orthodontic mini-implants. Braz J Oral Sci.

2008 Apr-June;7(25):1563-5.

24. Herman RJ, Currier GF, Miyakec A. Mini-implant anchorage for maxillary

canine retraction: A pilot study. Am J Orthod Dentofacial Orthop. 2006

Aug;130(2):228-35.

25. Morais LS, Serra GG, Muller CA, Andrade LR, Palermo EFA, Elias CN, et al.

Titanium alloy mini-implants for orthodontic anchorage: Immediate loading

and metal ion release. Acta Biomater. 2007 May;3(3):331-9.

26. Wilmes B, Ottenstreuer S, Su Y, Drescher D. Impact of implant design on

primary stability of orthodontic mini-implants. J Orofac Orthop. 2008

Jan;69(1):42-50.

27. Kyung HM, Park HS, Bae SM, Sung JH, Kim IB. Development of

orthodontic microimplants for intraoral anchorage. J Clin Orthod. 2003

June;37(6):321-8.

28. Papageorgiou SN, Zogakis IP, Papadopoulos MA. Failure rates and associated

risk factors of orthodontic miniscrew implants: a meta-analysis. Am J

Orthod Dentofacial Orthop. 2012 Nov;142(5):577-95.