API Spec 6A Tensile Test Spec Reference Requirements

Tim HaeberleAPI SC6 2012 Summer Meeting

2GE Confidential and Proprietary Information

GEÓ2010 All Rights Reserved

Background

CURRENT WORDING• 5.3.5.2 PSL 2 to 4 tensile testing (for mandrel tubing hangers

and casing hangers)

“b) test method:

Perform tensile tests at room temperature in accordance with the procedures specified in ISO 6892-1 or ASTM A370.

Perform a minimum of one tensile test. The results of the tensile test(s) shall satisfy the manufacturer’s specified requirements.”

• 5.4.2.3 PSL 2 to 4 tensile testing (for bodies, bonnets, and end and outlet connections)

“b) test method:

Perform tensile tests at room temperature in accordance with the procedures specified in ISO 6892-1 or ASTM A370.

Perform a minimum of one tensile test. The results of the tensile test(s) shall satisfy the applicable requirements of Table 6.”



BackgroundCURRENT WORDING• Section 5.6.4.1 (for TC’s for PSL 1)

Paragraph 5 - “Standard-sized, 12,5 mm (0,500 in) diameter tensile specimens shall be used to qualify carbon, low-alloy and stainless steels, unless the physical configuration of the TC prevents their use. In this case, the standard sub-size specimens referenced in ASTM A370 may be used. Either standard 12,7 mm (0,500 in) or standard sub-size specimens (see ASTM A370) may be used to qualify CRA materials.”

• Section 5.7.4.1 (for QTC’s for PSL 2-4)Paragraph 6 - “Standard-sized, 12,5 mm (0,500 in) diameter tensile specimens shall be used, unless the physical configuration of the QTC prevents their use. In this case, the standard sub-size specimens referenced in ASTM A370 may be used.”

PROBLEM: • These paragraphs do not state that the “standard” specimens are

ASTM A370 standard-sized specimens. This leaves open the use of ISO 6892-1 standard specimens. Additionally, they refer to the “standard sub-size specimens”, but the correct term in ASTM A370 is “small-size specimens”.



The Solution

PROPOSED REVISIONS: •Section 5.6.4.1

Paragraph 5 - “ASTM A370 standard-sized, 12,5 mm (0,500 in) diameter tensile specimens shall be used to qualify carbon, low-alloy and stainless steels, unless the physical configuration of the TC prevents their use. In this case, the standard sub-size specimens referenced in ASTM A370 may be used. Either standard 12,5 mm (0,500 in) or standard sub-size specimens (see ASTM A370) may be used to qualify CRA materials.”•Section 5.7.4.1

Paragraph 6 - “ASTM A370 standard-sized, 12,5 mm (0,500 in) diameter tensile specimens shall be used, unless the physical configuration of the QTC prevents their use. In this case, the standard sub-size specimens referenced in ASTM A370 may be used.”



The SolutionJUSTIFICATION:• “ASTM A370” needs to be added to clarify that the only

specimen sizes currently permitted are the ASTM A370 specimen sizes.

• ISO 6892-1 includes different size specimens that have a higher gage length to diameter ratio.

• The longer relative gage length of the ISO 6892-1 specimens can result in failure to meet the API 6A specified elongation acceptance criteria.

• The use of ASTM A370 specimen sizes meets ISO 6892-1, since ISO 6892-1, section 6.1.1, paragraphs 7 and 8 state:“The dimensional tolerances of the test pieces shall be in accordance with the Annexes B to E (see 6.2).” Other test pieces such as those specified in relevant product standards or national standards may be used by agreement with the customer, e.g. ISO 3183 [1] (API 5L), ISO 11960 [2] (API 5CT), ASTM A370 [6], ASTM E8M [7], DIN 50125 [10], IACS W2 [13], and JIS Z2201 [14]”.

• ASTM A370 specimen sizes are routinely used in the US and Europe.

6

API Ballot

• Ballot ready for SC6 to approve at the 2012 Summer Meeting for formal balloting



End Of Presentation



Backup Slides



ISO 6892-1 Circular Test Specimens